CN113151916A - 一种抗菌防霉改善睡眠的熔纺纤维的制备方法及系统 - Google Patents
一种抗菌防霉改善睡眠的熔纺纤维的制备方法及系统 Download PDFInfo
- Publication number
- CN113151916A CN113151916A CN202110531997.3A CN202110531997A CN113151916A CN 113151916 A CN113151916 A CN 113151916A CN 202110531997 A CN202110531997 A CN 202110531997A CN 113151916 A CN113151916 A CN 113151916A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- mildew
- melt
- proof
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌防霉改善睡眠的熔纺纤维的制备方法。该方法包括将竹子粉末制成防霉抗菌母粒，将制备得到防霉抗菌母粒与纺织材料制成防霉抗菌熔纺纤维；其中，纺织材料为涤纶、腈纶、锦纶、棉、莫代尔、莱赛尔中的至少一种；竹子粉末为竹子提取物所制得，纺织材料的重量百分比为80～90％，防霉抗菌母粒的重量百分比为10～20％。该纤维可应用于内衣、内裤、袜子、及家纺中，其抗菌、防霉、改善睡眠功效显著。
Description
技术领域
本发明涉及纺织纤维的技术领域，具体涉及一种抗菌防霉改善睡眠的熔纺纤维的制备方法及系统。
背景技术
失眠又称入睡和维持睡眠障碍，是指无法入睡或无法保持睡眠状态，导致睡眠不足。根据病因的不同，可将失眠划分为原发性失眠和继发性失眠。原发性失眠通常缺少明确的病因，主要包括心理生理性失眠、特发性失眠和主观性失眠3种类型。对原发性失眠的诊断主要是一种排除性诊断。当排除或治愈可能引起失眠的病因后，患者仍遗留失眠的症状时即可考虑为原发性失眠。继发性失眠是与睡眠呼吸紊乱、睡眠运动障碍等相关的失眠。是由于躯体疾病、精神障碍、药物滥用等引起的失眠。药物的长期服用，会破坏肝脏分泌酶的功能，导致肝功能下降，继而带来肝肾乃至五脏功能失调。目前改善睡眠的中药制剂，又大都药味众多、疗效不显著、制剂粗糙、质量不易控制、药品稳定性较差等，致使其不能长期应用于临床。
竹子在中国具有悠久的药食两用历史，是医学中一味注明的清热解毒良药。竹叶的功效是清热除烦、生津利尿。竹叶黄酮是竹叶提取物中的主要功能成分。竹叶黄酮具有明确的抑菌功效、原料来源丰富、制剂品质高效稳定，并且具有清新的竹子香味。而竹沥是竹子经加工后提取的汁液。它是一种无毒无副作用，集药、食两用的天然饮品。化痰止咳平喘药。中医认为竹沥性味甘寒，能清热祛痰、镇惊利窍。临床上常用于急、慢性气管炎等的治疗。据药理研究，竹沥含有酚类、多糖、甙类、氨基酸、蛋白质等有效成分。同时竹子中还含有多糖、氨基酸萜类、生物碱、酚酸、挥发性成分。
故而，发现竹的活性成分中存在着微量锗、硅等有机化合物，能活化人体细胞，具有一定的保健和药理作用。
但目前，大部分纺织材料或者纺织品中不具备抗菌、防霉、去噪安神等保健效果。
发明内容
本发明的目的在于提供一种抗菌防霉改善睡眠的熔纺纤维的制备方法，解决上述现有技术问题中的一个或者多个。
