CN112358786A - 一种防渗色水性封闭底漆及其制备方法 - Google Patents
一种防渗色水性封闭底漆及其制备方法 Download PDFInfo
- Publication number
- CN112358786A CN112358786A CN202011374459.XA CN202011374459A CN112358786A CN 112358786 A CN112358786 A CN 112358786A CN 202011374459 A CN202011374459 A CN 202011374459A CN 112358786 A CN112358786 A CN 112358786A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- aqueous
- dispersion
- primer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种防渗色水性封闭底漆及其制备方法，该底漆包括如下组分：水性自交联丙烯酸树脂：650～750份，水性聚氨酯丙烯酸分散体：50～150份，杀菌剂：1～4份，单宁酸抑制剂：30～50份，消泡剂：5～10份，润湿分散剂：4～10份，成膜助剂：50～70份，增稠剂：3～10份，水：70～200份；所述水性自交联丙烯酸树脂是指固体含量为40%～50%的水性自交联丙烯酸分散乳液。本发明的产品具有极好的附着力，可与各种底漆配套使用；快干、高透明、打磨性好，不粘砂纸、施工方便；超低VOC含量，无游离TDI，对环境和人畜危害极小。
Description
技术领域
本发明属于水性木器涂料领域，具体涉及一种防渗色水性封闭底漆及其制备方法。
技术背景
水性木器涂料的环保性和健康性已经逐渐被人们所重视，其市场占有率也相对前几年有了几何倍数的增长。而其中水性白色漆以及以白色为基础的浅色涂装效果得到了广大消费者的认可，已成为装饰涂装行业的主流行风格，但木质基材很容易诱发水性白色木器涂料黄变，例如木材中含有的单宁酸、色素、油脂及烟碱渍、表面残留的漂白剂等。丹宁酸(tanning)又称植物鞣质，属多元酚类的混合物，是在像雪松和红木这样的木质中自然产生的，可以延长木质寿命的物质。但是很多时候，这些丹宁酸会迁移到木质表面，将木质表面变为茶锈色。当木材在潮湿条件下与铁接触，其中的丹宁酸与铁会发生化学反应(络合反应)形成丹宁酸铁，丹宁酸铁呈黑色，因此使得木材的颜色变黑。木材与铜或铜合金接触，由于木材中的丹宁酸与铜发生化学反应，生成丹宁酸铜，会使木材变成浅红色。虽然丹宁酸是优质木材中所固有的成分，但它所引起的白色涂料变色往往会令消费者对这类木质产品有抵制感，从而影响了白色涂料的发展，所以为了解决该问题，水性封闭底漆应运而生。
现有水性封闭底漆大多数选用水性阳离子体系，但是阳离子类型产品也只能在酸性较弱的基材上起到很好的作用。而且，工厂常规使用的底漆为阴离子型产品，阳离子类型封闭底漆对现场施工便利性这一块也有不少影响。
发明内容
本发明的目的是提供一种防渗色水性封闭底漆及其制备方法，以解决现有防渗色封闭体系不能较好的完成封闭作用。
本发明的技术方案如下：
本发明的一种防渗色水性封闭底漆，其特征在于，包括如下组分：水性自交联丙烯酸树脂：650～750份，水性聚氨酯丙烯酸分散体：50～150份，杀菌剂：1～4份，单宁酸抑制剂：30～50份，消泡剂：5～10份，润湿分散剂：4～10份，成膜助剂：50～70份，增稠剂：3～10份，水：70～200份；
所述水性自交联丙烯酸树脂是指固体含量为40％～50％的水性自交联丙烯酸分散乳液，例如：BASF公司的Joncryl 8284牌号的产品，固体含量为45％；
所述水性聚氨酯丙烯酸分散体是指固体含量为35％～45％水性脂肪族聚氨酯丙烯酸共聚物分散液，例如：DSM帝斯曼公司的NeoPac E-129牌号的产品；DSM公司的NeoPacE-129，固体含量为40％；
所述杀菌剂选自异噻唑啉酮类杀菌剂或苯并异噻唑啉酮的水性混合物中的一种或两种；例如：科莱恩公司的Nipacide HF-I(多种异噻唑啉酮和甲醛的混合物)、PreventolBIT 20N(苯并异噻唑啉酮的水性混合物)；
