CN113100084A - 一种除味猫砂及其制备方法 - Google Patents
一种除味猫砂及其制备方法 Download PDFInfo
- Publication number
- CN113100084A CN113100084A CN202110360033.7A CN202110360033A CN113100084A CN 113100084 A CN113100084 A CN 113100084A CN 202110360033 A CN202110360033 A CN 202110360033A CN 113100084 A CN113100084 A CN 113100084A
- Authority
- CN
- China
- Prior art keywords
- parts
- cat litter
- disinfectant
- zinc
- litter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供了一种除味猫砂及其制备方法,按重量份计,制备原料至少包括:按重量份计,制备原料至少包括吸附剂80‑95份、吸水剂2‑10份、消毒剂0.05‑5份、粘结剂2‑4份、水5‑15份、除味剂0.1‑5份;本发明采用无机矿物原料作为猫砂吸附剂,他们具有不滋养微生物、吸水量高的特点,有利于延长猫砂的使用时间;同时猫砂添加量消毒剂和除味剂,防止致病微生物滋养和异味产生。
Description
技术领域
本发明涉及宠物用品技术领域,具体涉及一种除味猫砂及其制备方法。
背景技术
猫砂是饲主为其饲养的猫用来掩埋粪便和尿液的物体,有较好的吸水性,一般会与猫砂盆(或称猫厕所)一并使用,将适量的猫砂倒于猫砂盆内,受过训练的猫需要排泄时便会走进猫砂盆内排泄在猫砂上面。
目前按照化学属性及原料划分为:有机猫砂和无机猫砂。有机猫砂主要有纸屑猫砂和木屑猫砂;无机猫砂主要有膨润土猫砂和水晶猫砂。按照使用特点分为结团猫砂和不结团猫砂。结团猫砂是猫砂吸收尿液和粪便后会结成一团,配合猫砂铲,方便清理;不结团猫砂是猫砂遇到尿液和粪便后不会结团,使用后不方便清理,用量比结团猫砂大。
当猫的粪便或尿液与猫砂接触时,由于猫砂的吸湿作用,与粪便或尿液有接触的猫砂便与粪便或尿液形成一体的球状,而未沾染粪便或尿液的猫砂则不受污染,可继续使用,从而清理小动物的粪便和尿液变得极其轻松,也为饲养宠物带来轻松愉快和环保。
然而,现有的新型猫砂多注重吸水效果,而不具备好的抗菌除臭功效,因此,当猫砂受污染后,仅铲除肉眼观察到的受污染的局部猫砂,难以确保其余部分的猫砂未被污染,而这潜在的污染猫砂将不断滋生细菌,使得宠物生病。
发明内容
为了解决上述技术问题,本发明的第一个方面提供了一种除味猫砂,按重量份计,制备原料至少包括:按重量份计,制备原料至少包括吸附剂80-95份、吸水剂2-10份、消毒剂0.05-5份、粘结剂2-4份、水5-15份、除味剂0.1-5份。
作为本发明一种优选的技术方案,所述吸附剂选自蛭石粉、膨润土、硅藻土、活性炭粉、碳酸钙粉等的一种或多种。
作为本发明一种优选的技术方案,所述吸附剂为膨润土。
作为本发明一种优选的技术方案,所述吸水剂为硫酸盐。
作为本发明一种优选的技术方案,所述消毒剂选自高分子消毒剂、胍盐消毒剂、无机盐消毒剂、季铵盐消毒剂中的一种或多种。
作为本发明一种优选的技术方案,所述无机盐消毒剂为纳米银。
作为本发明一种优选的技术方案,所述粘结剂选自黄原胶、羟甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、聚乙烯吡咯烷酮、瓜尔胶中的一种或多种。
