CN100560667C - Marble paint for building, making method and construction technology thereof - Google Patents

Marble paint for building, making method and construction technology thereof Download PDF

Info

Publication number
CN100560667C
CN100560667C CNB2006100078783A CN200610007878A CN100560667C CN 100560667 C CN100560667 C CN 100560667C CN B2006100078783 A CNB2006100078783 A CN B2006100078783A CN 200610007878 A CN200610007878 A CN 200610007878A CN 100560667 C CN100560667 C CN 100560667C
Authority
CN
China
Prior art keywords
water
building
marble paint
marble
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2006100078783A
Other languages
Chinese (zh)
Other versions
CN101024750A (en
Inventor
郭祥恩
姜年超
赵雅文
刘东华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
First New Material Science & Technology Development Co., Ltd.
Original Assignee
FIRSTPAINT MANUFACTURING (BEIJING) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FIRSTPAINT MANUFACTURING (BEIJING) Co Ltd filed Critical FIRSTPAINT MANUFACTURING (BEIJING) Co Ltd
Priority to CNB2006100078783A priority Critical patent/CN100560667C/en
Publication of CN101024750A publication Critical patent/CN101024750A/en
Application granted granted Critical
Publication of CN100560667C publication Critical patent/CN100560667C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to marble paint for building, making method and construction technology thereof.This product is to comprise 11 kinds of raw materials such as natural stone-powder, water-based pure acrylic resin, water, inorganic dispersant, organic dispersing agent, film coalescence aid, thickening material, defoamer, wetting agent, sanitas and pH value conditioning agent, and each proportion of raw materials of marble paint, making method and construction technology see specification sheets for details.The present invention is a kind of water-borne coatings of single-component, and is nontoxic, and weathering resistance is good, exterior decorative effect with natural marble, relatively to have a cost low for natural marble, and the body of wall load-bearing is little, renovate characteristics such as easy, this products material is easy to get, and production method is simple, mainly is the process of mechanical dispersion and physical mixed, adopt the form of construction work of spraying, manual operation is convenient, meets environmental protection and service requirements, has broad application prospects.

