CN112411909A - Environment-friendly and energy-saving composite coating process and method for flat coating curtain wall - Google Patents
Environment-friendly and energy-saving composite coating process and method for flat coating curtain wall Download PDFInfo
- Publication number
- CN112411909A CN112411909A CN202011215436.4A CN202011215436A CN112411909A CN 112411909 A CN112411909 A CN 112411909A CN 202011215436 A CN202011215436 A CN 202011215436A CN 112411909 A CN112411909 A CN 112411909A
- Authority
- CN
- China
- Prior art keywords
- wall
- curtain wall
- primer
- coating
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly and energy-saving flat coating curtain wall composite coating process and method. In the present invention, the following raw materials and tools are required: the composite coating of the flat coating curtain wall can form a net-shaped protective layer on the surface of a wall body, and the flat coating curtain wall shows extremely low water absorption rate, wet expansion rate and good water impermeability in a humid environment, so that the curtain wall does not mildew or damp in use, and does not deform and fall off due to moisture absorption. The water permeability of the flat coating curtain wall composite coating is 0 through the detection of an authority mechanism. Steam meets the curtain surface and can form "the lotus leaf hangs the pearl" phenomenon, not only can not deepen the wall body, can also play the effect of clean wall dust, and the flat curtain composite coating of scribbling detects through the resistant brush 20000 times, and the paint film is not damaged.
Description
Technical Field
The invention belongs to the technical field of flat coating curtain walls, and particularly relates to an environment-friendly and energy-saving composite coating process and method for a flat coating curtain wall.
Background
The building curtain wall is composed of a supporting structure system and a panel, can have certain displacement capacity relative to the main body structure, and does not share the outer protective structure or the decorative structure of the building acted on the main body structure; the curtain wall is an outer wall enclosure of a building, does not bear load, is hung like a curtain, is also called a hanging wall, and is a light wall with decoration effect commonly used by modern large-scale and high-rise buildings. The building envelope structure consists of a structural frame and an embedded plate, and does not bear the load and the action of a main structure.
But common building curtain is environmental protection inadequately when using, and ordinary curtain water absorption rate is higher simultaneously, and the condition such as going mildy easily appears, and is comparatively inconvenient during the use.
Disclosure of Invention
The invention aims to: in order to solve the problems, an environment-friendly and energy-saving flat coating curtain wall composite coating process and method are provided.
The technical scheme adopted by the invention is as follows: the environment-friendly and energy-saving composite coating process and method for the flat coating curtain wall require the following raw materials and tools during operation: a two-component leveling material YY-50, a 0-component smooth surface material YY-60, a transparent water-based sealing bottom coat YY-100, a colored water-based middle coat YY-300 and a jade clothing cover porcelain YY-2000-JZ.
In a preferred embodiment, the environment-friendly and energy-saving flat coating curtain wall composite coating process and method comprises the following steps:
s1: determining whether the wall has water seepage and water leakage phenomena, if the wall is required to be repaired in time due to the water seepage phenomena caused by the cracking of the wall, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation;
s2: when the old wall is renovated, the old wall is damaged. Removing all putty layers of the original emulsion paint wall surface, cleaning floating ash and impurities of the wall surface, and sealing with transparent sealing primer;
s3: after the primer is dried, the wall surface is coated with the net and the leveling putty in batches once, the inner wall smooth surface putty is coated in batches twice, and after the primer is polished and leveled, the construction process for preparing the primer, the intermediate coat and the ceramic finish coat is carried out
S4: local peeling, namely removing the peeled and shelled wall surface, filling and coating putty, and then polishing and flattening;
s5: step S4, after polishing and flattening, spraying the primer, standing for a period of time, and naturally drying;
s6: after the spraying of the primer is finished, the spraying of the intermediate paint can be carried out, and the intermediate paint is kept stand for a period of time until the intermediate paint is naturally dried;
s7: after the spraying of the primer is finished, the spraying of the intermediate paint can be carried out, and the intermediate paint is kept stand for a period of time until the intermediate paint is naturally dried;
s8: after the spraying of the intermediate paint is finished, the ceramic finish paint can be sprayed, and the ceramic finish paint is kept stand for a period of time until the ceramic finish paint is naturally dried, so that the ceramic finish paint can be used.
