CN112574425A - 一种医用亲水有机硅油制备及应用 - Google Patents
一种医用亲水有机硅油制备及应用 Download PDFInfo
- Publication number
- CN112574425A CN112574425A CN202011432720.7A CN202011432720A CN112574425A CN 112574425 A CN112574425 A CN 112574425A CN 202011432720 A CN202011432720 A CN 202011432720A CN 112574425 A CN112574425 A CN 112574425A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicone oil
- polyether
- medical
- silicon oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种医用亲水有机硅油制备及应用，涉及有机硅油制备技术领域。一种医用亲水有机硅油制备的方法，包括以下步骤：S1.按重量份计，将二甲基环硅氧烷、六甲基二硅氧烷加入到已除水的甲苯中进行搅拌操作，搅拌反应的时间控制在0.5h‑2h，再然后缓慢滴加蒸馏水和浓硫酸进行搅拌得到反应产物A，搅拌反应的时间控制在1h‑2h，反应产物A用碳酸氢钠水溶液清洗至中性，再通过减压蒸馏，脱除低分子，得到无色透明的有机硅油。通过合理的制备方法所生产出的聚醚改性有机硅油无催化剂残留、低颗粒含量、含杂质少，色泽纯正，纯度高，性能优良的特点。
Description
技术领域
本发明涉及有机硅油制备技术领域，具体为一种医用亲水有机硅油制备及应用。
背景技术
聚醚改性硅油主要是指线型二甲基硅油的侧链或主链通过化学键与聚醚链段连接的一类油状聚合物，是目前应用和生产最多的一类，聚醚改性硅油由聚醚链段和聚硅氧烷链段组成，聚醚链段具有亲水性，其中的氧原子可以与水作用形成氢键，从而可溶解在水溶液中；聚硅氧烷链段则是疏水性的，可以降低水的表面张力；聚醚链段和聚硅氧烷链段通过硅氢加成反应生成化学键连接在一起，形成一种性能独特的非离子表面活性剂，聚硅氧烷链段亲油，聚醚链段亲水，使得聚醚改性硅油既能溶于水相也能溶于油相，可以作为有机硅表面活性剂使用，还可以作为乳化剂使乳液的性能保持稳定，聚醚改性硅油的具体结构及组成决定其用途，具有很强的针对性、选择性和专用性，主要用途包括用作匀泡剂、消泡剂、织物整理剂、柔软剂、乳化剂等，
医用硅油作为皮肤保护剂活性成分，能提供持久的润滑性，触感光滑，可以滋润皮肤，易于铺展，有助于预防皮肤与嘴唇发炎，皴裂、开裂以及风吹性皮肤伤，并具有短期保护作用，
现有的聚醚改性硅油生产工艺大多采用简单的过滤，活性炭吸附等方法进行产品提纯，所生产的产品容易残余催化剂、低挥发分等杂质，颗粒含量较高，影响产品性能，导致其不适于应用至皮肤处理、口腔材料、涂敷等医用领域，因此，研发一种无催化剂残留、消除低挥发分的高纯度、低颗粒含量的医用聚醚改性亲水有机硅油十分有必要。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种医用亲水有机硅油制备及应用，解决了所生产的产品容易残余催化剂、低挥发分等杂质，颗粒含量较高，影响产品性能，导致其不适于应用至皮肤处理、口腔材料、涂敷等医用领域的问题。
(二)技术方案
为实现以上目的，本发明通过以下技术方案予以实现：一种医用亲水有机硅油制备的方法，所述一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷0.1-1份、六甲基二硅氧烷0.5-1.5份、甲苯100份、蒸馏水20-30份、浓硫酸0.1-1份，氯铂酸1-5份、聚醚100份。
优选的，所述一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷0.2份、六甲基二硅氧烷0.7份、甲苯100份、有机硅油80份、蒸馏水22份、浓硫酸0.2份，氯铂酸2份、聚醚100份。
优选的，所述一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷1份、六甲基二硅氧烷1.5份、甲苯100份、有机硅油120份、蒸馏水30份、浓硫酸1份，氯铂酸4份、聚醚100份。
优选的，一种医用亲水有机硅油制备的方法，包括以下步骤：
S1.按重量份计，将二甲基环硅氧烷、六甲基二硅氧烷加入到已除水的甲苯中进行搅拌操作，搅拌反应的时间控制在0.5h-2h，再然后缓慢滴加蒸馏水和浓硫酸进行搅拌得到反应产物A，搅拌反应的时间控制在1h-2h，反应产物A用碳酸氢钠水溶液清洗至中性，再通过减压蒸馏，脱除低分子，得到无色透明的有机硅油。
S2.按重量份计，将上述有机硅油、氯铂酸、聚醚放置在氮气环境中进行加热得到反应产物B，加热的温度控制在60℃-100℃，反应的时间控制在1h-3h，再将反应产物B经减压蒸馏、过滤操作，得到聚醚改性硅油粗产品，再将聚醚改性硅油粗产品通入装有吸附剂的层析柱中，流速范围控制在0.5BV-1BV，即得到高纯度聚醚硅油产品。
优选的，所述S2中的有机硅油与氯铂酸与聚醚的比例为0.8～1.2：0.02～0.04：1。
优选的，所述方法制备得到的高纯度聚醚硅油产品。
