CN112431520A - 一种快装中空玻璃、制作方法及应用 - Google Patents
一种快装中空玻璃、制作方法及应用 Download PDFInfo
- Publication number
- CN112431520A CN112431520A CN202011314638.4A CN202011314638A CN112431520A CN 112431520 A CN112431520 A CN 112431520A CN 202011314638 A CN202011314638 A CN 202011314638A CN 112431520 A CN112431520 A CN 112431520A
- Authority
- CN
- China
- Prior art keywords
- glass
- adhesive
- spacing
- sealing
- hollow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于中空玻璃的生产技术领域，公开了一种快装中空玻璃、制作方法及应用，玻璃有两块、并且长宽相等，间隔条分段直接粘接在第一块玻璃粘接面的周边、并组成一个封闭的框，第二块玻璃粘接在间隔条的另一面上、并使两块玻璃的周边对齐；所述玻璃与间隔条通过密封胶或结构胶或双面胶带粘接在一起，两块玻璃与间隔条之间形成一个封闭的中空层；间隔条为空腔条，分子筛灌注到间隔条的空腔中；在两块玻璃与间隔条的外侧边部采用密封胶、结构胶、密封带和密封胶带中的一种或数种进行整体密封，封边后的中空玻璃无需养护固化就能直接运输和使用。本发明提高了中空玻璃的质量和缩短了生产周期、提高了生产效率。
Description
技术领域
本发明属于中空玻璃的生产技术领域，尤其涉及一种快装中空玻璃、制作方法及应用。
背景技术
目前，随着我国人民生活水平的不断提高，对居住的舒适度要求也越来越高，势必会不断增加采暖和空调设施，因而建筑能耗必将大幅度增加，建筑能耗占全社会总能耗的比重也越来越大。因此，建筑节能是我国保证国家能源安全以及建设节约型和环境友好型社会的重要举措。中空玻璃是将两片或多片玻璃以间隔框在边部均匀隔开，并在间隔框的外侧与玻璃周边粘结密封，使玻璃层间形成有干燥气体空间的玻璃制品。中空玻璃是一种具有良好的隔热、隔音性能的建筑节能产品，中空玻璃的构造虽然十分简单，但在使用过程中、尤其是处在低温寒冷的环境中，中空玻璃的中空层里面经常会发生起雾或结露现象、严重的会发生存水现象，极大地影响了中空玻璃的保温隔热性能和视觉效果、使其使用寿命大大缩短，这种现象的发生与中空玻璃生产组装工艺以及工人的技术闲熟程度有着十分密切的关系。现有中空玻璃质量不稳定的主要原因在于生产组装工艺落后、机械化和自动化程度低、受制于工人的责任心和操作水平等。因此，改进中空玻璃的生产工艺、提高中空玻璃生产的机械化和自动化程度，是提高中空玻璃质量的关键。
现有中空玻璃的生产工艺已经比较成熟和简单，影响生产机械化和自动化程度的生产工艺在于间隔框的安放，虽然已有间隔框的自动安放机械，但由于造价昂贵无法大范围推广应用，所以现有的中空玻璃生产线一般还是采用人工安装；采用人工安装，不但生产效率低、而且产品质量也得不到保证，尤其是大尺寸的产品，由于间隔框很容易变形、下垂，所以大尺寸的中空玻璃其间隔框很难保证与玻璃边缘平行，不但影响美观、而且也影响到结构胶的一致性，从而影响到中空玻璃的密封性能和力学强度。因此，利用简单易行的方法实现间隔框的自动安放，是提高中空玻璃生产的机械化和自动化程度以及生产效率和产品质量的关键。
现有中空玻璃的边部第一密封层般采用两道密封，第一道是间隔框与玻璃之间、一般采用丁基胶，丁基胶属于不干胶、具有较好的水汽阻隔能力，是阻隔水汽进入中空层的主要因素；但由于间隔框是由间隔条制成、至少有一个接缝，在接缝处的其中两个侧面没有用丁基胶密封，所以存在密封缺陷；第二道密封位于间隔框的外侧与两块玻璃之间，一般采用结构胶如硅酮胶和聚硫胶等，结构胶的主要作用是提供粘接强度、其密封性能相对丁基胶较差，其更为主要的缺点是固化时间长，至少需要24-48小时的静止固化时间，在此期间中空玻璃不能移动，否则容易造成两片玻璃之间的错位和损坏丁基胶密封层、对结构胶的力学性能也产生不良影响。因此，现有中空玻璃边部密封的主要缺点在于，一是丁基胶的密封性能虽然较好但没有对中空层进行全封闭密封、结构胶能够对中空层进行全封闭密封但密封性能较差，二是结构胶的固化时间太长，不仅严重影响了生产效率，而且对产品质量也有不利的影响。