Description

Marble paint for building, making method and construction technology thereof
Technical field
The present invention relates to the development technology and the operating technique of building coating, specifically, relate to marble paint for building, making method and construction technology thereof.
Background technology
The color of lithotome is subjected to the restriction of natural crystal color, make that the color of decorating back integral body can be not in full accord, and lithotome has from great, and is big to the load of body of wall, cost is high, be difficult to defective such as renovation, makes the coating of imitative stone effect arise at the historic moment.
After the common coating brushing, form the exterior decorative effect of concavo-convex match volume or layer planes, body of wall is played certain protection and decoration function, but the surface can not form the exterior decorative effect of lithotome.The coating surface that marble paint for building forms is level and smooth, bright, and lines is evenly clear, is exactly like lithotome in appearance.
The lithotome difficulty of construction is big, and especially the position, corner needs special processing treatment, and the slit between the stone material will add gap-filling glue, and construction finishes and will carry out whole waxing maintenance.And the marble paint for building hand spray, construct easily in the position, corner, and big area only needs lattice to handle, and need not joint filling.Surface spraying coating varnish is protected, and increases luminance brightness and texture effect.
The material cost height of lithotome, link plate need be beaten keel, and the cost and the stone material of keel are very nearly the same, and whole cost is higher, and the sheet material that particularly has arc modeling exceeds several times than planar.And the relative cost of marble paint for building is low, need not beat keel.
The decoration of lithotome is unalterable, can't renovate, and marble paint for building can directly renovate, and need not to destroy original basic unit.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art part, and provide a kind of raw material sources abundant, make simple, outer appearnce marble paint for building, making method and construction technology thereof like lithotome.
The object of the invention can reach by following measure: marble paint for building comprises natural stone-powder, water-based pure acrylic resin AC-261, water, inorganic dispersant sodium hexametaphosphate, organic dispersing agent SN-5040, film coalescence aid Texanol, thickening material HBR, defoamer NXZ, wetting agent X-405, sanitas LXZ and pH value conditioning agent AMP-95, and its mass percent is:
Constituent mass per-cent (%)
Natural stone-powder 50~70%
Water-based pure acrylic resin AC-261 20~40%
Water 4~6%
Inorganic dispersant sodium hexametaphosphate 0.8~1.5%
Organic dispersing agent SN-5040 0.4~0.6%
Film coalescence aid Texanol 0.2~1.4%
Thickening material HBR 0.12~0.15%
Defoamer NXZ 0.1~0.3%
Wetting agent X-405 0.1~0.2%
Sanitas LXZ 0.1~0.2%
PH value conditioning agent AMP-95 0.05~0.1%.
Water-based pure acrylic resin of the present invention is a high molecular synthetic resin, selects pure third resin of internationally renowned brand U.S. Rhom and Hass for use.
Selected filler is a natural stone-powder.
Auxiliary agent is meant 8 kinds of formulations such as inorganic dispersant, organic dispersing agent, film coalescence aid, thickening material, defoamer, wetting agent, sanitas and pH value conditioning agent.
Dispersion agent is some kinds in Henkel KGaA company and a Japanese Nuo Puke company, belongs to the polycarboxylic acid salt.
Film coalescence aid is the film-forming temperature that reduces acrylic resin, selects the product of U.S. Yi Shi Man for use.
Thickening material is a product of selecting U.S. Ya Kualong company for use, belongs to the Natvosol class.
Sanitas is a product of selecting U.S. Rhom and Hass for use.
PH value is adjusted and is belonged to the organic amine product.
Manufacture method is: elder generation joins 3% water, inorganic dispersant, organic dispersing agent, film coalescence aid, thickening material, defoamer, wetting agent, sanitas, pH value conditioning agent and water-based pure acrylic resin in the dispersion cylinder, under the state of 300-400rpm, stir evenly, with the water of remainder, all stone flour addings, 15min gets final product in the 1200-1600rpm high speed dispersion again.
Marble paint for building adopts the mode of hand spray to construct; After the paint film polishing, the body varnish cover.
The present invention compared with prior art has following advantage: product of the present invention is a kind of water-borne coatings of single-component, and is nontoxic, weathering resistance is good, has the exterior decorative effect of natural marble, relatively to have a cost low for natural marble, and the body of wall load-bearing is little, renovates characteristics such as easy, simultaneously, this products material is easy to get, and production method is simple, mainly is the process of mechanical dispersion and physical mixed, adopt the form of construction work of spraying, manual operation is convenient, meets environmental protection and service requirements, has broad application prospects.
Embodiment
Enumerate an embodiment below, the present invention is further specified, but the present invention is not only limited to this embodiment.
Embodiment 1
Marble paint for building is prepared by following prescription:
Component Mass percent (%)
Natural stone-powder 61%
Water-based pure acrylic resin AC-261 30%
Water 5.33%
The inorganic dispersant Sodium hexametaphosphate 99 1.3%
Organic dispersing agent SN-5040 0.4%
Film coalescence aid Texanol 1.4%
Thickening material HBR 0.12%
Defoamer NXZ 0.2%
Wetting agent X-405 0.1%
Sanitas LXZ 0.1%
PH value conditioning agent AMP-95 0.05%
Manufacture method: elder generation joins 3% water, inorganic dispersant, organic dispersing agent, film coalescence aid, thickening material, defoamer, wetting agent, sanitas, pH value conditioning agent and water-based pure acrylic resin in the dispersion cylinder, under the state of 300~400rpm, stir evenly, with the water of remainder, all stone flour addings, 15min gets final product in 1200~1600rpm high speed dispersion again.
Construction technology:
Construction process is: metope base treatment → scrape (smearing) is coated with anticracking grout 1 time, compound alkali-resistant glass fiber mesh cloth of while → scrape (smearing) to be coated with flexible waterproof putty 2-3 time → brush seal coat → snap the line, lattice, the marble paint of taping → apply → spray coating varnish.
The concrete operations step is:
1. processing base level: before base treatment, body of wall needs the maintenance of certain hour, and the curing time in general new cement wall surface winter is 28 days, and the curing time in summer is 14 days.Maintenance is arrived the pH value of basic unit less than 10, and water ratio carries out processing base level again after 10%.
Should thoroughly remove loose, peeling, hollowing, atomizing basic unit before the base treatment, then, remove pollutents such as dust, greasy dirt.
2. the blade coating anticracking grout meets alkaline-resisting screen cloth
By service requirements configuration anticracking grout 2-2.5mm, in time screen cloth is layered on the anticracking grout simultaneously after the cleaning basic unit, is pressed in the anticracking grout with trowel.The part is used the anticracking grout levelling again.The mortar total thickness is controlled at 2.5-3mm.Knife-coat application reduces as far as possible and connects stubble, checks planeness with guiding ruler at any time, guarantees that last vertical and planeness is less than 2mm (2m guiding ruler).
3. blade coating flexible waterproof putty
Repair metope with flexible waterproof putty, the local levelling in first road is filled up big hole and slit with putty or gap-filling glue, treat the putty drying after, detail sanding is completely criticized putty again and is made basic unit smooth.One time blade coating thickness should not surpass 0.5mm, divides twice above construction; Per pass was not less than 5 hours pitch time.(general 4-6 hour) polishing was in time revised after per pass putty blade coating finished.The flexible putty total thickness is controlled at 1.0-1.5mm.
Flexible waterproof putty is a cement system, need carry out maintenance equally, and general curing time is 14 days, to the pH value less than 10, water ratio can carry out the construction of next process after 10%.
4. brushing seal coat:
After treating that putty reaches requirement, basic unit should be polished flat before the brushing, the cleaning floating dust, hair rolls and should keep clean, and brushes watersoluble closed priming paint one time, brushes evenly, and the brush of leakage phenomenon never can be arranged.Forbid converting water when watersoluble closed priming paint is constructed, guarantee that simultaneously seal coat is not subjected to any pollution, is not with any color.
5. apply marble paint for building:
Spraying: after treating the seal coat drying, intersection sprays the marble paint product of two or more colors simultaneously, perhaps sprays the marble paint product of two kinds of colors with double headed spray gun.Spray into concave-convex effect, guarantee during spraying that sags and crests is evenly distributed, several color distribution are even.
Polishing: treat the sags and crests drying, polish that level and smooth the polishing of the part surface of projection, integral body presents the uniform in-plane shape with 60 order sand paper.
Repair: local levelling is repaired.
Polishing: treat that patched surface layer is not exclusively dry, but intensity polishes when withstanding polishing with the hand sand handle, begins to use the levigate coating surface of 120 order sand paper at last with 60 order sand paperings, present in one plane to three kinds of color even till.Guarantee that last film thickness reaches 2-3mm.Repair: after the polishing, as still have little hole, fill up levelling with the marble paint for building part.
Polishing: repair the position with 120 order sand paperings, smooth, smooth to integral surface.
The spraying coating varnish:
Notice treating that marble paint for building parches back (general fine day kept 3 days at least) fully, can spray coating varnish, note keeping viscosity during construction, air pressure, the spout size is consistent, notes pre-sag prevention phenomenon.Before the Lacquer finish, the fine powder of polishing must be cleaned out, not have any floating dust.The coating varnish construction time is not converted any thinner, must spray evenly and comprehensively, generally will spray twice, and phenomenons such as the spray of leakage never can be arranged.
6. construction precautions
Construction environment: guarantee that envrionment temperature should be greater than 5 ℃, relative humidity is less than 70%, and the weather of no strong wind is construction down, and rainy day or the weather that will soon rain also must not be constructed, and pay close attention to weather-forecast during construction more.
7. accumulating requirement
1. condition of storage: coating ventilate, dry, temperature stores under 5~35 ℃ environment.
2. quality guaranteed period: effective shelf lives of product is 1 year.
3. transport condition: transportation is handled by " non-dangerous goods transportation rule ".
The paint film fundamental property of marble paint for building sees Table 1
Table 1

