CN113526876A - Method for manufacturing glass with ice slush effect - Google Patents
Method for manufacturing glass with ice slush effect Download PDFInfo
- Publication number
- CN113526876A CN113526876A CN202010300713.5A CN202010300713A CN113526876A CN 113526876 A CN113526876 A CN 113526876A CN 202010300713 A CN202010300713 A CN 202010300713A CN 113526876 A CN113526876 A CN 113526876A
- Authority
- CN
- China
- Prior art keywords
- glass
- effect
- slush
- etching
- original sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of etched glass, and particularly discloses a method for manufacturing glass with a slush effect, which comprises the following steps: preparing a glass etching solution; covering and protecting the surface of the glass original sheet which does not need to be etched by using an instant protective film; cleaning one surface of the glass original sheet needing the etching of the ice effect with deionized water, soaking the glass original sheet in an etching solution for 5-10 minutes in a wet state, and taking out the glass original sheet to obtain etched glass; the invention has simple and practical process, easy operation and low cost, the particles on the surface of the prepared slush effect glass are uniformly distributed and have consistent size, the technical indexes of roughness, glossiness, light transmittance, haze and the like meet the specific requirements of the art glass industry, and the prepared slush effect glass has excellent decorative and aesthetic effects.
Description
Technical Field
The invention belongs to the technical field of etched glass, and particularly relates to a manufacturing method of glass with a slush effect.
Background
Along with the improvement of the living standard of people, the requirement grade of people on the aspects of furniture decoration, business space partition and the like is also improved, the ice effect glass presents a beautiful, noble and elegant fantasy ice visual effect, the product has excellent performances of anti-reflection light, anti-scratch, anti-dust, anti-fingerprint and the like, can be widely applied to the fields of architectural decoration glass, high-end business space partition, bathing rooms, high-grade furniture, glass wall paintings and the like, greatly enriches the style and variety of the decoration glass, provides more high-grade decoration glass varieties for people, and meets different requirements of people on glass decoration products. At present, the purpose of achieving the glass surface ice slush effect is generally achieved by adopting a decal process in the field of decorative glass production, and the glass ice slush effect achieved by the decal process has artificial drawing and decal marks, so that the whole decorative effect lacks natural inspiration, and the requirement that people tend to be natural and harmonious for decorative products cannot be met.
Disclosure of Invention
The invention aims to provide a method for manufacturing glass with a slush effect, and the glass manufactured by the method has excellent performances of reflection resistance, scratch resistance, dust resistance, fingerprint resistance and the like, and can be widely applied to architectural decoration glass.
In order to achieve the purpose, the invention adopts the technical scheme that:
a method for manufacturing glass with a slush effect comprises the following steps:
1) preparing a glass etching solution;
2) covering and protecting the surface of the glass original sheet which does not need to be etched by using an instant protective film;
3) and cleaning one surface of the glass original sheet needing the etching of the ice effect by using deionized water, soaking the glass original sheet in the etching solution for 5-10 minutes in a wet state, and taking out the glass original sheet to obtain the etched glass.
Further, the glass etching solution is composed of the following raw materials in percentage by mass: NH (NH)4HF2 20-25%、NH4F 8-15%、H2SO4 10-15%、 HNO3 8-15%、CuSO4 3-8%、ZnCL2 3-5%、Na2B4O7•10H20.5-0.8% of O, 4-6% of cane sugar and H2O15-25%, and when in specific preparation, the H is2SO4Slowly adding into water to prevent splashing, cooling to normal temperature, sequentially adding other raw materials, fully stirring to supersaturated state, standing at room temperature, and aging for 24-72 hr.
Further, the etching glass in the step 3) is taken out of the etching solution and then washed by deionized water, and then the etching glass is naturally dried or baked.
Further, the room temperature is 20-25 ℃.
The invention has the advantages that: the invention adopts the immersion etching process to manufacture the slush effect glass, optimizes the components and the content of the formula of the etching solution special for the slush effect glass, mixes the proper surface active substance and the viscosity regulator, and realizes the sodium adjustment through the proper formula proportionEtching the surface of the calcium glass to form a natural slush effect pattern on the surface of the glass, selecting proper etching raw materials to prepare etching solution according to a certain proportion, and carrying out immersion etching treatment on the glass sheet to enable the surface of the glass to present a natural slush fantasy visual effect, so that the slush effect glass product has excellent performances of anti-reflection light, anti-scratch, anti-dust, anti-fingerprint and the like; the fluoride in the formula of the etching solution has an etching effect on glass, the shapes of frosted particles generated by reaction with the surface of the glass in acid solutions with different concentrations and different types are different, the frosted microcrystalline particles formed by complex chemical reaction belong to silicate complex polymers, and different crystal form effects of the frosted microcrystalline particles on the surface of the glass can be realized by adding different types of salt substances, so that the desired etching effect on the surface of the glass is realized2B4O7•10H2O belongs to a surface active substance and aims to promote the etching solution to realize uniform and consistent chemical reaction on the surface of the glass, and the purpose of adding the sucrose is to adjust the viscosity of the etching solution and keep the stability and the suspension effect of the supersaturated etching solution.
