CN112251155B - 户外用耐气候广告车贴的制备方法 - Google Patents
户外用耐气候广告车贴的制备方法 Download PDFInfo
- Publication number
- CN112251155B CN112251155B CN201910659481.XA CN201910659481A CN112251155B CN 112251155 B CN112251155 B CN 112251155B CN 201910659481 A CN201910659481 A CN 201910659481A CN 112251155 B CN112251155 B CN 112251155B
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- outdoor weather
- substrate layer
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种户外用耐气候广告车贴的制备方法,包括基材层、背胶层和离型层,所述基材层的一面上涂覆于背胶层,所述背胶层相背于基材层的一面设有离型层,所述背胶层由胶液涂覆烘干获得,此胶液由以下步骤制得:S1、将甲基丙烯酸甲酯15~25份、苯乙烯15~25份、丙烯酸‑2‑乙基己酯15~20份、三甲基戊二醇1~1.5份、二甲氨基丙腈1~5份和去离子水50~75份混合均匀,升温至75~80℃,向该混合体系中滴加偶氮异丁氰基甲酰胺0.5~1.5份和丙烯酸1~10份,反应3~4h;S2、冷却至室温,加入过氧化双2,4一二氯苯甲酰1~5份、固化剂1~1.5份、乳化剂0.2~1份和对苯二酚0.1~1份,混合均匀得到胶液;S3、将胶液均匀涂覆于基材层上,烘干得到背胶层。本发明提高了防水性能,粘着力基本不变,使粘接稳定。
Description
技术领域
本发明属于胶带技术领域,尤其涉及一种户外用耐气候广告车贴的制备方法。
背景技术
现有的部分广告贴,例如车贴、水性高亮PVC,都具有PVC膜、粘接层和离型纸,其中离型纸由硅油层、淋膜层和底纸构成,硅油层与广告贴的粘接层连接,在使用时剥离离型纸,以将粘接层暴露,进而将广告贴贴于指定位置。
目前市面上及国内生产的广告贴使用的是油性体系压敏胶,胶水有溶剂残留,VOC排放不达标,只能应用于室外环境。因此环保型水基胶粘剂已成为胶粘剂的发展方向,而环保型胶粘剂的研制成果相对较少,防水性能不尽人意,且制造工艺比较复杂。因此,如何开发一种防水性能优良、可长期室外使用的车身贴成为本领域技术人员的研究方向。
发明内容
本发明目的在于提供一种户外用耐气候广告车贴的制备方法,该户外用耐气候广告车贴的制备方法既既提高了防水性能,也使得户外用耐气候广告车贴的制备方法在环境湿度较大的情况下,粘着力基本不变,使得粘接稳定,不会出现脱落的情况,从而适合长期室外使用,大大延长了车身贴的使用寿命。
为达到上述目的,本发明采用的技术方案是:一种户外用耐气候广告车贴的制备方法,包括基材层、背胶层和离型层,所述基材层的一面上涂覆于背胶层,所述背胶层相背于基材层的一面设有离型层,所述背胶层由胶液涂覆烘干获得,此胶液由以下步骤制得:
S1、将甲基丙烯酸甲酯15~25份、苯乙烯15~25份、丙烯酸-2-乙基己酯15~20份、三甲基戊二醇1~1.5份、二甲氨基丙腈1~5份和去离子水50~75份混合均匀,升温至75~80℃,向该混合体系中滴加偶氮异丁氰基甲酰胺0.5~1.5份和丙烯酸1~10份,反应3~4h;
S2、冷却至室温,加入过氧化双2,4一二氯苯甲酰1~5份、固化剂1~1.5份、乳化剂0.2~1份和对苯二酚0.1~1份,混合均匀得到胶液;
S3、将胶液均匀涂覆于基材层1上,烘干得到背胶层2。
上述技术方案中进一步改进的技术方案如下:
1. 上述方案中:所述甲基丙烯酸甲酯与苯乙烯的添加比例为2:1~1:1。
2. 上述方案中:所述固化剂选自固化剂S01-5、固化剂 MH2844、固化剂T-31中的一种。
3. 上述方案中:所述乳化剂乙氧基化C16-18-醇、吐温 20和甘油基聚环氧乙烷中的一种
