CN113355942A - 一种纸张浆内着色用色浆及其制备方法 - Google Patents
一种纸张浆内着色用色浆及其制备方法 Download PDFInfo
- Publication number
- CN113355942A CN113355942A CN202110536089.3A CN202110536089A CN113355942A CN 113355942 A CN113355942 A CN 113355942A CN 202110536089 A CN202110536089 A CN 202110536089A CN 113355942 A CN113355942 A CN 113355942A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- color paste
- paper pulp
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种纸张浆内着色用色浆及其制备方法，由以下重量份原料制备而成：40~55份颜料、6~12份有机溶剂、4~8份分散剂、0.2~0.7份消泡剂、0.1~0.5份增稠剂、0.1~0.4份pH调节剂、30~45份去离子水。本发明所述的纸张浆内着色用色浆纸张浆内着色用色浆粒径小，着色力强，与纤维亲合力高，且稳定性良好，能够有效的颜料的上色问题；所制备的改性炭黑通过3‑氯丙基三乙氧基硅烷改性与通过2‑丙烯酰胺‑2‑甲基丙磺酸制备得到的分散剂，能够通过氯元素、氮元素之间的电负性作用，将分散剂牢固的锚固在改性炭黑表面，从而显著提高改性炭黑的分散作用，提高其稳定性与着色力，降低粒径。
Description
技术领域
本发明涉及色浆技术领域，具体涉及一种纸张浆内着色用色浆及其制备方法。
背景技术
目前纸张浆内着色用染料进行着色，但是染料在着色过程中有几大缺陷：1、不环保，染料属于金属络合物；2、染料在水中溶解后，属于分子，在后端污水处理时，难以处理；3、染料的耐晒、耐温以及耐候性不佳，容易变色，有效的限制了其应用，因此采用颜料色浆成为了一种有效的替代方案。
专利201710430428.3公开了一种纸用纳米色浆分散剂的制备方法，其制备方法中是将十二烷基磺酸钠作为乳化剂与水形成乳化液，在引发剂下与亲水性单体、疏水性单体进行反应，再用稳定剂进行反应，首先，其制备工程中不可避免的含有与稳定剂反应这一步骤，其次，其用到的是十二烷基磺酸钠作为乳化剂与水进行反应，且根据其对比例2的记载，使用十二烷基磺酸钠作为乳化剂与其他亲水性单体、疏水性单体进行反应时，效果会显著下降。
发明内容
本发明提供一种纸张浆内着色用色浆及其制备方法，所述的纸张浆内着色用色浆粒径小，着色力强。
本发明解决其技术问题采用以下技术方案：
一种纸张浆内着色用色浆，由以下重量份原料制备而成：40~55份颜料、6~12份有机溶剂、4~8份分散剂、0.2~0.7份消泡剂、0.1~0.5份增稠剂、0.1~0.4份pH调节剂、30~45份去离子水。
作为一种优选方案，所述纸张浆内着色用色浆由以下重量份原料制备而成：45~55份颜料、8~12份有机溶剂、5~8份分散剂、0.3~0.6份消泡剂、0.1~0.4份增稠剂、0.1~0.3份pH调节剂、30~40份去离子水。
作为一种优选方案，所述纸张浆内着色用色浆由以下重量份原料制备而成：48份颜料、9份有机溶剂、6份分散剂、0.5份消泡剂、0.3份增稠剂、0.2份pH调节剂、36份去离子水。
作为一种优选方案，所述分散剂的制备方法为:
S1、将2.5~4重量份2-丙烯酰胺-2-甲基丙磺酸加入到90~120重量份去离子水，搅拌均匀，得到第一混合液；
S2、将4~6重量份苯乙烯、8~12重量份乙烯基苯甲酸加入到30~45重量份去离子水中，搅拌均匀，得到第二混合液；
S3、将第二混合液加入到第一混合液中，搅拌均匀，加入1~4重量份引发剂溶液，在65~78℃下反应3~7h，得到分散剂。
作为一种优选方案，所述引发剂溶液为质量分数为8~15%的过硫酸钾水溶液。
本发明通过制备得到了具有优异分散性能的分散剂，能够很好的分散颜料，通过使用含氮的2-丙烯酰胺-2-甲基丙磺酸进行反应，能够降低颜料的粒径，使其粒径不会过宽，同时提高其与纤维的亲和力， 提高着色力。
