CN111549997A - Preparation process of face brick imitating decorative plate - Google Patents
Preparation process of face brick imitating decorative plate Download PDFInfo
- Publication number
- CN111549997A CN111549997A CN202010401784.4A CN202010401784A CN111549997A CN 111549997 A CN111549997 A CN 111549997A CN 202010401784 A CN202010401784 A CN 202010401784A CN 111549997 A CN111549997 A CN 111549997A
- Authority
- CN
- China
- Prior art keywords
- brick
- drying
- decorative substrate
- cement
- template
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of building decorative plate preparation, and discloses a process for preparing a face brick imitating decorative plate, which comprises the following steps: a. processing counter bores on the decorative substrate, sanding and dedusting the back surface of the decorative substrate, and then coating a sealing inner coating; b. fixing the adapter piece and the counter bore, and filling putty at the counter bore; c. spraying a brick joint color primer on the front surface of the decorative substrate, drying to form a brick joint color primer layer after spraying, filling a cement-based pigment in the strip brick shaping template, and drying to form a cement-based color layer; d. filling a coloring coating in the brickwork joint repairing template, scraping by a scraper, taking down the brickwork joint repairing template, and drying the coloring coating to form a coloring coating layer; e. and scraping redundant slurry in the brick joints by using a brick joint scraper, spraying finishing paint on the surface of the coloring coating layer on the front surface of the decorative substrate and the surface of the brick joints, and drying to obtain the imitation face brick decorative plate. The invention has the advantages of good decorative effect, difficult cracking of the outer surface and long service life.
Description
Technical Field
The invention relates to the technical field of building decorative plate preparation, in particular to a process for preparing a face brick imitating decorative plate.
Background
With the continuous development of building technology and the continuous consumption and utilization of energy, the country actively advocates technical and economic policies such as resource saving, environmental protection, sustainable development promotion and the like. More and more novel buildings have higher requirements on the aspects of heat preservation, decoration, easy construction safety and the like of the outer wall. More and more existing buildings need to be repaired more economically and environmentally, so that not only are potential safety hazards eliminated, but also the appearance and the appearance of the buildings are improved.
In order to improve the aesthetic property of a plurality of building outer walls, ceramic tiles are usually pasted on the outer walls or a imitated tile paint coating is sprayed on the outer walls, the requirements of reconstruction and decoration of old and old urban areas of the outer walls are also met, the outer surfaces of buildings such as old buildings and schools in 80-90 years are also required to be secondarily reconstructed, and the ceramic tiles are pasted or the imitated tile paint coating is sprayed on the outer walls; however, the traditional ceramic tiles are exposed to rain, sunshine and the like, the ceramic tiles are easy to fall off, potential safety hazards exist, and the ceramic tiles are very troublesome to remove when the ceramic tiles are replaced on the wall surface; the spraying of the imitated face brick paint coating requires on-site wet operation, the engineering period is long, and the imitated face brick paint coating is easy to peel off when being exposed to rain and sunlight; the outer wall decorative board is the novel building outer wall decoration heat preservation integrated material of research and development in recent years, and various base plate, colour, surface structure and coating make it have very big flexibility and selectivity, however present common outer wall decorative board surface coating easily drops, the fracture produces the line, influences pleasing to the eye, can't obtain the effect of imitative face brick moreover, can't satisfy some aesthetic property demands.
Disclosure of Invention
The invention aims to solve the problems of building external decorative plates in the prior art and provides a preparation process of a face brick imitating decorative plate.
