CN204418561U - The decorative structure of the existing metope face brick processed of a kind of adhesive sticker sheet hollowed mould - Google Patents
The decorative structure of the existing metope face brick processed of a kind of adhesive sticker sheet hollowed mould Download PDFInfo
- Publication number
- CN204418561U CN204418561U CN201420870909.8U CN201420870909U CN204418561U CN 204418561 U CN204418561 U CN 204418561U CN 201420870909 U CN201420870909 U CN 201420870909U CN 204418561 U CN204418561 U CN 204418561U
- Authority
- CN
- China
- Prior art keywords
- coating
- adhesive sticker
- face brick
- mould
- decorative structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides the decorative structure of the existing metope face brick processed of a kind of adhesive sticker sheet hollowed mould, described face brick covers on metope, described face brick distance metope is extremely far comprised by near: inorganic powder screed, primer coating, facing coating, the pattern of described facing coating is realized by adhesive sticker sheet hollowed mould.The utility model provide a kind of can on building the decorative structure of the metope face brick of existing system, its face brick color lump is even, forming surface is regular, not outbound leg of circuit in work progress, and the decorative pattern rich color of face brick, presents ceramic tile decorative effect true to nature.
Description
Technical field
The utility model relates to building materials technical field of construction, particularly relates to the decorative structure of the existing metope face brick processed of a kind of adhesive sticker sheet hollowed mould.
Background technology
Special for walltile binding material and body of wall normally carry out boning by existing building wall face brick decoration, jointing.There is following shortcoming in this traditional patch block technique: (1) walltile decorations facing is from great (about 20kg/m
2above); (2) work efficiency such as (stickup, jointing operation) of constructing is low, and (work efficiency of conventional skilled worker is 7-8m
2/ sky/people); (3) because of walltile and the elastic modulus difference of binding material and the controllability difference of binding material and construction and the potential safety hazard causing walltile to come off, peel off; (4) the attractive in appearance of walltile decorative cover is affected because of the accumulation of salt in the surface soil of binding material (being generally cement mortar class); (5) because pointing and construction reason easily cause decorative layer to seep water; (6) figure because of walltile goods is abundant not, and the decoration of complex figure cannot realize; (7) consume a large amount of walltiles to energy-saving and environmental protection, economize on resources unfavorable.
In order to overcome the problems referred to above, those skilled in the art take to improve the adhesive property of binding material and the anti-accumulation of salt in the surface soil of pointing and water resistance and realize, and adopt walltile light as far as possible (suggestion controls at 20kg/m simultaneously
2below).The weak point of these measures is, more specifically requirement is proposed to the performance of walltile and binding material, pointing, and the deadweight of the difficulty to control of work progress and overall decorative layer cannot be reduced greatly, there is the long-term safety hidden danger of quality of engineering equally.
In order to overcome the problems referred to above further, those skilled in the art have developed following methods.
Chinese patent CN2849002Y, the back of its brick has groove, to increase the firm pasting of walltile.But the method still has the danger come off, and add an operation, improve cost.
Chinese patent CN1303456A (PCT/FR99101009), its method in primary coat, carries out press back pattern with a concavo-convex pattern template, the color treatments of its forming surface has two kinds of methods, one is painted by pit with filling paint after press back, and another kind is coated in by tintage paint in concavo-convex template to carry out transfer impression.These two kinds of methods all cannot obtain uniform color lump effect.Be not the uneven color rule of recess, the color at convex exactly place produces convex place and both sides uneven color rule owing to being squeezed uneven.In addition, due to the demoulding for convenience, mould is provided with about draft angle of 5 °, and under the state faced, side such as the uneven color rule of figure will have a strong impact on the regular aesthetic property of color lump.
Chinese patent CN1060134A, its method is being carved with the openworking template of decorative pattern by the metope after Lacquer finish, carrying out scraping coating layer, be similar to silk-screen printing technique.Because the method is that metope after Lacquer finish carries out, and revenue stamp process must carry out after the drying again, and the smooth process of metope simultaneously necessarily exists flatness error.By quarter dapple openworking template on the metope having certain flatness error by flat (now metope is dry), the gap of template and metope can be produced.When scraping coating layer, easily producing spillage and affecting decorative effect.In addition, template needs external force to fix.And when row graph stamp, error is certainly existed to the splicing between template and the figure that completes, operation easier is increased.