作为一种优选方案，所述颜料为改性炭黑，所述改性炭黑的制备方法为：
S11、将10~20重量份炭黑加入到30~50重量份混合酸中，静置4~8h，过滤，干燥，得到预处理炭黑；
S12、将8~15重量份预处理炭黑加入到30~50重量份无水乙醇中，分散均匀，再滴入0.5~1重量份3-氯丙基三乙氧基硅烷，500~800W超声处理25~40min，过滤，干燥，得到改性炭黑。
本发明通过将炭黑用浓酸处理，进行初步改性，浓酸能够对炭黑进行初步润湿，侵蚀，使用含氯的偶联剂，具有良好的电负性强，增强了炭黑颜料之间的相互排斥，避免发生团聚现象，显著提高了其分散性能，使其粒径分布均匀且粒径小，不会返粗。
本发明的发明人在大量的研究中发现，本发明所制备的改性炭黑通过3-氯丙基三乙氧基硅烷改性与通过2-丙烯酰胺-2-甲基丙磺酸制备得到的分散剂，能够通过氯元素（改性炭黑）、氮元素（分散剂）之间的电负性作用，将分散剂牢固的锚固在改性炭黑表面，从而显著提高改性炭黑的分散作用，提高其稳定性与着色力，降低粒径。
同时发明人在大量的研究中发现，采用硅烷偶联剂KH550、硅烷偶联剂KH560、硅烷偶联剂KH570不能发生上述的电负性作用，从而达不到效果。
作为一种优选方案，所述混合酸由浓硫酸、浓硝酸按照重量比1：0.5~2配制而成。
作为一种优选方案，所述有机溶剂为甘油、乙二醇、丙二醇中的一种或多种；所述增稠剂为气相二氧化硅，所述pH调节剂为三乙醇胺。
作为一种优选方案，所述消泡剂为2，4，7，9-四甲基-5-癸炔-4，7-二醇。
本发明还提供了一种纸张浆内着色用色浆的制备方法，包括以下步骤：
S21、将有机溶剂、分散剂、去离子水，以200~400rpm转速搅拌均匀，得到第一预混液；
S22、将消泡剂、增稠剂、pH调节剂加入到预混液中，以200~500rpm转速搅拌均匀，得到第二预混液；
S23、将颜料加入到第二预混液中，以300~600rpm转速搅拌均匀，研磨至D95＜0.2μm，即得纸张浆内着色用色浆。
本发明的有益效果：本发明所述的纸张浆内着色用色浆纸张浆内着色用色浆粒径小，着色力强，与纤维亲合力高，且稳定性良好，能够有效的颜料的上色问题；所制备的改性炭黑通过3-氯丙基三乙氧基硅烷改性与通过2-丙烯酰胺-2-甲基丙磺酸制备得到的分散剂，能够通过氯元素（改性炭黑）、氮元素（分散剂）之间的电负性作用，将分散剂牢固的锚固在改性炭黑表面，从而显著提高改性炭黑的分散作用，提高其稳定性与着色力，降低粒径。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
在本发明中，除特别声明，所述的份均为重量份。
实施例1
一种纸张浆内着色用色浆，所述纸张浆内着色用色浆由以下重量份原料制备而成：48份改性炭黑、4.5份甘油、4.5份乙二醇、6份分散剂、0.5份2，4，7，9-四甲基-5-癸炔-4，7-二醇、0.3份气相二氧化硅、0.2份三乙醇胺、36份去离子水。
所述分散剂的制备方法为:
S1、将3重量份2-丙烯酰胺-2-甲基丙磺酸加入到100重量份去离子水，搅拌均匀，得到第一混合液；
S2、将5重量份苯乙烯、11重量份乙烯基苯甲酸加入到34重量份去离子水中，搅拌均匀，得到第二混合液；
S3、将第二混合液加入到第一混合液中，搅拌均匀，加入1.5重量份引发剂溶液，在68℃下反应6h，得到分散剂。
所述引发剂溶液为质量分数为10%的过硫酸钾水溶液。
所述改性炭黑的制备方法为：
S11、将15重量份炭黑加入到35重量份混合酸中，静置5h，过滤，干燥，得到预处理炭黑；
S12、将10重量份预处理炭黑加入到40重量份无水乙醇中，分散均匀，再滴入0.8重量份3-氯丙基三乙氧基硅烷，600W超声处理30min，过滤，干燥，得到改性炭黑。
所述的纸张浆内着色用色浆的制备方法，包括以下步骤：
S21、将甘油、乙二醇、分散剂、去离子水，以300rpm转速搅拌均匀，得到第一预混液；
S22、将2，4，7，9-四甲基-5-癸炔-4，7-二醇、气相二氧化硅、三乙醇胺加入到预混液中，以300rpm转速搅拌均匀，得到第二预混液；