现有中空玻璃的间隔框中都要加入分子筛作干燥剂，以吸收中空层内的水汽和经中空玻璃边部进入到中空层的水汽，一般是间隔框做好后即进行灌注分子筛，从分子筛灌注到结构胶封闭这段时间内、分子筛会一直吸附环境中的水分，由于这段时间长达十几分钟到几十分钟，在湿度较大、尤其是夏季高温高湿的环境中，分子筛会大量地吸附外界空气中的水分，从而使其寿命大大缩短，因而影响到中空玻璃的使用寿命。
现有中空玻璃的边、角暴露在外，在搬运过程中很容易发生磕碰而产生缺口和微裂纹，玻璃属于脆性材料，普通玻璃的破裂、钢化玻璃的自爆大都是由微裂纹引起的，所以裸露的中空玻璃边、角是导致玻璃损坏的重要因素。
现有中空玻璃在国标中所标示的使用寿命也只有15年，而建筑物的寿命则高达70年，在建筑物的生命周期内需要多次更换所用的中空玻璃，不仅造成大量的人力、物力和财力的浪费，而且也给用户带来很多不必要的麻烦。中空玻璃的使用寿命只与玻璃本身和封边结构有关，玻璃是无机材料、性能非常稳定，可以与建筑物同寿命，所以中空玻璃封边的可靠性和耐久性就决定了中空玻璃的使用寿命。因此，提高中空玻璃的使用寿命尤其是提高中空玻璃的封边质量和性能是建筑领域节能降耗的关键。
通过上述分析，现有技术存在的问题及缺陷为：现有中空玻璃在国标中所标示的使用寿命也只有15年，而建筑物的寿命则高达70年，在建筑物的生命周期内需要多次更换所用的中空玻璃，不仅造成大量的人力、物力和财力的浪费，而且也给用户带来很多不必要的麻烦。
解决以上问题及缺陷的难度为：现有间隔框至少有一个对接缝，气密性好的丁基胶不能对中空层进行全密封，该对接缝很容易产生气体的渗漏；能够对中空层进行全密封的结构胶其气密性又较差，导致外界的水汽能够逐渐渗透到中空层内，使中空玻璃的使用寿命大大缩短。
解决以上问题及缺陷的意义为：提高中空玻璃的使用寿命，使其与建筑物同寿命，不但可以节省大量的能源、人力、物力和财力，而且提高居民居住的舒适性和稳定性，还可以减少大量的建筑垃圾，降低对污染的环境。
发明内容
针对现有技术存在的问题，本发明提供了一种快装中空玻璃、制作方法及应用。
本发明是这样实现的，一种快装中空玻璃，所述快装中空玻璃包括玻璃、间隔条、分子筛、玻璃与间隔条之间的粘接密封和玻璃周边的粘接密封；玻璃有两块、并且长宽相等，间隔条分段直接粘接在第一块玻璃粘接面的周边、并组成一个封闭的框，或者间隔条制成一个间隔框后再粘接在第一块玻璃粘接面的周边，第二块玻璃粘接在间隔条的另一面上、并使两块玻璃的周边对齐；
所述玻璃与间隔条通过密封胶或结构胶或双面胶带粘接在一起，两块玻璃与间隔条之间形成一个封闭的中空层；间隔条为空腔条，分子筛灌注到间隔条的空腔中；在两块玻璃与间隔条的外侧边部采用密封胶、结构胶、密封带和密封胶带中的一种或数种进行整体密封，封边后的中空玻璃无需养护固化就能直接运输和使用。
进一步，所述间隔条与玻璃之间的粘接，采用满粘或点粘的方式，所述满粘的方式为连续粘接，所述点粘的方式为断续式粘接，即采用点状、间隔粘接的粘接方式。
进一步，所述密封带或密封胶带的宽度与中空玻璃的中空层厚度相等或与中空玻璃的厚度相同；密封带为金属箔带或复合材料带，两端对接或搭接，对接或搭接处需要用胶带或胶密封固定；密封胶带为铝箔胶带或复合铝箔胶带或铝塑玻纤复合胶带。
进一步，所述密封胶带的宽度可以大于中空玻璃的厚度，密封胶带包裹中空玻璃的侧面后粘贴在中空玻璃两个表面的边部、呈U型。
进一步，在密封带或密封胶带的外面再包裹一层密封胶带，密封胶带包裹中空玻璃的侧面、或者包裹中空玻璃的侧面后呈U型。
本发明的另一目的在于提供一种由所述快装中空玻璃得到的两腔中空玻璃，所述两腔中空玻璃在玻璃的外表面再通过间隔条粘接一块同样大小的玻璃。
本发明的另一目的在于提供一种由所述快装中空玻璃得到的多腔中空玻璃。
本发明的另一目的在于提供一种所述快装中空玻璃的制作方法，所述快装中空玻璃的制作方法包括以下步骤：
第一步、根据所制作中空玻璃的外形尺寸切割两块同样大小玻璃，并进行磨边、清洗和干燥，若需钢化玻璃、还要进行钢化处理；
第二步、选取合适材质和尺寸的间隔条，根据玻璃的大小切割成相应长度的间隔条或制作相应大小的间隔框；
第三步、在间隔条或玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将间隔条粘接在玻璃上，并形成一个封闭的框；或者在间隔框或玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将间隔框粘接在玻璃上；