4. 上述方案中:所述基材层为PVC层。
5. 上述方案中:所述基材层的厚度为50~150μm。
6. 上述方案中:所述背胶层厚度为10~50μm。
由于上述技术方案的运用,本发明与现有技术相比具有下列优点:
本发明户外用耐气候广告车贴的制备方法,其通过在甲基丙烯酸甲酯、苯乙烯、丙烯酸-2-乙基己酯、丙烯酸和偶氮异丁氰基甲酰胺中添加三甲基戊二醇、二甲氨基丙腈,既提高了防水性能,也使得户外用耐气候广告车贴的制备方法在环境湿度较大的情况下,粘着力基本不变,使得粘接稳定,从而适合长期室外使用,不会出现脱落的情况,大大延长了车身贴的使用寿命。
附图说明
附图1为本发明 耐水性户外广告车身贴结构示意图。
以上附图中:1、基材层;2、背胶层;3、离型层。
具体实施方式
在本专利的描述中,需要说明的是,术语“中心”、“上”、“下”、“左”、“右”、“竖直”、“水平”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系,仅是为了便于描述本发明 和简化描述,而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作,因此不能理解为对本发明 的限制;术语“第一”、“第二”、“第三”仅用于描述目的,而不能理解为指示或暗示相对重要性;此外,除非另有明确的规定和限定,术语“安装”、“相连”、“连接”应做广义理解,例如,可以是固定连接,也可以是可拆卸连接,或一体地连接;可以是机械连接,也可以是电连接;可以是直接相连,也可以通过中间媒介间接相连,可以是两个元件内部的连通。对于本领域的普通技术人员而言,可以具体情况理解上述术语在本专利的具体含义。
下面结合实施例对本发明作进一步描述:
实施例1~4:一种户外用耐气候广告车贴的制备方法,包括基材层1、背胶层2和离型层3,所述基材层1的一面上涂覆于背胶层2,所述背胶层2相背于基材层1的一面设有离型层3,所述背胶层由胶液涂覆烘干获得,此胶液由以下步骤制得:
S1、将甲基丙烯酸甲酯15~25份、苯乙烯15~25份、丙烯酸-2-乙基己酯15~20份、三甲基戊二醇1~1.5份、二甲氨基丙腈1~5份和去离子水50~75份混合均匀,升温至75~80℃,向该混合体系中滴加偶氮异丁氰基甲酰胺0.5~1.5份和丙烯酸1~10份,反应3~4h;
S2、冷却至室温,加入过氧化双2,4一二氯苯甲酰1~5份、固化剂1~1.5份、乳化剂0.2~1份和对苯二酚0.1~1份,混合均匀得到胶液;
S3、将胶液均匀涂覆于基材层1上,烘干得到背胶层2
各实施例中上述各组分具体重量份数如表1所示:
表1
组分 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
甲基丙烯酸甲酯 | 15份 | 20份 | 18份 | 25份 |
苯乙烯 | 15份 | 10份 | 15份 | 25份 |
丙烯酸-2-乙基己酯 | 20份 | 16份 | 15份 | 18份 |
丙烯酸 | 6份 | 1份 | 5份 | 10份 |
过氧化双2,4一二氯苯甲酰 | 2份 | 3份 | 5份 | 1份 |
偶氮异丁氰基甲酰胺 | 0.5份 | 1份 | 1.5份 | 1.2份 |
三甲基戊二醇 | 1份 | 1.1份 | 1.2份 | 1.5份 |
二甲氨基丙腈 | 2份 | 5份 | 1份 | 3份 |
固化剂 | 1.5份 | 1份 | 1.2份 | 1.3份 |
去离子水 | 70份 | 60份 | 50份 | 75份 |
乳化剂 | 0.2份 | 0.5份 | 0.8份 | 1份 |
对苯二酚 | 0.1份 | 0.9份 | 0.5份 | 1份 |
实施例1中甲基丙烯酸甲酯与苯乙烯的添加比例为1:1,上述固化剂选自固化剂S01-5,上述乳化剂选自乙氧基化C16-18-醇,上述基材层为PVC层,上述基材层的厚度为70μm,上述背胶层厚度为15μm。
实施例2中甲基丙烯酸甲酯与苯乙烯的添加比例为2:1,上述固化剂选自固化剂MH2844,上述乳化剂选自甘油基聚环氧乙烷,上述基材层为PVC层,上述基材层的厚度为120μm,上述背胶层厚度为25μm。
