CN111962314A - Four-side elastic fabric and manufacturing process thereof - Google Patents
Four-side elastic fabric and manufacturing process thereof Download PDFInfo
- Publication number
- CN111962314A CN111962314A CN202010755702.6A CN202010755702A CN111962314A CN 111962314 A CN111962314 A CN 111962314A CN 202010755702 A CN202010755702 A CN 202010755702A CN 111962314 A CN111962314 A CN 111962314A
- Authority
- CN
- China
- Prior art keywords
- cloth
- temperature
- grey cloth
- minutes
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a four-side stretch fabric and a manufacturing process thereof, wherein the four-side stretch fabric comprises the following steps: the color fixing agent comprises 1-1.5% of polydimethyl allyl sodium chloride, 1-1.5% of hydroxypropyl trimethyl ammonium chloride chitosan, 5-8% of ethanol, 2-2.8% of catalyst and 1.8-2.5% of glacial acetic acid. The four-side stretch fabric manufactured by the process has excellent elasticity, can reduce the occurrence of fading, and is simple in process and low in manufacturing cost.
Description
Technical Field
The invention relates to the field of textile printing of cloth, in particular to a four-side stretch fabric and a manufacturing process thereof.
Background
Along with the continuous improvement of living conditions of people, the requirements of people on the functional selection of the clothing fabric are higher and higher, and the fabric has more performances besides the requirements of normal heat retention and wearing comfort. At present, when a research and development worker manufactures fabrics, functional indexes such as softness, moisture absorption and sweat release performance, abrasion resistance, wrinkle resistance and the like of the fabrics are considered at first, and because a lot of fabrics are seriously deformed after being worn and used for a certain time, the wearing comfort and the attractiveness are influenced.
The four-side elastic fabric can adapt to the movement of a human body due to excellent elasticity, can stretch and contract along with the movement, is light and comfortable, and can keep the external aesthetic property of the clothes, the parts of knees, elbows and the like of the common clothes can not be restored to the original shape in a short time due to long-time wearing or movement of the human body, so that the fabric of the parts still keeps the shapes of the bent knees and elbows and is bulged, and the four-side elastic fabric can restore the original shapes of the fabric in a short time, so that the aesthetic property of the clothes in the wearing process is kept, and the fabric is particularly suitable for being applied to sports and leisure clothes.
The existing manufacturing process of the four-side elastic fabric is relatively complicated, and the manufactured fabric is easy to fade.
Disclosure of Invention
The invention aims to overcome the technical defects and provides a four-side elastic fabric and a manufacturing process thereof.
In order to solve the problems, the technical scheme of the invention is as follows: the four-side elastic fabric and the manufacturing process thereof comprise the following steps:
(1) cloth preparation: adopting gray fabrics of light yarn nylon 70D and spandex 40D for cloth matching;
(2) pretreatment: padding the prepared grey cloth with a padding treatment fluid with a rolling residual rate of 120-150%, sealing and stacking at room temperature, stacking for 18-24 hours, and washing for 3-5 times by using clear water;
(3) presetting: shaping the pre-treated grey cloth at the temperature of 150-170 ℃ and the vehicle speed of 15-25 m/min to obtain pre-shaped grey cloth;
(4) cloth coiling: c, performing cloth coiling on the pre-shaped grey cloth obtained in the fourth step by using a beam cloth coiling machine, coiling the cloth subjected to cloth coiling on a beam net pipe at the temperature of 55-65 ℃ of a water tank, the tension of 4.5-5.5 kg and the vehicle speed of 50-70 m/min, and preparing for dyeing;
(5) dyeing: treating the grey cloth with a refining agent, washing and drying the grey cloth, heating the dye liquor to 50 ℃, putting the grey cloth into the dye liquor, raising the temperature to 80 ℃ at a speed of raising the temperature by 2 ℃ for 1-3 minutes, then raising the temperature to 100 ℃ at a speed of raising the temperature by 1 ℃ for 3-5 minutes, preserving the heat of the dye for 40-50 minutes, cooling, cleaning the cloth, and drying the cloth by hot air at a temperature of 50-60 ℃;
(6) and (3) fixation: pouring a color fixing agent into a color fixing pool, heating liquid in the color fixing pool to 55 ℃, completely immersing the gray fabric into the liquid, heating the liquid for 3-5 minutes to 5 ℃ until the temperature reaches 90 ℃, preserving the heat for 20-40 minutes, fishing out the gray fabric, and naturally drying in the shade;
(7) shaping and drying: placing the grey cloth into a baking box, baking at the temperature of 180-190 ℃, wherein the cloth moving speed is 15-20 m/min;
(8) and (3) post-treatment: according to the water content, 1.5-2.5% of resin is poured into the treatment tank, the shaped and dried gray fabric is completely immersed in the liquid, the liquid is kept for 15-25 minutes, then the gray fabric is fished out and dried, the liquid containing 1.5-2.5% of resin is uniformly brushed on two sides of the gray fabric by using a hairbrush, and meanwhile, the gray fabric is dried by using a hot air blower;
(9) and (3) detection: and (5) detecting the grey cloth obtained in the step (8) to obtain qualified grey cloth.