第四步、在间隔条或间隔框或第二块玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将第二块玻璃粘接在间隔条或间隔框上；
第五步、对合片后的两块玻璃进行板压或碾压，使其粘接牢固，并使两块玻璃保持平行；
第六步、通过在间隔条的侧面打孔或预留的间隔条开孔将分子筛灌注到间隔条的空腔中；
第七步、用结构胶或密封胶和/或密封带或密封胶带中的一种、两种或多种对两块玻璃和间隔条的周边侧面进行整体密封，对中空层形成一道、两道或多道密封；
第八步、根据需要，用密封带和/或密封胶带对中空玻璃的周边再进行强化密封。
进一步，重复第一步至第六步，得到双腔中空玻璃和多腔中空玻璃。
进一步，所述玻璃采用普通玻璃、超白玻璃、钢化玻璃、半钢化玻璃、Low-e玻璃、磨砂玻璃、着色玻璃、镀膜玻璃、压花玻璃、彩釉玻璃、变色玻璃、耐热玻璃、夹丝玻璃、夹层玻璃、覆膜玻璃、防火玻璃、复合玻璃或真空玻璃，还可以采用光伏玻璃，透明的碲化镉光伏玻璃或不透明的晶硅光伏玻璃和薄膜光伏玻璃；
进一步，所述玻璃组成中空玻璃时，采用玻璃采用普通玻璃、超白玻璃、钢化玻璃、半钢化玻璃、Low-e玻璃、磨砂玻璃、着色玻璃、镀膜玻璃、压花玻璃、彩釉玻璃、变色玻璃、耐热玻璃、夹丝玻璃、夹层玻璃、覆膜玻璃、防火玻璃、复合玻璃或真空玻璃中的一种、两种或三种；
进一步，所述玻璃是平面玻璃或弧面玻璃。
进一步，所述间隔条采用现有的暖边间隔条、铝间隔条或不锈钢间隔条。
进一步，所述间隔条采用断桥式间隔条、铰链式间隔条或伸缩式间隔条。
进一步，所述间隔条为单一间隔条或复合间隔条，所述复合间隔条为两条或多条间隔条通过胶、连接件或卡扣结构连接在一起，所述连接为间隔式的点连接、或为连续式的线连接。
进一步，所述间隔条与玻璃之间的粘接为间隔式的点状粘接、或为连续式的线状粘接。
进一步，所述分子筛采用在线灌装的方式，在间隔条安装后、玻璃合片前灌注或在玻璃合片后灌注。
进一步，所述中空层有单腔、两腔和多腔，所述中空层内一个空腔的厚度为3-30mm。
进一步，所述双腔或多腔中空玻璃中空层空腔的厚度为等厚或不等厚；
所述中空层内充气以取代空气，充入惰性气体氩气或温室气体二氧化碳；
所述中空层内放入支撑物、装饰物或气凝胶板材，充入水溶液、水凝胶或气凝胶；
所述中空层抽真空至负压状态；
所述中空层内安装灯光、影像装置；
所述密封胶，采用丁基胶、热熔胶、UV胶、压敏胶、AB胶、瞬干胶、硅酮胶、聚氨酯胶、聚硫胶、丙烯酸胶、厌氧胶、氯丁胶、PVC胶、沥青胶、酚醛树脂胶或环氧树脂胶；
所述结构胶，采用热熔胶、UV胶、压敏胶、AB胶、瞬干胶、硅酮胶、聚氨酯胶、聚硫胶、丙烯酸胶、酚醛树脂胶或环氧树脂胶；
所述密封带采用不锈钢带、铝箔带或铝塑复合带或铝塑玻纤复合带，两端对接或搭接，搭接的密封效果更好，对接或搭接处需要用胶带或胶密封固定；
所述密封胶带采用铝箔胶带或复合铝箔胶带或铝塑玻纤复合胶带；
所述密封带、所述密封胶带有一至数层，对中空玻璃的中空层实施一至数道密封；
所述隔膜和悬膜为塑料薄膜，pvc、pe、ps、pp、pc、pet或pof膜；
所述隔膜和悬膜是普通薄膜或功能膜，所述功能膜为热镜膜、彩印膜、发光膜、变色膜、阻隔红外线膜和阻隔紫外线膜以及水汽阻隔膜。
本发明的另一目的在于提供一种生产所述快装中空玻璃的连续化生产线，为了适应中空玻璃由白玻和Low-E玻璃组成的要求，所述连续化生产线能够使用一台钢化炉不停炉分别在线连续钢化两种玻璃---白玻和膜玻(Low-E玻璃)，并能连续式生产快装中空玻璃，其包括玻璃原片上片机、切割机、磨边机、清洗机、钢化炉、白玻储片机、白玻配片机、膜玻储片机、膜玻配片机、间隔条切割涂胶机、间隔条自动上条机、卧式转立式翻转机、合片机、板压机、分子筛自动灌装机、胶带封边机和自动下片机；整条生产线可以实现自动化、连续化生产，不但生产效率高，而且产品质量好。
本发明的另一目的在于提供一种安装有所述快装中空玻璃的门窗或幕墙。
结合上述的所有技术方案，本发明所具备的优点及积极效果为：本发明在两块玻璃与间隔条的外侧边部采用密封胶、结构胶、密封带和密封胶带中的一种或数种进行整体密封，封边后的中空玻璃无需养护固化就能直接运输和使用；本发明满粘的方式为连续粘接、如同现有中空玻璃的粘接方式，所述点粘的方式为断续式粘接，即采用点状、间隔粘接的粘接方式；满粘的方式有利于对中空层的密封，点粘的方式有利于减小边部的传热面积、提高中空玻璃边部的隔热性能；密封带或密封胶带的宽度与中空玻璃的中空层厚度相等或与中空玻璃的厚度相同，优选其宽度与中空玻璃的厚度相同，不但密封效果好，而且对玻璃起到保护作用、防止玻璃边角的磕碰；密封胶带的宽度还可以大于中空玻璃的厚度，密封胶带包裹中空玻璃的侧面后粘贴在中空玻璃两个表面的边部、呈U型，优选能够遮盖住间隔条，不但能够防止结构胶或密封胶和间隔条受到紫外线的照射，而且给中空玻璃提供更好的密封性能、更好的保护和更高的力学强度，无论结构胶是否固化中空玻璃都可以移动和使用，提高中空玻璃的质量和缩短生产周期、提高生产效率。
