CN103952052A - Travertine-like elastic texture coating and preparation method thereof - Google Patents
Travertine-like elastic texture coating and preparation method thereof Download PDFInfo
- Publication number
- CN103952052A CN103952052A CN201410219129.1A CN201410219129A CN103952052A CN 103952052 A CN103952052 A CN 103952052A CN 201410219129 A CN201410219129 A CN 201410219129A CN 103952052 A CN103952052 A CN 103952052A
- Authority
- CN
- China
- Prior art keywords
- coating
- texture coating
- flexible texture
- adopts
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a travertine-like elastic texture coating and a preparation method thereof, belonging to elastic texture coatings. The coating comprises the following components by mass percent: waterborne elastic pure acrylic emulsion, inorganic bentonite, a pH regulator, a wetting agent, a dispersing agent, a preservative, a film forming aid, an antifreezing agent, water, a defoaming agent, ground calcium carbonate powder, titanium dioxide, a thickening agent and sand. The travertine-like elastic texture coating has the beneficial effects that as the elastic pure acrylic emulsion is used, the coating has certain flexibility and can effectively make up the cracks of walls, improve the decorative effects of products, realize good weatherability, protect the walls and prolong the service lives of buildings; as inorganic bentonite is used in collocation with the thickening agent, the product has good storage stability, is beneficial for the forming effects during construction, and enables the travertine effect to be more vivid.
Description
Technical field
The present invention relates to stone-like coating preparation field, particularly relate to imitative hole stone flexible texture coating of a kind of imitative hole stone effect and preparation method thereof.
Background technology
At present, along with protection and aesthetic raising, the buildings to villa, European style, the wall of public building finishing requires more and more higher, if but building wall is imitated stone effect for reaching, and directly with stone material, not only material cost is high and construction cost is also higher.And common elastic coating is used on the wall of building, cannot reach again imitative stone, particularly the flexible texture of imitative hole stone is coated with effect, therefore, how to produce a kind of coating, can be the problem that need to solve in the flexible texture effect of the imitative hole of building wall realization stone.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of imitative hole stone flexible texture coating and preparation method thereof, can realize at building wall the flexible texture effect of imitative hole stone, cannot be in the problem of the flexible texture of the imitative hole of building wall realization stone thereby solve existing elastic coating.
For solving the problems of the technologies described above, the invention provides a kind of imitative hole stone elastic coating, the formula of this coating is by mass percentage:
The present invention also provides the preparation method of a kind of imitative hole stone flexible texture coating, gets each raw material by the formula of imitative hole of the present invention stone elastic coating, and preparation process is as follows:
By aqueous elastic pure acrylic latex, pH adjusting agent, wetting agent, dispersion agent, sanitas, film coalescence aid, frostproofer and defoamer add in disc type dispersion machine successively by formula consumption, stir 5 minutes in the speed of 400r/min by described disc type dispersion machine, after stirring, add successively dicalcium powder, titanium dioxide, wilkinite, described disc type dispersion machine speed is carried to the rotating speed of 400～1470r/min and carried out dispersed with stirring, fineness reaches after 70 microns and adds the thickening material that accounts for described thickening material gross weight 80～90% to regulate viscosity, by made slurry transport to the paint equipment of screw blade, add quartz sand to mix colours, after adding remaining thickening material to finely tune finished product viscosity after having mixed colours, make imitative hole stone flexible texture coating.
Beneficial effect of the present invention is: owing to using elasticity pure acrylic latex, make this coating have certain flexibility, can effectively make up body of wall crackle; improve the decorative effect of product; and can have good weathering resistance, protection body of wall, the work-ing life of prolongation buildings.Use inorganic bentonite collocation thickening material to make product there is good stability in storage, when construction, be conducive to molding effect, make hole stone effect more true to nature.This coating can reach hole stone material decorative effect after constructing by Recipe, and can be for indoor or outdoor, and all raw material is aqueous environment protection, and made finished product has the good feature of environmental protection, can HUMAN HEALTH and environment not damaged and be polluted.Use the engineering of this coating in reaching decorative effect, to save finishing work cost, save and protected natural Mineral resources.
Embodiment
Below the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiment.Based on embodiments of the invention, those of ordinary skill in the art, not making the every other embodiment obtaining under creative work prerequisite, belong to protection scope of the present invention.