作为本发明一种优选的技术方案,所述聚乙烯醇的醇解度为87-89%。
作为本发明一种优选的技术方案,所述除味剂选自蓖麻油酸锌、葡萄糖酸锌、甘草锌、醋酸锌、柠檬酸锌、氨基酸锌、乙二胺四乙酸锌钠、草酸锌、乳酸锌和酒石酸锌中的一种或多种。
本发明的第二个方面提供了除味猫砂的制备方法,所述制备方法至少包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成2-5mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度280-330℃,干燥时间2小时,即的。
本发明与现有技术相比,其有益效果为:
1)本发明采用无机矿物原料作为吸附剂;同时添加了纳米银消毒剂,与其他消毒剂相比,纳米银可以耐受成型干燥时的高温。基于上述原因,不会滋养微生物,有利于延长猫砂的使用时间;
2)本发明同时添加吸水剂,吸收量大,避免频繁更换猫砂;
3)本发明添加的除味剂,可以吸附猫咪排泄物散发的臭味,具有除味功能。
具体实施方式
参选以下本发明的优选实施方法的详述以及包括的实施例可更容易地理解本发明的内容。除非另有限定,本文使用的所有技术以及科学术语具有与本发明所属领域普通技术人员通常理解的相同的含义。当存在矛盾时,以本说明书中的定义为准。
如本文所用术语“由…制备”与“包含”同义。本文中所用的术语“包含”、“包括”、“具有”、“含有”或其任何其它变形,意在覆盖非排它性的包括。例如,包含所列要素的组合物、步骤、方法、制品或装置不必仅限于那些要素,而是可以包括未明确列出的其它要素或此种组合物、步骤、方法、制品或装置所固有的要素。
连接词“由…组成”排除任何未指出的要素、步骤或组分。如果用于权利要求中,此短语将使权利要求为封闭式,使其不包含除那些描述的材料以外的材料,但与其相关的常规杂质除外。当短语“由…组成”出现在权利要求主体的子句中而不是紧接在主题之后时,其仅限定在该子句中描述的要素;其它要素并不被排除在作为整体的所述权利要求之外。
当量、浓度、或者其它值或参数以范围、优选范围、或一系列上限优选值和下限优选值限定的范围表示时,这应当被理解为具体公开了由任何范围上限或优选值与任何范围下限或优选值的任一配对所形成的所有范围,而不论该范围是否单独公开了。例如,当公开了范围“1至5”时,所描述的范围应被解释为包括范围“1至4”、“1至3”、“1至2”、“1至2和4至5”、“1至3和5”等。当数值范围在本文中被描述时,除非另外说明,否则该范围意图包括其端值和在该范围内的所有整数和分数。
单数形式包括复数讨论对象,除非上下文中另外清楚地指明。“任选的”或者“任意一种”是指其后描述的事项或事件可以发生或不发生,而且该描述包括事件发生的情形和事件不发生的情形。
说明书和权利要求书中的近似用语用来修饰数量,表示本发明并不限定于该具体数量,还包括与该数量接近的可接受的而不会导致相关基本功能的改变的修正的部分。相应的,用“大约”、“约”等修饰一个数值,意为本发明不限于该精确数值。在某些例子中,近似用语可能对应于测量数值的仪器的精度。在本申请说明书和权利要求书中,范围限定可以组合和/或互换,如果没有另外说明这些范围包括其间所含有的所有子范围。
此外,本发明要素或组分前的不定冠词“一种”和“一个”对要素或组分的数量要求(即出现次数)无限制性。因此“一个”或“一种”应被解读为包括一个或至少一个,并且单数形式的要素或组分也包括复数形式,除非所述数量明显旨指单数形式。
为了解决上述技术问题,本发明的第一个方面提供了一种除味猫砂,按重量份计,制备原料至少包括吸附剂80-95份、吸水剂2-10份、消毒剂0.05-5份、粘结剂2-4份、水5-15份、除味剂0.1-5份。