本发明提供一种抗菌防霉改善睡眠的熔纺纤维的制备方法，包括以下步骤：(1)将竹子粉末制成防霉抗菌母粒，(2)将步骤(1)制备得到防霉抗菌母粒与纺织材料制成防霉抗菌熔纺纤维；其中，所述纺织材料为涤纶、腈纶、锦纶、棉、莫代尔、莱赛尔中的至少一种；所述竹子粉末为竹子提取物所制得，所述纺织材料的重量百分比为80～90％，所述防霉抗菌母粒的重量百分比为10～20％。
在一些实施方式中：步骤(1)包括称取竹子粉末、分散剂、抗氧剂，熔融共混挤出，切粒，得到抗菌防霉母粒。
在一些实施方式中：所述防霉抗菌母粒，以重量百分数计，由以下原料组成：竹子粉末为10％～12％，抗氧剂为0.1％～0.3％，分散剂为2％～7％，聚酯切片为69.7％～87.9％，原料的重量百分数之和为100％。
在一些实施方式中：选取竹子，洗净后晾干水分，研磨后置于容器中，加入乙醇溶液，摇匀，密封后在30-40℃恒温振荡水浴提取30-60分钟，转移至离心管中离心处理后，收集上清液，即得到竹子提取物)
在一些实施方式中：乙醇的浓度为15—30％，离心的条件为4500-5000r/min。
在一些实施方式中：所述抗菌防霉母粒的制备方法，包括以下步骤：将竹子提取物加水后搅拌均匀制成悬浮液，在悬浮液中加入水溶性聚季铵盐，得到第一悬浮液，将第一悬浮液进行超声震荡、清洗、过滤、烘干后得到竹子粉末；母粒制备：将竹子粉末和分散剂、氧化剂、聚酯切片混合搅拌均匀后得到第一混合物，将第一混合物在260-270℃进行熔融造粒。
在一些实施方式中：所述分散剂包括乙撑双硬脂酸酰胺蜡、乙烯基双硬脂酰胺、硬脂酸单甘油酯、三硬脂酸甘油酯、硬脂酸钡、硬脂酸锌、硬脂酸钙、硬脂酸镁、乙烯-丙烯酸共聚物、乙烯-醋酸乙烯共聚物和聚氧化乙烯蜡中的一种或几种。
本发明还提供一种根据上述的抗菌防霉熔纺纤维的制备方法所制备的抗菌防霉熔纺纤维。
在一些实施方式中：应用于内衣、内裤、袜子、运动衣、泳装、防晒衣及家纺面料中。
有益效果：
本发明实施例打破常规纺丝方法，采用将竹子粉末制成防霉抗菌母粒，将制备得到防霉抗菌母粒与纺织材料制成抗菌熔纺改善睡眠功效，具有优异的抗菌性能，同时具有防霉特性；可以大幅度降低抗菌织物的生产成本。
由于竹子中含竹叶黄酮具有抑菌性，本发明所述纤维可以有效的抑制、杀灭大肠杆菌、金黄色葡萄球菌等，同时，竹叶黄酮的特殊医用功效及清新气味，使用具有竹叶黄酮成分的纤维具有清心除烦等特点，可让人心情舒畅，使得所述家纺制品抗菌效果显著，本发明配方合理，适于大范围推广；
竹子提取物还具有通过抑菌、抗炎、抗过敏、抗氧作用，起到防止和减少生理性和精神压力型等现象的发生，让人心情愉悦，筑起良好的睡眠环境。
具体实施方式
下面结合实施例对本发明作进一步描述。以下实施例只是用于更加清楚地说明本发明的性能，而不能仅局限于下面的实施例。
实施例1
一种抗菌防霉改善睡眠的熔纺纤维的制备方法，包括以下步骤：(1)将竹子粉末制成防霉抗菌母粒，(2)将步骤(1)制备得到防霉抗菌母粒与纺织材料制成防霉抗菌熔纺纤维；其中，所述纺织材料为涤纶、腈纶、锦纶、棉、莫代尔、莱赛尔中的至少一种；
其中，所述竹子粉末为竹子提取物所制得，所述纺织材料的重量百分比为80％，所述防霉抗菌母粒的重量百分比为20％。
步骤(1)包括称取竹子粉末、分散剂、抗氧剂，熔融共混挤出，切粒，得到抗菌防霉母粒。
所述防霉抗菌母粒，以重量百分数计，由以下原料组成：竹子粉末为12％，抗氧剂为0.3％，分散剂为4％，聚酯切片为87.9％，原料的重量百分数之和为100％。