As an improvement, the color fixing agent comprises 1-1.5% of polydimethyl allyl sodium chloride, 1-1.5% of hydroxypropyl trimethyl ammonium chloride chitosan, 5-8% of ethanol, 2-2.8% of catalyst and 1.8-2.5% of glacial acetic acid.
Compared with the prior art, the invention has the advantages that: the four-side stretch fabric manufactured by the process has excellent elasticity, can reduce the occurrence of fading, and is simple in process and low in manufacturing cost.
Detailed Description
The present invention is further described below by way of specific examples, but the present invention is not limited to only the following examples. Variations, combinations, or substitutions of the invention, which are within the scope of the invention or the spirit, scope of the invention, will be apparent to those of skill in the art and are within the scope of the invention.
Example one
The four-side elastic fabric and the manufacturing process thereof comprise the following steps:
(1) cloth preparation: adopting gray fabrics of light yarn nylon 70D and spandex 40D for cloth matching;
(2) pretreatment: padding the prepared grey cloth with a padding treatment fluid to a padding rate of 120%, sealing and stacking at room temperature for 18 hours, and washing for 3 times by using clear water;
(3) presetting: shaping the pre-treated grey cloth at the temperature of 150 ℃ and the vehicle speed of 15 m/min to obtain pre-shaped grey cloth;
(4) cloth coiling: c, performing cloth coiling on the pre-shaped grey cloth obtained in the fourth step by using a beam cloth coiling machine, and coiling the cloth subjected to cloth coiling on a beam net pipe at the temperature of 55 ℃ of a water tank, the tension of 4.5 kilograms and the vehicle speed of 50 meters/minute to prepare for dyeing;
(5) dyeing: treating the grey cloth with a refining agent, washing and drying the grey cloth, heating the dye liquor to 50 ℃, putting the grey cloth into the dye liquor, raising the temperature to 80 ℃ at a speed of 2 ℃ for 1 minute, then raising the temperature to 100 ℃ at a speed of 1 ℃ for 3 minutes, preserving the heat of the dye for 40 minutes, cooling, cleaning the cloth, and drying the cloth by hot air at the drying temperature of 50 ℃;
(6) and (3) fixation: pouring a color fixing agent into a color fixing pool, heating liquid in the color fixing pool to 55 ℃, completely immersing the gray fabric into the liquid, heating the liquid to 5 ℃ for 3 minutes until the temperature reaches 90 ℃, preserving the heat for 20 minutes, fishing out the gray fabric, and naturally drying in the shade;
(7) shaping and drying: placing the grey cloth into a baking box, baking at the temperature of 180 ℃, wherein the cloth moving speed is 15 m/min;
(8) and (3) post-treatment: according to the water content, 1.5% of resin is poured into the treatment tank, the shaped and dried gray fabric is completely immersed in the liquid for 15 minutes, then the gray fabric is fished out and dried, the liquid containing 1.5% of resin is uniformly brushed on two sides of the gray fabric by using a hairbrush, and meanwhile, the gray fabric is dried by using an air heater;
(9) and (3) detection: and (5) detecting the grey cloth obtained in the step (8) to obtain qualified grey cloth.