在一种优选的实施方式中,本发明所述除味猫砂,按重量份计,制备原料至少包括吸附剂82-90份、吸水剂4-8份、消毒剂1-4份、粘结剂2.5-3.5份、水8-14份、除味剂1-3份。
在一种最优选的实施方式中,本发明所述除味猫砂,按重量份计,制备原料至少包括吸附剂85份、吸水剂6份、消毒剂3.4份、粘结剂3份、水12份、除味剂2份。
吸附剂
本发明所述吸附剂也称吸收剂,这种物质可使活性成分附着在其颗粒表面,使液态微量化合物添加剂变为固态化合物,有利于实施均匀混合,是一种能够有效地从气体或液体中吸附其中某些成分的固体物质,具有大的比表面、适宜的孔结构及表面结构;对吸附质有强烈的吸附能力;一般不与吸附质和介质发生化学反应;制造方便、容易再生;有极好的吸附性和机械性特性。
在一种优选的实施方式中,本发明所述吸附剂选自蛭石粉、膨润土、硅藻土、活性炭粉、碳酸钙粉等的一种或多种。
在一种优选的实施方式中,本发明所述吸附剂为膨润土。
在一种优选的实施方式中,本发明所述膨润土为钠基膨润土。
本发明将膨润土作为除味猫砂的有效吸附成分,在一定程度上提高了除味猫砂对于宠物排泄物的吸收性,可延长猫砂的使用时间,同时还提高了除味猫砂的成团性,避免了除味猫砂在使用过程中引起干净猫砂的浪费,提高了除味猫砂的使用率和去除率;尤其是本发明采用钠基膨润土代替现有技术中的其他吸附剂,其吸附效果更佳,其可能存在的原因是由于钠基膨润土的结构为层状硅酸盐结构,其中钠离子的半径小,在膨润土的单位晶层地面占据的面积小,晶体膨胀倍数较高,具有优异的水合性能;但是,钠基膨润土的吸水速率较慢,且在使用中亦有粉尘,会引起宠物打喷嚏等不适感。
吸水剂
在一种优选的实施方式中,本发明所述吸水剂为硫酸盐。
在一种优选的实施方式中,本发明所述吸水剂为硫酸镁和/或硫酸钙。
在一种最优选的实施方式中,本发明所述吸水剂为硫酸镁。
本发明所述硫酸镁是一种含镁的化合物,分子式为MgSO4,是一种常用的化学试剂及干燥试剂,为无色或白色晶体或粉末,无臭、味苦,有潮解性。
为了提高除味猫砂的吸水速率,本发明添加了硫酸盐作为吸水剂,利用硫酸盐的吸水性能,将水分子高效的传递到吸附材料中,实现锁水;发明人在实验中意外的发现,当本发明采用硫酸镁作为吸水剂时,还可以缓减钠基膨润土引起粉尘的现象发生,发明人推测,其可能存在的原因是由于,本发明采用的硫酸盐中含有二价镁离子,易与钠基膨润土中的层间离子实现交换,增加了电荷密度,使得颗粒之间的静电引力增强,提高了颗粒之间的联结性。
消毒剂
本发明所述消毒剂用于杀灭传播媒介上病原微生物,使其达到无害化要求。
在一种优选的实施方式中,本发明所述消毒剂选自高分子消毒剂、胍盐消毒剂、无机盐消毒剂、季铵盐消毒剂中的一种或多种。
在一种优选的实施方式中,本发明所述无机盐消毒剂为纳米银。
在一种优选的实施方式中,本发明所述纳米银的粒径为30-50nm。
在一种优选的实施方式中,本发明所述纳米银的形状为球形。
本发明所述纳米银可通过商购得到,厂家包括但不限于北京大华博科智能科技有限公司,牌号为AgNP50。
本发明所述纳米银就是将粒径做到纳米级的金属银单质,纳米银对大肠杆菌、淋球菌、沙眼衣原体等数十种致病微生物都有强烈的抑制和杀灭作用,而且不会产生耐药性,用纳米银制成的除味猫砂,具备很好的抗菌防臭的效果。
为增加除味猫砂的杀菌消毒作用,本发明在体系中添加了纳米银作为消毒剂;由于纳米银是无机材料,为提高纳米银在除味猫砂体系中的分散均匀性,本发明优于选择粒径30-50nm的粒子,尤其是选择牌号为AgNP50的纳米银,其分散效果较好,发明人推测,其可能的原因除粒径大小之外,还可能是由于本发明采用的纳米银的微观形貌为球形,提高了纳米银在体系材料中的填充性,不仅可以保证混合均匀,还可以提高除味猫砂的表面均匀性。
