CN206256617U - Inorganic board - Google Patents
Inorganic board Download PDFInfo
- Publication number
- CN206256617U CN206256617U CN201621333604.9U CN201621333604U CN206256617U CN 206256617 U CN206256617 U CN 206256617U CN 201621333604 U CN201621333604 U CN 201621333604U CN 206256617 U CN206256617 U CN 206256617U
- Authority
- CN
- China
- Prior art keywords
- coating
- ceramic
- inorganic
- seal coat
- ceramic coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides a kind of inorganic board, including：Inorganic plate；Seal coat coating, seal coat coating is coated on inorganic plate；Ceramic coating, ceramic coating is coated on seal coat coating.Inorganic plate is one or more in fiber cement board, calcium silicate board, plasterboard, aluminosilicate fiberboard.Seal coat coating is one or more in UV priming paint, epoxy primer.The thickness of seal coat coating is 10 μm~30 μm.Ceramic coating is one or more in ceramic plain color paint, ceramet paint, ceramic varnish.The thickness of ceramic coating is 25 μm~60 μm.Compared with prior art, the utility model inorganic board has advantages below：Combine ceramic coating and the respective advantage of inorganic plate, the non-ignitable, high hardness wear-resisting of fire prevention, light-weight environment-friendly, convenient construction and installation, long-acting durable, antibiosis and self-cleaning, sound-insulating and heat-insulating, and cost, well below lithotome, large-scale ceramic tile and ceramet plate, market application foreground is wide.
Description
Technical field
The utility model is related to curtain wall engineering, house ornamentation and track traffic furnishing fields, and in particular to a kind of surface coating pottery
The inorganic board of porcelain coating.
Background technology
The remarkable fire protecting performance of ceramic coating, good weatherability, resistance to marring, self-cleaning antibacterial, and aqueous inorganic
The feature of environmental protection that coating has so that ceramic coating is mainly used in the furnishing fields of high-end utilities building, such as the station base curtain of subway
Wall and rail are handed over large-scale people's stream aggregation such as automobile interior and hospital, tunnel, museum, market, gymnasium, school, fire prevention and are pacified
It is complete to require field higher.But current ceramic coating is mainly coated on the sheet metal based on aluminum alloy base material, sheet material
Limitation largely constrain the application extension of ceramic coating.
Utility model content
For defect of the prior art, the utility model purpose is to provide a kind of height for possessing ceramic coating firmly
Spend, the ceramic texture of prevent fires non-ignitable, long-acting durable, antibiosis and self-cleaning, the plurality of advantages of aqueous, environmental protective and uniqueness, while remaining
Inorganic plate insulation, sound insulation and noise reduction, material are slim and graceful, be easy to carrying and installation inherent characteristicses inorganic board.
In order to solve the above technical problems, the utility model provides a kind of inorganic board, including：Inorganic plate；Seal coat is applied
Layer, the seal coat coating is coated on the inorganic plate；Ceramic coating, the ceramic coating is coated in the closing
On primer coating.
Preferably, the inorganic plate is the one kind in fiber cement board, calcium silicate board, plasterboard, aluminosilicate fiberboard
Or it is various.
Preferably, the seal coat coating is one or more in UV priming paint, epoxy primer.
Preferably, the thickness of the seal coat coating is 10 μm~30 μm.
Preferably, the ceramic coating is one or more in ceramic plain color paint, ceramet paint, ceramic varnish.
Preferably, the thickness of the ceramic coating is 25 μm~60 μm.
Compared with prior art, the utility model inorganic board has advantages below：Combine ceramic coating and inorganic plate
Respective advantage, prevent fires non-ignitable, high hardness wear-resisting, light-weight environment-friendly, convenient construction and installation, long-acting durable, antibiosis and self-cleaning, sound insulation every
Heat, and cost, well below lithotome, large-scale ceramic tile and ceramet plate, market application foreground is wide.
Brief description of the drawings
The detailed description made to non-limiting example with reference to the following drawings by reading, other spies of the present utility model
Levying objects and advantages will become more apparent upon.