选取竹子，洗净后晾干水分，研磨后置于容器中，加入乙醇溶液，摇匀，密封后在30℃恒温振荡水浴提取60分钟，转移至离心管中离心处理后，收集上清液，即得到竹子提取物，乙醇的浓度为15％，离心的条件为4500r/min。
具体的，抗菌防霉母粒的制备方法，包括以下步骤：将竹子提取物加水后搅拌均匀制成悬浮液，在悬浮液中加入水溶性聚季铵盐，得到第一悬浮液，将第一悬浮液进行超声震荡、清洗、过滤、烘干后得到竹子粉末；母粒制备：将竹子粉末和分散剂、氧化剂、聚酯切片混合搅拌均匀后得到第一混合物，将第一混合物在260℃进行熔融造粒。
具体的，分散剂包括乙烯基双硬脂酰胺，抗氧剂，以重量份数计，由以下原料组成：1，3，5-三甲基-2，4，6-(3，5-二叔丁基-4-羟基苯甲基)苯为70％，硫代二丙酸双十八醇酯为30％。
实施例2
一种抗菌防霉改善睡眠的熔纺纤维的制备方法，包括以下步骤：(1)将竹子粉末制成防霉抗菌母粒，(2)将步骤(1)制备得到防霉抗菌母粒与纺织材料制成防霉抗菌熔纺纤维；其中，所述纺织材料为涤纶、腈纶、锦纶、棉、莫代尔、莱赛尔中的至少一种；
其中，所述竹子粉末为竹子提取物所制得，所述纺织材料的重量百分比为90％，所述防霉抗菌母粒的重量百分比为10％。
步骤(1)包括称取竹子粉末、分散剂、氧化锌，熔融共混挤出，切粒，得到抗菌防霉母粒。
所述防霉抗菌母粒，以重量百分数计，由以下原料组成：竹子粉末为10％，抗氧剂为0.2％，分散剂为7％，聚酯切片为69.7％，原料的重量百分数之和为100％。
竹子提取物的制备方法选取竹子，洗净后晾干水分，研磨后置于容器中，加入乙醇溶液，摇匀，密封后在40℃恒温振荡水浴提取30分钟，转移至离心管中离心处理后，收集上清液，即得到竹子提取物，乙醇的浓度为30％，离心的条件为5000r/min。
具体的，抗菌防霉母粒的制备方法，包括以下步骤：将竹子提取物加水后搅拌均匀制成悬浮液，在悬浮液中加入水溶性聚季铵盐，得到第一悬浮液，将第一悬浮液进行超声震荡、清洗、过滤、烘干后得到竹子粉末；母粒制备：将竹子粉末和分散剂、氧化剂、聚酯切片混合搅拌均匀后得到第一混合物，将第一混合物在270℃进行熔融造粒。
具体的，分散剂包括乙撑双硬脂酸酰胺蜡，抗氧剂以重量份数计，由以下原料组成：1，3，5-三甲基-2，4，6-(3，5-二叔丁基-4-羟基苯甲基)苯为70％，硫代二丙酸双十八醇酯为30％
实施例3
一种抗菌防霉改善睡眠的熔纺纤维的制备方法，包括以下步骤：(1)将竹子粉末制成防霉抗菌母粒，(2)将步骤(1)制备得到防霉抗菌母粒与纺织材料制成防霉抗菌熔纺纤维；其中，所述纺织材料为涤纶、腈纶、锦纶、棉、莫代尔、莱赛尔中的至少一种；
其中，所述竹子粉末为竹子提取物所制得，所述纺织材料的重量百分比为85％，所述防霉抗菌母粒的重量百分比为15％。
步骤(1)包括称取竹子粉末、分散剂、氧化锌，熔融共混挤出，切粒，得到抗菌防霉母粒。
所述防霉抗菌母粒，以重量百分数计，由以下原料组成：竹子粉末为11％，抗氧剂为0.1％，分散剂为2％，聚酯切片为75％，原料的重量百分数之和为100％。
竹子提取物的制备方法选取竹子，洗净后晾干水分，研磨后置于容器中，加入乙醇溶液，摇匀，密封后在35℃恒温振荡水浴提取45分钟，转移至离心管中离心处理后，收集上清液，即得到竹子提取物，乙醇的浓度为20％，离心的条件为4800r/min。
具体的，抗菌防霉母粒的制备方法，包括以下步骤：将竹子提取物加水后搅拌均匀制成悬浮液，在悬浮液中加入水溶性聚季铵盐，得到第一悬浮液，将第一悬浮液进行超声震荡、清洗、过滤、烘干后得到竹子粉末；母粒制备：将竹子粉末和分散剂、氧化剂、聚酯切片混合搅拌均匀后得到第一混合物，将第一混合物在265℃进行熔融造粒。