本发明在密封带或密封胶带的外面再包裹一层密封胶带，密封胶带包裹中空玻璃的侧面、或者包裹中空玻璃的侧面后呈U型，优选能够遮盖住间隔条，不但能够防止结构胶或密封胶和间隔条受到紫外线的照射，而且给中空玻璃提供更好的密封性能、更好的保护和更高的力学强度，无论结构胶是否固化中空玻璃都可以移动和使用，提高中空玻璃的质量和缩短生产周期、提高生产效率。
本发明强化密封：根据需要，用密封带和/或密封胶带对中空玻璃的周边再进行强化密封，进一步提高中空玻璃密封性能、力学强度和使用寿命。本发明提供快装中空玻璃的制作方法，不但工艺流程简单、机械化和自动化程度高，而且生产周期短、生产效率高和产品质量好，还能大大提高中空玻璃的使用寿命。
本发明采用间隔条代替间隔框直接粘接在玻璃上，不但省去了制作间隔框这一工艺过程，而且能够用简单的设备比如机械手就可以实现间隔条的自动安放，有利于机械化、自动化生产，不仅安放速率快、而且安装精度高，无论多大的玻璃，都能保证间隔条的平直性；用间隔条代替间隔框，可以在间隔条的两端涂密封胶后再拼装，就能实现密封胶对中空腔的全密封，从而提高密封效果；用间隔条代替间隔框，可以在相邻的间隔条接头处留有空隙，对于热膨胀系数大于玻璃的间隔条如金属间隔条就能减弱或防止其在夏季因阳光照射升温而导致的膨胀变形而导致密封胶层的破坏和中空玻璃使用寿命的缩减；用间隔条代替间隔框，可以在相邻的间隔条接头处留有空隙，间隔条内的分子筛通过空隙就可以吸附中空层内的水汽，从而省去了在间隔条上开气孔的工艺，进一步简化中空玻璃的生产工艺，提高生产效率；
本发明采用密封胶、结构胶以及密封带和密封胶带的各种不同组合对中空玻璃的边部进行粘接固定和密封，充分发挥几种材料之间的协同作用，兼顾密封性能、机械强度和流水线生产的时间要求，使中空玻璃的边部密封既有高的封接强度、又有更好的密封性能、还有更快的生产效率，使中空玻璃下线后即可使用，省去了现有中空玻璃24-48小时的结构胶固化时间；尤其是采用密封带和/或密封胶带封边、并结合点粘方式，不但使中空玻璃的边部隔热性能大幅度提高、防止边部结露，而且中空层的密封性能提高数百倍以上(丁基密封胶的水汽渗透系数是0.2克/平米天，铝塑复合膜的水汽渗透系数低于0.001克/平米天，金属箔带则不会透过水汽和空气)，不但大幅度提高中空玻璃的使用寿命，而且由于密封带和密封胶带能够提供很好的夹持和保护作用，中空玻璃的边部即使有尚未固化的结构胶也不妨碍中空玻璃下线后的移动和搬运，中空玻璃下线后即可使用，大大节省了中空玻璃的储存时间和储存场地。
本发明采用在线灌注分子筛的新工艺，不但避免了间隔条在车间内的来回运输、使生产线更加紧凑，而且避免了分子筛吸附环境中的湿气，大大提高了分子筛的使用寿命，加之极好的边部密封，因而中空玻璃的使用寿命会大大延长。本发明通过密封带和密封胶带对中空玻璃的边、角进行整体包裹和保护，防止了中空玻璃在搬运过程中对边、角部位的损伤和微裂纹的产生；密封带和密封胶带属于柔性或弹性材料，在中空玻璃的安装和使用过程中能够为中空玻璃的形变、膨胀提供缓冲空间，防止应力的产生；因而避免了中空玻璃在搬运、安装和使用过程中的破裂和自爆，从而大大提高中空玻璃的使用寿命。
国标中现有中空玻璃的预期使用寿命只有15年，现有的铝箔防水胶带在露天情况下的使用寿命已达30年以上，中空玻璃的边部处于窗框的保护中，所以用铝箔防水胶带封边的中空玻璃其使用寿命至少在30年以上，甚至于与建筑物同寿命。
附图说明
为了更清楚地说明本申请实施例的技术方案，下面将对本申请实施例中所需要使用的附图做简单的介绍，显而易见地，下面所描述的附图仅仅是本申请的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下还可以根据这些附图获得其他的附图。
图1是本发明实施例提供的快装中空玻璃的结构示意图；