Example two
The four-side elastic fabric and the manufacturing process thereof comprise the following steps:
(1) cloth preparation: adopting gray fabrics of light yarn nylon 70D and spandex 40D for cloth matching;
(2) pretreatment: padding the prepared grey cloth with a padding treatment fluid to a padding allowance of 135%, sealing and stacking at room temperature for 21 hours, and washing for 4 times by using clear water;
(3) presetting: shaping the pre-treated grey cloth at 160 ℃ and at a speed of 20 m/min to obtain a pre-shaped grey cloth;
(4) cloth coiling: c, performing cloth coiling on the pre-shaped grey cloth obtained in the fourth step by using a beam cloth coiling machine, and coiling the cloth subjected to cloth coiling on a beam net pipe at the temperature of 60 ℃ of a water tank, the tension of 5 kilograms and the vehicle speed of 60 meters/minute to prepare for dyeing;
(5) dyeing: treating the grey cloth with a refining agent, washing and drying the grey cloth, heating a dye solution to 50 ℃, putting the grey cloth into the dye solution, heating the grey cloth to 80 ℃ at a speed of 2 ℃ for 2 minutes, then heating the grey cloth to 100 ℃ at a speed of 1 ℃ for 4 minutes, preserving the heat of the dye for 45 minutes, cooling, cleaning the cloth, and drying the cloth by hot air at a drying temperature of 55 ℃;
(6) and (3) fixation: pouring a color fixing agent into a color fixing pool, heating liquid in the color fixing pool to 55 ℃, completely immersing the gray fabric into the liquid, heating the liquid for 4 minutes to 5 ℃ till 90 ℃, preserving the temperature for 30 minutes, fishing out the gray fabric, and naturally drying in the shade;
(7) shaping and drying: placing the grey cloth into a baking box, baking at 185 ℃, wherein the cloth moving speed is 18 m/min;
(8) and (3) post-treatment: according to the water content, 2% of resin is poured into the treatment tank, the shaped and dried gray fabric is completely immersed in the liquid for 20 minutes, then the gray fabric is fished out and dried, the liquid containing 2% of resin is uniformly brushed on two sides of the gray fabric by using a hairbrush, and meanwhile, an air heater is used for drying the gray fabric;
(9) and (3) detection: and (5) detecting the grey cloth obtained in the step (8) to obtain qualified grey cloth.
EXAMPLE III
The four-side elastic fabric and the manufacturing process thereof comprise the following steps:
(1) cloth preparation: adopting gray fabrics of light yarn nylon 70D and spandex 40D for cloth matching;
(2) pretreatment: padding the prepared grey cloth with a padding treatment fluid to a padding allowance of 150%, sealing and stacking at room temperature for 24 hours, and washing for 5 times by using clear water;
(3) presetting: shaping the pre-treated grey cloth at the temperature of 170 ℃ and the vehicle speed of 25 m/min to obtain pre-shaped grey cloth;
(4) cloth coiling: c, performing cloth coiling on the pre-shaped grey cloth obtained in the fourth step by using a beam cloth coiling machine, and coiling the cloth subjected to cloth coiling on a beam net pipe at the water tank temperature of 65 ℃, the tension of 5.5 kg and the vehicle speed of 70 m/min to prepare for dyeing;
(5) dyeing: treating the grey cloth with a refining agent, washing and drying the grey cloth, heating a dye solution to 50 ℃, putting the grey cloth into the dye solution, heating the grey cloth to 80 ℃ at a speed of 2 ℃ for 3 minutes, then heating the grey cloth to 100 ℃ at a speed of 1 ℃ for 5 minutes, preserving the heat of the dye for 50 minutes, cleaning the cloth after cooling, and drying the cloth by hot air at a drying temperature of 60 ℃;
(6) and (3) fixation: pouring a color fixing agent into a color fixing pool, heating liquid in the color fixing pool to 55 ℃, completely immersing the gray fabric into the liquid, heating the liquid to 5 ℃ for 5 minutes until the temperature reaches 90 ℃, preserving the heat for 40 minutes, fishing out the gray fabric, and naturally drying in the shade;
(7) shaping and drying: placing the grey cloth into a baking box, baking at the temperature of 190 ℃, wherein the cloth moving speed is 20 m/min;
(8) and (3) post-treatment: according to the water content, 2.5% of resin is poured into the treatment tank, the shaped and dried gray fabric is completely immersed in the liquid for 25 minutes, then the gray fabric is fished out and dried, the liquid containing 2.5% of resin is uniformly brushed on two sides of the gray fabric by using a hairbrush, and meanwhile, the gray fabric is dried by using an air heater;
(9) and (3) detection: and (5) detecting the grey cloth obtained in the step (8) to obtain qualified grey cloth.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the present invention, and any modifications, equivalents and improvements made within the spirit and principle of the present invention should be included in the scope of the present invention.