A kind of imitative hole of embodiment of the present invention stone elastic coating, the formula of this coating is by mass percentage:
In the stone elastic coating of above-mentioned imitative hole, pH adjusting agent adopts 2-amino-2 methyl isophthalic acid propyl alcohol;
Dispersion agent adopts sodium salt dispersion agent;
Sanitas adopts any in CMIT, MIT;
Film coalescence aid adopts alcohol ester 12;
Frostproofer adopts propylene glycol;
Defoamer adopts mineral oil type;
Dicalcium powder adopts water-ground limestone;
Titanium dioxide adopts Rutile type Titanium Dioxide;
Thickening material adopts alkali swelling type thickening material.
The embodiment of the present invention provides the preparation method of a kind of imitative hole stone flexible texture coating, gets each raw material by the formula of above-mentioned imitative hole stone flexible texture coating, and preparation process is as follows:
By aqueous elastic pure acrylic latex, water, pH adjusting agent, wetting agent, dispersion agent, sanitas, film coalescence aid, frostproofer and defoamer add in disc type dispersion machine successively by formula consumption, stir 5 minutes in the speed of 400r/min by described disc type dispersion machine, after stirring, add successively dicalcium powder, titanium dioxide, wilkinite, described disc type dispersion machine speed is carried to the rotating speed of 400～1470r/min and carried out dispersed with stirring, fineness reaches after 70 microns and adds the thickening material that accounts for described thickening material gross weight 80～90% to regulate viscosity, by made slurry transport to the paint equipment of screw blade, add quartz sand to mix colours, after adding remaining thickening material to finely tune finished product viscosity after having mixed colours, make imitative hole stone flexible texture coating.
Below in conjunction with specifically using the implementation process of coating of the present invention to coating of the present invention is described further.
Embodiment 1
The present embodiment provides a kind of imitative hole stone flexible texture coating, and its preparation method is as follows:
Get each raw material by following formula:
The preparation process of above-mentioned imitative hole stone flexible texture coating is as follows:
By aqueous elastic pure acrylic latex, water, pH adjusting agent, wetting agent, dispersion agent, sanitas, film coalescence aid, frostproofer and defoamer add in disc type dispersion machine successively by formula consumption, stir 5 minutes in the speed of 400r/min by described disc type dispersion machine, after stirring, add successively dicalcium powder, titanium dioxide, wilkinite, described disc type dispersion machine speed is carried to the rotating speed of 400～1470r/min and carried out dispersed with stirring, fineness reaches after 70 microns and adds the thickening material that accounts for described thickening material gross weight 80～90% to regulate viscosity, by made slurry transport to the paint equipment of screw blade, add quartz sand to mix colours, after adding remaining thickening material to finely tune finished product viscosity after having mixed colours, make imitative hole stone flexible texture coating.
Embodiment 2
The present embodiment provides a kind of imitative hole stone flexible texture coating, and its preparation method is as follows:
Get each raw material by following formula:
The preparation process of above-mentioned imitative hole stone flexible texture coating is as follows:
By aqueous elastic pure acrylic latex, water, pH adjusting agent, wetting agent, dispersion agent, sanitas, film coalescence aid, frostproofer and defoamer add in disc type dispersion machine successively by formula consumption, stir 5 minutes in the speed of 400r/min by described disc type dispersion machine, after stirring, add successively dicalcium powder, titanium dioxide, wilkinite, described disc type dispersion machine speed is carried to the rotating speed of 400～1470r/min and carried out dispersed with stirring, fineness reaches after 70 microns and adds the thickening material that accounts for described thickening material gross weight 80～90% to regulate viscosity, by made slurry transport to the paint equipment of screw blade, add quartz sand to mix colours, after adding remaining thickening material to finely tune finished product viscosity after having mixed colours, make imitative hole stone flexible texture coating.
Embodiment 3
The present embodiment provides a kind of imitative hole stone flexible texture coating, and its preparation method is as follows:
Get each raw material by following formula:
The preparation process of above-mentioned imitative hole stone flexible texture coating is as follows:
By aqueous elastic pure acrylic latex, water, pH adjusting agent, wetting agent, dispersion agent, sanitas, film coalescence aid, frostproofer and defoamer add in disc type dispersion machine successively by formula consumption, stir 5 minutes in the speed of 400r/min by described disc type dispersion machine, after stirring, add successively dicalcium powder, titanium dioxide, wilkinite, described disc type dispersion machine speed is carried to the rotating speed of 400～1470r/min and carried out dispersed with stirring, fineness reaches after 70 microns and adds the thickening material that accounts for described thickening material gross weight 80～90% to regulate viscosity, by made slurry transport to the paint equipment of screw blade, add quartz sand to mix colours, after adding remaining thickening material to finely tune finished product viscosity after having mixed colours, make imitative hole stone flexible texture coating.
