CN103253896B - Flexible face brick - Google Patents
Flexible face brick Download PDFInfo
- Publication number
- CN103253896B CN103253896B CN201310143356.6A CN201310143356A CN103253896B CN 103253896 B CN103253896 B CN 103253896B CN 201310143356 A CN201310143356 A CN 201310143356A CN 103253896 B CN103253896 B CN 103253896B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- powder
- slurry
- quartz sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a flexible face brick. The flexible face brick is prepared from the following materials in parts by weight: 35-45 parts of cement, 5-10 parts of fly ash, 20-30 parts of quartz sand with a fineness of about 60 meshes, 5-15 parts of quartz sand with a fineness of about 100 meshes, 1-3 parts of lignocelluloses, 1-5 parts of silica powder, 3-8 parts of talcum powder, 1-5 parts of calcium oxide, 1-3 parts of sodium silicate, 0.5-1 part of antalkaline, 2-3 parts of acrylic rubber powder and 2-5 parts of an iron oxide pigment. The flexible face brick is prepared in the following steps of: mixing the materials in a formula; adding 28 parts of water, usually deionized water to 100 parts of materials; adding powder into the water; pulping a mixture into slurry with a homogenizer; uniformly coating 2/3 slurry to a die according to a proportion of about 3kg of slurry per square meter; paving at least one layer of 4# alkali-proof fiberglass gridding cloth; then uniformly coating the remaining 1/3 slurry; and finally removing scratches with a blacking brush.
Description
Technical field
The present invention relates generally to that a kind of composite architectural materials, particularly one utilize matrix material to make flexible clay facing tile.
Background technology
In known flexible clay facing tile formula, caking agent, taking polymkeric substance as main, inside adds natural stone-powder, adopts special process to process.But along with oil price is constantly soaring in the world, make this based article high expensive, and expense is uneconomical, and pure resin, and resistance to phenology poor performance is easily aging, so seek better more economical facing tile goods, is to pursue in building trade always.
Summary of the invention
The object of the present invention is to provide one can overcome known technology shortcoming, cost of manufacture economy, the flexible clay facing tile of superior performance.
For achieving the above object, the solution of the present invention is: the material by following weight parts proportioning forms, cement 35-45, flyash 5-10, fineness is 60 order left and right quartz sand 20-30, fineness is 100 order left and right quartz sand 5-15, lignocellulose 1-3, silicon powder 1-5, talcum powder 3-8, calcium oxide 1-5, water glass 1-3, press down alkaline agent (ERA-100) 0.5-1, vinylformic acid rubber powder 2-3, iron oxide pigment 2-5.
Above-mentioned formula is made a method for flexible clay facing tile, is undertaken by following step:
1, soft mode is cleaned up, be laid in platform case, water-based or oily exterior wall paint are evenly sprayed on mould as finishing material with airless sprayer, by the infrared surface drying that is dried to, coat interfacial agents (modifying cinepazid emulsion);
2, by adding water 28 by every 100 weight parts after the material mixing in above-mentioned formula, conventionally use deionized water, powder is dropped in water, break into slurry with homogenizer, by approximately three kilograms of every square of materials, first by uniform 2/3rds slurry blade coating on mould, spread at least one deck 4
#alkali resistant glass fibre open weave cloth, then by the uniform blade coating of 1/3rd slurries of remainder, finally remove scratch by row brush;
3, the slab of making is moved to natural curing or the extremely energy demoulding of the maintenance of heating on frame.
4,, under 25 DEG C of left and right room temperature conditions, slab generally only needs maintenance can cut on request vanning in 5-7 days.
