CN112576010A - Construction method of outer wall surface of bark texture coating - Google Patents
Construction method of outer wall surface of bark texture coating Download PDFInfo
- Publication number
- CN112576010A CN112576010A CN202011413997.5A CN202011413997A CN112576010A CN 112576010 A CN112576010 A CN 112576010A CN 202011413997 A CN202011413997 A CN 202011413997A CN 112576010 A CN112576010 A CN 112576010A
- Authority
- CN
- China
- Prior art keywords
- wall surface
- coating
- paint
- bark
- steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a construction method of an outer wall surface of a bark texture coating, which comprises the following steps: cleaning the wall surface; coating a concrete base surface interface agent on the wall surface; painting waterproof paint on the wall surface; painting putty on the wall surface; adhering mesh cloth on the wall surface; painting the putty on the wall surface; coating sealing primer on the wall surface; coating elastic texture paint on the wall surface, and performing napping operation; polishing and modifying the bark veins formed after the napping operation; and spraying finishing paint on the wall surface. The invention has the beneficial effects that the problems that the traditional coating wall surface in the prior art is a smooth wall surface, has no three-dimensional sense, is lack of change, has poor artistry, is not durable enough, is easy to change color and fall off and has high maintenance cost are effectively solved, and the construction method of the bark texture coating outer wall surface, which has the advantages of simple construction method, no toxicity, no smell, environmental protection, more three-dimensional sense and artistry on the wall surface, durability, difficult color change and low maintenance cost, is provided.
Description
Technical Field
The invention belongs to the technical field of building construction, and particularly relates to a construction method of an outer wall surface of a bark texture coating.
Background
The texture paint is widely applied to the wall surface of a building, and various personalized decorative models are molded by various coating tools such as a roller, a spray gun, a brush and the like, so that the artistic design style is fully displayed, and the artistic decorative type water-based paint wall surface with natural material feeling is formed. The texture coating wall surface shows a unique space visual angle by the infinite three-dimensional texture and the multiple-choice individual matching, and is popular with people. Compared with the traditional coating wall surface, the texture coating wall surface has the following advantages: the decorative pattern is green, natural, environment-friendly, non-toxic, tasteless, waterproof, strong in decorative texture, individual in manufacturing of the three-dimensional decorative pattern, strong in artistry and relatively low in cost. Brings the smooth wall coating into the brand new period of natural environment-friendly concave-convex coating.
At present, in the prior art, the traditional coated wall surface is formed by coating the exterior wall paint on the surface of an exterior wall in a rolling coating or spraying manner. The limitations of this prior art are: the traditional coating wall surface is a smooth wall surface, has no stereoscopic impression, lacks change, has poor artistry, is not durable enough, is easy to change color and fall off, and has high maintenance cost.
Therefore, the construction method for the exterior wall surface with the texture paint is designed, the traditional paint wall surface can be improved, the artistry and the decorative feeling of the wall surface are obviously improved, the retention degree is improved, the maintenance cost is reduced, and the aesthetic requirements of the modern society are met.
Disclosure of Invention
The invention provides a construction method of an outer wall surface of a bark-pattern texture coating, which effectively solves the problems that the traditional coating wall surface in the prior art proposed in the background art is a smooth wall surface, has no three-dimensional sense, is lack of change, has poor artistry, is not durable enough, is easy to change colors and fall off, and has high maintenance cost, and provides the construction method of the outer wall surface of the bark-pattern texture coating, which has the advantages of simple construction method, no toxicity, no smell, environmental protection, more three-dimensional sense and artistry on the wall surface, durability, difficult color change, and low maintenance cost.
In order to solve the technical problems, the invention adopts the following technical scheme: a construction method of an outer wall surface of a bark texture coating is characterized by comprising the following steps:
cleaning the wall surface;
coating a concrete base surface interface agent on the wall surface;
painting waterproof paint on the wall surface;
painting putty on the wall surface;
adhering a mesh cloth on the wall surface;
painting the putty on the wall surface;
coating sealing primer on the wall surface;
coating elastic texture paint on the wall surface, and performing napping operation;
polishing and modifying the bark veins formed after the napping operation;
and spraying finishing paint on the wall surface.
