CN113150470A - 一种低密度、高挤出速率pvc防火密封条及其制备方法 - Google Patents
一种低密度、高挤出速率pvc防火密封条及其制备方法 Download PDFInfo
- Publication number
- CN113150470A CN113150470A CN202110535449.8A CN202110535449A CN113150470A CN 113150470 A CN113150470 A CN 113150470A CN 202110535449 A CN202110535449 A CN 202110535449A CN 113150470 A CN113150470 A CN 113150470A
- Authority
- CN
- China
- Prior art keywords
- pvc
- sealing strip
- mixture
- rate
- low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低密度、高挤出速率PVC防火密封条，其包括如下质量百分比的各组分：聚氯乙烯树脂粉10‑40％，膨胀石墨10‑40％，填料5‑30％，轻质填料2‑10％，发泡剂0.5‑5％，泡孔调节剂0.5‑5％，增塑剂10‑40％，热稳定剂0.5‑5％、阻燃剂2‑6％和加工助剂0.5‑5％。本发明利用轻质防火原材料替代部分填料，同时增加发泡剂和泡孔调节剂，在不增加成本、不损失性能的前提下，降低了PVC密封条的密度，使密封条在使用过程中不至于因自身重量过高而脱落，降低了PVC密封条的使用条件。
Description
技术领域
本发明属于防火密封条领域，具体涉及一种低密度、高挤出速率PVC防火密封条及其制备方法。
背景技术
目前市面上的密封条为了降低自重，通过发泡或增加PVC树脂、PVC回收料等方法来降低自身密度，但是添加PVC回收料会在一定程度上降低密封条的强度和防火能力，而增加PVC新料又会大幅度提高成本。
发明内容
本发明的目的是提供一种低密度、高挤出速率PVC防火密封条及其制备方法，以期解决背景技术中的问题。
本发明更具体的技术方案如下：
一种低密度、高挤出速率PVC防火密封条，包括如下质量百分比的各组分：聚氯乙烯树脂粉10-40％，膨胀石墨10-40％，填料5-30％，轻质填料2-10％，发泡剂0.5-5％，泡孔调节剂0.5-5％，增塑剂10-40％，热稳定剂0.5-5％、阻燃剂2-6％和加工助剂0.5-5％。
在一些实施例中，所述聚氯乙烯树脂粉为SG-3型、SG-5型的一种或两种混合物。
在一些实施例中，所述膨胀石墨为80目、120目、150目和200目的一种或两种混合物。
在一些实施例中，所述填料为轻质碳酸钙、重质碳酸钙中的一种或两种混合物。
在一些实施例中，所述轻质填料为珍珠岩、50-100目的漂珠粉和50-100目的玻璃微珠中的一种或几种混合物。
在一些实施例中，所述热稳定剂为复合铅盐、硬脂酸锌、硬脂酸钡和硬脂酸钙的一种或几种混合物。
在一些实施例中，所述泡孔调节剂为丙烯酸酯类聚合物。
在一些实施例中，增塑剂为邻苯二甲酸二丁酯或邻苯二甲酸二辛酯其中一种或两种混合物。
在一些实施例中，所述阻燃剂为三氧化二锑、硼酸锌、碳黑及包覆红磷中的一种或几种的混合物；加工助剂为以甲基丙烯酸甲酯为主体的丙烯酸ACR树脂、硬脂酸锌、硬脂酸钡和硬脂酸钙的一种或几种混合物。
本发明还提供了一种低密度、高挤出速率PVC防火密封条的制备方法，包括任一上述的低密度、高挤出速率PVC防火密封条，制备方法如下：将各组分原料按照用量占比，依次称料，并加入高速搅拌缸内，200-500转/min混合搅抖3-10分钟后，降至低速搅拌1-5分钟，经过造粒、挤出成型、冷却粘结双面胶后得到PVC阻燃密封条成品。
具体实施方式
下面结合实施例对本发明作进一步的描述，所描述的实施例仅仅是本发明一部分实施例，并不是全部的实施例。基于本发明中的实施例，本领域的普通技术人员在没有做出创造性劳动前提下所获得的其他所用实施例，都属于本发明的保护范围。
实施例1：
本配方以重量百分比计，SG-5聚氯乙烯树脂粉25％，80目膨胀石墨25％，轻质碳酸钙16.5％，增塑剂27％，热稳定剂1％、阻燃剂4.5％和加工助剂1％，200-500转/min混合搅抖3-10分钟后，降至低速搅拌1-5分钟，经过造粒、挤出成型、冷却、裁切和粘贴双面胶后得到PVC阻燃密封条成品。
实施例2:
本配方以重量百分比计，SG-5聚氯乙烯树脂粉25％，80目膨胀石墨25％，轻质碳酸钙13.5％，珍珠岩3％，塑剂27％，热稳定剂1％、阻燃剂4.5％和加工助剂1％，200-500转/min混合搅抖3-10分钟后，降至低速搅拌1-5分钟，经过造粒、挤出成型、冷却、裁切和粘贴双面胶后得到PVC阻燃密封条成品。
实施例3：
本配方以重量百分比计，SG-5聚氯乙烯树脂粉25％，80目膨胀石墨25％，轻质碳酸钙9％，珍珠岩3％，AC发泡剂1.5％，泡孔调节剂3％，增塑剂27％，热稳定剂1％、阻燃剂4.5％和加工助剂1％，200-500转/min混合搅抖3-10分钟后，降至低速搅拌1-5分钟，经过造粒、挤出成型、冷却、裁切和粘贴双面胶后得到PVC阻燃密封条成品。
实施例4：
本配方以重量百分比计，SG-5聚氯乙烯树脂粉25％，80目膨胀石墨25％，轻质碳酸钙7.5％，珍珠岩3％，AC发泡剂2％，泡孔调节剂4％，增塑剂27％，热稳定剂1％、阻燃剂4.5％和加工助剂1％，200-500转/min混合搅抖3-10分钟后，降至低速搅拌1-5分钟，经过造粒、挤出成型、冷却、裁切和粘贴双面胶后得到PVC阻燃密封条成品。
产品质量检测标准及使用要求
下面结合具体实施例对本发明的技术方案作进一步的说明，但本发明不以任何形式受限于实施例内容。
本发明以下实施例制得的成品按国标《GB/T 16807-2009防火膨胀密封件》检测以下项目:
外观:外观应保持平整、光滑，不应有扭曲变形、裂纹、破损、气泡、杂质、色差、污垢或粉化等现象.