粘结剂
本发明所述粘结剂主要是指起到粘结作用的物质。
在一种优选的实施方式中,本发明所述粘结剂选自黄原胶、羟甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、聚乙烯吡咯烷酮、瓜尔胶中的一种或多种。
在一种优选的实施方式中,本发明所述粘结剂为聚乙烯醇。
在一种优选的实施方式中,本发明所述聚乙烯醇的醇解度为87-89%。
在一种最优选的实施方式中,本发明所述聚乙烯醇的醇解度为88%,牌号为聚乙烯醇1788。
本发明添加聚乙烯醇作为粘结剂,有效的提高了除味猫砂中无机材料之间的粘结性,其可能存在的原因是由于本发明采用的粘结剂中含有大量羟基,易与无机材料表面的极性材料结合形成氢键和分子间作用力,一方面提高了粘结性,另一方面本发明控制聚乙烯醇的醇解度以及分子量,提高聚乙烯醇的成膜性,促进聚乙烯醇包覆无机材料,与吸水剂具有协同作用,在一定程度上缓解了除味猫砂的粉尘性。
除味剂
本发明所述除味剂是指可以去除异味的物质。
在一种优选的实施方式中,本发明所述除味剂选自蓖麻油酸锌、葡萄糖酸锌、甘草锌、醋酸锌、柠檬酸锌、氨基酸锌、乙二胺四乙酸锌钠、草酸锌、乳酸锌和酒石酸锌中的一种或多种。
在一种优选的实施方式中,本发明所述除味剂为葡萄糖酸锌。
本发明所述葡萄糖酸锌化学式为C12H22O14Zn,是葡萄糖酸的锌盐,常温下为白色结晶或颗粒性粉末,无臭,味微涩,在沸水中极易溶解,在水中溶解,在无水乙醇、三氯甲烷或乙醚中不溶。临床上适用于小儿厌食症、各种皮肤痤疮、复发性阿弗口腔溃疡等缺锌性疾病。
本发明采用同时在除味猫砂中添加量消毒剂和除味剂,防止致病微生物滋养和异味产生。
本发明的第二个方面提供了除味猫砂的制备方法,所述制备方法至少包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成2-5mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度280-330℃,干燥时间2小时,即的。
有必要在此指出的是,以下实施例只用于对本发明作进一步说明,不能理解为对本发明保护范围的限制,该领域的专业技术人员根据上述本发明的内容做出的一些非本质的改进和调整,仍属于本发明的保护范围。
另外,如果没有其它说明,所用原料都是市售的,购于国药化学试剂。
实施例
实施例1
提供了一种除味猫砂,按重量份计,制备原料包括吸附剂85份、吸水剂6份、消毒剂3.4份、粘结剂3份、水12份、除味剂2份。
所述吸附剂为膨润土。
所述膨润土为钠基膨润土。
所述吸水剂为硫酸镁。
所述消毒剂为纳米银,可通过商购得到,厂家为北京大华博科智能科技有限公司,牌号为AgNP50。
所述粘结剂为聚乙烯醇,牌号为聚乙烯醇1788。
所述除味剂为葡萄糖酸锌。
提供了除味猫砂的制备方法,所述制备方法包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成3mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度300℃,干燥时间2小时,即的。
实施例2
提供了一种除味猫砂,按重量份计,制备原料包括吸附剂80份、吸水剂2份、消毒剂0.05份、粘结剂2份、水5份、除味剂0.1份。
所述吸附剂为膨润土。
所述膨润土为钠基膨润土。
所述吸水剂为硫酸镁。
所述消毒剂为纳米银,可通过商购得到,厂家为北京大华博科智能科技有限公司,牌号为AgNP50。
所述粘结剂为聚乙烯醇,牌号为聚乙烯醇1788。