Further, the method also comprises the following steps before the wall surface is cleaned: and plastering and polishing the wall surface.
Further, in the step of painting the waterproof paint on the wall surface, the waterproof paint is painted twice.
Furthermore, in the step of coating the sealing primer on the wall surface, the sealing primer is coated twice.
Further, in the step of spraying finishing paint on the wall surface, the finishing paint is sprayed twice.
And further, coating a waterproof coating on the wall surface for more than 4 hours after the step of coating the concrete base surface interface agent on the wall surface is completed.
Further, in the step of coating the waterproof coating on the wall surface, the thickness of the waterproof coating is not less than 1.5 mm.
Further, before the step of coating and sealing the priming paint on the wall surface, the water content of the base layer of the wall surface is less than 10%, and the PH value is less than 10.
Furthermore, the wall surface is coated with the elastic texture paint, in the napping operation step, the thickness of the plane layer of the elastic texture paint is not less than 2mm, the thickness of the grain layer is 1-3mm higher than that of the plane layer, and the width of the grain formed by napping is 10-25 mm.
Further, in the step of spraying the finishing coat on the wall surface, a spray gun is used for operation, the pressure of the spray gun is 0.4-0.8Mpa, the spray gun is perpendicular to the wall surface during operation, and the distance between the gun head and the wall surface is 500 mm.
The construction method of the outer wall surface of the bark texture paint, which is designed by the invention, is simple, nontoxic, odorless, green and environment-friendly, the wall surface has more stereoscopic impression and artistry, is durable in use, is not easy to discolor, is low in maintenance cost, the artistry and the decorative impression of the wall surface are obviously improved, and the aesthetic requirements of the modern society are met.
Drawings
In order to more clearly illustrate the embodiments of the present invention or the technical solutions in the prior art, the drawings used in the description of the embodiments or the prior art will be briefly described below, and it is obvious that the drawings in the following description are only some embodiments of the present invention, and for those skilled in the art, other drawings can be obtained according to these drawings without creative efforts.
FIG. 1 is a flow chart of method steps for one embodiment of the present invention;
FIG. 2 is a schematic view of the structure of each layer of the outer wall surface of the bark-textured paint according to one embodiment of the present invention.
In the figure:
1. plastering layer 2, concrete interface treating agent 3 and polyurethane waterproof coating layer
4. First waterproof anti-crack putty 5, alkali-resistant fiber mesh cloth 6 and second waterproof anti-crack putty
7. Alkali-resistant sealing primer 8, elastic texture paint 9 and finishing paint
10. Wall surface
Detailed Description
The invention is further illustrated by the following examples and figures.
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention will be described in further detail with reference to the accompanying drawings in conjunction with the following detailed description. It should be understood that the description is intended to be exemplary only, and is not intended to limit the scope of the present invention. Moreover, in the following description, descriptions of well-known structures and techniques are omitted so as to not unnecessarily obscure the concepts of the present invention.
Referring to the attached drawings 1 and 2, the invention provides a construction method of an external wall surface of a bark texture coating, which comprises the following steps:
cleaning the wall surface 10;
coating a concrete base surface interface agent 2 on the wall surface 10;
painting waterproof paint on the wall surface 10;
painting putty on the wall surface 10;
adhering a mesh cloth on the wall surface 10;
painting the putty on the wall surface 10;
coating sealing primer on the wall surface 10;
coating the elastic texture paint 8 on the wall surface 10 and performing napping operation;
polishing and modifying the bark veins formed after the napping operation;
and spraying finishing paint 9 on the wall surface 10.