所述单宁酸抑制剂为氨盐基稳定的锆盐，例如：HALOX公司的xtain L-44、L-66和L-77等产品；
所述消泡剂为有机硅氧烷类和聚醚改性硅氧烷类中的一种或两种，例如：德国BYK公司的BYK-024、BYK1770、BYK-028(在聚乙二醇中的憎水固体和破泡聚硅氧烷的混合物，属于有机硅氧烷类)，EVONIK公司的TEGO foamex 810(聚硅氧烷-聚醚共聚物，属于聚醚改性硅类)；
所述润湿分散剂为聚二甲基硅氧烷和/或聚硅氧烷-聚醚共聚物，例如：德国BYK公司的BYK345、BYK346(属聚醚改性聚二甲基硅氧烷类)，德国EVONIK公司的TEGO Wet 270(属聚醚硅氧烷共聚物类)；
所述成膜助剂选自二丙二醇丁醚(DPnB)、二乙二醇丁醚(DB)或乙二醇单丁醚(BCS)的一种或两种；例如：陶氏的DALPADTMD(二丙二醇丁醚)或伊斯曼化学的二乙二醇丁醚(DB)；
所述增稠剂选自丙烯酸类增稠剂、聚氨酯类增稠剂或纤维素醚类增稠剂的一种或两种；例如：法国COATEX的Thixol 53L(丙烯酸共聚物溶液)和Coapur 830w(非离子型水性聚氨酯)，德国明凌的PUR62和PU40(聚氨酯类)等。
本发明所述的一种防渗色水性封闭底漆的制备方法，其特征在于，包括如下步骤：
(1)将所述水性自交联丙烯酸树脂和所述水性聚氨酯丙烯酸分散体置于分散缸中；(2)在转速为1～800转/min的搅拌状态下，将所述杀菌剂、单宁酸抑制剂、消泡剂和润湿分散剂加入分散缸中，再以1000～1500转/min的转速下分散10～30min；(3)在转速为800～1000转/min的搅拌状态下，依次将所述成膜助剂、增稠剂和剩余的去离子水加入到分散缸中，搅拌均匀并调整粘度到18～22秒/25℃，即得本发明的防渗色水性封闭底漆。
本发明的一种防渗色水性封闭底漆，固体含量为30％～36％，可直接用于涂装施工，施工方式包括刷涂、浸涂以及喷涂；涂装施工时，可根据具体情况加入适量的水调节粘度。
本发明的防渗色水性封闭底漆，采用超细粒径的水性自交联丙烯酸乳液为主体成膜物质，搭配水性聚氨酯丙烯酸分散体，并辅以单宁酸抑制剂，具有超强的封闭木质素和单宁酸的能力；极好的附着力，可与各种底漆配套使用；快干、高透明、打磨性好，打磨时间仅约40分钟，不粘砂纸、施工方便；超低VOC含量，无游离TDI，对环境和人畜危害极小。本发明的方法简单，容易操作，对操作人员无害，产品在使用时只需要添加少量水或不加水调稀后喷涂施工即可。
具体施工方式：
下面通过实施例的方式进一步说明本发明，应注意本发明的实施例只是对本发明的内容予以解释说明，并不构成对本发明技术方案的限制。
实施例1
一种防渗色水性封闭底漆，其原料组分列于表1。
表1实施例1的原料和重量份
一种防渗色水性封闭底漆的制备方法，包括如下步骤：
(1)将700kg Joncryl 8284和100kg NeoPac E-129置于分散缸中，开始搅拌；(2)在转速为500转/min的搅拌状态下，将3kg Nipacide HF-I杀菌剂、30kg的XTAIN L-66单宁酸抑制剂、4kg的BYK024和2kg的BYK1770消泡剂以及6kg的BYK346润湿分散剂加入分散缸中，再以1300转/min的转速下分散15min；(3)在转速为800转/min的搅拌状态下，依次将40kg DPnB和20kgDB成膜助剂、3kg的PUR62和2kg Thixol 53L增稠剂和90kg去离子水加入到分散缸中，搅拌均匀并调整粘度到20秒/25℃，过滤包装即得本发明的防渗色水性封闭底漆。
实施例2
一种防渗色水性封闭底漆，其原料组分列于表2。
表2实施例2的原料和重量份
一种防渗色水性封闭底漆的制备方法，包括如下步骤：
(1)将750kg的Joncryl 8284和50kg的NeoPac E-129置于分散缸中，开始搅拌；(2)在转速为800转/min的搅拌状态下，将3kg的Nipacide HF-I杀菌剂、40kg的XTAIN L-66单宁酸抑制剂、4kg的BYK024和2kg的BYK1770消泡剂和8kg的BYK346润湿分散剂加入分散缸中，再以1500转/min的转速下分散10min；(3)将成膜助剂50kg的DPnB和10kg的DB先混合均匀后，在转速为900转/min的搅拌状态下慢速加入到分散缸中；再将3kg的PU40和2kg的Thixol53L增稠剂和78kg的去离子水加入到分散缸中，搅拌均匀并调整粘度到21秒/25℃，过滤包装即得本发明的防渗色水性封闭底漆。
