CN104652733A - Non-setting adhesive mold and method for fabricating facing bricks on site using mold - Google Patents
Non-setting adhesive mold and method for fabricating facing bricks on site using mold Download PDFInfo
- Publication number
- CN104652733A CN104652733A CN201410854678.6A CN201410854678A CN104652733A CN 104652733 A CN104652733 A CN 104652733A CN 201410854678 A CN201410854678 A CN 201410854678A CN 104652733 A CN104652733 A CN 104652733A
- Authority
- CN
- China
- Prior art keywords
- mould
- coating
- mold
- adhesive sticker
- primer coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a facing brick mold for fabricating facing bricks on the surface of a building on site. The mold is a sheet-shaped hollow mold, wherein a bottom layer laminating film and a surface layer laminating film are respectively arranged on the bottom surface and external surface of the mold, a non-setting adhesive bonding layer is arranged on the bottom layer laminating film, and a layer of anti-sticking paper is further arranged on the non-setting adhesive bonding layer. The invention further provides a method for fabricating wall facing bricks on site by using the mold. The wall facing brick mold and the method for fabricating the wall facing bricks on site by using the mold, provided by the invention, have the advantages that the facing bricks can be fabricated on the building on site, are uniform in color lump and regular in molded face, can be demolded in one time and cannot generate fins.
Description
Technical field
The present invention relates to building materials technical field of construction, particularly relate to a kind of adhesive sticker mould and use the method for the existing face brick processed of this mould.
Background technology
Special for walltile binding material and body of wall normally carry out boning by existing building wall face brick decoration, jointing.There is following shortcoming in this traditional patch block technique: (1) walltile finish coat is from great (about 20kg/m
2above); (2) work efficiency such as (stickup, jointing operation) of constructing is low, and (work efficiency of conventional skilled worker is 7-8m
2/ sky/people); (3) because of walltile and the elastic modulus difference of binding material and the controllability difference of binding material and construction and the potential safety hazard causing walltile to come off, peel off; (4) the attractive in appearance of walltile decorative cover is affected because of the accumulation of salt in the surface soil of binding material (being generally cement mortar class); (5) because pointing and construction reason easily cause decorative layer to seep water; (6) figure because of walltile goods is abundant not, and the decoration of complex figure cannot realize; (7) consume a large amount of walltiles to energy-saving and environmental protection, economize on resources unfavorable.
In order to overcome the problems referred to above, those skilled in the art take to improve the adhesive property of binding material and the anti-accumulation of salt in the surface soil of pointing and water resistance and realize, and adopt walltile light as far as possible (suggestion controls at 20kg/m simultaneously
2below).The weak point of these measures is, more specifically requirement is proposed to the performance of walltile and binding material, pointing, and the deadweight of the difficulty to control of work progress and overall decorative layer cannot be reduced greatly, there is the long-term safety hidden danger of quality of engineering equally.
In order to overcome the problems referred to above further, those skilled in the art have developed following methods.
Chinese patent CN2849002Y, the back of its brick has groove, to increase the firm pasting of walltile.But the method still has the danger come off, and add an operation, improve cost.
Chinese patent CN1303456A (PCT/FR99101009), its method in primary coat, carries out press back pattern with a concavo-convex pattern template, the color treatments of its forming surface has two kinds of methods, one is painted by pit with filling paint after press back, and another kind is coated in by tintage paint in concavo-convex template to carry out transfer impression.These two kinds of methods all cannot obtain uniform color lump effect.Be not the uneven color rule of recess, the color at convex exactly place produces convex place and both sides uneven color rule owing to being squeezed uneven.In addition, due to the demoulding for convenience, mould is provided with about draft angle of 5 °, and under the state faced, side such as the uneven color rule of figure will have a strong impact on the regular aesthetic property of color lump.
Chinese patent CN1060134A, its method is being carved with the openworking template of decorative pattern by the metope after Lacquer finish, carrying out scraping coating layer, be similar to silk-screen printing technique.Because the method is that metope after Lacquer finish carries out, and revenue stamp process must carry out after the drying again, and the smooth process of metope simultaneously necessarily exists flatness error.By quarter dapple openworking template on the metope having certain flatness error by flat (now metope is dry), the gap of template and metope can be produced.When scraping coating layer, easily producing spillage and affecting decorative effect.In addition, template needs external force to fix.And when row graph stamp, error is certainly existed to the splicing between template and the figure that completes, operation easier is increased.
