CN1132959C - 清除镀锌体表面锈斑的方法 - Google Patents

清除镀锌体表面锈斑的方法 Download PDF

Info

Publication number
CN1132959C
CN1132959C CN 99117420 CN99117420A CN1132959C CN 1132959 C CN1132959 C CN 1132959C CN 99117420 CN99117420 CN 99117420 CN 99117420 A CN99117420 A CN 99117420A CN 1132959 C CN1132959 C CN 1132959C
Authority
CN
China
Prior art keywords
galvanized
rust
galvanized body
body face
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 99117420
Other languages
English (en)
Other versions
CN1298035A (zh
Inventor
袁思胜
徐开树
陈文明
马建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Iron and Steel Group Co Ltd
Original Assignee
Chongqing Iron and Steel Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Iron and Steel Group Co Ltd filed Critical Chongqing Iron and Steel Group Co Ltd
Priority to CN 99117420 priority Critical patent/CN1132959C/zh
Publication of CN1298035A publication Critical patent/CN1298035A/zh
Application granted granted Critical
Publication of CN1132959C publication Critical patent/CN1132959C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种清除镀锌体表面锈斑的方法,用砂纸将镀锌体表面的白锈除去,用化学剂处理后,再涂上钝化剂,其特征在于化学剂采用浓度为5~10%(重量百分比)的硫酸亚铁铵溶液,钝化剂用三氧化铬:硫酸:水配置而成。本发明利用了氧化还原原理,用硫酸亚铁铵将氧化物质进行还原,能将镀锌体表面氧化后产生的深色痕迹除去。利用氧化铬钝化液在24小时内使镀锌体表面形成钝化膜,抑制锌的活泼性,不易产生氧化反应。有能去除镀锌产品氧化后产生的深色痕迹,并且经除锈后产品不易再次产生白锈的特点。

Description

清除镀锌体表面锈斑的方法
(一).技术领域
本发明涉及一种除锈的方法,特别涉及一种用于清除热镀锌制品表面锈斑的方法。
(二).背景技术
镀锌产品,尤其是热镀锌产品在生产、运输和使用过程中,由于潮湿的空气和大气中氧化物如O2等以及灰尘的作用,使镀锌产品表面产生一种氢氧化物和氧化锌的白色混合物锈斑(俗称白锈)。这种白锈的生成,除影响镀锌产品的外观质量,还会使其使用寿命降低。
由陈厚戴编著的《热镀锌技术1000例》(上海交大出版社)中介绍了用“滑石粉+氢氧化钠”的方法除镀锌产品的白锈,其只能用于轻微和一般的白锈去除,并且除锈后,易再次产生白锈。
有李荣福编写的《防锈知识问答》(广东科技出版社)中介绍了用“乙酸铵饱和溶液”的方法除镀锌产品的白锈,其只能用于轻微和一般的白锈去除,并且对镀锌产品氧化后产生的深色痕迹不能除去。
(三).发明内容
本发明的目的,是提供一种清除镀锌体表面锈斑的方法。它能去除镀锌体表面的白锈,还能去除镀锌产品氧化后产生的深色痕迹,并且经除锈后产品不易再次产生白锈。
为达上述目的,本发明的方法是用砂纸将镀锌体表面的白锈除去,用化学剂处理后,再涂上钝化剂,其特征在于化学剂采用浓度为5~10%(重量百分比)的硫酸亚铁铵溶液,钝化剂用三氧化二铬∶硫酸∶水配置而成。钝化剂氧化铬∶硫酸∶水配置而成(以重量份计)1.5~2.5∶0.5~2∶1000。
化学剂处理是将硫酸亚铁铵涂在镀锌体上待反应30~300秒后,用水冲洗。
本发明利用了氧化还原原理,用硫酸亚铁铵将氧化物质进行还原,因此能将镀锌体表面氧化后产生的深色痕迹除去。利用氧化铬钝化液在24小时内使镀锌体表面形成钝化膜,抑制锌的活泼性,不易产生氧化反应,因此有能去除镀锌体表面的白锈和镀锌产品氧化后产生的深色痕迹,并且经除锈后产品不易再次产生白锈的特点。
下面通过实施例对本发明做进一步的说明。但本发明不仅限于这些例子。
(五).具体实施方式
实施例1
用砂纸将镀锌体表面的白锈擦去,用清水洗净。将5%(重量百分比)硫酸亚铁铵溶液均匀涂在已处理的镀锌体表面,待氢氧化锌和氧化锌与硫酸亚铁铵反应30秒后,用水冲洗残余的硫酸亚铁铵溶液。立即将用三氧化二铬∶硫酸∶水=1.5∶0.5∶1000(以重量份计)配置的钝化液均匀涂抹在镀锌体表面。
实施例2
用砂纸将镀锌体表面的白锈擦去,用清水洗净。将7%(重量百分比)硫酸亚铁铵溶液均匀涂在已处理的镀锌体表面,待氢氧化锌和氧化锌与硫酸亚铁铵反应50秒后,用水冲洗残余的硫酸亚铁铵溶液。立即将用三氧化二铬∶硫酸∶水=2∶1∶1000(以重量份计)配置的钝化液均匀涂抹在镀锌体表面。
实施例3
用砂纸将镀锌体表面的白锈擦去,用清水洗净。将9%(重量百分比)硫酸亚铁铵溶液均匀涂在已处理的镀锌体表面,待氢氧化锌和氧化锌与硫酸亚铁铵反应100秒后,用水冲洗残余的硫酸亚铁铵溶液。立即将用三氧化二铬∶硫酸∶水=2.5∶1.5∶1000(以重量份计)配置的钝化液均匀涂抹在镀锌体表面。
实施例4
用砂纸将镀锌体表面的白锈擦去,用清水洗净。将10%(重量百分比)硫酸亚铁铵溶液均匀涂在已处理的镀锌体表面,待氢氧化锌和氧化锌与硫酸亚铁铵反应200秒后,用水冲洗残余的硫酸亚铁铵溶液。立即将用三氧化二铬∶硫酸∶水=2.5∶2∶1000(以重量份计)配置的钝化液均匀涂抹在镀锌体表面。
实施例5
用砂纸将镀锌体表面的白锈擦去,用清水洗净。将10%(重量百分比)硫酸亚铁铵溶液均匀涂在已处理的镀锌体表面,待氢氧化锌和氧化锌与硫酸亚铁铵反应300秒后,用水冲洗残余的硫酸亚铁铵溶液。立即将用三氧化二铬∶硫酸∶水=2∶1.5∶1000(以重量份计)配置的钝化液均匀涂抹在镀锌体表面。

Claims (1)

1.一种清除镀锌体表面锈斑的方法,包括砂纸将镀锌体表面的白锈除去,用化学剂处理后,再涂上钝化剂,其特征在于化学剂采用重量百分比浓度为5~10%的硫酸亚铁铵溶液,采用重量份计的钝化剂为三氧化二铬∶硫酸∶水=1.5~2.5∶0.5~2∶1000配置而成,将硫酸亚铁铵涂在镀锌体上待反应30~300秒后,用水冲洗。
CN 99117420 1999-12-02 1999-12-02 清除镀锌体表面锈斑的方法 Expired - Fee Related CN1132959C (zh)