实施例3
一种防渗色水性封闭底漆，其原料组分列于表3。
表3实施例3的原料和重量份
一种防渗色水性封闭底漆的制备方法，包括如下步骤：
(1)将650kg的Joncryl 8284和150kg的NeoPac E-129置于分散缸中，开始搅拌；(2)在转速为200转/min的搅拌状态下，将3kg的Nipacide HF-I杀菌剂、30kg的XTAIN L-66单宁酸抑制剂、4kg的BYK024和2kg的BYK1770消泡剂和4kg的BYK346润湿分散剂加入分散缸中，再以1000转/min的转速下分散30min；(3)先将30kg的DPnB和30kg的DB成膜助剂混合均匀，在转速为1000转/min的搅拌状态下，依次将3kg的PU40和2kg的Thixol 53L增稠剂和92kg的去离子水加入到分散缸中，搅拌均匀并调整粘度到19秒/25℃，过滤包装即得本发明的防渗色水性封闭底漆。
对比例1
对比例1的水性封闭底漆的各组分列于表4，其制备过程同实施例1，主要差别在于树脂选用普通纯丙烯酸树脂，具体为ALBERDINGK BOLEY GmbH公司的Alberdingk AC 2514，该水性树脂为丙烯酸乳液，固体含量为43％，其原料组分列于表4。
表4对比例1的原料和重量份
对比例2
对比例2的水性封闭底漆的各组分列于表5，其制备过程同实施例1，主要差别在于树脂选用水性阳离子树脂，具体为DSM的NeoCryl XK-350，该水性树脂为丙烯酸乳液，固体含量为42.5％，其原料组分列于表5。
表5对比例2的原料和重量份
按照GB/T23999-2009《室内装饰装修用水性木器涂料》标准对实施例1～3和对比例1、2分别进行测试，测试结果见表6。
表6实施例1～3和对比例1、2的标准检测结果
从表6的结果可以看出，实施例1～3在表干时间、实干时间和耐黄变性上要明显的优于对比例1，同时跟对比例2阳离子类型水性产品对比在耐黄性上也要有较明显的优势，整体黄变性要明显低，从而可以更好的保护木材及颜色的变色问题。
Claims (8)
1.一种防渗色水性封闭底漆，其特征在于，包括如下组分：水性自交联丙烯酸树脂：650～750份，水性聚氨酯丙烯酸分散体：50～150份，杀菌剂：1～4份，单宁酸抑制剂：30～50份，消泡剂：5～10份，润湿分散剂：4～10份，成膜助剂：50～70份，增稠剂：3～10份，水：70～200份；
所述水性自交联丙烯酸树脂是指固体含量为40%～50%的水性自交联丙烯酸分散乳液。
2.根据权利要求1所述的防渗色水性封闭底漆，其特征在于，所述水性聚氨酯丙烯酸分散体是指固体含量为35%～45%水性脂肪族聚氨酯丙烯酸共聚物分散液。
3.根据权利要求1所述的防渗色水性封闭底漆，其特征在于，所述杀菌剂选自异噻唑啉酮类杀菌剂或苯并异噻唑啉酮的水性混合物中的一种或两种。
4.根据权利要求1所述的防渗色水性封闭底漆，其特征在于，所述单宁酸抑制剂为氨盐基稳定的锆盐。
5.根据权利要求1所述的防渗色水性封闭底漆，其特征在于，所述消泡剂为有机硅氧烷类和聚醚改性硅氧烷类中的一种或两种；所述润湿分散剂为聚二甲基硅氧烷和/或聚硅氧烷-聚醚共聚物。
6.根据权利要求1所述的防渗色水性封闭底漆，其特征在于，所述成膜助剂选自二丙二醇丁醚(DPnB)、二乙二醇丁醚(DB)或乙二醇单丁醚（BCS）的一种或两种；所述增稠剂选自丙烯酸类增稠剂、聚氨酯类增稠剂或纤维素醚类增稠剂的一种或两种。
7.根据权利要求1～6任意一项所述的防渗色水性封闭底漆的制备方法，其特征在于，包括如下步骤：
（1）将所述水性自交联丙烯酸树脂和所述水性聚氨酯丙烯酸分散体置于分散缸中；（2）在转速为1～800转/min的搅拌状态下，将所述杀菌剂、单宁酸抑制剂、消泡剂和润湿分散剂加入分散缸中，再以1000～1500转/min的转速下分散10～30min；（3）在转速为800～1000转/min的搅拌状态下，依次将所述成膜助剂、增稠剂和剩余的去离子水加入到分散缸中，搅拌均匀并调整粘度到18～22秒/25℃，即得本发明的防渗色水性封闭底漆。
8.根据权利要求1～6任意一项所述的防渗色水性封闭底漆，其特征在于，固体含量为30%～36%，直接用于涂装施工，施工方式包括刷涂、浸涂以及喷涂。