Specifically, before the step of cleaning the wall surface 10, the method further comprises the steps of: plastering and sanding the wall surface 10. In the step of plastering the wall surface 10, cement mortar with strength greater than M15 can be used for plastering, and it should be noted that gypsum mortar and mixed mortar are strictly forbidden because the gypsum mortar has lower strength than cement mortar and the setting process is slower than cement mortar, so that the phenomena of uneven hardness and poor hardness can be generated, and the wall surface is easy to break when being subjected to external force. Preferably, in order to prevent the plastering layer 1 from cracking, the average thickness of the plastering layer 1 should be not more than 20mm, and the maximum thickness of the plastering layer 1 should be not more than 25 mm.
Preferably, in the step of plastering the wall surface 10, the flatness of the wall surface 10 is less than 2 mm.
If the wall surface 10 has good flatness or the out-of-tolerance is not too serious, the plastering step can be omitted, and the next step can be directly carried out after the grinding machine is used for grinding the out-of-tolerance part.
Specifically, in the polishing step, the loose, skinned, hollowed, and differentiated wall surface base layer is to be thoroughly removed.
Specifically, in the step of cleaning the wall surface 10, a high-pressure air pump or a high-pressure water gun may be used to purge or clean the wall surface 10, so as to ensure that the wall surface 10 is clean and free of dust.
Preferably, if the surface of the wall 10 is heavily soiled, the wall 10 may be flushed with a soda solution to ensure that the wall 10 is level, firm, solid, clean, dry, and free of oil stains.
Specifically, in the step of coating the concrete base surface interface agent 2 on the wall surface 10, in order to coat the concrete base surface interface agent 2 once, a concrete base surface interface agent having high permeability and matching with the polyurethane coating can be used, so as to enhance the binding degree of the polyurethane coating and the cement surface, and prevent the coating layer from falling or cracking.
Specifically, after the step 2 of coating the concrete-based surface interface agent on the wall surface 10 is completed for more than 4 hours, the step of coating the waterproof coating on the wall surface 10 is performed after the concrete-based surface interface agent 2 is completely dried.
Specifically, in the step of applying the waterproof coating material on the wall surface 10, in order to apply the waterproof coating material twice, preferably, a polyurethane waterproof coating material may be used. The polyurethane waterproof coating has the characteristics of high strength, high elongation, good water resistance, high durability and the like, has strong adaptability to deformation of a base layer, is green and environment-friendly, is nontoxic and tasteless, does not pollute the environment, and does not harm a human body. In the process of brushing the polyurethane waterproof coating, the polyurethane waterproof coating is uniformly brushed and cannot be missed, and the thickness of the polyurethane waterproof coating layer 3 is not less than 1.5 mm.
Specifically, in the substep of painting putty on the wall surface 10, in order to paint putty once, preferably, the adopted putty is the first waterproof anti-cracking putty 4, and the waterproof anti-cracking putty 4 has waterproof and anti-cracking functions, so that the wall surface can be effectively prevented from being affected with damp, cracked and the like. And leveling the base layer of the wall surface 10.
Specifically, in the step of adhering the mesh cloth to the wall surface 10, in order to adhere a layer of mesh cloth, preferably, the adopted mesh cloth is an alkali-resistant fiber mesh cloth 5, and the alkali-resistant fiber mesh cloth 5 has super-strong alkali-resistant performance, good flexibility and strong high tensile force. Specifically, the alkali-resistant fiber mesh cloth 5 is pressed into the first waterproof anti-cracking putty 4 by using an iron trowel, so that the alkali-resistant fiber mesh cloth 5 is ensured to be flat, and the phenomena of folds, hollowing and the like cannot occur.
Specifically, after the step of adhering the mesh cloth to the wall surface 10, in the substep of brushing putty on the wall surface 10, in order to brush putty once, preferably, the adopted putty is second waterproof anti-crack putty 6, and the waterproof anti-crack putty 6 has waterproof and anti-crack functions, so that the conditions of wetting, cracking and the like of the wall surface can be effectively prevented. And accurately level the wall surface 10. The second waterproof anti-crack putty 6 is to completely cover the alkali-resistant fiber mesh cloth 5, so that the whole wall surface is kept smooth and flat without scratches, cracks and the like.