所述除味剂为葡萄糖酸锌。
提供了除味猫砂的制备方法,所述制备方法包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成3mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度300℃,干燥时间2小时,即的。
实施例3
提供了一种除味猫砂,按重量份计,制备原料包括吸附剂95份、吸水剂10份、消毒剂5份、粘结剂4份、水15份、除味剂5份。
所述吸附剂为膨润土。
所述膨润土为钠基膨润土。
所述吸水剂为硫酸镁。
所述消毒剂为纳米银,可通过商购得到,厂家为北京大华博科智能科技有限公司,牌号为AgNP50。
所述粘结剂为聚乙烯醇,牌号为聚乙烯醇1788。
所述除味剂为葡萄糖酸锌。
提供了除味猫砂的制备方法,所述制备方法包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成3mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度300℃,干燥时间2小时,即的。
实施例4
提供了一种除味猫砂,按重量份计,制备原料包括吸附剂85份、吸水剂6份、消毒剂3.4份、粘结剂3份、水12份、除味剂2份。
所述吸附剂为硅藻土。
所述吸水剂为硫酸镁。
所述消毒剂为纳米银,可通过商购得到,厂家为北京大华博科智能科技有限公司,牌号为AgNP50。
所述粘结剂为聚乙烯醇,牌号为聚乙烯醇1788。
所述除味剂为葡萄糖酸锌。
提供了除味猫砂的制备方法,所述制备方法包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成3mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度300℃,干燥时间2小时,即的。
实施例5
提供了一种除味猫砂,按重量份计,制备原料包括吸附剂85份、消毒剂3.4份、粘结剂3份、水12份、除味剂2份。
所述吸附剂为膨润土。
所述膨润土为钠基膨润土。
所述消毒剂为纳米银,可通过商购得到,厂家为北京大华博科智能科技有限公司,牌号为AgNP50。
所述粘结剂为聚乙烯醇,牌号为聚乙烯醇1788。
所述除味剂为葡萄糖酸锌。
提供了除味猫砂的制备方法,所述制备方法包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成3mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度300℃,干燥时间2小时,即的。
实施例6
提供了一种除味猫砂,按重量份计,制备原料包括吸附剂85份、吸水剂6份、消毒剂3.4份、粘结剂3份、水12份、除味剂2份。
所述吸附剂为膨润土。
所述膨润土为钠基膨润土。
所述吸水剂为硫酸镁。
所述消毒剂为纳米银,可通过商购得到,厂家为北京大华博科智能科技有限公司,牌号为AgNP50。
所述粘结剂为聚乙烯醇,牌号为聚乙烯醇0578。
所述除味剂为葡萄糖酸锌。
提供了除味猫砂的制备方法,所述制备方法包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成3mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度300℃,干燥时间2小时,即的。
实施例7
提供了一种除味猫砂,按重量份计,制备原料包括吸附剂85份、吸水剂6份、消毒剂3.4份、粘结剂3份、水12份、除味剂2份。
所述吸附剂为膨润土。
所述膨润土为钠基膨润土。
所述吸水剂为硫酸镁。