Imitative hole of the present invention stone elastic coating, makes finishing material on the wall such as the base material that is used in buildings, the public building of villa, European style is outward cement, concrete, bake bricks, and forms hole stone effect, thereby plays the function of protection, decoration and beautifying city.
Owing to adopting emulsion and the natural siliceous sand as aggregate layer to prepare, weathering resistance is splendid, aqueous, environmental protective, nontoxic, harmless, pollution-free.
The technical parameter of this coating is as follows:
Store: depositing in 0～40 DEG C of dry place (avoiding sunlight direct irradiation), is at least one year not opening in original packing situation;
At condition in container: thick-slurry type liquid;
Brushing condition: envrionment temperature is higher than the non-overcast and rainy construction of 5 DEG C, and basic unit's temperature is not higher than 40 DEG C;
Theoretical consumption: 2.5-3.0kg/m
2(different according to basic unit's situation and the different material consumptions of workman's construction level);
Surface drying time: 4 hours (23 DEG C of temperature, relative humidity 50%);
Can repainting hours: 8 hours (temperature is more than 23 DEG C, and relative humidity is below 50%).
Utilize the construction requirement of this coating as follows:
The requirement of base material:
Before base treatment, body of wall needs the maintenance of certain hour, and the curing time in general new cement wall surface winter is 28 days, and the curing time in summer is 14 days.Maintenance is less than 10 to the pH value of basic unit, after water ratio is less than 10%, then carries out processing base level.
Basic unit should clean, surperficial free from dust, without laitance, oil stains-less, without rust staining, without mildew, without salt precipitate with without foreign material such as mosses.
Matching system:
The constructing operation method of this flexible texture coating is:
Form of construction work: trowelling or spraying application;
Dilution: without the construction that adds water, but according to execution conditions, can suitably add water and regulate working viscosity;
Instrument clean: clean with clean water.
Concrete operation step is:
(1) metope base treatment → scrape (smearing) to be coated with 1-2 time → roller coating alkali-resistant sealing primer of Special flexible repairing material, 1 time → roller coating environmental-protection decorative priming paint, 1-2 time → snap the line lattice → brushing environmental-protection decorative priming paint → paste U.S. line paper → trowelling or spray flexible texture coating 1-2 time, remove adhesive tape → spraying environmental protection coating varnish, 1-2 time
(2) processing base level:
Before base treatment, should thoroughly remove loose, peeling,
The basic unit of hollowing, efflorescence, removes the pollutents such as floating ash, greasy dirt.
(3) Special flexible is repaired material:
Special flexible is repaired material and is divided twice construction, and one time blade coating thickness should not exceed 2mm, and per pass is not less than 5 hours (25 DEG C) interval time.After per pass blade coating, to suitably (25 DEG C, dry 4-6 hour) polishing finishing of part, after polishing, remove floating ash.
Special flexible is repaired material needs abundant dry solidification, is less than 10 to pH value, after water ratio is less than 10%, can carry out the construction of next process.
(4) roller coating alkali-resistant sealing primer:
After Special flexible is repaired the abundant dry solidification of material, roller coating alkali-resistant sealing primer one time, requires brushing evenly, never can have holiday phenomenon.When alkali-resistant sealing primer construction, forbid being watered, guarantee that priming paint is not polluted simultaneously.
(5) roller coating priming paint:
The brushing of special alkali resistant priming paint must be even, converts the water of 5-10%, makes it hide ground completely, the color of special alkali resistant priming paint will with the solid colour of texture coating, there is grow diming phenomenon to prevent that texture coating from revealing the exact details, dividing joint need to use special product to retouch seam.
(6) snap the line lattice, retouches seam, tapes:
Carry out snap the line, lattice, tape according to design requirements.When texture coating large-area construction, interlayer seam is stayed in suggestion, while not staying interlayer seam, can use stowing as design.
