CN112111341A - 注塑机模具用清洗剂及其制备方法 - Google Patents
注塑机模具用清洗剂及其制备方法 Download PDFInfo
- Publication number
- CN112111341A CN112111341A CN202010960504.3A CN202010960504A CN112111341A CN 112111341 A CN112111341 A CN 112111341A CN 202010960504 A CN202010960504 A CN 202010960504A CN 112111341 A CN112111341 A CN 112111341A
- Authority
- CN
- China
- Prior art keywords
- acid
- stirring
- cleaning agent
- injection molding
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种注塑机模具用清洗剂，包括按质量百分比计的下列组分：柠檬酸40‑50％；酒石酸5‑6％；乙酸0‑10％；丁二酸3‑4％；苯甲酸0‑10％；丙二酸4‑7％；邻苯二甲酸7‑10％；元明粉9‑15％。制备方法，其特征在于，包括以下步骤：将柠檬酸倒入反应釜搅拌至40℃，搅拌40分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸或羟基乙酸搅拌30分钟，加温至45℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌40分钟后，停止加温，加入元明粉，搅拌1小时，自然冷却即可。注塑机模具用清洗剂，其能清洗中高温条件下产生的水垢，清洗效果良好。
Description
技术领域
本发明涉及一种注塑机模具用清洗剂及其制备方法。
背景技术
市场上现有除垢剂只能清洗水路产生的水垢问题，清洗不了在中高温下产生的水垢水锈污泥的结合体，因为在高温100℃下产生的水垢是白色的，在中高温60-80℃产生的水垢是褐红色或黑色结合体，而市场上现有的除垢剂是难以实现清洗的有效工作。
发明内容
本发明要解决的技术问题是提供一种注塑机模具用清洗剂，其能清洗中高温条件下产生的水垢，清洗效果良好。
为了实现上述发明目的，本发明采用下述技术方案：
本发明提出了一种注塑机模具用清洗剂，包括按质量百分比计的下列组分：
作为本发明进一步的改进：所述乙酸采用羟基乙酸代替。
作为本发明进一步的改进：所述清洗剂使用时，将其与水按体积比1：(5-10)使用。
作为本发明进一步的改进：所述清洗剂使用时，将其与水按体积比1：10或1：5使用。
本发明还提供一种产品性能良好的注塑机模具用清洗剂的制备方法，包括以下步骤：
将柠檬酸倒入反应釜搅拌至38-42℃，搅拌35-45分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸或羟基乙酸搅拌28-32分钟，加温至40-50℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌35-42分钟后，停止加温，加入元明粉，搅拌1-1.5小时，自然冷却即可。
作为本发明进一步的改进，包括以下步骤：
将柠檬酸倒入反应釜搅拌至40℃，搅拌40分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸或羟基乙酸搅拌30分钟，加温至45℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌40分钟后，停止加温，加入元明粉，搅拌1小时，自然冷却即可。
柠檬酸：在室温下，柠檬酸为无色半透明晶体或白色颗粒或白色结晶性粉末，无臭、味极酸，有涩味，有微弱腐蚀性，潮解性强，并伴有结晶水化合物生成，在潮湿的空气中微有潮解性。
酒石酸是一种羧酸﹐存在于多种植物中﹐如葡萄和罗望子﹐也是葡萄酒中主要的有机酸之一。作为食品中添加的抗氧化剂﹐其能使食物具有酸味。酒石酸最大的用途是饮料添加剂。也是药物工业原料。在制镜工业中，酒石酸是一个重要的助剂和还原剂，可以控制银镜的形成速度，获得非常均一的镀层。
乙酸，也叫醋酸、冰醋酸，是一种有机一元酸，为食醋内酸味及刺激性气味的来源。纯的无水乙酸(冰醋酸)是无色的吸湿性液体，凝固点为16.7℃(62℉)，凝固后为无色晶体。
丁二酸主要用于制取丁二酸酐、丁二酸酯类等衍生物，用作涂料、染料、粘合剂、药物等的原料。
苯甲酸为具有苯或甲醛的气味的鳞片状或针状结晶。在100℃时迅速升华，它的蒸气有很强的刺激性，吸入后易引起咳嗽。微溶于水，易溶于乙醇、乙醚等有机溶剂。苯甲酸是弱酸，比脂肪酸强。
丙二酸又称缩苹果酸，以钙盐形式存在于甜菜根中，甜菜制糖的浓缩罐里沉积的水垢即丙二酸钙。
邻苯二甲酸为无色结晶或结晶性粉末，两个羧基分别与苯环中相邻的两个碳原子相连而成的二元芳香羧，在应用中，可用邻苯二甲酸酐代替邻苯二甲酸。邻苯二甲酸是合成树脂、纤维、药物等的原料。
元明粉：硫酸钠，无机化合物，十水合硫酸钠又名芒硝、高纯度、颗粒细的无水物称为元明粉，元明粉白色、无臭、有苦味的结晶或粉末，有吸湿性。外形为无色、透明、大的结晶或颗粒性小结晶。主要用于制水玻璃、玻璃、瓷釉、纸浆、致冷混合剂、洗涤剂、干燥剂、染料稀释剂、分析化学试剂、医药品等。