In order to achieve the purpose, the invention adopts the following technical scheme:
a process for preparing a face brick imitating decorative plate comprises the following steps: a. processing a plurality of counter bores penetrating through the decorative substrate on the decorative substrate, sanding the back surface of the decorative substrate, removing dust after sanding, and coating a sealing inner coating on the back surface of the decorative substrate after dust removal; b. taking a plurality of adapters with connecting through holes, wherein the number of the adapters corresponds to the number of the counter bores one by one, the adapters are fixed with the counter bores on the back side of the decorative substrate through rivets or bolts, putty is filled in the counter bores on the front side of the decorative substrate, sanding treatment is carried out after the putty is compacted and leveled, dust is removed after the sanding treatment, a sealing outer coating is coated on the front side of the decorative substrate after the dust is removed, and drying treatment is carried out; c. spraying a brick joint color primer on the front surface of the decorative substrate, drying to form a brick joint color primer layer after spraying, placing a strip brick shaping template on the front surface of the decorative substrate and positioning, uniformly distributing hollow frames in the strip brick shaping template, filling cement-based pigment in the hollow frames, scraping by a scraper, enabling the height of the cement-based pigment to be flush with the top surface of the strip brick shaping template, taking down the strip brick shaping template, drying the cement-based pigment to form a cement-based color layer, and forming a brick joint between two adjacent cement-based color layers; d. installing and positioning a brickwork joint repairing template on the front surface of the decorative substrate, wherein repairing frames which correspond to the hollowed-out frames one by one are uniformly distributed on the brickwork joint repairing template, and the rib width of each repairing frame is 0.7-0.95 times of the rib width of each hollowed-out frame; filling the colored paint in the repairing frame, scraping by a scraper, taking down the brickwork joint repairing template, and drying the colored paint to form a colored paint layer; e. and scraping redundant slurry in the brick joints by using a brick joint scraper, spraying finishing paint on the surface of the coloring coating layer on the front surface of the decorative substrate and the surface of the brick joints, and drying to obtain the imitation face brick decorative plate. The outer surface of the imitation face brick decorative plate prepared by the process has the decoration effect of an imitation face brick, brick joints exist among all the coloring coating layers (cement-based color layers), and because each coloring coating layer has small influence on expansion with heat and contraction with cold, the imitation face brick decorative plate cannot arch or crack due to the factors of expansion with heat and contraction with cold, and the service life of the whole imitation face brick decorative plate is long; when in use, after the keel is arranged on the outer wall surface of the building, the adaptor on the back surface of the face brick imitating decorative plate is directly connected with the keel, so that the installation is very convenient; the face brick imitating decorative plate can be used for an outer decorative plate of a new building and can also be used for the reconstruction of the outer wall surface of an old building.
Preferably, the putty in the step b is prepared from the following components in parts by weight: 5-7 parts of putty powder, 20-28 parts of quartz sand, 10-15 parts of vinyl acetate-ethylene copolymer emulsion and 5-10 parts of water; filling the putty in two ways, wherein after the first putty is filled, the second putty is filled after 8-10 h. Through two putty layers, the inner part of the counter bore on the front surface of the decorative substrate is more compact and smooth.
Preferably, in step c, the amount of the color coat sprayed is 0.12-0.15 kg/m2The drying temperature after spraying is 60 ℃, and the drying time is 8-12 min.
Preferably, the thickness of the strip brick shaping template is 1.8-2.2mm, and the thickness of the brick joint repairing template is 0.45-0.6mm larger than that of the strip brick shaping template; the width of the hollow frame rib is 9-11mm, and the strip brick shaping template and the brick joint repairing template are both made of ABS plastic.
Preferably, in the step c, the left end of the strip brick shaping template is fixed with the wide edge of the left end of the decorative substrate through a positioning clamp, a scraper scrapes the blank from left to right at an angle of 45 degrees, and the scraping speed of the scraper is 0.6-1.0 m/s; in the step d, the right end of the brickwork joint repairing template is fixed with the right end wide edge of the decorative substrate through a positioning clamp, a scraper scrapes the materials from right to left at an angle of 45 degrees, and the scraping speed of the scraper is 0.3-0.5 m/s.
Preferably, the cement-based coloring material contains glass fibers, and the mass ratio of the glass fibers to the cement-based coloring material is 5: 95. The glass fiber can effectively prevent the cement-based color layer from cracking.
Preferably, in the step c, the cement-based coloring material is scraped and then placed in a ventilation chamber for ventilation and drying, the temperature of the ventilation chamber is 20-25 ℃, the humidity of the ventilation chamber is 40% -60%, the drying time is 12-15h, after drying, sanding treatment is carried out on the surface of the cement-based coloring layer through 80-mesh abrasive paper, and after sanding treatment, the flatness of the cement-based coloring layer is detected until the flatness error of the cement-based coloring layer is less than 0.35 mm; in the step d, the colored coating is scraped and then is placed in a drying chamber for drying, the temperature of the drying chamber is 35-45 ℃, the humidity of a ventilation chamber is 30% -50%, and the drying time is 8-12 h. The cement-based pigment is not easy to crack after being air-dried in an environment with high humidity.
