CN1130018A - 加热蒸散用的吸液芯棒 - Google Patents

加热蒸散用的吸液芯棒 Download PDF

Info

Publication number
CN1130018A
CN1130018A CN95109561.7A CN95109561A CN1130018A CN 1130018 A CN1130018 A CN 1130018A CN 95109561 A CN95109561 A CN 95109561A CN 1130018 A CN1130018 A CN 1130018A
Authority
CN
China
Prior art keywords
core rod
soup
weight
imbibiting core
imbibiting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN95109561.7A
Other languages
English (en)
Inventor
竹林祯浩
片山泰之
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Chemical Co Ltd
Original Assignee
Sumitomo Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP7042801A external-priority patent/JPH08239303A/ja
Application filed by Sumitomo Chemical Co Ltd filed Critical Sumitomo Chemical Co Ltd
Publication of CN1130018A publication Critical patent/CN1130018A/zh
Pending legal-status Critical Current

Abstract

本发明是有关加热蒸散用的吸液芯棒。该吸液芯棒含有一种或一种以上的多孔质粉末70～80重量％，一种或一种以上的粘合剂1～20重量％以及一种或一种以上的阴离子表面活性剂0.01～10重量％。本发明的吸液芯棒吸液性能优良，尽管在长时间使用的情况下也不会降低吸液的能力，因此能够均匀稳定地进行蒸散药液。