S23、将改性炭黑加入到第二预混液中，以500rpm转速搅拌均匀，研磨至D95＜0.2μm，即得纸张浆内着色用色浆。
实施例2
一种纸张浆内着色用色浆，所述纸张浆内着色用色浆由以下重量份原料制备而成：40份改性炭黑、3份甘油、3份乙二醇、4份分散剂、0.2份2，4，7，9-四甲基-5-癸炔-4，7-二醇、0.1份气相二氧化硅、0.1份三乙醇胺、40份去离子水。
所述分散剂的制备方法为:
S1、将3重量份2-丙烯酰胺-2-甲基丙磺酸加入到100重量份去离子水，搅拌均匀，得到第一混合液；
S2、将5重量份苯乙烯、11重量份乙烯基苯甲酸加入到34重量份去离子水中，搅拌均匀，得到第二混合液；
S3、将第二混合液加入到第一混合液中，搅拌均匀，加入1.5重量份引发剂溶液，在68℃下反应6h，得到分散剂。
所述引发剂溶液为质量分数为10%的过硫酸钾水溶液。
所述改性炭黑的制备方法为：
S11、将15重量份炭黑加入到35重量份混合酸中，静置5h，过滤，干燥，得到预处理炭黑；
S12、将10重量份预处理炭黑加入到40重量份无水乙醇中，分散均匀，再滴入0.8重量份3-氯丙基三乙氧基硅烷，600W超声处理30min，过滤，干燥，得到改性炭黑。
所述的纸张浆内着色用色浆的制备方法，包括以下步骤：
S21、将甘油、乙二醇、分散剂、去离子水，以300rpm转速搅拌均匀，得到第一预混液；
S22、将2，4，7，9-四甲基-5-癸炔-4，7-二醇、气相二氧化硅、三乙醇胺加入到预混液中，以300rpm转速搅拌均匀，得到第二预混液；
S23、将改性炭黑加入到第二预混液中，以500rpm转速搅拌均匀，研磨至D95＜0.2μm，即得纸张浆内着色用色浆。
实施例3
一种纸张浆内着色用色浆，所述纸张浆内着色用色浆由以下重量份原料制备而成：45份改性炭黑、5份甘油、5份乙二醇、5份分散剂、0.7份2，4，7，9-四甲基-5-癸炔-4，7-二醇、0.5份气相二氧化硅、0.4份三乙醇胺、45份去离子水。
所述分散剂的制备方法为:
S1、将3重量份2-丙烯酰胺-2-甲基丙磺酸加入到100重量份去离子水，搅拌均匀，得到第一混合液；
S2、将5重量份苯乙烯、11重量份乙烯基苯甲酸加入到34重量份去离子水中，搅拌均匀，得到第二混合液；
S3、将第二混合液加入到第一混合液中，搅拌均匀，加入1.5重量份引发剂溶液，在68℃下反应6h，得到分散剂。
所述引发剂溶液为质量分数为10%的过硫酸钾水溶液。
所述改性炭黑的制备方法为：
S11、将15重量份炭黑加入到35重量份混合酸中，静置5h，过滤，干燥，得到预处理炭黑；
S12、将10重量份预处理炭黑加入到40重量份无水乙醇中，分散均匀，再滴入0.8重量份3-氯丙基三乙氧基硅烷，600W超声处理30min，过滤，干燥，得到改性炭黑。
所述的纸张浆内着色用色浆的制备方法，包括以下步骤：
S21、将甘油、乙二醇、分散剂、去离子水，以300rpm转速搅拌均匀，得到第一预混液；
S22、将2，4，7，9-四甲基-5-癸炔-4，7-二醇、气相二氧化硅、三乙醇胺加入到预混液中，以300rpm转速搅拌均匀，得到第二预混液；
S23、将改性炭黑加入到第二预混液中，以500rpm转速搅拌均匀，研磨至D95＜0.2μm，即得纸张浆内着色用色浆。
对比例1
对比例1与实施例1不同之处在于，对比例1采用炭黑替换改性炭黑，其他都相同。
对比例2
对比例2与实施例1不同之处在于，对比例2所述的改性炭黑的制备方法不同于实施例1，其他都相同。
所述改性炭黑的制备方法为：
S11、将15重量份炭黑加入到35重量份混合酸中，静置5h，过滤，干燥，得到预处理炭黑；
S12、将10重量份预处理炭黑加入到40重量份无水乙醇中，分散均匀，再滴入0.8重量份硅烷偶联剂KH550，600W超声处理30min，过滤，干燥，得到改性炭黑。
对比例3
对比例3与实施例1不同之处在于，所述的分散剂的制备方法不同于实施例1，其他都相同。
所述分散剂的制备方法为:
S1、将3重量份十二烷基磺酸钠加入到100重量份去离子水，搅拌均匀，得到第一混合液；
S2、将5重量份苯乙烯、11重量份乙烯基苯甲酸加入到34重量份去离子水中，搅拌均匀，得到第二混合液；
S3、将第二混合液加入到第一混合液中，搅拌均匀，加入1.5重量份引发剂溶液，在68℃下反应6h，得到分散剂。