Claims (2)
1. The four-side elastic fabric and the manufacturing process thereof are characterized by comprising the following steps:
(1) cloth preparation: adopting gray fabrics of light yarn nylon 70D and spandex 40D for cloth matching;
(2) pretreatment: padding the prepared grey cloth with a padding treatment fluid with a rolling residual rate of 120-150%, sealing and stacking at room temperature, stacking for 18-24 hours, and washing for 3-5 times by using clear water;
(3) presetting: shaping the pre-treated grey cloth at the temperature of 150-170 ℃ and the vehicle speed of 15-25 m/min to obtain pre-shaped grey cloth;
(4) cloth coiling: c, performing cloth coiling on the pre-shaped grey cloth obtained in the fourth step by using a beam cloth coiling machine, coiling the cloth subjected to cloth coiling on a beam net pipe at the temperature of 55-65 ℃ of a water tank, the tension of 4.5-5.5 kg and the vehicle speed of 50-70 m/min, and preparing for dyeing;
(5) dyeing: treating the grey cloth with a refining agent, washing and drying the grey cloth, heating the dye liquor to 50 ℃, putting the grey cloth into the dye liquor, raising the temperature to 80 ℃ at a speed of raising the temperature by 2 ℃ for 1-3 minutes, then raising the temperature to 100 ℃ at a speed of raising the temperature by 1 ℃ for 3-5 minutes, preserving the heat of the dye for 40-50 minutes, cooling, cleaning the cloth, and drying the cloth by hot air at a temperature of 50-60 ℃;
(6) and (3) fixation: pouring a color fixing agent into a color fixing pool, heating liquid in the color fixing pool to 55 ℃, completely immersing the gray fabric into the liquid, heating the liquid for 3-5 minutes to 5 ℃ until the temperature reaches 90 ℃, preserving the heat for 20-40 minutes, fishing out the gray fabric, and naturally drying in the shade;
(7) shaping and drying: placing the grey cloth into a baking box, baking at the temperature of 180-190 ℃, wherein the cloth moving speed is 15-20 m/min;
(8) and (3) post-treatment: according to the water content, 1.5-2.5% of resin is poured into the treatment tank, the shaped and dried gray fabric is completely immersed in the liquid, the liquid is kept for 15-25 minutes, then the gray fabric is fished out and dried, the liquid containing 1.5-2.5% of resin is uniformly brushed on two sides of the gray fabric by using a hairbrush, and meanwhile, the gray fabric is dried by using a hot air blower;
(9) and (3) detection: and (5) detecting the grey cloth obtained in the step (8) to obtain qualified grey cloth.
2. The four-side stretch fabric and the manufacturing process thereof according to claim 1, characterized in that: the color fixing agent comprises 1-1.5% of polydimethyl allyl sodium chloride, 1-1.5% of hydroxypropyl trimethyl ammonium chloride chitosan, 5-8% of ethanol, 2-2.8% of catalyst and 1.8-2.5% of glacial acetic acid.