Preferably, after the step d, selectively rubbing the surface of the colored coating layer by a coating roller to form a dyed layer on the surface of the colored coating layer, wherein the thickness of the dyed layer is less than 0.2 mm. The color wiping operation is to selectively color some coloring coating layers according to the actual decoration effect, so that the color difference is formed on the surfaces of the coloring coating layers to meet some specific decoration requirements.
Preferably, in step e, a protective film is coated on the outer side of the finishing paint layer on the front surface of the simulated tile decorative plate. The protective film plays a role in protecting the surface of the imitation face brick decorative plate and prevents the front surface of the imitation face brick decorative plate from being scratched in the processes of carrying and mounting.
Therefore, the decorative plate has the beneficial effects of good decorative effect, difficult cracking of the outer surface and long service life.
Drawings
FIG. 1 is a schematic front view of a simulated tile decorative board.
FIG. 2 is a schematic cross-sectional view of a simulated tile decorative board.
Fig. 3 is a partially enlarged view of a portion a in fig. 2.
Fig. 4 is a schematic structural view of a bar brick setting form.
FIG. 5 is a schematic structural diagram of a brickwork joint repair formwork.
In the figure: the color-changeable decorative plate comprises a decorative substrate 1, a sealing inner coating 2, an adapter piece 3, putty 4, a sealing outer coating 5, a brick joint color primer layer 6, a strip brick shaping template 7, a hollow frame 70, a hollow frame rib 71, a cement-based color layer 8, a brick joint 9, a brick joint repairing template 10, a repairing frame 100, a repairing frame rib 101, a coloring paint layer 11 and a dyeing layer 12.
Detailed Description
The invention is further described with reference to the accompanying drawings and the detailed description below:
as shown in figures 1, 2 and 3, the process for preparing the imitation face brick decorative plate comprises the following steps: a. processing a plurality of counter bores penetrating through the decorative substrate on the decorative substrate 1, sanding the back surface of the decorative substrate, removing dust after sanding, and coating a sealing inner coating 2 on the back surface of the decorative substrate after dust removal, wherein the decorative substrate is in a rectangular structure and is a cement-based fiberboard or a calcium silicate board; b. get a plurality of adapters 3 that have connect the through-hole, the quantity and the counter bore quantity one-to-one of adapter 3, adapter 3 passes through the rivet or the bolt is fixed with the counter bore at the decorative substrate back, and putty 4 is filled to the positive counter bore department of decorative substrate, and putty is made according to the part by weight ratio by following component: 5-7 parts of putty powder, 20-28 parts of quartz sand, 10-15 parts of vinyl acetate-ethylene copolymer emulsion and 5-10 parts of water, wherein the putty is filled in two ways, after the first course of putty is filled, the second course of putty is filled in after 8-10 hours, the putty is compacted and scraped flatly, then sanding treatment is carried out, dust is removed after sanding treatment, a sealing outer coating 5 is coated on the front surface of the decorative substrate after dust removal, and drying treatment is carried out;
c. spraying the brick seam color primer on the front surface of the decorative substrate, wherein the spraying amount of the brick seam color primer is 0.12-0.15 kg/m2The drying temperature after spraying is 60 ℃, the drying time is 8-12min, the color priming layer 6 of the brick joints is formed by drying after spraying, the strip brick shaping template 7 is arranged on the front surface of the decorative substrate, the left end of the strip brick shaping template is fixed with the wide edge of the left end of the decorative substrate through a positioning clamp, the structure of the strip brick shaping template 7 is shown in figure 5, the thickness of the strip brick shaping template is 1.8-2.2mm, the strip brick shaping template is made of ABS plastic, hollow frames 70 are uniformly distributed in the strip brick shaping template, the width of hollow frame ribs 71 is 9-11mm, cement-based pigments are filled in the hollow frames and then are scraped in batches through a scraper, the cement-based pigments contain glass fibers, the mass ratio of the glass fibers to the cement-based