With small brushes brushing dividing joint along the line paint, retouch line width and be controlled in the design each 1cm in width both sides, can not be wide or narrow, so as not to there is bottom drain, not cover end impact attractive in appearance.
After environmental-protection decorative priming paint complete drying, Continuous pressing device for stereo-pattern along the line, requires smooth vertical and horizontally, hands over circle.Select suitable U.S. line paper according to different construction seasons.
(7) trowelling or spraying flexible texture coating:
After treating that adhesive tape posts, application flexible texture coating, trowelling texture coating 1-2 time.Open bucket stir evenly rear with plasterer's trowel by even texture coating blade coating the surface to body of wall, then with special instrument, coating is carefully rubbed to concavo-convex hole stone effect back and forth, then with spatula, its surface is received to effect even, as need reach better effect can twice construction.
The linking of construction operation section should remain on dividing joint negative and positive angle or downcomer place, and the metope without lattice is required to reasonable arrangement personnel and facility, keeps wet and touches wet linking, avoids occurring connecing stubble.Summer temperature is higher, while using between nacelle construction and floor without frame bar, for avoiding occurring the irregular stubble that connects, suggestion is divided into construction operation section three crosspieces (every section as 1 meter left and right) taking layer as unit, the first paragraph of first constructing, construct the 3rd section, the second segment of finally constructing, uses adhesive tape to carry out dark parting when one section of every construction again.For avoiding occurring vertically connecing stubble, the several hanging baskets of each metope synchronously operate.
(8) spraying fine work environmental protection coating varnish:
After texture coating complete drying, spray environmental protection coating varnish 1～2 time, when environmental protection coating varnish uses, forbid to be watered, when spraying application, muzzle need be perpendicular to metope, and each rifle presses 1/3rd of a rifle, and when construction, spray gun at the uniform velocity moves, and can not occur holiday phenomenon.
The above; only for preferably embodiment of the present invention, but protection scope of the present invention is not limited to this, is anyly familiar with in technical scope that those skilled in the art disclose in the present invention; the variation that can expect easily or replacement, within all should being encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claims.
Claims (9)
1. an imitative hole stone flexible texture coating, is characterized in that, the formula of this coating is by mass percentage:
2. imitative hole according to claim 1 stone flexible texture coating, is characterized in that, described pH adjusting agent adopts 2-amino-2 methyl isophthalic acid propyl alcohol.
3. imitative hole according to claim 1 stone flexible texture coating, is characterized in that, described dispersion agent adopts sodium salt dispersion agent;
Described sanitas adopts any in CMIT, MIT.
4. imitative hole according to claim 1 stone flexible texture coating, is characterized in that, described film coalescence aid adopts alcohol ester 12.
5. imitative hole according to claim 1 stone flexible texture coating, is characterized in that, described frostproofer adopts propylene glycol.
6. imitative hole according to claim 1 stone flexible texture coating, is characterized in that, described defoamer adopts mineral oil defoaming agent.
7. imitative hole according to claim 1 stone flexible texture coating, is characterized in that, described dicalcium powder adopts water-ground limestone;
Described titanium dioxide adopts Rutile type Titanium Dioxide.
8. imitative hole according to claim 1 stone flexible texture coating, is characterized in that,
Described thickening material adopts alkali swelling type thickening material.
9. a preparation method for imitative hole stone flexible texture coating, is characterized in that, gets each raw material by the formula of the imitative hole stone flexible texture coating described in claim 1 to 8 any one, and preparation process is as follows:
By aqueous elastic pure acrylic latex, water, pH adjusting agent, wetting agent, dispersion agent, sanitas, film coalescence aid, frostproofer and defoamer add in disc type dispersion machine successively by formula consumption, stir 5 minutes in the speed of 400r/min by described disc type dispersion machine, after stirring, add successively dicalcium powder, titanium dioxide, inorganic bentonite, described disc type dispersion machine speed is carried to the rotating speed of 400～1470r/min and carried out dispersed with stirring, fineness reaches after 70 microns and adds the thickening material that accounts for described thickening material gross weight 80～90% to regulate viscosity, by made slurry transport to the paint equipment of screw blade, add quartz sand to mix colours, after adding remaining thickening material to finely tune finished product viscosity after having mixed colours, make imitative hole stone flexible texture coating.