Chinese patent CN101122165A, its method is before primary coat initial set, is overlayed by certain thickness sheet hollowed mould and is fixed in primary coat, then be coated with in surperficial coated side, obtained figure after the demoulding.There is following problem in the method, as the state adopting primary coat wet, then after the demoulding, the forming surface of primary coat has plucking phenomenon, has a strong impact on attractive in appearance in knockout course; As adopted primary coat dry state, face is coated with dry state bottom knockout, then due to demoulding shearing and friction effect, can produce forming surface and to rive finning; As adopted primary coat dry state, face is coated in wet state, and now face is coated with and does not also form structural strength, and the mould in embedding primary coat is deviate from, and the frictional force between face painting and mould makes primary coat produce friction overlap and is coated with disengaging with face, and affects forming surface.Meanwhile, due to face be coated with employing have aggregate coating, its construction can only be trowelling or spraying, twice working face connect stubble and facing skin texture difference will produce aberration.Therefore the method be difficult to obtain color evenly, the decorative effect of graphics standardization.
In sum, this area lack a kind of can on building the metope face brick of existing system, its face brick color lump is even, forming surface is regular, not outbound leg of circuit in work progress.
Utility model content
Technical problem to be solved in the utility model is: for the defect of prior art, provide a kind of can on building the decorative structure of the metope face brick of existing system, its face brick color lump is even, forming surface is regular, not outbound leg of circuit in work progress.
The utility model is for solving the problems of the technologies described above by the following technical solutions:
The utility model provides the decorative structure of the existing metope face brick processed of a kind of adhesive sticker sheet hollowed mould, described face brick covers on metope, described face brick distance metope by near to as far as comprising less: inorganic powder screed, primer coating, facing coating, the pattern of described facing coating is realized by adhesive sticker sheet hollowed mould.
In the decorative structure of above-mentioned face brick, preferably, described adhesive sticker sheet hollowed mould has following structure before construction: on the basal surface and external surface of described mould, be respectively equipped with bottom overlay film and top layer overlay film, bottom overlay film is provided with adhesive sticker tack coat, described adhesive sticker tack coat is provided with one deck separate paper further.
Preferably, the gross thickness of described sheet hollowed mould is 0.3-2mm.
Preferably, the coating weight of described adhesive sticker tack coat is 50-150g/m
2.
Preferably, 180 ° of peel strengths of described adhesive sticker tack coat are 1.5-4.0N/cm, are more preferably 2.0-3.5N/cm, such as 2.5-3.0N/cm.
Preferably, the material of described mould to be selected from art post paperboard, craft paper, kraft, plastics, composite material, material with carbon element, silicon materials any one or multiple.
In the decorative structure of above-mentioned face brick, preferably, described inorganic powder screed is used for levelling described metope, and has firmly adhesion with body of wall, and its thickness is 1-2mm.
In the decorative structure of above-mentioned face brick, preferably, described primer coating provides the brickwork joint color of face brick, and improve the firmness of basic unit's coating further, prevent the accumulation of salt in the surface soil, its thickness is 0.1-0.3mm.
In the decorative structure of above-mentioned face brick, preferably, described facing coating has certain texture skin texture and abundant color, and the weatherability that Long-Time Service possesses, on body of wall, various abundant pattern is now made by using above-mentioned adhesive sticker sheet hollowed mould, present ceramic tile decorative effect true to nature, its thickness is 1-2mm.
The construction method of the existing metope face brick processed of adhesive sticker sheet hollowed mould of the present utility model comprises the steps:
Step 1: at described building surface coating inorganic dry powder and mortar layer, for levelling described metope, and have firmly adhesion with body of wall, its thickness is 1-2mm;
Step 2: then apply primer coating, provides the brickwork joint color of face brick, and improve the firmness of basic unit's coating further, prevent the accumulation of salt in the surface soil, its thickness is 0.1-0.3mm;
Step 3: after primer coating is done solid work, primer coating is pasted the sheet hollowed mould tearing outer separate paper off, and the adhesive sticker tack coat on described sheet hollowed mould and described primer coating bond;
Step 4: after having pasted sheet hollowed mould, applies facing coating immediately, and under the state of the non-surface drying of facing coating, sloughs sheet hollowed mould; Described facing coating has certain texture skin texture and abundant color, and the weatherability that Long-Time Service possesses, by using above-mentioned adhesive sticker sheet hollowed mould now to make various abundant pattern on body of wall, present ceramic tile decorative effect true to nature, its thickness is 1-2mm.