本发明提供的一种注塑机模具用清洗剂，能把中高温60-80℃产生的水垢水锈污泥清洗的干干净净。市场上现有的除垢剂清洗不了中高温产生的水垢水锈污泥结合体，清洗不了注塑机模具生产过程中产生的水垢水锈污泥结合体，有效降低了生产成本及在生产过程中因高温产生的残次率。如模具10毫米使用半年后，水垢水锈污泥产生厚度，达到5毫米，使用本发明塑机模具清洗剂可在2-4小时清洗达到10毫米的清洗效果。其制备方法，产品性能稳定，工艺简单且便于操作。
附图说明
图1为：实验三的产品使用前后效果对比图Ι，其中左清洗前；右清洗后。
图2为：实验四的产品使用前后效果对比图Ⅱ，其中左清洗前；右清洗后。
具体实施方式
以下通过具体实施例对本发明提供的一种注塑机模具用清洗剂及其制备方法做进一步更详细的说明：
实验一、将注塑机模具用清洗剂，包括按质量百分比计的下列组分：
按不同组合制备成产品，在同等条件下使用，观察其除中高温条件下的水垢效果见下表1：
表1中高温条件下的除水垢效果
从上表可以看出，组分柠檬酸，酒石酸、乙酸、丁二酸、苯甲酸、丙二酸、邻苯二甲酸元明粉组合在一起使用，效果更为突出明显。
实验二、将注塑机模具用清洗剂，包括按质量百分比计的下列组分：
按不同组合混合，观察其产品性能稳定性见下表2：
表2产品性能稳定性观察
从上表可以看出，组分柠檬酸，酒石酸、乙酸、丁二酸、苯甲酸、丙二酸、邻苯二甲酸元明粉混合在一起的性质更加稳定。
实验三、注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
将柠檬酸倒入反应釜搅拌至40℃，搅拌40分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸搅拌30分钟，加温至45℃，加入丁二酸，苯甲酸，搅拌一小时，加入丙二酸，邻苯二甲酸，搅拌40分钟后，停止加温，加入元明粉，搅拌1小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：10，通过脉冲模具水路清洗机连接模具水路，冷却器水路，冷却环水路进行清洗2小时后，清洗前后对比图如图1所示，从图中可以看出，水垢被清洗的很干净。
实验四、注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
柠檬酸倒入反应釜搅拌至40℃，搅拌40分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸搅拌30分钟，加温至45℃，加入丁二酸，苯甲酸，搅拌一小时，加入丙二酸，邻苯二甲酸，搅拌40分钟后，停止加温，加入元明粉，搅拌1小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：5，通过模具水路清洗机连接模具水路，冷却器水路，冷却环水路进行清洗2小时，清洗前后对比图如图2所示，从图2可以看出，水垢被完全冲洗掉。
实施例1
本实施例的注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
将柠檬酸倒入反应釜搅拌至38℃，搅拌35分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸搅拌28分钟，加温至40℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌35分钟后，停止加温，加入元明粉，搅拌1小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：6，通过脉冲模具水路清洗机/模具水路清洗机连接模具水路，也可采用其他清洗机清洗，冷却器水路，冷却环水路进行清洗4小时，常年未清洗结垢严重时，需延长清洗时间，或者二次重复清洗。
本实验地区如10毫米使用半年后，水垢水锈污泥产生厚度，达到5毫米，使用本发明塑机模具清洗剂可在2小时清洗达到10毫米的清洗效果。
实施例2
本实施例的注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
将柠檬酸倒入反应釜搅拌至38℃，搅拌45分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸搅拌32分钟，加温至50℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌42分钟后，停止加温，加入元明粉，搅拌1.5小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：10，通过脉冲模具水路清洗机/模具水路清洗机连接模具水路，也可采用其他清洗机清洗，冷却器水路，冷却环水路进行清洗4小时，常年未清洗结垢严重时，需延长清洗时间，或者二次重复清洗。
本实验地区如10毫米使用半年后，水垢水锈污泥产生厚度，达到5毫米，使用本发明塑机模具清洗剂可在3小时清洗达到10毫米的清洗效果。
实施例3
本实施例的注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