所述引发剂溶液为质量分数为10%的过硫酸钾水溶液。
为了进一步证明本发明的效果，提供了以下测试方法：
1. 相对着色强度测试：以化工行业标准《HG/T 4786-2014 胶乳色浆》附录 B 中规定的方法进行测试，以实施例 1 制备的纸张浆内着色用色浆作为标准色浆，即为100%，测试实施例2~3、对比例1~3制备纸张浆内着色用色浆的相对着色强度，测试结果见表1。
表1 测试结果
从表1中可看出，本发明所述的纸张浆内着色用色浆具有良好的着色力，且粒径小。
对比实施例1~3可知，不同原料的配比能够影响纸张浆内着色用色浆的粒径以及着色力。
对比实施例1与对比例1、2可知，本发明通过对炭黑进行改性，显著降低了其粒径，提高了其着色力，采用其他偶联剂替换本发明所述的3-氯丙基三乙氧基硅烷，效果会显著下降。
对比实施例1与对比例3可知，采用十二烷基磺酸钠替换2-丙烯酰胺-2-甲基丙磺酸效果会显著下降。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本发明技术思想的范围内，进行多样的变更以及修改。本发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (10)
1.一种纸张浆内着色用色浆，其特征在于，由以下重量份原料制备而成：40~55份颜料、6~12份有机溶剂、4~8份分散剂、0.2~0.7份消泡剂、0.1~0.5份增稠剂、0.1~0.4份pH调节剂、30~45份去离子水。
2.根据权利要求1所述的纸张浆内着色用色浆，其特征在于，所述纸张浆内着色用色浆由以下重量份原料制备而成：45~55份颜料、8~12份有机溶剂、5~8份分散剂、0.3~0.6份消泡剂、0.1~0.4份增稠剂、0.1~0.3份pH调节剂、30~40份去离子水。
3.根据权利要求1所述的纸张浆内着色用色浆，其特征在于，所述纸张浆内着色用色浆由以下重量份原料制备而成：48份颜料、9份有机溶剂、6份分散剂、0.5份消泡剂、0.3份增稠剂、0.2份pH调节剂、36份去离子水。
4.根据权利要求1所述的纸张浆内着色用色浆，其特征在于，所述分散剂的制备方法为:
S1、将2.5~4重量份2-丙烯酰胺-2-甲基丙磺酸加入到90~120重量份去离子水，搅拌均匀，得到第一混合液；
S2、将4~6重量份苯乙烯、8~12重量份乙烯基苯甲酸加入到30~45重量份去离子水中，搅拌均匀，得到第二混合液；
S3、将第二混合液加入到第一混合液中，搅拌均匀，加入1~4重量份引发剂溶液，在65~78℃下反应3~7h，得到分散剂。
5.根据权利要求4所述的纸张浆内着色用色浆，其特征在于，所述引发剂溶液为质量分数为8~15%的过硫酸钾水溶液。
6.根据权利要求1所述的纸张浆内着色用色浆，其特征在于，所述颜料为改性炭黑，所述改性炭黑的制备方法为：
S11、将10~20重量份炭黑加入到30~50重量份混合酸中，静置4~8h，过滤，干燥，得到预处理炭黑；
S12、将8~15重量份预处理炭黑加入到30~50重量份无水乙醇中，分散均匀，再滴入0.5~1重量份3-氯丙基三乙氧基硅烷，500~800W超声处理25~40min，过滤，干燥，得到改性炭黑。
7.根据权利要求6所述的纸张浆内着色用色浆，其特征在于，所述混合酸由浓硫酸、浓硝酸按照重量比1：0.5~2配制而成。
8.根据权利要求1所述的纸张浆内着色用色浆，其特征在于，所述有机溶剂为甘油、乙二醇、丙二醇中的一种或多种；所述增稠剂为气相二氧化硅，所述pH调节剂为三乙醇胺。
9.根据权利要求1所述的纸张浆内着色用色浆，其特征在于，所述消泡剂为2，4，7，9-四甲基-5-癸炔-4，7-二醇。
10.一种纸张浆内着色用色浆的制备方法，其特征在于，用于制备权利要求1~9任一所述的纸张浆内着色用色浆，包括以下步骤：
S21、将有机溶剂、分散剂、去离子水，以200~400rpm转速搅拌均匀，得到第一预混液；
S22、将消泡剂、增稠剂、pH调节剂加入到预混液中，以200~500rpm转速搅拌均匀，得到第二预混液；
S23、将颜料加入到第二预混液中，以300~600rpm转速搅拌均匀，研磨至D95＜0.2μm，即得纸张浆内着色用色浆。