In the above-mentioned methods, preferably, described primer coating comprises gel rubber material, filler, pigment, optional additive and optional aggregate, and described gel rubber material is inorganic gel materials, organic gel materials or its combination.
In the above-mentioned methods, preferably, described facing coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.
The utility model adopts above technical scheme, compared with prior art, has following technique effect:
The utility model provide a kind of can on building the metope face brick of existing system, its face brick color lump is even, forming surface is regular, not outbound leg of circuit in work progress, and the decorative pattern rich color of face brick, presents ceramic tile decorative effect true to nature.
Accompanying drawing explanation
Fig. 1 is the front schematic view of a detailed description of the invention of mould described in the utility model;
Fig. 2 is the side schematic view of a detailed description of the invention of mould described in the utility model;
Fig. 3 a demoulding wall facing bricks die can cover front schematic view on building masonry wall;
Fig. 3 b is the side schematic view in primer coating after pasting mould;
Fig. 3 c is the side schematic view of the wall facing brick after sloughing mould;
In figure, 1-adherent layer, 2-adhesive sticker tack coat, 3-bottom tectorial paper, 4-paper body, 5-top layer tectorial paper, 6-die ontology, 7-brick hole, 8-body of wall, 9-inorganic powder screed, 10-primer coating, 11-facing coating.
Detailed description of the invention
As used herein, described " sheet hollowed mould ", except as otherwise noted, refer to the sheet mould that front has pierced pattern (being such as the hole of hollow out), described pierced pattern can design arbitrarily, be not particularly limited, can determine according to the shape forming wall facing brick, such as: brick shape, cobble shaped, geometric figure, flowers figure etc.Described " front " refers to the elevation of metope.
As used herein, described " building surface ", except as otherwise noted, refers to the metope of building, end face etc., such as exterior wall, interior wall, smallpox.Described metope can be insulated wall, also can be common metope.
As used herein, described " primer coating ", except as otherwise noted, refers to one or more layers coating (described coating such as mortar) directly contacted with the surface of building.In one or more layers coating described, can be one or many coating each time and be formed.
As used herein, described " facing coating ", except as otherwise noted, refer to sheet hollowed mould external surface, be exposed to one or more layers coating with sheet hollowed mould pattern of air.In one or more layers coating described, can be one or many coating each time and be formed.
Can have " middle coat " between described " primer coating " and " facing coating ", described " middle coat ", except as otherwise noted, refer to together with can being embedded in sheet hollowed mould of the present utility model, also can not one or more layers coating together with sheet hollowed mould is embedded in.In one or more layers coating described, can be one or many coating each time and be formed.
The utility model provides a kind of face brick now can made on building surface, and this face brick color lump evenly, can not outbound leg of circuit in regular, the work progress of a demoulding, forming surface, the decorative pattern rich color of face brick, presents ceramic tile decorative effect true to nature; Additionally provide the method making the mould that uses of wall facing brick and use the existing wall facing brick processed of this mould.
Particularly, the decorative structure of the existing metope face brick processed of a kind of adhesive sticker sheet hollowed mould, described face brick covers on metope, described face brick distance metope is extremely far comprised by near: inorganic powder screed, primer coating, facing coating, the pattern of described facing coating is realized by adhesive sticker sheet hollowed mould.
In the decorative structure of above-mentioned face brick, particularly, a kind of wall facing bricks die for existing face brick processed on building surface, described mould is sheet hollowed mould, the basal surface and external surface of described mould are respectively equipped with bottom overlay film and top layer overlay film, bottom overlay film is provided with adhesive sticker tack coat, described adhesive sticker tack coat is provided with one deck separate paper further.