In a preferred embodiment, in step S1, if the wall cannot be repaired, the cement painting layer is directly painted with the jade liquid YY-3000, and then the putty coating operation is performed.
In a preferred embodiment, in the step S5, the transparent water-based seal coat YY-100 is used as the primer; the theoretical coating rate is 1.8-2.0 kg/m2。
In a preferred embodiment, the putty layer in the step S4 adopts a two-component leveling material YY-50 and a one-component smooth material YY-60, and the theoretical coating rate is 1.8kg/m2And 1.5kg/m2。
In a preferred embodiment, the colored water-based intermediate coating YY-300 is adopted as the paint in the step S6, and the theoretical coating rate is 0.25kg/m2。
In a preferred embodiment, the glaze surface in the step S7 is sprayed by yu-shirt covering porcelain YY-2000-JZ, and the theoretical coating rate is 0.07kg/m2。
In summary, due to the adoption of the technical scheme, the invention has the beneficial effects that:
1. in the invention, the reflection and heat insulation performance of the porcelain glaze curtain wall is detected according to JG/T235-2014 standard, the solar reflectance ratio is 0.82, and the hemispherical emissivity is 0.90, which all accord with the reflection and heat insulation standard of buildings. For low-latitude areas with longer direct sunlight time and high-altitude areas with strong ultraviolet rays, the flat coating curtain wall can form a protective layer on the wall surface, so that the phenomenon that the wall surface coating is cracked and dropped off finally due to frequent shrinkage and expansion of the putty layer caused by larger temperature difference is prevented; can also effectively solve the problem of 'sunny and shady surfaces' caused by different ultraviolet irradiation time.
2. According to the invention, the composite coating of the flat coating curtain wall can form a net-shaped protective layer on the surface of the wall body, and the flat coating curtain wall shows extremely low water absorption rate, wet expansion rate and good water impermeability in a humid environment, so that the curtain wall is not mildewed and damp-proof in use, and cannot deform and fall off due to moisture absorption. The water permeability of the flat coating curtain wall composite coating is 0 through the detection of an authority mechanism. Steam meets the curtain surface and can form "the lotus leaf hangs the pearl" phenomenon, not only can not deepen the wall body, can also play the effect of clean wall dust, and the flat curtain composite coating of scribbling detects through the resistant brush 20000 times, and the paint film is not damaged.
Detailed Description
In order to make the objects, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are some embodiments of the present invention, but not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows:
the environment-friendly and energy-saving flat coating curtain wall composite coating process and the method need the following raw materials and tools during operation: a two-component leveling material YY-50, a 0-component smooth surface material YY-60, a transparent water-based sealing bottom coat YY-100, a colored water-based middle coat YY-300 and a jade clothing cover porcelain YY-2000-JZ.