具体的，分散剂包括硬脂酸单甘油酯，抗氧剂，以重量份数计，由以下原料组成：1，3，5-三甲基-2，4，6-(3，5-二叔丁基-4-羟基苯甲基)苯为70％，硫代二丙酸双十八醇酯为30％。
实施例4
一种抗菌防霉改善睡眠的熔纺纤维的制备方法，包括以下步骤：(1)将竹子粉末制成防霉抗菌母粒，(2)将步骤(1)制备得到防霉抗菌母粒与纺织材料制成防霉抗菌熔纺纤维；其中，所述纺织材料为涤纶、腈纶、锦纶、棉、莫代尔、莱赛尔中的至少一种；
其中，所述竹子粉末为竹子提取物所制得，所述纺织材料的重量百分比为80％，所述防霉抗菌母粒的重量百分比为20％。
步骤(1)包括称取竹子粉末、分散剂、抗氧剂，熔融共混挤出，切粒，得到抗菌防霉母粒。
所述防霉抗菌母粒，以重量百分数计，由以下原料组成：竹子粉末为12％，抗氧剂为0.3％，分散剂为4％，聚酯切片为87.9％，原料的重量百分数之和为100％。
竹子提取物的提取工艺为渗漉法或烘烤法，优选烘烤法，其提取工艺为：
(a)取鲜竹干约70cm长，两端去节，劈成二片，两头架起，中部用火徐徐烧烤，温度≥160℃，两端即有液汁流出，以容器盛之，用100目筛过滤获得过滤液；
(b)过滤液中加入重量0.4％的苯甲酸钠溶解后，测pH值4.0－6.0，低温2－4℃保存。
具体的，抗菌防霉母粒的制备方法，包括以下步骤：将竹子提取物加水后搅拌均匀制成悬浮液，在悬浮液中加入水溶性聚季铵盐，得到第一悬浮液，将第一悬浮液进行超声震荡、清洗、过滤、烘干后得到竹子粉末；母粒制备：将竹子粉末和分散剂、氧化剂、聚酯切片混合搅拌均匀后得到第一混合物，将第一混合物在268℃进行熔融造粒。
具体的，分散剂包括乙烯基双硬脂酰胺，抗氧剂，以重量份数计，由以下原料组成：1，3，5-三甲基-2，4，6-(3，5-二叔丁基-4-羟基苯甲基)苯为70％，硫代二丙酸双十八醇酯为30％。
本发明中采用的纤维不局限于上述实施例中的棉、莱赛尔纤维素纤维，也同样适用于Tencel、莫代尔、竹纤维、甲壳素纤维、铜氨纤维等纤维素纤维，采用本发明方法生产的抗菌防霉熔纺纤维很适宜应用于内衣、内裤、袜子、衬衣或家纺中。
.按照GB/T20944.3-2008《纺织品抗菌性能的评价第3部分：振荡法》，对本发明实施例1-3所制备的纤维素纤维进行金黄葡萄球菌(AATCC6538)、大肠杆菌(AATCC8739)及白色念珠菌(AATCC10231)的抗菌效果测试，其中，抗菌性能依照GB/T20944.3-2008，纺织品抗菌性能的评价第3部分测定对本发明实施例1-3所制备的纤维素纤维进行抗菌测试，按照BSEN14119-2003标准对防霉性进行测试，其测试结果如表1所示。
安神睡眠测试
年龄在18～50周岁之间，睡眠质量测试者600名进行实验，随机分为六组，各组之间无显著性差异。每天使用实施例1～4的抑菌湿巾液制成的抗菌防霉熔纺纤维制成的四件套入睡，实验共进行60天。
实验结果发现60天的测试过程中，并未有使用该四件套的受试者睡眠质量没有使用该四件套的受试者的睡眠质量高。通过佩戴睡眠测试仪测试是否进入深入睡眠测试，结果可以发现，超过80％的使用该四件套的受试者的睡眠质量越来越好。
由表1可以看出，本发明中抗菌防霉改善睡眠的熔纺纤维的防霉性，抑菌性好，且对人的睡眠具有改善效果，起到安神作用。
有益效果：