所述消毒剂为纳米银,可通过商购得到,厂家为北京大华博科智能科技有限公司,牌号为AgNP50。
所述粘结剂为聚乙烯醇,牌号为聚乙烯醇1799。
所述除味剂为葡萄糖酸锌。
提供了除味猫砂的制备方法,所述制备方法包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成3mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度300℃,干燥时间2小时,即的。
性能评价
1、将相同量的实施例1-5所制备的除味猫砂倒入干净的猫砂盆中,在其上方倾倒100ml含1g/100ml尿素的生理盐水,测试其完全吸收水分所需要的时间及结团时间;结团后将猫砂团铲除,观察实施例1-7所制备的除味猫砂散碎情况;观察并感受实施例1-7所制备的除味猫砂的粉尘性;结果列于表1。
表1测试结果
结团时间 | 吸水时间 | 散碎情况 | 粉尘性 | |
实施例1 | 4s | 3s | 未散碎 | 无粉尘 |
实施例2 | 6s | 5s | 未散碎 | 无粉尘 |
实施例3 | 5s | 4s | 未散碎 | 无粉尘 |
实施例4 | 13s | 7s | 未散碎 | 轻微粉尘 |
实施例5 | 10s | 25s | 未散碎 | 轻微粉尘 |
实施例6 | / | / | 未散碎 | 轻微粉尘 |
实施例7 | / | / | 未散碎 | 轻微粉尘 |
前述的实例仅是说明性的,用于解释本发明所述方法的一些特征。所附的权利要求旨在要求可以设想的尽可能广的范围,且本文所呈现的实施例仅是根据所有可能的实施例的组合的选择的实施方式的说明。因此,申请人的用意是所附的权利要求不被说明本发明的特征的示例的选择限制。在权利要求中所用的一些数值范围也包括了在其之内的子范围,这些范围中的变化也应在可能的情况下解释为被所附的权利要求覆盖。
Claims (10)
1.一种除味猫砂,其特征在于,按重量份计,制备原料至少包括:按重量份计,制备原料至少包括吸附剂80-95份、吸水剂2-10份、消毒剂0.05-5份、粘结剂2-4份、水5-15份、除味剂0.1-5份。
2.根据权利要求1所述的除味猫砂,其特征在于,所述吸附剂选自蛭石粉、膨润土、硅藻土、活性炭粉、碳酸钙粉等的一种或多种。
3.根据权利要求1或2所述的除味猫砂,其特征在于,所述吸附剂为膨润土。
4.根据权利要求1所述的除味猫砂,其特征在于,所述吸水剂为硫酸盐。
5.根据权利要求1所述的除味猫砂,其特征在于,所述消毒剂选自高分子消毒剂、胍盐消毒剂、无机盐消毒剂、季铵盐消毒剂中的一种或多种。
6.根据权利要求5所述的除味猫砂,其特征在于,所述无机盐消毒剂为纳米银。
7.根据权利要求1所述的除味猫砂,其特征在于,所述粘结剂选自黄原胶、羟甲基纤维素、羟丙基甲基纤维素、聚乙烯醇、聚乙烯吡咯烷酮、瓜尔胶中的一种或多种。
8.根据权利要求7所述的除味猫砂,其特征在于,所述聚乙烯醇的醇解度为87-89%。
9.根据权利要求1所述的除味猫砂,其特征在于,所述除味剂选自蓖麻油酸锌、葡萄糖酸锌、甘草锌、醋酸锌、柠檬酸锌、氨基酸锌、乙二胺四乙酸锌钠、草酸锌、乳酸锌和酒石酸锌中的一种或多种。
10.一种权利要求1-9任一项所述的除味猫砂的制备方法,其特征在于,所述制备方法至少包括以下步骤:
1)混料:按比例称取吸附剂、粘结剂、吸水剂、除味剂,通过混合搅拌机混合,之后过200目筛网;
2)造粒:将混料后的粉料加入球盘机,将消毒剂溶解于水中,再喷雾于球盘机中,待粉料形成2-5mm猫砂颗粒进入下一步;
3)干燥:通过输送设备将猫砂颗粒送入烘干机干燥,干燥温度280-330℃,干燥时间2小时,即的。