The basal surface of described mould and external surface are respectively equipped with bottom overlay film and top layer overlay film, and preferably, described bottom overlay film has smooth surface, makes described bottom overlay film be easily fixed on the surface of described building by adhesive sticker tack coat.Its advantage is: after the primer coating of building is done solid work, described mould is overlayed in described primer coating, then apply facing coating immediately, under the state of the non-surface drying of facing coating, the top layer overlay film with smooth surface makes described mould can the easily demoulding, and can not produce overlap; Meanwhile, it is more smooth and easy when the smooth surface in front can make coating facing coating.The adhesion of described top layer overlay film is not specifically limited, and only otherwise to goal of the invention of the present utility model produces and limits.
In above-mentioned mould, preferably, the gross thickness of described sheet hollowed mould is 0.3-2mm, such as 1mm, 1.5mm.
In above-mentioned mould, preferably, the coating weight of described adhesive sticker tack coat is 50-150g/m
2, such as 100g/m
2, 120g/m
2.Between described adhesive sticker tack coat and the bottom overlay film of described mould, there is not detachment.The preferred acrylic glue of described adhesive sticker.Above-mentioned coating weight can not increase deadweight on the one hand, provides enough adhesion stresss on the other hand, and the effect of two aspects produces the technique effect reducing and come off simultaneously, and knockout course can also be made more smooth.
In above-mentioned mould, preferably, 180 ° of peel strengths of described adhesive sticker tack coat are 1.5-4.0N/cm, are more preferably 2.0-3.5N/cm, such as 2.5-3.0N/cm.
In above-mentioned mould, preferably, the material of described mould to be selected from art post paperboard, craft paper, kraft, plastics, composite material, material with carbon element, silicon materials any one or multiple.
In the decorative structure of above-mentioned face brick, preferably, described inorganic powder screed is used for levelling described metope, and has firmly adhesion with body of wall, and its thickness is 1-2mm.
In the decorative structure of above-mentioned face brick, preferably, described primer coating provides the brickwork joint color of face brick, and improve the firmness of basic unit's coating further, prevent the accumulation of salt in the surface soil, its thickness is 0.1-0.3mm.
In the decorative structure of above-mentioned face brick, preferably, described facing coating has certain texture skin texture and abundant color, and the weatherability that Long-Time Service possesses, on body of wall, various abundant pattern is now made by using above-mentioned adhesive sticker sheet hollowed mould, present ceramic tile decorative effect true to nature, its thickness is 1-2mm.
In the decorative structure of above-mentioned face brick, particularly, also provide a kind of method of existing wall facing brick processed on building, described method comprises the steps:
Step 1: at described building surface coating inorganic dry powder and mortar layer, for levelling described metope, and have firmly adhesion with body of wall, its thickness is 1-2mm;
Step 2: then apply primer coating, provides the brickwork joint color of face brick, and improve the firmness of basic unit's coating further, prevent the accumulation of salt in the surface soil, its thickness is 0.1-0.3mm;
Step 3: after primer coating is done solid work, primer coating is pasted the sheet hollowed mould tearing outer separate paper off, and the adhesive sticker tack coat on described sheet hollowed mould and described primer coating bond;
Step 4: after having pasted sheet hollowed mould, applies facing coating immediately, and under the state of the non-surface drying of facing coating, sloughs sheet hollowed mould; Described facing coating has certain texture skin texture and abundant color, and the weatherability that Long-Time Service possesses, by using above-mentioned adhesive sticker sheet hollowed mould now to make various abundant pattern on body of wall, present ceramic tile decorative effect true to nature, its thickness is 1-2mm.
In the above-mentioned methods, preferably, described primer coating comprises gel rubber material, filler, pigment, optional additive and optional aggregate, and described gel rubber material is inorganic gel materials, organic gel materials or its combination.
In the above-mentioned methods, preferably, described facing coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.
The composition of primer coating of the present utility model is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.Such as can adopt the conventional formulation of this area.Particularly such as, described primer coating comprises gel rubber material, filler, pigment, optional additive and optional aggregate, and described gel rubber material is inorganic gel materials, organic gel materials or its combination.
Inorganic gel materials of the present utility model is not particularly limited, such as, adopt cement, gypsum, lime, water glass material etc., only otherwise to goal of the invention of the present utility model produces and limits.The consumption of inorganic gel materials is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.