结构尺寸要求:各类防火胶条的结构尺寸应符合样品要求，尺寸允许偏差应符合下表1要求。
表1
膨胀性能要求:检测结果应要求值偏差范围应在15％以内。
耐空气老化性能要求：按规定的条件试验后，用玻璃棒按压胶条膨胀体表面，应无明显粉化、脱落现象。空气老化试验后膨胀体的膨胀倍率应不小于初始膨胀倍率。
耐水性要求：试验后无明显溶蚀、溶胀、粉化、脱落等现象，质量变化率不大于5％，试验后膨胀体的膨胀倍率应不小于初始膨胀倍率。
耐酸性要求：试验后无明显溶蚀、溶胀、粉化、脱落等现象，质量变化率不大于5％，试验后膨胀体的膨胀倍率应不小于初始膨胀倍率。
耐碱性要求：试验后无明显溶蚀、溶胀、粉化、脱落等现象，质量变化率不大于5％，试验后膨胀体的膨胀倍率应不小于初始膨胀倍率。
耐冻融循环性要求：按规定的条件试验后，观察并用玻璃棒按压胶条膨胀体表面，应无明显粉化、脱落现象。试验后膨胀体的膨胀倍率应不小于初始膨胀倍率。.
本发明与现有技术相比具有的有益效果包括但不限于：
1、所发明的密封胶条阻燃能力好,膨胀倍率高,能达到国家3C要求,辅助防火门达到烧检条件。
2、所发明的密封胶条配料方便,制作工艺更是简单,同时生产过程不受温度限制,成品无收缩情况.
3、在不添加回收料的情况下，降低密封条的密度、自重，密封条在使用过程中不易掉落。
4、本发明在使用挤出机时，可加快生产速率，提高生产效率。
本发明利用轻质防火原材料替代部分填料，同时增加发泡剂和泡孔调节剂，在不增加成本、不损失性能的前提下，降低了PVC密封条的密度，使密封条在使用过程中不至于因自身重量过高而脱落，降低了PVC密封条的使用条件。
本发明提供的低密度、高挤出速率PVC防火密封条所有检测标准均能达到并优于国标《GB/T 16807-2009防火膨胀密封件》对防火膨胀密封件的要求,在不添加回收料的前提下，降低了PVC防火膨胀密封条的密度，同时提高了其挤出速率。
表2
表2是各实施例的性能测试结果，从表2可看出，珍珠岩的加入可提高挤出速率，但对密度的降低起不了太大作用；发泡剂和泡孔调节剂共同使用可降低PVC膨胀密封条的密度，并且加入量越多，发泡效果越好。
尽管这里参照本发明的解释性实施例对本发明进行了描述，上述实施例仅为本发明较佳的实施方式，本发明的实施方式并不受上述实施例的限制，应该理解，本领域技术人员可以设计出很多其他的修改和实施方式，这些修改和实施方式将落在本申请公开的原则范围和精神之内。
Claims (10)
1.一种低密度、高挤出速率PVC防火密封条，其特征在于，包括如下质量百分比的各组分：聚氯乙烯树脂粉10-40％，膨胀石墨10-40％，填料5-30％，轻质填料2-10％，发泡剂0.5-5％，泡孔调节剂0.5-5％，增塑剂10-40％，热稳定剂0.5-5％、阻燃剂2-6％和加工助剂0.5-5％。
2.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，所述聚氯乙烯树脂粉为SG-3型、SG-5型的一种或两种混合物。
3.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，所述膨胀石墨为80目、120目、150目和200目的一种或两种混合物。
4.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，所述填料为轻质碳酸钙、重质碳酸钙中的一种或两种混合物。
5.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，所述轻质填料为珍珠岩、50-100目的漂珠粉和50-100目的玻璃微珠中的一种或几种混合物。
6.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，所述热稳定剂为复合铅盐、硬脂酸锌、硬脂酸钡和硬脂酸钙的一种或几种混合物。
7.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，所述泡孔调节剂为丙烯酸酯类聚合物。
8.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，增塑剂为邻苯二甲酸二丁酯或邻苯二甲酸二辛酯其中一种或两种混合物。
9.根据权利要求1所述的一种低密度、高挤出速率PVC防火密封条，其特征在于，所述阻燃剂为三氧化二锑、硼酸锌、碳黑及包覆红磷中的一种或几种的混合物；加工助剂为以甲基丙烯酸甲酯为主体的丙烯酸ACR树脂、硬脂酸锌、硬脂酸钡和硬脂酸钙的一种或几种混合物。
10.一种低密度、高挤出速率PVC防火密封条的制备方法，包括权利要求1-9任一权利要求所述的低密度、高挤出速率PVC防火密封条，其特征在于，制备方法如下：将各组分原料按照用量占比，依次称料，并加入高速搅拌缸内，200-500转/min混合搅抖3-10分钟后，降至低速搅拌1-5分钟，经过造粒、挤出成型、冷却粘结双面胶后得到PVC阻燃密封条成品。