The environment-friendly and energy-saving flat coating curtain wall composite coating process and the method comprise the following steps:
s1: determining whether the wall has water seepage and water leakage phenomena, if the water seepage phenomena is caused by the cracking of the wall, repairing the wall in time, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation, and in step S1, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation;
s2: when the old wall is renovated, the old wall is damaged. Removing all putty layers of the original emulsion paint wall surface, cleaning floating ash and impurities of the wall surface, and sealing with transparent sealing primer;
s3: after the primer is dried, the wall surface is coated with the net and the leveling putty in batches once, the inner wall smooth surface putty is coated in batches twice, and after the primer is polished and leveled, the construction process for preparing the primer, the intermediate coat and the ceramic finish coat is carried out
S4: the local peeling phenomenon is that the peeled and shelled wall surface is removed, putty is filled and coated, then the wall surface is polished and leveled, the putty layer in the step S4 adopts a two-component leveling material YY-50 and a one-component smooth surface material YY-60, and the theoretical coating rate is 1.8kg/m2And 1.5kg/m2；
S5: after the polishing is carried out in the step S4, spraying of the primer can be started, standing is carried out for a period of time, and when the primer is naturally dried completely, in the step S5, the primer is transparent water-based seal primer YY-100; the theoretical coating rate is 1.8kg/m2；
S6: after the spraying of the primer is finished, the spraying of the intermediate paint can be carried out, the mixture is kept stand for a period of time and naturally dries, the colored water-based intermediate paint YY-300 is adopted in the step S6, and the theoretical coating rate is 0.25kg/m2；
S7: after the spraying of the primer is finished, the spraying of the primer can be carried out, the mixture is kept stand for a period of time and naturally dried, the glaze surface in the step S7 adopts the jade clothing covering porcelain YY-2000-JZ spraying, and the theoretical coating rate is 0.07kg/m2；
S8: after the spraying of the intermediate paint is finished, the ceramic finish paint can be sprayed, and the ceramic finish paint is kept stand for a period of time until the ceramic finish paint is naturally dried, so that the ceramic finish paint can be used.
Example two:
the environment-friendly and energy-saving flat coating curtain wall composite coating process and the method need the following raw materials and tools during operation: a two-component leveling material YY-50, a 0-component smooth surface material YY-60, a transparent water-based sealing bottom coat YY-100, a colored water-based middle coat YY-300 and a jade clothing cover porcelain YY-2000-JZ.
The environment-friendly and energy-saving flat coating curtain wall composite coating process and the method comprise the following steps:
s1: determining whether the wall has water seepage and water leakage phenomena, if the water seepage phenomena is caused by the cracking of the wall, repairing the wall in time, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation, and in step S1, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation;
s2: when the old wall is renovated, the old wall is damaged. Removing all putty layers of the original emulsion paint wall surface, cleaning floating ash and impurities of the wall surface, and sealing with transparent sealing primer;
s3: after the primer is dried, the wall surface is coated with the net and the leveling putty in batches once, the inner wall smooth surface putty is coated in batches twice, and after the primer is polished and leveled, the construction process for preparing the primer, the intermediate coat and the ceramic finish coat is carried out
S4: the local peeling phenomenon is that the peeled and shelled wall surface is removed, putty is filled and coated, then the wall surface is polished and leveled, the putty layer in the step S4 adopts a two-component leveling material YY-50 and a one-component smooth surface material YY-60, and the theoretical coating rate is 1.8kg/m2And 1.5kg/m2；
S5: after the polishing is carried out in the step S4, spraying of the primer can be started, standing is carried out for a period of time, and when the primer is naturally dried completely, in the step S5, the primer is transparent water-based seal primer YY-100; the theoretical coating rate is 2.0kg/m2；
S6: after the spraying of the primer is finished, the spraying of the intermediate paint can be carried out, the mixture is kept stand for a period of time and naturally dries, the colored water-based intermediate paint YY-300 is adopted in the step S6, and the theoretical coating rate is 0.25kg/m2；
S7: after the spraying of the primer is finished, the spraying of the primer can be carried out, the mixture is kept stand for a period of time and naturally dried, the glaze surface in the step S7 adopts the jade clothing covering porcelain YY-2000-JZ spraying, and the theoretical coating rate is 0.07kg/m2；
S8: after the spraying of the intermediate paint is finished, the ceramic finish paint can be sprayed, and the ceramic finish paint is kept stand for a period of time until the ceramic finish paint is naturally dried, so that the ceramic finish paint can be used.
Example three:
the environment-friendly and energy-saving flat coating curtain wall composite coating process and the method need the following raw materials and tools during operation: a two-component leveling material YY-50, a 0-component smooth surface material YY-60, a transparent water-based sealing bottom coat YY-100, a colored water-based middle coat YY-300 and a jade clothing cover porcelain YY-2000-JZ.