Organic gel materials of the present utility model is not specifically limited, and only otherwise to goal of the invention of the present utility model produces and limits.
Filler of the present utility model is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.Such as, the stone flour, fiber etc. that adopt this area conventional.The consumption of filler is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.
Additive of the present utility model is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.Such as the additive that this areas such as polymer glue powder, pigment, cellulose ether are commonly used particularly.The consumption of additive is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.
Aggregate of the present utility model is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.Coarse aggregate, fines or its combination can be adopted.Particularly such as, the coarse aggregate that this area is conventional comprises quartz, granite, andesite etc.The conventional fines in this area comprises quartz sand, natural and husky etc.When adopting the combination of coarse aggregate and fines, its portfolio ratio is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.
Other material can also be added in primer coating of the present utility model.Such as, filler is added.Particularly as fibre structure shaping in advance, as adopted grid cloth.The fibrous raw material of described grid cloth is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.
Described facing coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.The implication of described " inorganic gel materials ", " organic gel materials ", " filler ", " pigment ", " additive " is identical with the term in primer coating.And the concrete composition of each coating described can be identical or different.
Other material can also be added in described facing coating, such as add the filler producing various surface property and physical and chemical performance, described filler is not specifically limited, described facing coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.Preferred luminescent powder, metallic particles, shell particles etc. particularly.
The method of now wall facing brick processed of the present utility model is applicable to the surface of various building, such as common exterior wall, heat preserving exterior wall, interior wall, smallpox etc.The method of now wall facing brick processed of the present utility model is applicable to various heat preserving exterior wall.The preparation method of described heat preserving exterior wall is unrestricted, can adopt in various manners.Such as, polystyrene foam plate is pasted onto on exterior wall by adhesive material, then smears the primer coating being added with grid cloth therebetween onboard, and described cystosepiment can also be fixed by crab-bolt; Or heat insulation coating (being such as granules of polystyrene) pressure is smeared on exterior wall.
The concrete time of primer coating of the present utility model " doing solid work " is not particularly limited, as long as coating does not have plasticity, surperficial bone dry, such as, after applying coating after 12 hours.Usually, the step that overlays of described wall facing bricks die is carried out after primer coating " is done solid work ", particularly such as, overlays after coating primer coating after 12 hours.
The concrete time of " the non-surface drying " of facing coating of the present utility model is not particularly limited, as long as coating does not have plasticity but the non-bone dry in surface, such as, after applying coating in 3 hours.
" stickup " mode of " pasting the sheet hollowed mould tearing outer separate paper off in primer coating " of the present utility model is not particularly limited, and only otherwise to goal of the invention of the present utility model produces and limits.Mould is pasted onto in primer coating by usual employing spatula, cylinder.
Carry out detailed and concrete introduction below by specific embodiment to the utility model, to make better to understand the utility model, but following embodiment does not limit the utility model scope.
embodiment
adhesive sticker sheet hollowed mould:
Fig. 1 is can the front schematic view of a demoulding wall facing bricks die, and Fig. 2 is can the side schematic view of a demoulding wall facing bricks die.
As shown in Figure 1, a kind of on building surface now the wall facing bricks die of face brick processed there is sheet engraved structure, die ontology 6 has the brick hole 7 of hollow out.The gross thickness of described sheet hollowed mould is the thickness summation of each layer of Fig. 2, about about 0.6mm.
As shown in Figure 2, wherein, described mould from inside to outside comprises adherent layer 1, adhesive sticker tack coat 2, bottom tectorial paper 3, paper body 4, top layer tectorial paper 5.The thickness of bottom tectorial paper 3 is about 0.05mm.Outermost skin layers tectorial paper 5 is the coloured overlay film in front, and to facilitate the front or the back side of distinguishing mould, its material is identical with bottom tectorial paper, and thickness is about about 0.1mm.Described adherent layer 1, adhesive sticker tack coat 2, bottom tectorial paper 3 and top layer tectorial paper 5 can cover on paper body 4 according to the technique of existing tectorial paper.The colloid coating weight of adhesive sticker tack coat 2 is 50-150g/m
2.