Description

加热蒸散用的吸液芯棒
本发明是有关加热蒸散用的吸液芯棒事宜。
过去，将吸液芯棒的一部分浸渍于杀虫液、芳香剂溶液等液体内。通过加热该芯棒的上部，使被芯棒吸入的液体蒸散。这种通过加热蒸散液剂的方法，许多人都比较熟悉了。
但是芯棒吸液能力(性能)优良，而且不会由于芯棒孔隙的堵塞引起吸液能力低下，在长时间使用的情况下，能够进行长时间稳定地蒸散药液是很难达到的。因此，希望能够开发出一种能使药液均匀并且稳定蒸散的吸液芯棒。
本发明的发明者，针对上述课题进行了各种各样的研究工作。结果发现通过添加阴离子表面活性剂，可使加热蒸散用吸液芯棒得到改善。经过长时间的测试实用观察，药液均匀蒸散并且药量的挥发得到了稳定，由此获得了本发明。
本发明涉及加热蒸散用吸液芯棒，它含有一种或一种以上的多孔质粉末70～98重量％和一种或一种以上粘合剂1～20重量％以及一种或一种以上阴离子表面活性剂0.01～10重量％(以下按本发明吸液芯棒记载)。
本发明的吸液芯棒中所使用的阴离子表面活性剂，可例举如下：
①脂肪酸的金属盐(钠、钾盐等碱金属盐)，②聚氧乙烯烷基芳基醚硫酸盐，③聚氧乙烯烷基磷酸酯盐等的磷酸酯盐类，④月桂基硫酸钠等的高级醇的硫酸酯盐，⑤十二烷基苯磺酸钠盐等的烷基芳基磺酸盐，⑥烷基磺酸盐，⑦芳基磺酸盐，⑧二辛基硫代丁二酸酯钠等的磺基丁二酸酯盐
本发明提到的表面活性剂，是指连木质素磺酸盐、芳香族磺酸盐的福尔马林缩合物、聚羧酸的碱金属盐等分散剂都包括在内的所谓广义的表面活性剂。
阴离子表面活性剂，在本发明的吸液芯棒中所配合的使用比率，通常为0.01～10重量％，比较合适的配合比率是0.1～5重量％。
本发明吸液芯棒所采用的多孔质粉末，可列举如下：
◆粘土    ◆滑石  ◆高岭土    ◆硅藻土◆石膏    ◆珍珠岩◆膨润土    ◆酸性白土◆玻璃纤维◆石绵  ◆氧化铝等无机粉末和有机粉末等。
该多孔质粉末的用量，占本发明的吸液芯棒总重量的比例，一般为70～98重量％，比较合适的比例是75～95重量％。
本发明的吸液芯棒所采用的粘合剂，可列举如下：
▲羧甲基纤维素钠 ▲甲基纤维素  ▲淀粉▲阿拉伯橡胶     ▲明胶        ▲聚乙烯醇等
该粘合剂的用量，占本发明的吸液芯棒总重量的比例为1～20重量％，比较合适的比例是3～15重量％。
另外，在本发明的吸液芯棒中，也可以再适量的添加色素，防腐剂等。
本发明的吸液芯棒，其操作工艺是先将粘合剂与多孔质粉末混合。然后，添加表面活性剂和水，通过混合、挤压、成型、干燥为成品。还有，使用水溶性表面活性剂情况时，也可以在混合搅拌时，预先将表面活性剂加到水中去。
本发明的吸液芯棒，可以采用将其中的一部分浸渍于药液中，使之吸取药液。通过加热芯棒的上部使该芯棒吸入的药液挥发出去的方法。
所用的药液中含杀虫活性成份和芳香成份等。
作为杀虫成份的种类，现列举如下：
◎丙烯菊酯     ◎丙炔菊酯     ◎呋喃菊酯◎戊炔菊酯     ◎苄呋菊酯     ◎生物反式丙烯菊酯◎生物丙烯菊酯 ◎右旋苯醚菊酯 ◎二氯苯醚菊酯◎五氟氯菊酯   ◎Terallethrin ◎Silafluofen◎MT1-500
等等拟除虫菊酯化合物。通常，该杀虫成份在药液中含0.1～10重量％。
另外，作为芳香成份，例如可列举出蔷薇花香料、茉莉花香料等。
所使用的药液中，较好是将含杀虫活性成分以及根据需要添加有香料、稳定剂、缓释剂等的杀虫液、芳香剂溶液等溶解于脂肪族饱和碳氢化合物(正链烷属烃)等溶剂中。这一类合适的溶剂中，现列举如下：
有机溶剂(生产厂家) ◇IP溶剂2028(出光石油化学产)◇NEOCHIOZOL(中央化成产)◇NORPAR-12(埃克森化学产)◇NORPAR-13(埃克森化学产)◇NORPAR-15(埃克森化学产)◇ISOPAR-M(埃克森化学产)等
◇0号溶剂 H    (日本石油产)◇0号溶剂 M    (日本石油产)◇0号溶剂 L    (日本石油产)◇正(链)烷属烃(三石.德士古化学产)◇DEOTOMIZOLA-1(吉富制药产)
使用上述列举的碳原子数10～18的脂肪族饱和碳氢化合物溶剂比较好。
在使用本发明的吸液芯棒之际，例如，可以适用于「特公平2-25885号公报」等记载的加热蒸散型杀虫装置，并且能够提高和发挥理想的杀虫效果。
该芯棒的加热温度，虽然是根据药液种类的不同而异。但是吸液芯棒的表面温度一般约为60℃～160℃，比较合适的温度在大约110℃～135℃的范围之内。
图1表示采用本发明的吸液芯棒所用的加热蒸散装置的范例。如图所示，在药液1中，吸液芯棒3的一部分浸渍在药液3中，使芯棒吸入药液。用加热器发热体2间接加热该芯棒的上部，以蒸散杀虫活性达到目的。
图1中1为药液，2为发热体，3为吸液芯棒。
【实施例】
表示生产制造本发明的吸液芯棒的制造例
 制造例    粘土重量％    珍珠岩重量％   α-淀粉重量％  羧甲基纤维素钠盐重量％  SorpolR 5060重量％
    1.   37.3    49.7*     6.2     3.7     3.1◆
    2.   39.0    52.0     6.5     1.9     0.6
    3.   36.9    49.1     6.1     1.8     6.1
    4.   34.7    46.2     5.8     1.7     11.6
    5.   37.3    49.7*     6.2     3.7     3.1
    6.   38.2    51.0*     6.4     3.8     0.6
    7.   37.8    50.2     6.3     3.8     1.9