Adopt such scheme, described flexible clay facing tile cement, comprise that No. 42.5 ash concretes or white cement are as gelifying agent, with flyash, quartz sand, silicon powder, talcum powder, calcium oxide, water glass is made reinforcing filler, lignocellulose makes to strengthen skeleton, utilize fiber to increase product strength and toughness, adding vinylformic acid rubber powder is to add resin-oatmeal, the heat of utilizing hydrated reaction of cement to produce makes vinylformic acid rubber powder expanded by heating, fill up the space of formation, make goods more real close, gain in strength and toughness, thereby make goods formula adopt gum blend gel material, composite strongthener, composite toughening material forms the facing tile of composite shape matl, finish coatings, make goods there is beautiful gloss, increase item property, but whole making processes is due to the economy of drawing materials, making processes is also uncomplicated, thereby realize object of the present invention.
Below in conjunction with specific embodiment, scheme is described in more detail.
Embodiment
First make soft mode, the present embodiment utilizes silicon rubber to make mold glue, is certainly used as the also available rubber of mold glue etc., first designs the picture on surface of this facing tile, picture on surface is three-dimensional also will carving out, then make former with silicon rubber, same former will be made multiple, because silicon rubber is pasty state, add linking agent, after solidifying agent, congeal into and be with elastic solid in very short time, the mould making with silicon rubber can clone the goods of same shape, and its clone's precision is very high.
Get white cement 40kg, flyash 8 kg, 60 order quartz sand 25 kg, 100 order quartz sand 10 kg, lignocellulose 1 kg tears, silicon powder is also named perlite 3 kg, talcum powder 5 kg, calcium oxide 2 kg, water glass powder 1 kg, press down alkaline agent 0.5 kg, vinylformic acid rubber powder 2.5 kg, add iron oxide pigment 2.5 kg to mix, 28.28 kg water are contained in a clean container, again mixed powder is poured into, and stir pulping with homogenizer, die surface is sprayed to colourless varnish, dry with infrared oven, coat again can with paint and the affine interfacial agents of cement, by approximately three kilograms of slurries of every square of materials, first by uniform 2/3rds slurry blade coating on mould, first cut out No. 4 alkali resistant glass fibre open weave cloths for subsequent use in flakes, need to spread one deck or two-layer depending on product strength, and with brush stamp glass-fiber-fabric surface, make the slurry glass-fiber-fabric that drenches, again by the uniform blade coating of 1/3rd slurries of remainder on glass-fiber-fabric surface, finally scrape overleaf lines.The slab of handling well is moved to natural curing on frame, need heat winter and accelerate cement setting speed.
Whole making processes can form streamline, raises the efficiency.
The flexible veneers that adopts this programme to make, light (2.5-3.5 ㎏/㎡), thin (2-3 ㎜), firm pliable and tough, outward appearance is beautiful, long service life, a blank of having supplied existing finishing material, is specially adapted to external thermal insulation system and reconstruction of the old city town renovation.Its cost and general cement products are similar, economical and practical, are that architectural decoration is happy to adopt.
Claims (2)
1. a flexible clay facing tile, is characterized in that: the material by following weight parts proportioning forms, cement 35-45, flyash 5-10, fineness is 60 order left and right quartz sand 20-30, fineness is 100 order left and right quartz sand 5-15, lignocellulose 1-3, silicon powder 1-5, talcum powder 3-8, calcium oxide 1-5, water glass 1-3, press down alkaline agent 0.5-1, vinylformic acid rubber powder 2-3, iron oxide pigment 2-5.
2. flexible clay facing tile according to claim 1, is characterized in that: undertaken by following step
(1) soft mode is cleaned up, be laid in platform case, water-based or oily exterior wall paint are evenly sprayed on mould as finishing material with airless sprayer, by the infrared surface drying that is dried to, coat interfacial agents;
(2) will after the material mixing of claim 1, add water 28 by every 100 weight parts, water is deionized water, and powder is dropped in water, break into slurry with homogenizer, by approximately three kilograms of every square of materials, first by uniform 2/3rds slurry blade coating on mould, spread at least one deck 4
#alkali resistant glass fibre open weave cloth, then by the uniform blade coating of 1/3rd slurries of remainder, finally remove scratch by row brush;
(3) slab of making is moved to natural curing or the extremely energy demoulding of the maintenance of heating on frame.