Chinese patent CN101122165A, its method is before primary coat initial set, is overlayed by certain thickness sheet hollowed mould and is fixed in primary coat, then be coated with in surperficial coated side, obtained figure after the demoulding.There is following problem in the method, as the state adopting primary coat wet, then after the demoulding, the forming surface of primary coat has plucking phenomenon, has a strong impact on attractive in appearance in knockout course; As adopted primary coat dry state, face is coated with dry state bottom knockout, then due to demoulding shearing and friction effect, can produce forming surface and to rive finning; As adopted primary coat dry state, face is coated in wet state, and now face is coated with and does not also form structural strength, and the mould in embedding primary coat is deviate from, and the frictional force between face painting and mould makes primary coat produce friction overlap and is coated with disengaging with face, and affects forming surface.Meanwhile, due to face be coated with employing have aggregate coating, its construction can only be trowelling or spraying, twice working face connect stubble and facing skin texture difference will produce aberration.Therefore the method be difficult to obtain color evenly, the decorative effect of graphics standardization.
In sum, this area lacks that one can now face brick processed and face brick color lump be even on building, the method for the wall facing bricks die that forming surface is regular and now face brick processed.
Summary of the invention
The present invention solves the aforementioned problems in the prior proposition.
The invention provides a kind of can on building surface now face brick processed and face brick color lump evenly, can the regular face brick adhesive sticker mould of a demoulding, forming surface.
Present invention also offers a kind of can on building surface now face brick processed and face brick color lump evenly, can the method existing processed of the regular wall facing brick of a demoulding, forming surface.
For achieving the above object, the present invention is by the following technical solutions:
First aspect of the present invention is to provide a kind of wall facing bricks die for existing face brick processed on building surface, described mould is sheet hollowed mould, the basal surface and external surface of described mould are respectively equipped with bottom overlay film and top layer overlay film, bottom overlay film is provided with adhesive sticker tack coat, described adhesive sticker tack coat is provided with one deck separate paper further.
In above-mentioned mould, preferably, the gross thickness of described sheet hollowed mould is 0.3-2mm.
In above-mentioned mould, preferably, the coating weight of described adhesive sticker tack coat is 50-150g/m
2.
In above-mentioned mould, preferably, 180 ° of peel strengths of described adhesive sticker tack coat are 1.5-4.0N/cm, are more preferably 2.0-3.5N/cm, such as 2.5-3.0N/cm.
In above-mentioned mould, preferably, the material of described mould to be selected from art post paperboard, craft paper, kraft, plastics, composite material, material with carbon element, silicon materials any one or multiple.
Second aspect of the present invention is to provide a kind of method of existing wall facing brick processed on building, and described method comprises the steps:
Step 1: in described building surface coating primer coating;
Step 2: after primer coating is done solid work, primer coating is pasted the sheet hollowed mould tearing outer separate paper off, and the adhesive sticker tack coat on described sheet hollowed mould and described primer coating bond;
Step 3: after having pasted sheet hollowed mould, applies surface layer coating immediately, and under the state of the non-surface drying of surface layer coating, sloughs sheet hollowed mould.
In the above-mentioned methods, preferably, described primer coating comprises gel rubber material, filler, pigment, optional additive and optional aggregate, and described gel rubber material is inorganic gel materials, organic gel materials or its combination.
In the above-mentioned methods, preferably, described surface layer coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.
The present invention adopts technique scheme, compared with prior art, has following technique effect:
A kind of wall facing bricks die provided by the invention and use this mould now wall facing brick processed method can on building now face brick processed and face brick color lump evenly, can a demoulding, forming surface regular, can not overlap be produced.
Accompanying drawing explanation
Fig. 1 is the front schematic view of a detailed description of the invention of mould of the present invention;
Fig. 2 is the side schematic view of a detailed description of the invention of mould of the present invention;
In figure, 1-adherent layer, 2-adhesive sticker tack coat, 3-bottom tectorial paper, 4-paper body, 5-top layer tectorial paper, 6-die ontology, 7-brick hole.
Detailed description of the invention
As used herein, described " sheet hollowed mould ", except as otherwise noted, refer to the sheet mould that front has pierced pattern (being such as the hole of hollow out), described pierced pattern can design arbitrarily, be not particularly limited, can determine according to the shape forming wall facing brick, such as: brick shape, cobble shaped, geometric figure, flowers figure etc.Described " front " refers to the elevation of metope.