Fig. 1 is the inorganic plate structure schematic diagram of the utility model.
In figure：
1- inorganic plate 2- seal coat coating 3- ceramic coatings
Specific embodiment
The utility model is described in detail with reference to specific embodiment.Following examples will be helpful to this area
Technical staff further understands the utility model, but does not limit the utility model in any form.It should be pointed out that to ability
For the those of ordinary skill in domain, without departing from the concept of the premise utility, some changing and modifications can also be made.
As shown in figure 1, the utility model inorganic board is as base material with inorganic plate 1, after coating seal coat coating 2, then
Coated ceramic coating 3.Manufacturing process steps include：
Step one a, there is provided base material, typically including fiber cement board, calcium silicate board, plasterboard, aluminosilicate fiberboard etc.
In interior inorganic plate 1, it is necessary to be processed before carrying out simple polishing and dedusting.
Step 2, using carried out on inorganic plate 1 including the seal coat including UV priming paint, epoxy primer etc. roller coat or
Spraying, forms seal coat coating 2, and the main purpose of seal coat coating 2 is the hole and defect filled up on inorganic plate, while
For the ceramic coating on top layer provides good adhesion.
Step 3, solidifies to the inorganic plate 1 after application seal coat, and UV priming paint needs to carry out photocuring, typically
UV light irradiate solidification in 8 seconds~10 seconds can straight forming, epoxy primer then needs to carry out low-temperature bake solidification, seal coat coating
2 thickness is 10 μm~30 μm.
Step 4, the inorganic plate 1 after being closed to priming paint is polished, dedusting so that plate face reaches application ceramic coating
The flatness requirement of finish paint.
Step 5, is sprayed or roller coat on the inorganic plate 1 using ceramic coating after seal coat, is formed ceramics and is applied
Layer 3, ceramic coating 3 reacts the coating to be formed, thickness 25 through sol-gel chemistry for inorganic oxide sol with water-disintegrable alkoxide
μm~60 μm, ceramic coating 3 has prevent fires non-ignitable, high rigidity, wear-resisting scratch resistance, long-acting durable, antibiosis and self-cleaning distinguishing feature.
Step 6, installs the inorganic board of ceramic coating and solidifies to painting, and solidification temperature is 80 DEG C~100 DEG C, time
10min~20min, solidification can make ceramic coating 3 reach bond strength in itself, realize the exclusive performance characteristics of ceramic coating 3 and
Decorative effect.
On the one hand the utility model inorganic board, the pore closure of inorganic plate is realized by seal coat coating, another
Aspect also solves adhesion problem of the ceramic coating on inorganic plate, and cost is lower compared with traditional ceramet plate,
It is breakthrough that ceramic coating is applied in inorganic plate field.
Specific embodiment of the utility model is described above.It is to be appreciated that the utility model not office
It is limited to above-mentioned particular implementation, those skilled in the art can within the scope of the claims make a variety of changes or change,
This has no effect on substance of the present utility model.In the case where not conflicting, the spy in embodiments herein and embodiment
Levying arbitrarily to be mutually combined.
Claims (6)
1. a kind of inorganic board, it is characterised in that including：
Inorganic plate；
Seal coat coating, the seal coat coating is coated on the inorganic plate；
Ceramic coating, the ceramic coating is coated on the seal coat coating.
2. inorganic board according to claim 1, it is characterised in that the inorganic plate be fiber cement board, calcium silicate board,
One or more in plasterboard, aluminosilicate fiberboard.
3. inorganic board according to claim 1, it is characterised in that the seal coat coating is UV priming paint, epoxy primer
In one or more.
4. the inorganic board according to claim 1 or 3, it is characterised in that the thickness of the seal coat coating is 10 μm~
30μm。
5. inorganic board according to claim 1, it is characterised in that the ceramic coating is ceramic plain color paint, ceramet
One or more in paint, ceramic varnish.
6. inorganic board according to claim 1 or 5, it is characterised in that the thickness of the ceramic coating is 25 μm~60 μm.