The environment-friendly and energy-saving flat coating curtain wall composite coating process and the method comprise the following steps:
s1: determining whether the wall has water seepage and water leakage phenomena, if the water seepage phenomena is caused by the cracking of the wall, repairing the wall in time, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation, and in step S1, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation;
s2: when the old wall is renovated, the old wall is damaged. Removing all putty layers of the original emulsion paint wall surface, cleaning floating ash and impurities of the wall surface, and sealing with transparent sealing primer;
s3: after the primer is dried, the wall surface is coated with the net and the leveling putty in batches once, the inner wall smooth surface putty is coated in batches twice, and after the primer is polished and leveled, the construction process for preparing the primer, the intermediate coat and the ceramic finish coat is carried out
S4: the local peeling phenomenon is that the peeled and shelled wall surface is removed, putty is filled and coated, then the wall surface is polished and leveled, the putty layer in the step S4 adopts a two-component leveling material YY-50 and a one-component smooth surface material YY-60, and the theoretical coating rate is 1.8kg/m2And 1.5kg/m2；
S5: after the polishing is carried out in the step S4, spraying of the primer can be started, standing is carried out for a period of time, and when the primer is naturally dried completely, in the step S5, the primer is transparent water-based seal primer YY-100; theoretical coating rate of 1.9kg/m2；
S6: after the spraying of the primer is finished, the spraying of the intermediate paint can be carried out, the mixture is kept stand for a period of time and naturally dries, the colored water-based intermediate paint YY-300 is adopted in the step S6, and the theoretical coating rate is 0.25kg/m2；
S7: after the spraying of the primer is finished, the spraying of the primer can be carried out, the mixture is kept stand for a period of time and naturally dried, the glaze surface in the step S7 adopts the jade clothing covering porcelain YY-2000-JZ spraying, and the theoretical coating rate is 0.07kg/m2；
S8: after the spraying of the intermediate paint is finished, the ceramic finish paint can be sprayed, and the ceramic finish paint is kept stand for a period of time until the ceramic finish paint is naturally dried, so that the ceramic finish paint can be used.
In the environment-friendly and energy-saving flat coating curtain wall composite coating process and method, the reflective heat-insulating performance of the porcelain glaze curtain wall is detected according to JG/T235-2014 standard, the solar reflectance ratio is 0.82, and the hemispherical emissivity is 0.90, which all accord with the reflective heat-insulating standard of buildings. For low-latitude areas with longer direct sunlight time and high-altitude areas with strong ultraviolet rays, the flat coating curtain wall can form a protective layer on the wall surface, so that the phenomenon that the wall surface coating is cracked and dropped off finally due to frequent shrinkage and expansion of the putty layer caused by larger temperature difference is prevented; can also effectively solve the problem of 'sunny and shady surfaces' caused by different ultraviolet irradiation time.
In the environment-friendly and energy-saving flat coating curtain wall composite coating process and method, the flat coating curtain wall composite coating can form a net-shaped protective layer on the surface of a wall body, and the flat coating curtain wall shows extremely low water absorption rate, wet expansion rate and good water impermeability in a humid environment, so that the curtain wall is not mildewed and damp-proof in use, and cannot deform and have finish paint falling due to moisture absorption. The water permeability of the flat coating curtain wall composite coating is 0 through the detection of an authority mechanism. Steam meets the curtain surface and can form "the lotus leaf hangs the pearl" phenomenon, not only can not deepen the wall body, can also play the effect of clean wall dust, and the flat curtain composite coating of scribbling detects through the resistant brush 20000 times, and the paint film is not damaged.
It is noted that, herein, relational terms such as first and second, and the like may be used solely to distinguish one entity or action from another entity or action without necessarily requiring or implying any actual such relationship or order between such entities or actions. Also, the terms "comprises," "comprising," or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. Without further limitation, an element defined by the phrase "comprising an … …" does not exclude the presence of other identical elements in a process, method, article, or apparatus that comprises the element.