As used herein, described " building surface ", except as otherwise noted, refers to the metope of building, end face etc., such as exterior wall, interior wall, smallpox.Described metope can be insulated wall, also can be common metope.
As used herein, described " primer coating ", except as otherwise noted, refers to one or more layers coating (described coating such as mortar) directly contacted with the surface of building.In one or more layers coating described, can be one or many coating each time and be formed.
As used herein, described " surface layer coating ", except as otherwise noted, refer to sheet hollowed mould external surface, be exposed to one or more layers coating with sheet hollowed mould pattern of air.In one or more layers coating described, can be one or many coating each time and be formed.
Can have " middle coat " between described " primer coating " and " surface layer coating ", described " middle coat ", except as otherwise noted, refer to together with can being embedded in sheet hollowed mould of the present invention, also can not one or more layers coating together with sheet hollowed mould is embedded in.In one or more layers coating described, can be one or many coating each time and be formed.
The invention provides a kind of can on building surface now face brick processed and face brick color lump evenly, can the regular wall facing bricks die of a demoulding, forming surface and use the method for the existing wall facing brick processed of this mould.
Particularly, a kind of wall facing bricks die for existing face brick processed on building surface, described mould is sheet hollowed mould, the basal surface and external surface of described mould are respectively equipped with bottom overlay film and top layer overlay film, bottom overlay film is provided with adhesive sticker tack coat, described adhesive sticker tack coat is provided with one deck separate paper further.
The basal surface of described mould and external surface are respectively equipped with bottom overlay film and top layer overlay film, and preferably, described bottom overlay film has smooth surface, makes described bottom overlay film be easily fixed on the surface of described building by adhesive sticker tack coat.Its advantage is: after the primer coating of building is done solid work, described mould is overlayed in described primer coating, then apply surface layer coating immediately, under the state of the non-surface drying of surface layer coating, the top layer overlay film with smooth surface makes described mould can the easily demoulding, and can not produce overlap; Meanwhile, it is more smooth and easy when the smooth surface in front can make coating surface layer coating.The adhesion of described top layer overlay film is not specifically limited, and only otherwise to goal of the invention of the present invention produces and limits.
In above-mentioned mould, preferably, the gross thickness of described sheet hollowed mould is 0.3-2mm, such as 1mm, 1.5mm.
In above-mentioned mould, preferably, the coating weight of described adhesive sticker tack coat is 50-150g/m
2, such as 100g/m
2, 120g/m
2.Between described adhesive sticker tack coat and the bottom overlay film of described mould, there is not detachment.The preferred acrylic glue of described adhesive sticker.Above-mentioned coating weight can not increase deadweight on the one hand, provides enough adhesion stresss on the other hand, and the effect of two aspects produces the technique effect reducing and come off simultaneously, and knockout course can also be made more smooth.
In above-mentioned mould, preferably, 180 ° of peel strengths of described adhesive sticker tack coat are 1.5-4.0N/cm, are more preferably 2.0-3.5N/cm, such as 2.5-3.0N/cm.
In above-mentioned mould, preferably, the material of described mould to be selected from art post paperboard, craft paper, kraft, plastics, composite material, material with carbon element, silicon materials any one or multiple.
Particularly, also provide a kind of method of existing wall facing brick processed on building, described method comprises the steps:
Step 1: in described building surface coating primer coating;
Step 2: after primer coating is done solid work, primer coating is pasted the sheet hollowed mould tearing outer separate paper off, and the adhesive sticker tack coat on described sheet hollowed mould and described primer coating bond;
Step 3: after having pasted sheet hollowed mould, applies surface layer coating immediately, and under the state of the non-surface drying of surface layer coating, sloughs sheet hollowed mould.
In the above-mentioned methods, preferably, described primer coating comprises gel rubber material, filler, pigment, optional additive and optional aggregate, and described gel rubber material is inorganic gel materials, organic gel materials or its combination.
In the above-mentioned methods, preferably, described surface layer coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.
Can have " middle coat " between described " primer coating " and " surface layer coating ".The composition of middle coat of the present invention and primer coating is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.Such as can adopt the conventional formulation of this area.Particularly such as, described primer coating/middle coat comprises gel rubber material, filler, pigment, optional additive and optional aggregate, and described gel rubber material is inorganic gel materials, organic gel materials or its combination.