Preferably, before the step of coating the sealing primer on the wall surface 10, the wall surface 10 is polished flat with fine sand paper, and the floating dust is blown clean. The water content of the base layer of the wall surface 10 is less than 10 percent, and the pH value is less than 10.
Specifically, in the step of applying the sealing primer on the wall surface 10, the sealing primer is applied twice, and preferably, the sealing primer used is the alkali-resistant sealing primer 7, which is of a type of coloring type for supporting the overall color of the wall surface 10.
Preferably, in the step of applying the sealing primer to the wall surface 10, a roller coating using a brush roller is performed. The roller coating needs to be uniform and cannot be missed.
Specifically, the wall surface 10 is coated with the elastic texture coating 8, and in the roughening operation step, preferably, the roughening operation direction is vertical roughening to form a bark texture wall surface, or horizontal roughening or inclined roughening can be selected to form artistic texture wall surfaces with different texture effects.
Preferably, the method of painting the flexible texture paint 8 on the wall surface 10 is roll coating.
Preferably, the thickness of the plane layer of the elastic texture coating 8 is not less than 2mm, the thickness of the grain layer is 1-3mm higher than that of the plane layer, and the width of the grain formed by galling is 10-25 mm.
Specifically, in the napping operation step, the elastic texture coating 8 is coated on the wall surface 10 by a roller or a scraper, the thickness of the elastic texture coating 8 is kept uniform, the viscosity is proper, then the napping is carried out by a bare plastic roller, the roller is kept uniform in dipping during napping, the force is consistent, the napping is carried out from top to bottom, one plate is close to the other plate, the joint of the two plates is pulled by the roller again, and the napping can be carried out for multiple times until the napping effect with clear texture, narrow width and consistent depth style is formed.
Preferably, the two sides and the corners of the door/window opening of the wall surface 10 are brushed by a hairbrush and a 4-inch smooth roller.
Preferably, when the wall surface is high, double rows of scaffolds need to be erected under the wall, one step is performed in the vertical direction of 1.8m, one person operates each step, the wall surface 10 is napped from top to bottom, each plate is napped from top to bottom, and the texture is ensured to be communicated up and down, so that the effect is consistent.
It should be noted that the wall surface 10 may be hardened about 40 minutes after the roughening operation, and before the hardening, the roughening effect needs to be checked, and if the roughening effect is found to be unsatisfactory, the roughening operation needs to be performed again. If the galling effect is found to be not satisfactory after hardening, only the galling effect can be ground off, and construction is carried out again.
Preferably, the finishing step is performed by drying the wall surface 10 for at least 48 hours before the finishing step is performed on the bark lines formed after the napping operation.
Preferably, in the step of polishing and modifying the bark veins formed after the napping operation, fine sand paper with a size of more than P280 meshes can be adopted, light polishing is carried out manually, only barbs, isolated sand and sharp corners on the surface are polished, and the formed outer surface veins are deeper and can reach 1-3 mm. The polishing method has the advantages of clear layering, rough visual effect and strong visual impact.
Preferably, in another scheme, in the step of polishing and modifying the bark veins formed after the napping operation, P80 sand paper can be used for mechanical polishing, the napped twigs are all polished off, only the main twigs and the knots are reserved, and the distance between the main twigs and the knots and the distance between the knots and the wall surface 10 are 0.5-1 mm. The polishing method has the advantages that after the step of spraying the finishing finish 9 on the wall surface 10, trunk-shaped branches can be formed, and the ornamental effect of three-dimensional painting is achieved.