将柠檬酸倒入反应釜搅拌至40℃，搅拌38分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸搅拌30分钟，加温至45℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌37分钟后，停止加温，加入元明粉，搅拌1小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：9，通过脉冲模具水路清洗机/模具水路清洗机连接模具水路，也可采用其他清洗机清洗，冷却器水路，冷却环水路进行清洗2小时，常年未清洗结垢严重时，需延长清洗时间，或者二次重复清洗。
本实验地区如10毫米使用半年后，水垢水锈污泥产生厚度，达到5毫米，使用本发明塑机模具清洗剂可在2.5小时清洗达到10毫米的清洗效果。
实施例4
本实施例的注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
将柠檬酸倒入反应釜搅拌至42℃，搅拌45分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸搅拌32分钟，加温至50℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌42分钟后，停止加温，加入元明粉，搅拌1.5小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：10，通过脉冲模具水路清洗机/模具水路清洗机连接模具水路，也可采用其他清洗机清洗，冷却器水路，冷却环水路进行清洗2小时，常年未清洗结垢严重时，需延长清洗时间，或者二次重复清洗。
本实验地区如10毫米使用半年后，水垢水锈污泥产生厚度，达到5毫米，使用本发明塑机模具清洗剂可在4小时清洗达到10毫米的清洗效果。
实施例5
本实施例的注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
将柠檬酸倒入反应釜搅拌至42℃，搅拌37分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸搅拌30分钟，加温至42℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌38分钟后，停止加温，加入元明粉，搅拌1.5小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：8，通过脉冲模具水路清洗机/模具水路清洗机连接模具水路，也可采用其他清洗机清洗，冷却器水路，冷却环水路进行清洗4小时，常年未清洗结垢严重时，需延长清洗时间，或者二次重复清洗。
本实验地区如10毫米使用半年后，水垢水锈污泥产生厚度，达到5毫米，使用本发明塑机模具清洗剂可在3小时清洗达到10毫米的清洗效果。
实施例6
本实施例的注塑机模具用清洗剂，包括按质量百分比计的下列组分：
注塑机模具用清洗剂制备方法：
将柠檬酸倒入反应釜搅拌至42℃，搅拌45分钟，柠檬酸致蓬松状态，加入酒石酸，羟基乙酸搅拌29分钟，加温至47℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌38分钟后，停止加温，加入元明粉，搅拌1.5小时，自然冷却即可。
注塑机模具用清洗剂使用方法：将清洗剂溶解在盛有水的塑料桶里，药剂与水比例1：7，通过脉冲模具水路清洗机/模具水路清洗机连接模具水路，也可采用其他清洗机清洗，冷却器水路，冷却环水路进行清洗2小时，常年未清洗结垢严重时，需延长清洗时间，或者二次重复清洗。
本实验地区如10毫米使用半年后，水垢水锈污泥产生厚度，达到5毫米，使用本发明塑机模具清洗剂可在2小时清洗达到10毫米的清洗效果。
应当理解，这些实施例的用途仅用于说明本发明而非意欲限制本发明的保护范围。此外，也应理解，在阅读了本发明的技术内容之后，本领域技术人员可以对本发明作各种改动、修改和/或变型，所有的这些等价形式同样落于本申请所附权利要求书所限定的保护范围之内。
由技术常识可知，本发明可以通过其它的不脱离其精神实质或必要特征的实施方案来实现。因此，上述公开的实施方案，就各方面而言，都只是举例说明，并不是仅有的。所有在本发明范围内或在等同于本发明的范围内的改变均被本发明包含。
Claims (6)
1.注塑机模具用清洗剂，其特征在于，包括按质量百分比计的下列组分：
2.根据权利要求1所述的注塑机模具用清洗剂，其特征在于：所述乙酸采用羟基乙酸代替。
3.根据权利要求1所述的注塑机模具用清洗剂，其特征在于：所述清洗剂使用时，将其与水按体积比1：(5-10)使用。
4.根据权利要求4所述的注塑机模具用清洗剂，其特征在于：所述清洗剂使用时，将其与水按体积比1：10或1：5使用。
5.根据权利要求1-4之任一所述的注塑机模具用清洗剂的制备方法，其特征在于，包括以下步骤：
将柠檬酸倒入反应釜搅拌至38-42℃，搅拌35-45分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸或羟基乙酸搅拌28-32分钟，加温至40-50℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌35-42分钟后，停止加温，加入元明粉，搅拌1-1.5小时，自然冷却即可。
6.根据权利要求5所述的注塑机模具用清洗剂的制备方法，其特征在于，包括以下步骤：
将柠檬酸倒入反应釜搅拌至40℃，搅拌40分钟，柠檬酸致蓬松状态，加入酒石酸，乙酸或羟基乙酸搅拌30分钟，加温至45℃，加入丁二酸，苯甲酸，搅拌1小时，加入丙二酸，邻苯二甲酸，搅拌40分钟后，停止加温，加入元明粉，搅拌1小时，自然冷却即可。