实施例3中甲基丙烯酸甲酯与苯乙烯的添加比例为1.2:1,上述固化剂选自固化剂T-31,上述乳化剂选自乙氧基化C16-18-醇,上述基材层为PVC层,上述基材层的厚度为100μm,上述背胶层厚度为18μm。
实施例4中甲基丙烯酸甲酯与苯乙烯的添加比例为1:1,上述固化剂选自固化剂T-31,上述乳化剂选自吐温 20,上述基材层为PVC层,上述基材层的厚度为85μm,上述背胶层厚度为25μm。
对比例1~2:一种户外用广告车贴的制备方法,包括基材层1、背胶层2和离型层3,所述基材层1的一面上涂覆于背胶层2,所述背胶层2相背于基材层1的一面设有离型层3,所述背胶层由胶液涂覆烘干获得,此胶液由以下重量份组分组成,如表2所示:
表2
组分 | 对比例1 | 对比例2 |
甲基丙烯酸甲酯 | 18份 | 20份 |
苯乙烯 | 15份 | 10份 |
丙烯酸-2-乙基己酯 | 15份 | 16份 |
丙烯酸 | 3份 | 1份 |
过氧化双2,4一二氯苯甲酰 | 2份 | 3份 |
偶氮异丁氰基甲酰胺 | 0.5份 | 0.8份 |
三甲基戊二醇 | - | 1.1份 |
二甲氨基丙腈 | 2份 | - |
固化剂 | 1.5份 | 1份 |
去离子水 | 75份 | 60份 |
乳化剂 | 0.2份 | 0.5份 |
对苯二酚 | 0.1份 | 0.5份 |
对比例制备方法同实施例。
上述实施例1~4和对比例1~2制得的抗静电膜的性能如表3所示:
表3
测试方法:
耐水试验测定方法:所制得试样在沸水(100℃)条件下蒸煮,经过1H、10H和24H分别测试粘着力情况。
如表3的评价结果所示,实施例户外用耐气候广告车贴的制备方法防水性能优良,在水中浸泡长时间粘着力几乎不会发生变化,而对比例1防水性能相对差,对比例2粘着力随着浸泡时间变化,粘着力快速下降;可知,本发明既提高了防水性能,也使得户外用耐气候广告车贴的制备方法在水中浸泡时间较长的情况下,粘着力变化很小,防水性能稳定,不会产生脱落的现象,从而适合长期室外使用,大大延长了车身贴的使用寿命。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。
Claims (7)
1.一种户外用耐气候广告车贴的制备方法,其特征在于:包括基材层(1)、背胶层(2)和离型层(3),所述基材层(1)的一面上涂覆于背胶层(2),所述背胶层(2)相背于基材层(1)的一面设有离型层(3),所述背胶层由胶液涂覆烘干获得,此胶液由以下步骤制得:
S1、将甲基丙烯酸甲酯15~25份、苯乙烯15~25份、丙烯酸-2-乙基己酯15~20份、三甲基戊二醇1~1.5份、二甲氨基丙腈1~5份和去离子水50~75份混合均匀,升温至75~80℃,向该混合体系中滴加偶氮异丁氰基甲酰胺0.5~1.5份和丙烯酸1~10份,反应3~4h;
S2、冷却至室温,加入过氧化双2,4一二氯苯甲酰1~5份、固化剂1~1.5份、乳化剂0.2~1份和对苯二酚0.1~1份,混合均匀得到胶液;
S3、将胶液均匀涂覆于基材层( 1) 上,烘干得到背胶层( 2) 。
2.根据权利要求1所述的户外用耐气候广告车贴的制备方法,其特征在于:所述甲基丙烯酸甲酯与苯乙烯的添加比例为2:1~1:1。
3.根据权利要求1所述的户外用耐气候广告车贴的制备方法,其特征在于:所述固化剂选自固化剂S01-5、固化剂 MH2844、固化剂T-31中的一种。
4.根据权利要求1所述的户外用耐气候广告车贴的制备方法,其特征在于:所述乳化剂乙氧基化C16-18-醇、吐温 20和甘油基聚环氧乙烷中的一种。
5.根据权利要求1~4中任一项所述的户外用耐气候广告车贴的制备方法,其特征在于:所述基材层(1)为PVC层。
6.根据权利要求1~4中任一项所述的户外用耐气候广告车贴的制备方法,其特征在于:所述基材层(1)的厚度为50~150μm。
7.根据权利要求1~4中任一项所述的户外用耐气候广告车贴的制备方法,其特征在于:所述背胶层(2)厚度为10~50μm。