 制造例   粘土重量％  珍珠岩重量％  α-淀物重量％  羧甲基纤维素钠型重量％  表面活性剂重量％/型号
    8  38.2  51.0  6.4     3.8  0.6/sorpolR 5029-0
    9  38.2  51.0  6.4     3.8  0.6/sorpolR 5039
 制造例   粘土重量％   珍珠岩重量％  硅藻土重量％  羧甲基纤维素钠盐重量％ 十二烷基苯磺酸钠重量％
   10   5.0   44.0    45     4.0     2.0
   11   40.0   40.0    10     8.0     2.0
※将上记各成份按照各制造例的不同比例要求进行充分混合，加水搅拌混练挤压成型后以35℃的温度进行12小时烘干，制成直径7毫米的吸液芯棒。
【注】制造例1.*：东兴珍珠岩工业株式会社产珍珠岩#52；粒子中内含
       250微米的粒子占30重量％以上。制造例5*：东兴珍珠岩工业株式会社产珍珠岩#54；粒子中内含
      5～10微米的粒子占43重量％。制造例6*：东兴珍珠岩工业株式会社产珍珠岩#38；粒子中内含
      40微米以上的粒子占43重量％。制造例1.◆：东邦化学产阴离子系表面活性剂、主成分：烷基芳基
        磺酸钠。制造例8.◆：东邦化学产阴离子系表面活性剂、主成分：烷基硫酸
        酯的钠盐。制造例9.◆：东邦化学产阴离子系表面活性剂、主成分：聚氧乙烯
        烷基芳基硫酸酯铵盐。
※下述的试验例是为了进行对比而将试验用的吸液芯棒的制造例作为参考例公布。
参考例1
粘土 38.5重量％
珍珠岩 51.3重量％(珍珠岩#52.同上)
α-淀粉 6.4重量％
羧甲基纤维素钠盐 3.8重量％
参考例2
粘土 39.2重量％
珍珠岩 52.3重量％(珍珠岩#52.同上)
α-淀粉 6.5重量％
羧甲基纤维素钠盐 2.0重量％
※将上记各成分按照参考例1和2要求的比例充分进行混合，加水搅拌混练。挤压成型后以35℃的温度进行12小时烘干，制成7毫米的吸液芯棒。
试验例1
将含有丙炔菊酯【益多克】(拟除虫菊酯化合物)0.667％(W/V)的正链烷属烃溶液，装入药液容器内。并将芯棒与瓶盖紧密组合成一体，使用附图1所示的装置，加热使发热体的表面温度大约在120℃左右，用硅胶柱捕集，加热开始之后4～6小时、104～106小时以及204～206小时的各2小时中挥散的药剂。然后用丙酮萃取，并测定药剂的挥发量。另外，由加热前后药液容器重量的减少测定药液的消失量。结果如表1所示
表1使用本发明的芯棒【益多克】挥发状况的观察
试验芯棒Sample  经过不同时间(小时) 【益多克】挥发量(毫克/2小时)  药液挥发量(毫克)
制造例1     4～6104～106204～206     1.471.621.75     234257215
制造例6     4～6104～106204～206     1.081.271.46     289202205
制造例7     4～6104～106204～206     1.061.371.40     283183215
制造例8     4～6104～106204～206     1.221.511.11     323192193
制造例9     4～6104～106204～206     0.941.321.22     266166351
参考例1     4～6104～106204～206     0.06小于0.01小于0.01     19小于1小于1
正如表1结果所示，由于使用了本发明的吸液芯棒，所以能够进行稳定的药剂的挥发。
为了确认本发明的吸液芯棒的吸液能力，进行了如下所示吸引【盖多克】药液的上升速度的试验。
将【益多克】药液(益多克0.667％W/V与正链烷属烃溶液)装入玻璃容器内，然后将芯棒下部垂直地浸渍于【益多克】药液中垂直放稳，测定将【益多克】药液吸上升至2厘米或3厘米所需要的时间。
结果示于表2中。
表2本发明的芯棒吸液速度的观察
    试验芯棒Sample     吸上药液所要时间(分)
    到达2厘米     到达3厘米
    制造例2制造例3制造例4制造例5     70525242     17010997100
    参考例1参考例2     180以上*1180以上*2
*1.时间180分钟后，吸液上升的距离为1.4厘米。
*2.时间180分钟后，吸液上升的距离为1.8厘米。
※经过检测结果表明，本发明的吸液芯棒吸液性能优良。即使长时间使用也没有降低吸液的能力，因此，能够稳定的进行药液的蒸散。

Claims (5)

1.一种加热蒸散用的吸液芯棒，它含有一种或一种以上的多孔质粉末70～98重量％，一种或一种以上的粘合剂1～20重量％以及一种或一种以上的阴离子表面活性剂0.01～10重量％。
2.根据权利要求1所述的吸液芯棒，它是采用以下的加热蒸散方法使药液加热蒸散的吸液芯棒，将吸液芯棒的一部分浸渍于药液中，使该芯棒吸入药液，通过加热该芯棒的上部使所吸入的药液蒸散出去。
3.根据权利要求1所述的吸液芯棒，它是将多孔质粉末、粘合剂和阴离子表面活性剂混合而制成的。
4.根据权利要求1-3中任何一项所述的吸液芯棒，其中所述阴离子表面活性剂是磺酸系或硫酸酯系的阴离子表面活性剂。
5.一种加热蒸散药液的方法，它包括将权利要求1-4中任何一项所述的吸液芯棒的一部分浸渍入药液中，使该吸液芯棒吸入药液，通过加热该吸液芯棒的上部使所吸入的药液蒸散出去。
CN95109561.7A 1995-03-02 1995-09-20 加热蒸散用的吸液芯棒 Pending CN1130018A (zh)