Inorganic gel materials of the present invention is not particularly limited, such as, adopt cement, gypsum, lime, water glass material etc., only otherwise to goal of the invention of the present invention produces and limits.The consumption of inorganic gel materials is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.
Organic gel materials of the present invention is not specifically limited, and only otherwise to goal of the invention of the present invention produces and limits.
Filler of the present invention is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.Such as, the stone flour, fiber etc. that adopt this area conventional.The consumption of filler is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.
Additive of the present invention is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.Such as the additive that this areas such as polymer glue powder, pigment, cellulose ether are commonly used particularly.The consumption of additive is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.
Aggregate of the present invention is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.Coarse aggregate, fines or its combination can be adopted.Particularly such as, the coarse aggregate that this area is conventional comprises quartz, granite, andesite etc.The conventional fines in this area comprises quartz sand, natural and husky etc.When adopting the combination of coarse aggregate and fines, its portfolio ratio is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.
Other material can also be added in primer coating of the present invention or middle coat.Such as, filler is added.Particularly as fibre structure shaping in advance, as adopted grid cloth.The fibrous raw material of described grid cloth is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.
Described surface layer coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.The implication of described " inorganic gel materials ", " organic gel materials ", " filler ", " pigment ", " additive " is identical with the term in primer coating.And the concrete composition of each coating described can be identical or different.
Other material can also be added in described surface layer coating, such as add the filler producing various surface property and physical and chemical performance, described filler is not specifically limited, described surface layer coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate, described gel rubber material is inorganic gel materials, organic gel materials or its combination.Preferred luminescent powder, metallic particles, shell particles etc. particularly.
The method of now wall facing brick processed of the present invention is applicable to the surface of various building, such as common exterior wall, heat preserving exterior wall, interior wall, smallpox etc.The method of now wall facing brick processed of the present invention is applicable to various heat preserving exterior wall.The preparation method of described heat preserving exterior wall is unrestricted, can adopt in various manners.Such as, polystyrene foam plate is pasted onto on exterior wall by adhesive material, then smears the primer coating being added with grid cloth therebetween onboard, and described cystosepiment can also be fixed by crab-bolt; Or heat insulation coating (being such as granules of polystyrene) pressure is smeared on exterior wall.
The concrete time of primer coating of the present invention " doing solid work " is not particularly limited, as long as coating does not have plasticity, surperficial bone dry, such as, after applying coating after 12 hours.Usually, the step that overlays of described wall facing bricks die is carried out after primer coating " is done solid work ", particularly such as, overlays after coating primer coating after 12 hours.
The concrete time of " the non-surface drying " of surface layer coating of the present invention is not particularly limited, as long as coating does not have plasticity but the non-bone dry in surface, such as, after applying coating in 3 hours.
" stickup " mode of " pasting the sheet hollowed mould tearing outer separate paper off in primer coating " of the present invention is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.Mould is pasted onto in primer coating by usual employing spatula, cylinder.
Carry out detailed and concrete introduction below by specific embodiment to the present invention, to make better to understand the present invention, but following embodiment does not limit the scope of the invention.
embodiment
Fig. 1 is can the front schematic view of a demoulding wall facing bricks die, and Fig. 2 is can the side schematic view of a demoulding wall facing bricks die.
As shown in Figure 1, a kind of on building surface now the wall facing bricks die of face brick processed there is sheet engraved structure, die ontology 6 has the brick hole 7 of hollow out.The gross thickness of described sheet hollowed mould is the thickness summation of each layer of Fig. 2, about about 0.6mm.
As shown in Figure 2, wherein, described mould from inside to outside comprises adherent layer 1, adhesive sticker tack coat 2, bottom tectorial paper 3, paper body 4, top layer tectorial paper 5.The thickness of bottom tectorial paper 3 is about 0.05mm.Outermost skin layers tectorial paper 5 is the coloured overlay film in front, and to facilitate the front or the back side of distinguishing mould, its material is identical with bottom tectorial paper, and thickness is about about 0.1mm.Described adherent layer 1, adhesive sticker tack coat 2, bottom tectorial paper 3 and top layer tectorial paper 5 can cover on paper body 4 according to the technique of existing tectorial paper.The colloid coating weight of adhesive sticker tack coat 2 is 50-150g/m
2.
