CN111961788A - 一种低钒高碳铬铁的冶炼工艺 - Google Patents

一种低钒高碳铬铁的冶炼工艺 Download PDF

Info

Publication number
CN111961788A
CN111961788A CN202010792606.9A CN202010792606A CN111961788A CN 111961788 A CN111961788 A CN 111961788A CN 202010792606 A CN202010792606 A CN 202010792606A CN 111961788 A CN111961788 A CN 111961788A
Authority
CN
China
Prior art keywords
carbon ferrochrome
vanadium
converter
low
smelting process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010792606.9A
Other languages
English (en)
Inventor
罗洪杰
龚晓俅
邵珠航
王应青
王德清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuzhou Hongyang New Material Technology Co ltd
Original Assignee
Xuzhou Hongyang New Material Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuzhou Hongyang New Material Technology Co ltd filed Critical Xuzhou Hongyang New Material Technology Co ltd
Priority to CN202010792606.9A priority Critical patent/CN111961788A/zh
Publication of CN111961788A publication Critical patent/CN111961788A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种低钒高碳铬铁的冶炼工艺，包括如下步骤：(1)使用中频感应炉熔化高碳铬铁合金；(2)将铁水导入转炉，由转炉上安装的顶底复吹系统对铁水进行降钒处理。所述顶底复吹系统包括安装在转炉顶部和底部的氧枪；其中，底部氧枪持续喷吹惰性气体，顶部持续喷吹氧化性气体。本发明一种低钒高碳铬铁的冶炼工艺，有效地降低了高碳铬铁中的钒含量，提高了高碳铬铁的韧性。

Description

一种低钒高碳铬铁的冶炼工艺
技术领域
本发明涉及金属冶炼领域，具体是一种低钒高碳铬铁的冶炼工艺。
背景技术
在轴承钢生产过程中钛与溶解在钢液中的氮结合生成几乎不溶于钢液中的氮化钛。氮化钛的熔点高达2930℃，在钢液冷却过程中，其呈弥漫分布而夹杂在钢锭中。由于氮化钛的硬度较大，使得轴承钢的使用寿命受到影响。同样，钒无减低回火脆性的作用，因为钒可提高回火稳定性，可细化晶粒，所以当钒量不高时，也可适当提高韧性，而降低回火脆性。钒有阻碍钢的脱碳及石墨化的作用。钒含量达0.05％时将使硅钢矫顽力降低。
发明内容
本发明的目的是提供一种低钒高碳铬铁的冶炼工艺，可以有效降低高碳铬铁中的钒含量。
本发明采用的技术方案是：一种低钒高碳铬铁的冶炼工艺，包括如下步骤：
(1)使用中频感应炉熔化高碳铬铁合金；
(2)将铁水导入转炉，由转炉上安装的顶底复吹系统对铁水进行降钒处理。
进一步地，所述顶底复吹系统包括安装在转炉顶部和底部的氧枪；其中，底部氧枪持续喷吹惰性气体，顶部持续喷吹氧化性气体。
进一步地，所述顶部氧枪喷吹粉末状氧化剂。
优选地，所述粉末氧化剂包括二氧化锰、氧化铁或氧化铬中的一种或以上。
本发明一种低钒高碳铬铁的冶炼工艺，有效地降低了高碳铬铁中的钒含量，提高了高碳铬铁的韧性。
具体实施方式
下面结合实施例对本发明作进一步详细说明。
实施例
冶炼一批高碳铬铁，包括如下步骤：
(1)使用中频感应炉熔化高碳铬铁合金；
(2)将铁水导入转炉，由转炉上安装的顶底复吹系统对铁水进行降钒处理。
所述顶底复吹系统包括安装在转炉顶部和底部的氧枪；其中，底部氧枪持续喷吹惰性气体，所述顶部氧枪喷吹粉末状氧化剂。所述粉末氧化剂为二氧化锰。

Claims (4)

1.一种低钒高碳铬铁的冶炼工艺，其特征在于，包括如下步骤：
(1)使用中频感应炉熔化高碳铬铁合金；
(2)将铁水导入转炉，由转炉上安装的顶底复吹系统对铁水进行降钒处理。
2.根据权利要求1所述的一种低钒高碳铬铁的冶炼工艺，其特征在于，所述顶底复吹系统包括安装在转炉顶部和底部的氧枪；其中，底部氧枪持续喷吹惰性气体，顶部持续喷吹氧化性气体。
3.根据权利要求2所述的一种低钒高碳铬铁的冶炼工艺，其特征在于，所述顶部氧枪喷吹粉末状氧化剂。
4.根据权利要求3所述的一种低钒高碳铬铁的冶炼工艺，其特征在于，所述粉末氧化剂包括二氧化锰、氧化铁或氧化铬中的一种或以上。
CN202010792606.9A 2020-08-09 2020-08-09 一种低钒高碳铬铁的冶炼工艺 Pending CN111961788A (zh)