pigments is 5:95, the scraper is scraped to the right at an angle of 45 degrees, the scraping speed of the scraper is 0.6-1.0m/s, the height of the cement-based pigments is flush with the top surface of the strip brick, scraping, taking down the strip brick forming template 7, scraping, putting the cement-based pigment into a ventilation chamber for ventilation and drying, wherein the temperature of the ventilation chamber is 20-25 ℃, the humidity of the ventilation chamber is 40% -60%, the drying time is 12-15h, the cement-based pigment is dried to form a cement-based color layer 8, a brick joint 9 is formed between two adjacent cement-based color layers, sanding is carried out on the surface of the cement-based color layer 8 through 80-mesh abrasive paper, and the flatness of the cement-based color layer is detected after sanding until the flatness error of the cement-based color layer is less than 0.35 mm;
d. installing a brickwork joint repairing template 10 on the front surface of a decorative substrate 1, wherein the structure of the brickwork joint repairing template 10 is shown in figure 5, repairing frames 100 which correspond to the hollowed frames one by one are uniformly distributed on the brickwork joint repairing template 10, the brickwork joint repairing template is 0.45-0.6mm thicker than a bar brick shaping template, the bar brick shaping template is made of ABS plastic, the width of a repairing frame rib 101 is 0.7-0.95 times of the width of the hollowed frame rib, the right end of the brickwork joint repairing template is fixed with the right end wide edge of the decorative substrate through a positioning clamp, after filling coloring paint in the repairing frame, scraping is carried out through a scraper which scrapes from right to left at an angle of 45 degrees, the scraping speed of the scraper is 0.3-0.5 m/s, the brickwork joint repairing template is taken down, the coloring paint is dried in a drying chamber after scraping, the drying chamber is at the temperature of 35-45 ℃, the humidity of a ventilation chamber is 30-, forming a coloring coating layer 11 after the coloring coating is dried; selectively wiping the surface of the coloring coating layer by a coating roller to form a dyeing layer 12 on the surface of the coloring coating layer 11, wherein the thickness of the dyeing layer is less than 0.2mm, and the wiping operation is selected according to actual requirements;
e. scraping redundant slurry in the brick joints by using a brick joint scraper, spraying finishing paint on the surface of the coloring coating layer on the front surface of the decorative substrate and the surface of the brick joints, and drying to obtain a face brick imitating decorative plate; and a protective film is coated on the outer side of the finishing paint layer on the front surface of the face brick imitating decorative plate.
The outer surface of the imitation face brick decorative plate prepared by the process has the decoration effect of an imitation face brick, brick joints exist among all the coloring coating layers (cement-based color layers), and because each coloring coating layer has small influence on expansion with heat and contraction with cold, the imitation face brick decorative plate cannot arch or crack due to the factors of expansion with heat and contraction with cold, and the service life of the whole imitation face brick decorative plate is long; when in use, after the keel is arranged on the outer wall surface of the building, the adaptor on the back surface of the face brick imitating decorative plate is directly connected with the keel, so that the installation is very convenient; the face brick imitating decorative plate can be used for an outer decorative plate of a new building and can also be used for the reconstruction of the outer wall surface of an old building.
The above is only a specific embodiment of the present invention, but the technical features of the present invention are not limited thereto, for example, the decorative substrate may adopt other regular polygon structures, the shapes of the strip brick shaping template and the brick seam repairing template may also adopt regular polygon structures corresponding to the decorative substrate, and the shapes and arrangement of the hollow frame and the repairing frame may also be adaptively adjusted and modified according to actual requirements. Any simple changes, equivalent substitutions or modifications made based on the present invention to solve the same technical problems and achieve the same technical effects are within the scope of the present invention.