Specifically, in the step of spraying the finishing coat 9 on the wall surface 10, the finishing coat 9 is sprayed twice, so that the finishing coat 9 is fully penetrated. The wall surface 10 is in a concave-convex state, and is painted by a spray gun. Preferably, the pressure of the spray gun is 0.4-0.8Mpa, the spray gun is perpendicular to the wall surface 10 during spraying, and the distance between the gun head and the wall surface 10 is 500 mm. When the spray gun is used for spraying, the spray gun moves in parallel at a constant speed.
The finishing coat 9 has waterproof and antifouling functions, contains fluorocarbon, and has strong weather resistance and durability.
In other embodiments of the invention, the construction method can also be used for decorating inner walls and non-spraying wall surfaces, and the steps of coating waterproof paint on the wall surfaces and pasting the mesh cloth on the wall surfaces can be omitted when the inner walls and the non-spraying wall surfaces are decorated.
It is to be understood that the above-described embodiments of the present invention are merely illustrative of or explaining the principles of the invention and are not to be construed as limiting the invention. Therefore, any modification, equivalent replacement, improvement and the like made without departing from the spirit and scope of the present invention should be included in the protection scope of the present invention. Further, it is intended that the appended claims cover all such variations and modifications as fall within the scope and boundaries of the appended claims or the equivalents of such scope and boundaries.
Claims (10)
1. A construction method of an outer wall surface of a bark texture coating is characterized by comprising the following steps:
cleaning the wall surface;
coating a concrete base surface interface agent on the wall surface;
painting waterproof paint on the wall surface;
painting putty on the wall surface;
adhering a mesh cloth on the wall surface;
painting the putty on the wall surface;
coating sealing primer on the wall surface;
coating elastic texture paint on the wall surface, and performing napping operation;
polishing and modifying the bark veins formed after the napping operation;
and spraying finishing paint on the wall surface.
2. The method as claimed in claim 1, further comprising the steps of: and plastering and polishing the wall surface.
3. The method as claimed in claim 1, wherein the step of applying the waterproof paint to the wall surface comprises applying the waterproof paint twice.
4. The method for constructing an exterior wall surface with a bark texture coating as claimed in claim 1, wherein the method comprises the following steps: and in the step of coating the sealing primer on the wall surface, the sealing primer is coated twice.
5. The method for constructing an exterior wall surface with a bark texture coating as claimed in claim 1, wherein the method comprises the following steps: and in the step of spraying finishing paint on the wall surface, spraying the finishing paint twice.
6. The method for constructing an exterior wall surface with a bark texture coating as claimed in claim 1, wherein the method comprises the following steps: and coating a waterproof coating on the wall surface after the step of coating the concrete base surface interface agent on the wall surface is completed for more than 4 hours.
7. The method for constructing an exterior wall surface with a bark texture coating as claimed in claim 1, wherein the method comprises the following steps: and in the step of coating the waterproof coating on the wall surface, the thickness of the waterproof coating is not less than 1.5 mm.
8. The method for constructing an exterior wall surface with a bark texture coating as claimed in claim 1, wherein the method comprises the following steps: before the step of coating and sealing the priming paint on the wall surface, the water content of the base layer of the wall surface is less than 10%, and the PH value is less than 10.
9. The method for constructing an exterior wall surface with a bark texture coating as claimed in claim 1, wherein the method comprises the following steps: and brushing an elastic texture coating on the wall surface, wherein in the step of napping, the thickness of a plane layer of the elastic texture coating is not less than 2mm, the thickness of a grain layer is 1-3mm higher than that of the plane layer, and the width of grains formed by napping is 10-25 mm.
10. The method for constructing an exterior wall surface with a bark texture coating as claimed in claim 1, wherein the method comprises the following steps: and in the step of spraying the finishing coat on the wall surface, a spray gun is used for operation, the pressure of the spray gun is 0.4-0.8Mpa, the spray gun is perpendicular to the wall surface during operation, and the distance between the gun head and the wall surface is 500 mm.