图2是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图3是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图4是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图5是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图6是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图7是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图8是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图9是本发明实施例提供的另一种快装中空玻璃的结构示意图；
图10是本发明实施例提供的间隔条摆放的结构示意图；
图11是本发明实施例提供的另一种间隔条摆放的结构示意图；
图12是本发明实施例提供的另一种间隔条摆放的结构示意图；
图13是本发明实施例提供的快装中空玻璃的连续化生产线的示意图。
图中：1、玻璃；2、间隔条；3、第一密封层；4、第二密封层；5、第三密封层；6、第四密封层。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
针对现有技术存在的问题，本发明提供了一种快装中空玻璃、制作方法及应用，下面结合附图对本发明作详细的描述。
本发明提供的快装中空玻璃的制作方法包括以下步骤：
第一步、制作玻璃：根据所制作中空玻璃的外形尺寸切割两块同样大小玻璃，并进行磨边、清洗和干燥，若需钢化玻璃、还要进行钢化处理；
第二步、切割间隔条或制作间隔框：选取合适材质和尺寸的间隔条，根据玻璃的大小切割成相应长度的间隔条或制作相应大小的间隔框；
第三步、固定间隔条或间隔框：在间隔条或玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将间隔条粘接在玻璃上，并形成一个封闭的框；或者在间隔框或玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将间隔框粘接在玻璃上；
第四步、安装第二块玻璃：在间隔条或间隔框或第二块玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将第二块玻璃粘接在间隔条或间隔框上；
第五步、板压或碾压：对合片后的两块玻璃进行板压或碾压，使其粘接牢固，并使两块玻璃保持平行；
第六步、灌注分子筛：通过在间隔条的侧面打孔或预留的间隔条开孔将分子筛灌注到间隔条的空腔中；
第七步、边部密封：用结构胶或密封胶和/或密封带或密封胶带中的一种、两种或多种对两块玻璃和间隔条的周边侧面进行整体密封，因而对中空层形成一道、两道或多道密封；
第八步、强化密封：根据需要，用密封带和/或密封胶带对中空玻璃的周边再进行强化密封，进一步提高中空玻璃密封性能、力学强度和使用寿命。
下面结合具体实施例对本发明的技术方案作进一步的描述。
实施例1：参考图1和图10，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第二密封层4和第三密封层5，根据所制作的中空玻璃的大小切割两块同样大小的玻璃1，并进行磨边和清洗；当需要钢化玻璃时，进钢化炉进行钢化处理；采用现有中空玻璃的间隔条、优选暖边条，根据玻璃1的大小和形状以及第二密封层4所用密封胶或结构胶的涂胶厚度按照图10的摆放方式来确定各条间隔条2的长度，长方形的中空玻璃采用4条间隔条2、异形的中空玻璃根据玻璃的形状和大小来确定间隔条2的数量；在图10中4条间隔条2的两端分别切割成45度角、使其能够拼装成一个间隔框，在玻璃1或间隔条2的粘接处涂有密封胶(如丁基胶等)或采用结构胶(如瞬干胶或压敏胶等)或采用双面胶带等用作第一密封层3，然后利用专用设备如机械手直接将4条间隔条2分别固定在玻璃1上、并拼装成一个间隔框；间隔框的4个角的拼接处可以是相邻的两条间隔条2直接对接在一起，也可以是涂上密封胶后再对接、便于对中空层进行全密封，还可以留有一定的空隙，空隙的大小小于分子筛的直径、防止分子筛流出，留有空隙的好处是既便于间隔条2的安放，又给间隔条2的膨胀留有空间，还有利于分子筛吸附中空层内的水汽、省去在间隔条上打吸气孔的工艺；在另一块玻璃1上或间隔条2的另一面涂上密封胶或结构胶或采用双面胶带等，把两块玻璃1合在一起、周边对齐，利用板压或碾压使之粘接牢固、并使两块玻璃1保持平行；据此，可以在两块玻璃的任一表面再粘接一层间隔条2和一块玻璃1使之成为三玻两腔的中空玻璃；两块或三块玻璃合片后处于立式或倾斜状态如在中空玻璃立式生产线上，利用分子筛灌装机在上部的间隔条2的两个角或一个角打孔将分子筛灌注到竖立的间隔条中；分子筛灌注完毕，立即用打胶机在两块玻璃1与间隔条2的外侧形成的空间中涂满第二密封层4如硅酮结构胶或聚硫胶或聚氨酯胶或热熔胶或丁基胶等，避免了分子筛吸附环境中的水汽；最后在玻璃1的周边、第二密封层4的外面缠上或粘贴上第三密封层5如密封带(不锈钢带、铝箔带、铝塑复合膜带或铝塑玻纤复合带等)或密封胶带(铝箔复合胶带、丁基胶铝箔防水胶带或铝塑玻纤复合胶带等)，密封带或密封胶带根据使用要求可以有一层、两层或多层，对中空玻璃的中空层实施两道或多道密度；中空玻璃下线后即可使用，大大节省了中空玻璃的储存时间和储存场地。