On building surface existing wall facing brick processed method in, comprise the steps:
1, first primer coating is applied at described building surface (such as metope);
2, after primer coating is done solid work, such as, primer coating is applied after 12 hours, first the adherent layer 1 of sheet hollowed mould is torn, then sheet hollowed mould is overlayed in primer coating, by adhesive sticker tack coat 2 and the bonding of primer coating, sheet hollowed mould is fixed on metope;
3, construct after complete metope, apply surface layer coating immediately, and under the state of the non-surface drying of surface layer coating, such as apply in surface layer coating 3 hours, slough sheet hollowed mould, the pattern of hollow out shape is fixed on metope.
In said method, the mode that overlays of adhesive sticker mould is not particularly limited, and only otherwise to object of the present invention produces and limits.Mould overlays in primer coating by usual employing spatula, cylinder.
In said method, the coating method of each coating is not particularly limited, and only otherwise to goal of the invention of the present invention produces and limits.Particularly, as adopted spraying, blade coating, roll coating model etc.Preferably, primer coating, middle coat adopt spraying, blade coating mode, and surface layer coating adopts spraying, roller coat, brushing mode.
Described primer coating and/or surface layer coating can by primary coating or repeatedly coating obtain.Preferably, repeatedly coating is adopted to obtain described primer coating and/or surface layer coating.Described repeatedly coating comprises more than twice or twice coating.Applicant finds, by repeatedly applying the aberration phenomenon can eliminating finish coat.
Described now face brick processed can also apply one or more layers external coating.Described external coating kind and the number of plies are not particularly limited, and only otherwise to goal of the invention of the present invention produce and limit, can with described primer coating and/or surface layer coating identical or different.Particularly, be such as transparent coating or opaque coating.
The mode of described now face brick processed can also comprise other operation, limits as long as these operations do not produce goal of the invention of the present invention.Such as before coating primer coating, first on metope, carry out blade coating; And for example on middle coat and/or surface layer coating, carry out facing work, form the texture finishes moulding such as light face, hair side or half light hair particularly.
By the present invention's above-mentioned wall facing bricks die and use this mould now wall facing brick processed method can on building now face brick processed and face brick color lump evenly, can a demoulding, forming surface regular, can not overlap be produced.
Be described in detail specific embodiments of the invention above, but it is just as example, the present invention is not restricted to specific embodiment described above.To those skilled in the art, any equivalent modifications that the present invention is carried out and substituting also all among category of the present invention.Therefore, equalization conversion done without departing from the spirit and scope of the invention and amendment, all should contain within the scope of the invention.
Claims (10)
1. the wall facing bricks die for existing face brick processed on building surface, it is characterized in that, described mould is sheet hollowed mould, the basal surface and external surface of described mould are respectively equipped with bottom overlay film and top layer overlay film, bottom overlay film is provided with adhesive sticker tack coat, described adhesive sticker tack coat is provided with one deck separate paper further.
2. mould according to claim 1, is characterized in that, the gross thickness of described sheet hollowed mould is 0.3-2mm.
3. mould according to claim 1, is characterized in that, the coating weight of described adhesive sticker tack coat is 50-150g/m
2.
4. mould according to claim 1, is characterized in that, 180 ° of peel strengths of described adhesive sticker tack coat are 1.5-4.0N/cm.
5. mould according to claim 1, is characterized in that, the material of described mould to be selected from art post paperboard, craft paper, kraft, plastics, composite material, material with carbon element, silicon materials any one or multiple.
6. the method for existing wall facing brick processed on building, it is characterized in that, described method comprises the steps:
Step 1: in described building surface coating primer coating;
Step 2: after primer coating is done solid work, primer coating is pasted the sheet hollowed mould tearing outer separate paper off, and the adhesive sticker tack coat on described sheet hollowed mould and described primer coating bond;
Step 3: after having pasted sheet hollowed mould, applies surface layer coating immediately, and under the state of the non-surface drying of surface layer coating, sloughs sheet hollowed mould.
7. method according to claim 6, is characterized in that, described primer coating comprises gel rubber material, filler, pigment, optional additive and optional aggregate.
8. method according to claim 7, is characterized in that, described gel rubber material is inorganic gel materials, organic gel materials or its combination.
9. method according to claim 6, is characterized in that, described surface layer coating comprises gel rubber material, filler, pigment, optional additive and not containing aggregate.
10. method according to claim 9, is characterized in that, described gel rubber material is inorganic gel materials, organic gel materials or its combination.