Claims (9)
1. A process for preparing a face brick imitating decorative plate is characterized by comprising the following steps:
a. processing a plurality of counter bores penetrating through the decorative substrate on the decorative substrate, sanding the back surface of the decorative substrate, removing dust after sanding, and coating a sealing inner coating on the back surface of the decorative substrate after dust removal;
b. taking a plurality of adapters with connecting through holes, wherein the number of the adapters corresponds to the number of the counter bores one by one, the adapters are fixed with the counter bores on the back side of the decorative substrate through rivets or bolts, putty is filled in the counter bores on the front side of the decorative substrate, sanding treatment is carried out after the putty is compacted and leveled, dust is removed after the sanding treatment, a sealing outer coating is coated on the front side of the decorative substrate after the dust is removed, and drying treatment is carried out;
c. spraying a brick joint color primer on the front surface of the decorative substrate, drying to form a brick joint color primer layer after spraying, placing a strip brick shaping template on the front surface of the decorative substrate and positioning, uniformly distributing hollow frames in the strip brick shaping template, filling cement-based pigment in the hollow frames, scraping by a scraper, enabling the height of the cement-based pigment to be flush with the top surface of the strip brick shaping template, taking down the strip brick shaping template, drying the cement-based pigment to form a cement-based color layer, and forming a brick joint between two adjacent cement-based color layers;
d. installing and positioning a brickwork joint repairing template on the front surface of the decorative substrate, wherein repairing frames which correspond to the hollowed-out frames one by one are uniformly distributed on the brickwork joint repairing template, and the rib width of each repairing frame is 0.7-0.95 times of the rib width of each hollowed-out frame; filling the colored paint in the repairing frame, scraping by a scraper, taking down the brickwork joint repairing template, and drying the colored paint to form a colored paint layer;
e. and scraping redundant slurry in the brick joints by using a brick joint scraper, spraying finishing paint on the surface of the coloring coating layer on the front surface of the decorative substrate and the surface of the brick joints, and drying to obtain the imitation face brick decorative plate.
2. The process for preparing a simulated face brick decorative plate as claimed in claim 1, wherein the putty in the step b is prepared from the following components in parts by weight: 5-7 parts of putty powder, 20-28 parts of quartz sand, 10-15 parts of vinyl acetate-ethylene copolymer emulsion and 5-10 parts of water; filling the putty in two ways, wherein after the first putty is filled, the second putty is filled after 8-10 h.
3. The process for preparing a simulated face brick decorative plate as claimed in claim 1, wherein in the step c, the spraying amount of the color primer for brick joints is 0.12-0.15 kg/m2The drying temperature after spraying is 60 ℃, and the drying time is 8-12 min.
4. The process for preparing a face brick-imitating decorative plate according to claim 1, wherein the thickness of the strip brick shaping template is 1.8-2.2mm, and the thickness of the brick joint repairing template is 0.45-0.6mm larger than that of the strip brick shaping template; the width of the hollow frame rib is 9-11mm, and the strip brick shaping template and the brick joint repairing template are both made of ABS plastic.
5. The process for preparing a simulated face brick decorative plate according to claim 1 or 4, wherein in the step c, the left end of the strip brick shaping template is fixed with the wide edge of the left end of the decorative substrate through a positioning clamp, a scraper scrapes the blank from left to right at an angle of 45 degrees, and the scraping speed of the scraper is 0.6-1.0 m/s; in the step d, the right end of the brickwork joint repairing template is fixed with the right end wide edge of the decorative substrate through a positioning clamp, a scraper scrapes the materials from right to left at an angle of 45 degrees, and the scraping speed of the scraper is 0.3-0.5 m/s.
6. The process for preparing a simulated face brick decorative plate as claimed in claim 1, wherein the cement-based pigment contains glass fiber, and the mass ratio of the glass fiber to the cement-based pigment is 5: 95.
7. The process for preparing the simulated face brick decorative plate as claimed in claim 1, wherein in the step c, the cement-based coloring material is scraped and put into a ventilation chamber for ventilation and drying, the temperature of the ventilation chamber is 20-25 ℃, the humidity of the ventilation chamber is 40-60%, the drying time is 12-15h, after drying, sanding treatment is carried out on the surface of the cement-based color layer through 80-mesh abrasive paper, and the flatness of the cement-based color layer is detected after sanding treatment until the flatness error of the cement-based color layer is less than 0.35 mm; in the step d, the colored coating is scraped and then is placed in a drying chamber for drying, the temperature of the drying chamber is 35-45 ℃, the humidity of a ventilation chamber is 30% -50%, and the drying time is 8-12 h.
8. The process of claim 6, wherein after step d, the surface of the layer of pigmented paint is selectively wiped with a paint roller to form a layer of dye on the surface of the layer of pigmented paint, the dye having a thickness of less than 0.2 mm.
9. The process for preparing a simulated tile decorative plate as claimed in claim 6, wherein in the step e, a protective film is coated on the outer side of the finishing paint layer on the front surface of the simulated tile decorative plate.