实施例2：参考图2和图11，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第二密封层4和第四密封层6，基本上同实施例1，不同之处在于间隔条2的摆放方式如图11所示，左右两侧竖立放置的间隔条2的上端开口部分暴露在外(暴露的大小可以通过切角的大小来调节)，方便分子筛的灌注，省去了在间隔条2上打孔这一工序，节省了设备投入和加工时间；不同之处还在于用第四密封层6来代替第三密封层5，第四密封层6为密封胶带(铝箔复合胶带、丁基胶防水胶带等)，第四密封层6呈U型密封中空玻璃的周边，与实施例1相比，不但密封效果好、密封时效长，而且对两块玻璃1有更好的夹持固定和保护作用，此外还对间隔条2和第一密封层3有很好的保护作用，防止紫外线对它们的损伤。
实施例3：参考图3和图12，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第二密封层4、第三密封层5和第四密封层6，基本上同实施例1，不同之处在于间隔条2的摆放方式如图12所示，间隔条2为平切口，与45度角的斜切口相比可以减少一半多的切割量，而且不产生或少产生下脚料；此外，摆放定位也比较简单，分子筛的灌装也比较方便；不同之处还在于同时具有第一密封层3、第二密封层4、第三密封层5和第四密封层6四道密封，所以密封性能更好、对玻璃的固定和保护作用更强。
实施例4：参考图4，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3和第四密封层6，基本上同实施例2，不同之处在于省去了第二密封层4，在保证密封性能的前提下使中空玻璃的边部更窄、视野更大、边部隔热性能更好。
实施例5：参考图5，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第三密封层5和第四密封层6，基本上同实施例3，不同之处在于省去了第二密封层4，在保证密封性能的前提下使中空玻璃的边部更窄、视野更大、边部隔热性能更好。
实施例6：参考图6，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第二密封层4和第三密封层5，基本上同实施例1，不同之处在于第三密封层5置于第二密封层4的里面，这样与现有的中空玻璃在外观上一样，密封性能却大幅度提高，使用寿命也相应提高。
实施例7：参考图7，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第二密封层4和第三密封层5，基本上同实施例1，不同之处在于第二密封层4的里面又增加了一道第三密封层5，其密封性能又进一步提高，使用寿命也相应提高。
实施例8：参考图8，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第二密封层4、第三密封层5和第四密封层6，基本上同实施例2，不同之处在于第二密封层4的里面又增加了一道第三密封层5，其密封性能又进一步提高，使用寿命也相应提高。
实施例9：参考图9，一种快装中空玻璃，包括玻璃1、间隔条2、第一密封层3、第二密封层4、第三密封层5和第四密封层6，基本上同实施例3，不同之处在于第二密封层4的里面又增加了一道第三密封层5，其密封性能又进一步提高，使用寿命也相应提高。
实施例10：参考实施例1-实施例9，一种三玻两腔的快装中空玻璃，与实施例1-9基本相同，不同之处在于玻璃1有三块、间隔条2围成的间隔框有两个，三块玻璃1与两个间隔框形成两个中空腔，经边部密封后成为三玻两腔的中空玻璃。
实施例11：参考实施例1-实施例10，一种快装真空复合中空玻璃，与实施例1-实施例14基本相同，不同之处在于玻璃1中至少有一块是真空玻璃，真空玻璃优先安装在室内侧。
实施例12：参考实施例1-实施例10，一种快装防火中空玻璃，与实施例1-实施例14基本相同，不同之处在于玻璃1中至少有一块是防火玻璃，防火玻璃优先安装在室内侧；不同之处还在于间隔条2为金属间隔条或金属复合间隔条，密封胶和结构胶为交联固化的热固性胶，防止在发生火灾时间隔条、密封胶和结构胶因熔融而失去支撑作用。
