CN1134468A - 贝氏体球墨铸铁磨球 - Google Patents

贝氏体球墨铸铁磨球 Download PDF

Info

Publication number
CN1134468A
CN1134468A CN 96100468 CN96100468A CN1134468A CN 1134468 A CN1134468 A CN 1134468A CN 96100468 CN96100468 CN 96100468 CN 96100468 A CN96100468 A CN 96100468A CN 1134468 A CN1134468 A CN 1134468A
Authority
CN
China
Prior art keywords
ball
cast iron
grinding ball
graphite cast
nodular graphite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 96100468
Other languages
English (en)
Other versions
CN1042657C (zh
Inventor
梁吉
高志栋
魏秉庆
吴德海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tsinghua University
Original Assignee
Tsinghua University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tsinghua University filed Critical Tsinghua University
Priority to CN96100468A priority Critical patent/CN1042657C/zh
Publication of CN1134468A publication Critical patent/CN1134468A/zh
Application granted granted Critical
Publication of CN1042657C publication Critical patent/CN1042657C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种贝氏体球墨铸铁磨球，属金属材料领域。本发明磨球成分为：
C 3.4—3.8％ Si 2.5—3.5％
Mn 2.0—3.5％ Cr 0.1—1.0％
S≤0.03％ P≤0.1％
Mg 0.03—0.08％ Re 0.02—0.07％余为Fe，其热处理工艺为820—920℃，保温2—8小时，在pH值为9—14，比重在1.05—1.8范围内的钠盐或钾盐水溶液中淬火。再在150℃—300℃温度下保温2—8小时。本发明磨球的综合性能较好，HRC≥55，aK≥10J/CM2，使用寿命长，成本低。

Description

贝氏体球墨铸铁磨球
本发明涉及球墨铸铁磨球，属金属材料领域。
目前国内外粉碎物料仍然大量使用球磨机，它广泛使用于矿山、冶金、建筑水泥、火力发电、化肥化工……。磨球是粉碎物料中的消耗件，要求硬度(耐磨)、韧性(不碎)兼备，低成本低消耗高效益。目前国内外使用的磨球分锻钢球和铸铁球，前者若非高合金材质一般硬度很低极不耐磨，而高合金材质钢球价格昂贵。而铸铁球常用磨球有高铬铸铁、中锰球铁、低铬铸铁等主要几种，性能及优缺点比较如下：
铸球种类     高    铬 中    锰 白口铁
优    点 ①适用于水泥、磨煤行业(干磨)，磨耗低 ①价廉②不用电炉 ①价廉②不用电炉
缺    点 ①成本高②需电炉③铬铁要进口④不适于湿磨 ①质量不稳容易碎球②硬度较低 ①质量不稳容易碎球②硬度较低
上表显示现有铸铁磨球中硬度高且耐磨(干磨)性好的高铬磨球需要电炉熔炼耗电多，含铬15％以上价格贵，且大部分需要进口，又不适宜湿磨。中锰球铁、低铬白口磨球虽然成本较低工艺简便但因碎球率高，韧性指示低不耐用。
本发明的目的是提供一种价格低耐磨性好工艺简便适合干磨湿磨的磨球。
本发明贝氏体球墨铸铁磨球成分为：
C3.4—3.8％       Si2.5—3.5％
Mn2.0-3.5％       Cr0.1—1.0％
S≤0.03％         P≤0.1％
Mg 0.03—0.08％   Re0.02—0.07％ 余为Fe
本发明采用以下热处理工艺以获得贝氏体为主的球墨铸铁。
820—920℃保温2—8小时，然后在PH值为9—14，比重在1.05—1.8范围内的钠盐或钾盐水溶液中淬火。然后在150℃—300℃温度下保温2—8小时。
说明实施例如下：
化学成分为：
C3.4—3.6％       Si3.0-3.5％
Mn2.0-2.5％       Cr0.2—0.6％
S≤0.03％         P≤0.1％
Mg 0.03—0.05％   Re0.02—0.05％余为Fe
热处理工艺：880℃—900℃，保温2小时淬入PH9—11，比重d＝1.2的钠盐水溶液中淬火，冷却后在160℃—180℃保温2小时。
在本溪发电厂Φ2.5×4M磨煤磨机上考核，球耗＜50g/吨煤。
本发明贝氏体球墨铸铁磨球的综合性能较好，HRC≥55，aK≥10J/CM2，使用寿命长，成本低。

Claims (1)

1、一种贝氏体球墨铸铁磨球，其特征是成分为：C3.4—3.8％     Si2.5—3.5％Mn2.0-3.5％     Cr0.1—1.0％S≤0.03％       P≤0.1％Mg0.03—0.08％  Re0.02—0.07％余为Fe
CN96100468A 1996-02-02 1996-02-02 贝氏体球墨铸铁磨球 Expired - Fee Related CN1042657C (zh)