Detailed Description
Example 1
1) Preparing a glass etching solution with a slush effect according to the following formula (wt%): NH (NH)4HF2 24.6%、NH4F 12.5%、H2SO4 14.6%、HNO3 11.7%、CuSO4 4.2%、ZnCL2 3.6%、Na2B4O7•10H20.6% of O, 4.8% of cane sugar and H2O23.4%, and mixing with H2SO4Slowly adding the mixture into water to prevent splashing, sequentially adding other raw materials after the solution is uniformly stirred and cooled, fully and uniformly stirring the mixture to form a uniform and stable supersaturated solution state, and standing and curing the supersaturated solution state for 24 to 72 hours to start the etching treatment work of the original glass sheet with the ice effect;
2. covering and protecting the surface of the glass original sheet which does not need to be etched by using an instant protective film;
3. cleaning one surface of the glass original sheet needing the etching of the ice effect with deionized water, and putting the glass original sheet into etching solution in a wet state for soaking type etching treatment;
4. controlling the temperature of the etching solution to be 20-25 ℃, and controlling the soaking etching time to be 5-10 minutes;
5. and after the requirement of the soaking etching time is met, taking out the etched glass from the etching solution in time, cleaning the glass by using deionized water, and air-drying or drying the glass to obtain the glass product with the ice effect.
Example 2
Example 2 differs from example 1 in that: the formulation of the glass etchant in example 2 was as follows: NH (NH)4HF223.5%、NH4F 13.6%、H2SO4 13.3%、HNO3 12.8%、CuSO4 4.3%、ZnCL2 3.5%、 Na2B4O7•10H20.5% of O, 4.9% of cane sugar and H2O 23.6%。
Example 3
Example 3 differs from example 1 in that: the formulation of the glass etchant of example 3 was as follows: NH (NH)4HF2 22.8%、NH4F 13.6%、H2SO4 14.2%、HNO3 13.2%、CuSO4 4.0%、ZnCL2 3.0%、 Na2B4O7•10H20.6% of O, 4.5% of cane sugar and H2O 24.1%。
Performance testing
The properties of the original glass before etching and the etched glass prepared in examples 1 to 3 were measured according to a uniform test method in the glass industry, and the various performance indexes were compared as follows in table 1:
TABLE 1 comparison of the glass flakes with the etched Performance index of the slush Effect
Performance of | Original glass before etching | Example 1 | Example 2 | Example 3 |
Gloss (%) | 110.6 | 30.8 | 31.2 | 31.6 |
Light transmittance (%) | 96.6 | 60.2 | 60.8 | 61.5 |
Haze (%) | 0.08 | 42.7 | 43.6 | 43.8 |
Roughness (μm) | 0 | 3.5 | 3.6 | 3.6 |
Reflectance (%) | 8.8 | 3.0 | 3.3 | 3.2 |
Claims (4)
1. The method for manufacturing the glass with the ice slush effect is characterized by comprising the following steps of:
preparing a glass etching solution;
covering and protecting the surface of the glass original sheet which does not need to be etched by using an instant protective film;
and cleaning one surface of the glass original sheet needing the etching of the ice effect by using deionized water, soaking the glass original sheet in the etching solution for 5-10 minutes in a wet state, and taking out the glass original sheet to obtain the etched glass.
2. The method of making glass having a slush effect as in claim 1, wherein: the glass etching solution is composed of the following raw materials in percentage by mass: NH (NH)4HF2 20-25%、NH4F 8-15%、H2SO4 10-15%、 HNO3 8-15%、CuSO4 3-8%、ZnCL2 3-5%、Na2B4O7•10H20.5-0.8% of O, 4-6% of cane sugar and H2O15-25%, and when in specific preparation, the H is2SO4Slowly adding into water to prevent splashing, cooling to normal temperature, sequentially adding other raw materials, fully stirring to supersaturated state, standing at room temperature, and aging for 24-72 hr.
3. The method of making glass having a slush effect as in claim 2, wherein: and 3) after the etching glass is taken out from the etching solution in the step 3), washing the etching glass by using deionized water, and naturally drying or baking the etching glass.
4. A method of making glass having a slush effect in accordance with claim 3, wherein: the room temperature is 20-25 ℃.