实施例13：参考实施例1-实施例10，一种快装光伏中空玻璃，与实施例1-实施例14基本相同，不同之处在于玻璃1中有一块是光伏玻璃，光伏玻璃安装在室外侧。
实施例14：参考实施例1-实施例10，一种快装覆膜中空玻璃，与实施例1-实施例14基本相同，不同之处在于玻璃1中至少有一块是覆膜玻璃，覆膜玻璃优先安装在室外侧。
实施例15：参考实施例1-实施例10，一种快装夹层中空玻璃，与实施例1-14基本相同，不同之处在于玻璃1中至少有一块是夹层玻璃，夹层玻璃优先安装在室外侧。
实施例16：参考实施例1-实施例10，一种快装遮阳中空玻璃，与实施例1-实施例14基本相同，不同之处在于至少一个中空层内安装有用于遮阳的卷帘、百叶窗或百褶帘等，卷帘、百叶窗或百褶帘可以手动、电动或自动控制，可以分段控制、多段控制或整体控制。
实施例17：参考实施例1-实施例10，一种快装气凝胶中空玻璃，与实施例1-实施例14基本相同，不同之处在于至少一个中空层内装填有气凝胶，气凝胶的形状为板材、颗粒和粉体中的一种或两种的组合；气凝胶板材在玻璃合片前摆放在中空层内，气凝胶颗粒和粉体可在玻璃合片后采用真空灌装的方式充填到中空层内。
实施例18：参考实施例1-实施例10，一种快装水凝胶中空玻璃，与实施例1-实施例14基本相同，不同之处在于至少一个中空层内充满水凝胶，密封胶采用具有防水功能的丁基胶、聚氨酯胶或玻璃胶等，水凝胶的颜色、透明度或透视度等可以通过温度、电压、日光等的变化而发生变化，不但能够控制阳光的进入量，而且还有防火、防盗、隔音、吸能等功能。
实施例19：参考实施例1-实施例10，一种快装景观中空玻璃，与实施例1-实施例14基本相同，不同之处在于至少一个中空层内充满水溶胶或水溶液等，密封胶采用具有防水功能的丁基胶、聚氨酯胶或玻璃胶等，水溶胶或水溶液的颜色、透明度或透视度等可以通过温度、电压、日光等的变化而发生变化，水溶胶或水溶液中有机器鱼、鳖、虾、蟹以及水草等，机器鱼等采用无线充电方式、可自动充电，并能完成一系列设定的动作；间隔条处安装有灯光秀、气泡发生器等；不但是一处景观，而且能够控制阳光的进入量，还有防火、防盗、隔音、吸能、蓄能、调温等功能。
在本发明的描述中，除非另有说明，“多个”的含义是两个或两个以上；术语“上”、“下”、“左”、“右”、“内”、“外”、“前端”、“后端”、“头部”、“尾部”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。此外，术语“第一”、“第二”、“第三”等仅用于描述目的，而不能理解为指示或暗示相对重要性。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种快装中空玻璃，其特征在于，所述快装中空玻璃包括玻璃、间隔条、分子筛、玻璃与间隔条之间的粘接密封和玻璃周边的粘接密封；玻璃有两块、并且长宽相等，间隔条分段直接粘接在第一块玻璃粘接面的周边、并组成一个封闭的框，或者间隔条制成一个间隔框后再粘接在第一块玻璃粘接面的周边，第二块玻璃粘接在间隔条的另一面上、并使两块玻璃的周边对齐；
所述玻璃与间隔条通过密封胶或结构胶或双面胶带粘接在一起，两块玻璃与间隔条之间形成一个封闭的中空层；间隔条为空腔条，分子筛灌注到间隔条的空腔中；在两块玻璃与间隔条的外侧边部采用密封胶、结构胶、密封带和密封胶带中的一种或数种进行整体密封，封边后的中空玻璃无需养护固化就能直接运输和使用。
2.如权利要求1所述的快装中空玻璃，其特征在于，所述间隔条与玻璃之间的粘接，采用满粘或点粘的方式，所述满粘的方式为连续粘接，所述点粘的方式为断续式粘接，即采用点状、间隔粘接的粘接方式；
所述密封带或密封胶带的宽度与中空玻璃的中空层厚度相等或与中空玻璃的厚度相同；密封带为金属箔带或复合材料带，两端对接或搭接，对接或搭接处需要用胶带或胶密封固定；密封胶带为铝箔胶带或复合铝箔胶带或铝塑玻纤复合胶带；密封胶带的宽度可以大于中空玻璃的厚度，密封胶带包裹中空玻璃的侧面后粘贴在中空玻璃两个表面的边部、呈U型。
3.如权利要求2所述的快装中空玻璃，其特征在于，在密封带或密封胶带的外面再包裹一层密封胶带，密封胶带包裹中空玻璃的侧面、或者包裹中空玻璃的侧面后呈U型。
4.一种由权利要求1～2任意一项所述快装中空玻璃得到的两腔中空玻璃，其特征在于，所述两腔中空玻璃在玻璃的外表面再通过间隔条粘接一块同样大小的玻璃。
5.一种由权利要求1～2任意一项所述快装中空玻璃得到的多腔中空玻璃。