优选的，所述高纯度聚醚硅油产品应用于牙齿材料、皮肤处理、医疗涂敷等医疗行业。
(三)有益效果
本发明提供了一种医用亲水有机硅油制备及应用。具备以下有益效果：
1、本发明提供的一种医用亲水有机硅油制备方法，通过合理的制备方法所生产出的聚醚改性有机硅油无催化剂残留、低颗粒含量、含杂质少，色泽纯正，纯度高，性能优良的特点。
具体实施方式
下面将结合对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：
本发明实施例提供一种医用亲水有机硅油制备的方法，其中的一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷0.2份、六甲基二硅氧烷0.7份、甲苯100份、有机硅油80份、蒸馏水22份、浓硫酸0.2份，氯铂酸2份、聚醚100份。
其中的一种医用亲水有机硅油制备的方法，包括以下步骤：
S1.按重量份计，将二甲基环硅氧烷、六甲基二硅氧烷加入到已除水的甲苯中进行搅拌操作，搅拌反应的时间控制在1h，再然后缓慢滴加蒸馏水和浓硫酸进行搅拌得到反应产物A，搅拌反应的时间控制在1h，反应产物A用碳酸氢钠水溶液清洗至中性，再通过减压蒸馏，脱除低分子，得到无色透明的有机硅油。
S2.按重量份计，将上述有机硅油、氯铂酸、聚醚放置在氮气环境中进行加热得到反应产物B，加热的温度控制在70℃，反应的时间控制在3h，再将反应产物B经减压蒸馏、过滤操作，得到聚醚改性硅油粗产品，再将聚醚改性硅油粗产品通入装有吸附剂的层析柱中，流速范围控制在1BV，即得到高纯度聚醚硅油产品。
其中的S2中的有机硅油与氯铂酸与聚醚的比例为0.8：0.02：1。
其中的方法制备得到的高纯度聚醚硅油产品。
其中的高纯度聚醚硅油产品应用于牙齿材料、皮肤处理、医疗涂敷等医疗行业。
实施例二：
本发明实施例提供一种医用亲水有机硅油制备的方法，其中的一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷1份、六甲基二硅氧烷1.5份、甲苯100份、有机硅油120份、蒸馏水30份、浓硫酸1份，氯铂酸4份、聚醚100份。
其中的一种医用亲水有机硅油制备的方法，包括以下步骤：
S1.按重量份计，将二甲基环硅氧烷、六甲基二硅氧烷加入到已除水的甲苯中进行搅拌操作，搅拌反应的时间控制在2h，再然后缓慢滴加蒸馏水和浓硫酸进行搅拌得到反应产物A，搅拌反应的时间控制在2h，反应产物A用碳酸氢钠水溶液清洗至中性，再通过减压蒸馏，脱除低分子，得到无色透明的有机硅油。
S2.按重量份计，将上述有机硅油、氯铂酸、聚醚放置在氮气环境中进行加热得到反应产物B，加热的温度控制在100℃，反应的时间控制在2h，再将反应产物B经减压蒸馏、过滤操作，得到聚醚改性硅油粗产品，再将聚醚改性硅油粗产品通入装有吸附剂的层析柱中，流速范围控制在0.5BV，即得到高纯度聚醚硅油产品。
其中的S2中的有机硅油与氯铂酸与聚醚的比例为1.2：0.04：1。
其中的方法制备得到的高纯度聚醚硅油产品。
其中的高纯度聚醚硅油产品应用于牙齿材料、皮肤处理、医疗涂敷等医疗行业。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (7)
1.一种医用亲水有机硅油制备的方法，其特征在于：所述一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷0.1-1份、六甲基二硅氧烷0.5-1.5份、甲苯100份、蒸馏水20-30份、浓硫酸0.1-1份，氯铂酸1-5份、聚醚100份。
2.根据权利要求1所述的一种医用亲水有机硅油的方法，其特征在于：所述一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷0.2份、六甲基二硅氧烷0.7份、甲苯100份、有机硅油80份、蒸馏水22份、浓硫酸0.2份，氯铂酸2份、聚醚100份。
3.根据权利要求1所述的一种医用亲水有机硅油的方法，其特征在于：所述一种医用亲水有机硅油包括以下的重量份成分组成：二甲基环硅氧烷1份、六甲基二硅氧烷1.5份、甲苯100份、有机硅油120份、蒸馏水30份、浓硫酸1份，氯铂酸4份、聚醚100份。
4.根据权利要求2-3所述的一种医用亲水有机硅油制备的方法，其特征在于，包括以下步骤：
S1.按重量份计，将二甲基环硅氧烷、六甲基二硅氧烷加入到已除水的甲苯中进行搅拌操作，搅拌反应的时间控制在0.5h-2h，再然后缓慢滴加蒸馏水和浓硫酸进行搅拌得到反应产物A，搅拌反应的时间控制在1h-2h，反应产物A用碳酸氢钠水溶液清洗至中性，再通过减压蒸馏，脱除低分子，得到无色透明的有机硅油。
S2.按重量份计，将上述有机硅油、氯铂酸、聚醚放置在氮气环境中进行加热得到反应产物B，加热的温度控制在60℃-100℃，反应的时间控制在1h-3h，再将反应产物B经减压蒸馏、过滤操作，得到聚醚改性硅油粗产品，再将聚醚改性硅油粗产品通入装有吸附剂的层析柱中，流速范围控制在0.5BV-1BV，即得到高纯度聚醚硅油产品。
5.根据权利要求4所述的一种医用亲水有机硅油制备的方法，其特征在于：所述S2中的有机硅油与氯铂酸与聚醚的比例为0.8～1.2：0.02～0.04：1。
6.根据权利要求2-5任一项所述方法制备得到的高纯度聚醚硅油产品。
7.根据权利要求6所述高纯度聚醚硅油产品应用于牙齿材料、皮肤处理、医疗涂敷等医疗行业。