The above examples are only intended to illustrate the technical solution of the present invention, but not to limit it; although the present invention has been described in detail with reference to the foregoing embodiments, it will be understood by those of ordinary skill in the art that: the technical solutions described in the foregoing embodiments may still be modified, or some technical features may be equivalently replaced; and such modifications or substitutions do not depart from the spirit and scope of the corresponding technical solutions of the embodiments of the present invention.
Claims (7)
1. An environment-friendly and energy-saving flat coating curtain wall composite coating process and a method are characterized in that: the environment-friendly and energy-saving flat coating curtain wall composite coating process and the method need the following raw materials and tools during operation: a two-component leveling material YY-50, a 0-component smooth surface material YY-60, a transparent water-based sealing bottom coat YY-100, a colored water-based middle coat YY-300 and a jade clothing cover porcelain YY-2000-JZ.
2. The environment-friendly and energy-saving flat coating curtain wall composite coating process and method as claimed in claim 1, characterized in that: the environment-friendly and energy-saving flat coating curtain wall composite coating process and the method comprise the following steps:
s1: determining whether the wall has water seepage and water leakage phenomena, if the wall is required to be repaired in time due to the water seepage phenomena caused by the cracking of the wall, if the wall cannot be repaired, directly painting the jade liquid YY-3000 on the cement painting layer, and then performing putty coating operation;
s2: when the old wall is renovated, the old wall is damaged. Removing all putty layers of the original emulsion paint wall surface, cleaning floating ash and impurities of the wall surface, and sealing with transparent sealing primer;
s3: after the primer is dried, the wall surface is coated with the net and the leveling putty in batches once, the inner wall smooth surface putty is coated in batches twice, and after the primer is polished and leveled, the construction process for preparing the primer, the intermediate coat and the ceramic finish coat is carried out
S4: local peeling, namely removing the peeled and shelled wall surface, filling and coating putty, and then polishing and flattening;
s5: step S4, after polishing and flattening, spraying the primer, standing for a period of time, and naturally drying;
s6: after the spraying of the primer is finished, the spraying of the intermediate paint can be carried out, and the intermediate paint is kept stand for a period of time until the intermediate paint is naturally dried;
s7: after the spraying of the primer is finished, the spraying of the intermediate paint can be carried out, and the intermediate paint is kept stand for a period of time until the intermediate paint is naturally dried;
s8: after the spraying of the intermediate paint is finished, the ceramic finish paint can be sprayed, and the ceramic finish paint is kept stand for a period of time until the ceramic finish paint is naturally dried, so that the ceramic finish paint can be used.
3. The environment-friendly and energy-saving flat coating curtain wall composite coating process and method as claimed in claim 1, characterized in that: in the step S1, if the wall cannot be repaired, the cement plastering layer is directly painted with the jade liquid YY-3000, and then the putty is painted.
4. The environment-friendly and energy-saving flat coating curtain wall composite coating process and method as claimed in claim 1, characterized in that: in the step S5, the primer adopts a transparent water-based seal primer YY-100; the theoretical coating rate is 1.8-2.0 kg/m2。
5. The environment-friendly and energy-saving flat coating curtain wall composite coating process and method as claimed in claim 1, characterized in that: the putty layer in the step S4 adopts a two-component leveling material YY-50 and a single-component smooth surface material YY-60, and the theoretical coating rate is 1.8kg/m2And 1.5kg/m2。
6. The method of claim 1The environment-friendly and energy-saving flat coating curtain wall composite coating process and the method are characterized in that: in the step S6, the colored water-based intermediate coat YY-300 is adopted, and the theoretical coating rate is 0.25kg/m2。
7. The environment-friendly and energy-saving flat coating curtain wall composite coating process and method as claimed in claim 1, characterized in that: in the step S7, the glaze surface is sprayed by the jade clothing covering porcelain YY-2000-JZ, and the theoretical coating rate is 0.07kg/m2。