CN112063223A - Method for extracting special carbon black for ink from black rock - Google Patents
Method for extracting special carbon black for ink from black rock Download PDFInfo
- Publication number
- CN112063223A CN112063223A CN202010920257.4A CN202010920257A CN112063223A CN 112063223 A CN112063223 A CN 112063223A CN 202010920257 A CN202010920257 A CN 202010920257A CN 112063223 A CN112063223 A CN 112063223A
- Authority
- CN
- China
- Prior art keywords
- ink
- black
- carbon black
- component
- materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a method for extracting special carbon black for ink from black rocks, and relates to the field of ink. According to the invention, a black shale is subjected to dry purification of mineral black elements, extracted melanin, modified solid powder desalination by a scientific and technological nano technology, penetrant, colorant and adsorbent are added, the extracted element materials are softened by high-speed high-temperature equipment, and then a special high-carbon black semi-finished product for ink can be obtained; the product is widely used in printing ink, coating, plastic color master batch, offset printing ink and product characteristics, and the product is the medium and high pigment furnace carbon black with good dispersibility: stable hue, high brightness, etc.
Description
Technical Field
The invention relates to the field of ink, in particular to a method for extracting special carbon black for ink from black rocks.
Background
The ink is an important material for printing packaging materials, is a sticky fluid substance with certain color, and can be used for expressing patterns and characters on a printing material through printing.
However, the prior art for extracting the carbon black special for the ink from the black rocks is not perfect, so that a method for extracting the carbon black special for the ink from the black rocks is needed.
Disclosure of Invention
The invention aims to provide a method for extracting carbon black special for ink from black rocks, so as to solve the technical problem.
In order to solve the technical problems, the invention adopts the following technical scheme: the method for extracting the carbon black special for the ink from the black rock comprises the following components:
a first component:
mineral high carbon black semi-finished product: 30-300 g;
mineral ink: 30-300 g;
direct black mineral: 30-300 g;
a second component:
petroleum black: 50-500 g;
melanin: 50-500 g;
titanium melanin: 50-500 g;
and (3) third component:
and (3) corrosion inhibitor: 5.5-15 g;
antistatic agent: 4.9-10.8 g;
oil refers to transforming agent: 16.3-23.1 g;
the ink comprises the following process flow steps:
s1: taking the first component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s2: taking the second component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s3: taking a third component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s4: taking three standby materials, unwinding in a vacuum pressurization reaction kettle, starting a heating system to heat to 100 ℃, opening a high-speed dispersion system, dispersing at a high speed for 15-25 minutes, opening the pressurization system to pressurize to 6 air pressures, continuing to disperse, pressurizing while dispersing, then opening the vacuum system to continue dispersing for 15 minutes, stopping heating, opening a water cooling system to cool to 25 ℃ at normal temperature, not opening the reaction kettle, continuing to cool for 4 hours, taking out the materials, placing in a sealed oak for two periods of cooling, taking out and subpackaging, and obtaining the special carbon black for the printing ink.
The invention has the beneficial effects that:
according to the invention, a black shale is subjected to dry purification of mineral black elements, extracted melanin, modified solid powder desalination by a scientific and technological nano technology, penetrant, colorant and adsorbent are added, the extracted element materials are softened by high-speed high-temperature equipment, and then a special high-carbon black semi-finished product for ink can be obtained;
the product is widely used in printing ink, coating, plastic color master batch, offset printing ink and product characteristics, and the product is the medium and high pigment furnace carbon black with good dispersibility: stable hue, high brightness, etc.
Detailed Description
The present invention will be further described with reference to specific embodiments for the purpose of facilitating an understanding of technical means, characteristics of creation, objectives and functions realized by the present invention, but the following embodiments are only preferred embodiments of the present invention, and are not intended to be exhaustive. Based on the embodiments in the implementation, other embodiments obtained by those skilled in the art without any creative efforts belong to the protection scope of the present invention.
Specific embodiments of the present invention are described below.
Example 1
A method for extracting carbon black special for ink from black rocks comprises the following components,
a first component:
mineral high carbon black semi-finished product: 30-300 g;
mineral ink: 30-300 g;
direct black mineral: 30-300 g;
a second component:
petroleum black: 50-500 g;
melanin: 50-500 g;
titanium melanin: 50-500 g;
and (3) third component:
and (3) corrosion inhibitor: 5.5-15 g;
antistatic agent: 4.9-10.8 g;
oil refers to transforming agent: 16.3-23.1 g;
the ink comprises the following steps:
s1: taking the first component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s2: taking the second component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s3: taking a third component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s4: taking three standby materials, unwinding in a vacuum pressurization reaction kettle, starting a heating system to heat to 100 ℃, opening a high-speed dispersion system, dispersing at a high speed for 15-25 minutes, opening the pressurization system to pressurize to 6 air pressures, continuing to disperse, pressurizing while dispersing, then opening the vacuum system to continue dispersing for 15 minutes, stopping heating, opening a water cooling system to cool to 25 ℃ at normal temperature, not opening the reaction kettle, continuing to cool for 4 hours, taking out the materials, placing in a sealed oak for two periods of cooling, taking out and subpackaging, and obtaining the special carbon black for the printing ink.
The invention relates to a black shale, which is prepared by purifying mineral black elements by a dry method, extracting melanin, desalting modified solid powder by a scientific and technological nano technology, adding penetrant, colorant and adsorbent, softening the extracted element materials by high-speed high-temperature equipment to obtain a special high-carbon black semi-finished product for ink;
the product is widely used in printing ink, coating, plastic color master batch, offset printing ink and product characteristics, and the product is the medium and high pigment furnace carbon black with good dispersibility: stable hue, high brightness, etc.
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, and the preferred embodiments of the present invention are described in the above embodiments and the description, and are not intended to limit the present invention. The scope of the invention is defined by the appended claims and equivalents thereof.
Claims (1)
1. The method for extracting the carbon black special for the ink from the black rock comprises the following components:
a first component:
mineral high carbon black semi-finished product: 30-300 g;
mineral ink: 30-300 g;
direct black mineral: 30-300 g;
a second component:
petroleum black: 50-500 g;
melanin: 50-500 g;
titanium melanin: 50-500 g;
and (3) third component:
and (3) corrosion inhibitor: 5.5-15 g;
antistatic agent: 4.9-10.8 g;
oil refers to transforming agent: 16.3-23.1 g;
the ink comprises the following process flow steps:
s1: taking the first component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s2: taking the second component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s3: taking a third component, and uniformly stirring the three materials by a high-speed stirrer for later use;
s4: taking three standby materials, unwinding in a vacuum pressurization reaction kettle, starting a heating system to heat to 100 ℃, opening a high-speed dispersion system, dispersing at a high speed for 15-25 minutes, opening the pressurization system to pressurize to 6 air pressures, continuing to disperse, pressurizing while dispersing, then opening the vacuum system to continue dispersing for 15 minutes, stopping heating, opening a water cooling system to cool to 25 ℃ at normal temperature, not opening the reaction kettle, continuing to cool for 4 hours, taking out the materials, placing in a sealed oak for two periods of cooling, taking out and subpackaging, and obtaining the special carbon black for the printing ink.