本发明实施例打破常规纺丝方法，采用将竹子粉末制成防霉抗菌母粒，将制备得到防霉抗菌母粒与纺织材料制成抗菌熔纺改善睡眠功效，具有优异的抗菌性能，同时具有防霉特性；可以大幅度降低抗菌织物的生产成本。
由于竹子中含竹叶黄酮具有抑菌性，本发明所述纤维可以有效的抑制、杀灭大肠杆菌、金黄色葡萄球菌等，同时，竹叶黄酮的特殊医用功效及清新气味，使用具有竹叶黄酮成分的纤维具有清心除烦等特点，可让人心情舒畅，使得所述家纺制品抗菌效果显著。本发明配方合理，适于大范围推广；
竹子提取物还具有通过抑菌、抗炎、抗过敏、抗氧作用，起到防止和减少生理性和精神压力型等现象的发生，让人心情愉悦，筑起良好的睡眠环境。
上述仅为本发明的较佳实施例及所运用技术原理。本领域技术人员会理解，本发明不限于这里所述的特定实施例，对本领域技术人员来说能够进行各种明显的变化、重新调整和替代而不会脱离本发明的保护范围。因此，虽然通过以上实施例对本发明进行了较为详细的说明，但是本发明不仅仅限于以上实施例，在不脱离本发明构思的情况下，还可以包括更多其他等效实施例，而本发明的范围由所附的权利要求范围决定。
Claims (9)
1.一种抗菌防霉改善睡眠的熔纺纤维的制备方法，包括以下步骤：(1)将竹子粉末制成防霉抗菌母粒，(2)将步骤(1)制备得到防霉抗菌母粒与纺织材料制成防霉抗菌熔纺纤维；其中，所述纺织材料为涤纶、腈纶、锦纶、棉、莫代尔、莱赛尔中的至少一种；所述竹子粉末为竹子提取物所制得，所述纺织材料的重量百分比为80～90％，所述防霉抗菌母粒的重量百分比为10～20％。
2.根据权利要求1所述的一种抗菌防霉改善睡眠的熔纺纤维的制备方法，其特征在于，步骤(1)包括称取竹子粉末、分散剂、抗氧剂，熔融共混挤出，切粒，得到抗菌防霉母粒。
3.根据权利要求1所述的一种抗菌防霉改善睡眠的熔纺纤维的制备方法，其特征在于，所述防霉抗菌母粒，以重量百分数计，由以下原料组成：竹子粉末为10％～12％，抗氧剂为0.1％～0.3％，分散剂为2％～7％，聚酯切片为69.7％～87.9％，原料的重量百分数之和为100％。
4.根据权利要求1所述的一种抗菌防霉改善睡眠的熔纺纤维的制备方法，其特征在于，所述竹子提取物的制备方法是选取竹子，洗净后晾干水分，研磨后置于容器中，加入乙醇溶液，摇匀，密封后在30-40℃恒温振荡水浴提取30-60分钟，转移至离心管中离心处理后，收集上清液，即得到竹子提取物。
5.根据权利要求1所述的一种抗菌防霉熔纺纤维，其特征在于，乙醇的浓度为15—30％，离心的条件为4500-5000r/min。
6.根据权利要求1所述的一种抗菌防霉改善睡眠的熔纺纤维的制备方法，其特征在于，所述抗菌防霉母粒的制备方法，包括以下步骤：将竹子提取物加水后搅拌均匀制成悬浮液，在悬浮液中加入水溶性聚季铵盐，得到第一悬浮液，将第一悬浮液进行超声震荡、清洗、过滤、烘干后得到竹子粉末；母粒制备：将竹子粉末和分散剂、氧化剂、聚酯切片混合搅拌均匀后得到第一混合物，将第一混合物在260-270℃进行熔融造粒。
7.根据权利要求1所述的一种抗菌防霉改善睡眠的熔纺纤维的制备方法，其特征在于，所述分散剂包括乙撑双硬脂酸酰胺蜡、乙烯基双硬脂酰胺、硬脂酸单甘油酯、三硬脂酸甘油酯、硬脂酸钡、硬脂酸锌、硬脂酸钙、硬脂酸镁、乙烯-丙烯酸共聚物、乙烯-醋酸乙烯共聚物和聚氧化乙烯蜡中的一种或几种。
8.一种根据权利要求1-7任一项所述的抗菌防霉熔纺纤维的制备方法所制备的抗菌防霉熔纺纤维。
9.一种根据权利要求8所述的抗菌防霉熔纺纤维的用途，特征在于，应用于内衣、内裤、袜子、运动衣、泳装、家纺面料和填充物中。