6.一种如权利要求1～2任意一项所述快装中空玻璃的制作方法，其特征在于，所述快装中空玻璃的制作方法包括以下步骤：
第一步、根据所制作中空玻璃的外形尺寸切割两块同样大小玻璃，并进行磨边、清洗和干燥，若需钢化玻璃、还要进行钢化处理；
第二步、选取合适材质和尺寸的间隔条，根据玻璃的大小切割成相应长度的间隔条或制作相应大小的间隔框；
第三步、在间隔条或玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将间隔条粘接在玻璃上，并形成一个封闭的框；或者在间隔框或玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将间隔框粘接在玻璃上；
第四步、在间隔条或间隔框或第二块玻璃的粘接面上涂上密封胶或结构胶或粘上双面胶带，将第二块玻璃粘接在间隔条或间隔框上；
第五步、对合片后的两块玻璃进行板压或碾压，使其粘接牢固，并使两块玻璃保持平行；
第六步、通过在间隔条的侧面打孔或预留的间隔条开孔将分子筛灌注到间隔条的空腔中；
第七步、用结构胶或密封胶和/或密封带或密封胶带中的一种、两种或多种对两块玻璃和间隔条的周边侧面进行整体密封，对中空层形成一道、两道或多道密封；
第八步、根据需要，用密封带和/或密封胶带对中空玻璃的周边再进行强化密封。
7.如权利要求6所述的快装中空玻璃的制作方法，其特征在于，重复第一步至第六步，得到双腔中空玻璃和多腔中空玻璃；
所述玻璃采用普通玻璃、超白玻璃、钢化玻璃、半钢化玻璃、Low-e玻璃、磨砂玻璃、着色玻璃、镀膜玻璃、压花玻璃、彩釉玻璃、变色玻璃、耐热玻璃、夹丝玻璃、夹层玻璃、覆膜玻璃、防火玻璃、复合玻璃或真空玻璃，还可以采用光伏玻璃，透明的碲化镉光伏玻璃或不透明的晶硅光伏玻璃和薄膜光伏玻璃；
所述玻璃组成中空玻璃时，采用玻璃采用普通玻璃、超白玻璃、钢化玻璃、半钢化玻璃、Low-e玻璃、磨砂玻璃、着色玻璃、镀膜玻璃、压花玻璃、彩釉玻璃、变色玻璃、耐热玻璃、夹丝玻璃、夹层玻璃、覆膜玻璃、防火玻璃、复合玻璃或真空玻璃中的一种、两种或三种；
所述玻璃是平面玻璃或弧面玻璃；所述间隔条采用现有的暖边间隔条、铝间隔条或不锈钢间隔条；所述间隔条采用断桥式间隔条、铰链式间隔条或伸缩式间隔条；所述间隔条为单一间隔条或复合间隔条，所述复合间隔条为两条或多条间隔条通过胶、连接件或卡扣结构连接在一起，所述连接为间隔式的点连接、或为连续式的线连接；所述间隔条与玻璃之间的粘接为间隔式的点状粘接、或为连续式的线状粘接；所述分子筛在玻璃合片后灌注或在玻璃合片前灌注；所述中空层有单腔、两腔和多腔，所述中空层内一个空腔的厚度为3-30mm。
8.如权利要求6所述的快装中空玻璃的制作方法，其特征在于，所述双腔或多腔中空玻璃中空层空腔的厚度为等厚或不等厚；所述中空层内充气以取代空气，充入惰性气体氩气或温室气体二氧化碳；所述中空层内放入支撑物、装饰物或气凝胶板材，充入水溶液、水凝胶或气凝胶；所述中空层抽真空至负压状态；所述中空层内安装灯光、影像装置；所述密封胶，采用丁基胶、热熔胶、UV胶、压敏胶、AB胶、瞬干胶、硅酮胶、聚氨酯胶、聚硫胶、丙烯酸胶、厌氧胶、氯丁胶、PVC胶、沥青胶、酚醛树脂胶或环氧树脂胶；所述结构胶，采用热熔胶、UV胶、压敏胶、AB胶、瞬干胶、硅酮胶、聚氨酯胶、聚硫胶、丙烯酸胶、酚醛树脂胶或环氧树脂胶；所述密封带采用不锈钢带、铝箔带或铝塑复合带或铝塑玻纤复合带，两端对接或搭接，搭接的密封效果更好，对接或搭接处需要用胶带或胶密封固定；所述密封胶带采用铝箔胶带或复合铝箔胶带或铝塑玻纤复合胶带；所述密封带、所述密封胶带有一至数层，对中空玻璃的中空层实施一至数道密封；所述隔膜和悬膜为塑料薄膜，pvc、pe、ps、pp、pc、pet或pof膜；所述隔膜和悬膜是普通薄膜或功能膜，所述功能膜为热镜膜、彩印膜、发光膜、变色膜、阻隔红外线膜和阻隔紫外线膜以及水汽阻隔膜。
9.一种安装有权利要求1～2任意一项所述快装中空玻璃的门窗或幕墙。
10.一种生产所述快装中空玻璃的连续化生产线，其特征在于，所述连续化生产线适应中空玻璃由白玻和Low-E玻璃组成的要求，所述连续化生产线使用一台钢化炉不停炉分别在线连续钢化两种玻璃---白玻和膜玻，并能连续式生产快装中空玻璃，其包括玻璃原片上片机、切割机、磨边机、清洗机、钢化炉、白玻储片机、白玻配片机、膜玻储片机、膜玻配片机、间隔条切割涂胶机、间隔条自动上条机、卧式转立式翻转机、合片机、板压机、分子筛自动灌装机、胶带封边机和自动下片机；整条生产线可以实现自动化、连续化生产，不但生产效率高，而且产品质量好。