Claims (4)

1. marble paint for building, it is characterized in that it comprises natural stone-powder, water-based pure acrylic resin AC-261, water, inorganic dispersant sodium hexametaphosphate, organic dispersing agent SN-5040, film coalescence aid Texanol, thickening material HBR, defoamer NXZ, wetting agent X-405, sanitas LXZ and pH value conditioning agent AMP-95, its mass percent is:
Constituent mass per-cent (%)
Natural stone-powder 50~70%
Water-based pure acrylic resin AC-261 20~40%
Water 4~6%
Inorganic dispersant sodium hexametaphosphate 0.8~1.5%
Organic dispersing agent SN-5040 0.4~0.6%
Film coalescence aid Texanol 0.2~1.4%
Thickening material HBR 0.12~0.15%
Defoamer NXZ 0.1~0.3%
Wetting agent X-405 0.1~0.2%
Sanitas LXZ 0.1~0.2%
PH value conditioning agent AMP-95 0.05~0.1%.
The preparation method of 2 one kinds of marble paint for building as claimed in claim 1, it is characterized in that this method is: elder generation joins 3% water, inorganic dispersant, organic dispersing agent, film coalescence aid, thickening material, defoamer, wetting agent, sanitas, pH value conditioning agent and water-based pure acrylic resin in the dispersion cylinder, under the state of 300-400rpm, stir evenly, with the water of remainder, all stone flour addings, 15min gets final product in the 1200-1600rpm high speed dispersion again.
3. the constructional method of marble paint for building according to claim 1 is characterized in that this method is: the metope base treatment, scrape or trowelling anticracking grout 1 time, simultaneously compound alkali-resistant glass fiber mesh cloth, scrape or trowelling flexible waterproof putty 2-3 all over, brush seal coat, snap the line, lattice, tape, apply marble paint for building as claimed in claim 1, spray coating varnish.
4. the constructional method of marble paint for building according to claim 3 is characterized in that marble paint for building adopts the mode of hand spray to construct in this method.
CNB2006100078783A 2006-02-23 2006-02-23 Marble paint for building, making method and construction technology thereof Active CN100560667C (en)