the method of existing face brick processed on building surface:
On building surface existing wall facing brick processed method in, comprise the steps:
Step 1: at described building surface (such as metope) coating inorganic dry powder and mortar layer, for levelling described metope, and have firmly adhesion with body of wall, its thickness is 1-2mm;
Step 2: then apply primer coating, provides the brickwork joint color of face brick, and improve the firmness of basic unit's coating further, prevent the accumulation of salt in the surface soil, its thickness is 0.1-0.3mm;
Step 3: after primer coating is done solid work, after such as coating primer coating after 12 hours, primer coating is pasted the sheet hollowed mould tearing outer separate paper off, and the adhesive sticker tack coat on described sheet hollowed mould and described primer coating bond;
Step 4: after having pasted sheet hollowed mould, applies facing coating immediately, and under the state of the non-surface drying of facing coating, such as, after coating facing coating, in 3 hours, sloughs sheet hollowed mould; Described facing coating has certain texture skin texture and abundant color, and the weatherability that Long-Time Service possesses, by using above-mentioned adhesive sticker sheet hollowed mould now to make various abundant pattern on body of wall, present ceramic tile decorative effect true to nature, its thickness is 1-2mm.
Above-mentioned facing coating is the facing coating of the metope face brick existing processed that the utility model provides.
adhesive sticker sheet hollowed mould is metope face brick processed now:
Fig. 3 a demoulding wall facing bricks die can cover front schematic view on building masonry wall.
Fig. 3 b is the side schematic view in primer coating after pasting mould, and in Fig. 3 b, coating inorganic dry powder and mortar layer 9 on body of wall 8, coating rate is about 1.5-3kg/m
2.After inorganic powder screed 9 is done solid work, coating one deck primer coating 10, coating rate is about 1.5-2.5kg/m
2.After primer coating 10 is done solid work, wall facing brick die ontology 6 cylinder is overlayed in primer coating 10.
Then apply facing coating 11 immediately, applied in such as 30 minutes, taken out by die ontology 6, the adhesive sticker of adhesive sticker tack coat 2 is followed bottom overlay film 3 and is sloughed, and obtains the side schematic view sloughing the wall facing brick after mould shown in Fig. 3 c.
Be described in detail specific embodiment of the utility model above, but it is as example, the utility model is not restricted to specific embodiment described above.To those skilled in the art, any equivalent modifications that this practicality is carried out and substituting also all among category of the present utility model.Therefore, not departing from the equalization conversion and amendment done under spirit and scope of the present utility model, all should be encompassed in scope of the present utility model.
Claims (9)
1. the decorative structure of the existing metope face brick processed of an adhesive sticker sheet hollowed mould, described face brick covers on metope, it is characterized in that, described face brick distance metope by near to as far as comprising less: inorganic powder screed, primer coating, facing coating, the pattern of described facing coating is realized by adhesive sticker sheet hollowed mould.
2. decorative structure according to claim 1, it is characterized in that, described adhesive sticker sheet hollowed mould has following structure before construction: on the basal surface and external surface of described mould, be respectively equipped with bottom overlay film and top layer overlay film, bottom overlay film is provided with adhesive sticker tack coat, described adhesive sticker tack coat is provided with one deck separate paper further.
3. decorative structure according to claim 2, is characterized in that, the gross thickness of described sheet hollowed mould is 0.3-2mm.
4. decorative structure according to claim 2, is characterized in that, the coating weight of described adhesive sticker tack coat is 50-150g/m
2.
5. decorative structure according to claim 2, is characterized in that, 180 ° of peel strengths of described adhesive sticker tack coat are 1.5-4.0N/cm.
6. decorative structure according to claim 2, is characterized in that, the material of described mould to be selected from art post paperboard, craft paper, kraft, plastics, composite material, material with carbon element, silicon materials any one or multiple.
7. decorative structure according to claim 1, is characterized in that, described inorganic powder screed is used for levelling described metope, and its thickness is 1-2mm.
8. decorative structure according to claim 1, is characterized in that, described primer coating provides the brickwork joint color of face brick, and thickness is 0.1-0.3mm.
9. decorative structure according to claim 1, is characterized in that, the thickness of described facing coating is 1-2mm.