CN111850763A - 一种锦氨磁疗保健空气包覆丝 - Google Patents
一种锦氨磁疗保健空气包覆丝 Download PDFInfo
- Publication number
- CN111850763A CN111850763A CN202010760404.6A CN202010760404A CN111850763A CN 111850763 A CN111850763 A CN 111850763A CN 202010760404 A CN202010760404 A CN 202010760404A CN 111850763 A CN111850763 A CN 111850763A
- Authority
- CN
- China
- Prior art keywords
- nylon
- air
- spandex
- yarn
- physiotherapy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及合成纤维空气包覆丝技术领域，特别涉及一种锦氨磁疗保健空气包覆丝。该空气包覆丝采用聚酰胺切片和磁石理疗母粒制备而成，所述磁石理疗母粒，按重量百分比包括以下原料：碳化复合磁石15‑25%、砭石微粉5‑15%、硬脂酸锌1.5‑3%、SanstabTPO330 0.5‑0.8%、季戊四醇硬脂酸酯1‑3%，余量为锦纶6切片。本申请所生产的锦氨磁疗保健空气包覆丝产品具有促进血液循环、吸湿快干等功能，是一种很有潜力的功能性锦氨空气包覆丝产品，可满足制作高档服装的需求，可取代低端的锦氨包覆丝产品，提高公司产品竞争力，收获更好的经济效益。
Description
技术领域
本发明涉及合成纤维空气包覆丝技术领域，特别涉及一种锦氨磁疗保健空气包覆丝。
背景技术
随着合成纤维纺丝技术的进步和人们消费水平的提高，人们对合成纤维及其纺织品的特性提出了新的要求。包覆丝作为一种新的合成纤维，市场对此类产品的需求量很大。锦氨空气包覆丝是近年来市场上较为流行的一种特色纱线。它是以氨纶丝为芯，与锦纶长丝包缠复合而成。氨纶和锦纶的交织，不仅可以使织物可在常温常压下染色，避免高温高压对织物的损伤，而且使得针织物具有吸湿透气，手感柔软、有弹性和回复性，满足了人们对服装穿着舒适，贴身和保持外形不变的要求，被广泛用于袜品、内衣、运动衣等。
锦氨空气包覆丝作为一类越来越受市场接受的锦纶产品，其具有较高的强度、弹性，而且耐磨性好，但随着人们生活水平的不断提高，人们对服饰的多样性、舒适性、功能性要求越来越广泛。纤维细旦化、功能化是锦氨空气包覆丝产品的必然趋势。
同时，人们对健康养生的关注也随着生活水平的不断提高而不断增高。因此，开发一种差异化的新产品，不仅能够提高公司的产品竞争力，还能够丰富市场，使市场的产品更加多样化。
如果从健康养生角度对锦氨空气包覆丝进行功能化开发，开发出一种功能性的产品，具有非常大的意义。
发明内容
本发明的目的是为了提供一种锦氨磁疗保健空气包覆丝，通过该产来丰富市场的产品多样化，同时，提高公司的产品竞争力，以便于收获更好的的经济效益。
本发明所采用的具体技术方案是：
一种锦氨磁疗保健空气包覆丝，该空气包覆丝采用聚酰胺切片和磁石理疗母粒制备而成，所述磁石理疗母粒，按重量百分比包括以下原料：碳化复合磁石15-25%、砭石微粉5-15%、硬脂酸锌1.5-3%、 SanstabTPO330 0.5-0.8%、季戊四醇硬脂酸酯1-3%，余量为锦纶6切片。
作为优选，所述磁石理疗母粒的加入量为原料总量的2-5%。
作为优选，所述锦纶磁疗保健空气包覆丝的制备工艺如下：
（1）熔融纺丝：将聚酰胺切片和磁石理疗母粒在氮气保护条件下喂入料仓，进入双螺杆挤出机，在挤出机内经过各区段加热、在250-260℃熔融混合均匀后，通过喷丝板熔融纺丝；
（2）侧吹风冷却：在温度为16-25℃，湿度为70-80%，风速为0.4-0.6m/s的条件下侧吹风冷却成型；
（3）上油集束：经侧吹风冷却的纤维经上油装置的油雾喷嘴上油集束，上油率为0.6%；
（4）卷绕：上油丝束经预网络器、导丝盘、主网络器，开始卷绕纺丝，纺丝速度为680m/min,得到POY长丝；
（5）空气包覆：在空气包覆机上以氨纶为芯，与上述制备得到的POY长丝包覆合成锦纶磁疗保健空气包覆丝。
作为优选，步骤（3）中所用油剂按重量百分比包括：癸二酸二辛脂50-55%、油酸乙酯磺酸钾20-28%、仲烷基醇聚氧乙烯醚5-8%、三乙醇胺0.5-0.6%、油酸3-8%、渗透剂2-5%、椰子油乙二醇酰胺1-3%；水余量。
作为优选，步骤（5）的具体工艺为：
将氨纶丝经由喂丝罗拉、止捻器、牵伸罗拉、变形热箱加热进入牵伸罗拉，再进入冷却装置，假捻引出后经过牵伸处理，变形热箱的温度为175-178℃；冷却装置中冷却温度为5-10℃；牵伸处理采用三段牵伸法，牵伸倍数为依次为1.5倍、2倍和1.5倍；
然后作为芯纱，以上述制备得到的多根POY长丝为外包纱，经过网络喷嘴的气流将POY长丝和氨纶丝包缠在一起，通过牵伸罗拉、变形热箱加热，进入牵伸罗拉，冷却装置，再通过上油罗拉上油后收卷，制成锦纶磁疗保健空气包覆丝；牵伸倍数为1.3-1.5倍，变形热箱的温度为190-200℃，再次牵伸倍数为1.1-1.5倍，冷却温度为10-15℃。
作为优选，所述氨纶丝为十字异形氨纶丝。
本发明的有益效果是：本申请所生产的锦氨磁疗保健空气包覆丝产品具有促进血液循环、吸湿快干等功能，是一种很有潜力的功能性锦氨空气包覆丝产品，可满足制作高档服装的需求，可取代低端的锦氨包覆丝产品，提高公司产品竞争力，收获更好的经济效益。
具体实施方式
现在将进一步细化代表性实施方案。应当理解，以下描述并非旨在将实施方案限制于一个优选实施方案。相反，其旨在涵盖可被包括在由所附权利要求限定的所述实施方案的实质和范围内的替代形式、修改形式和等同形式。
以下实施例中，若非特指，所采用的原料和设备均可从市场购得或是本领域常规所用的；所用的方法，如无特别说明，均为本领域的常规方法。
实施例1：
首先，是制备磁石理疗母粒，采用螺杆挤出机采用常规工艺按照以下配比挤出造粒，碳化复合磁石15%、砭石微粉15%、硬脂酸锌1.5%、 SanstabTPO330 0.8%、季戊四醇硬脂酸酯1%，余量为锦纶6切片。
然后按照以下制备工艺制备包覆丝：
（1）熔融纺丝：将聚酰胺切片和磁石理疗母粒在氮气保护条件下喂入料仓，进入双螺杆挤出机，在挤出机内经过各区段加热、在250-260℃熔融混合均匀后，通过喷丝板熔融纺丝；磁石理疗母粒的加入量为原料总量的5%。
（2）侧吹风冷却：在温度为16℃，湿度为80%，风速为0.4m/s的条件下侧吹风冷却成型。
（3）上油集束：经侧吹风冷却的纤维经上油装置的油雾喷嘴上油集束，上油率为0.6%；所用油剂按重量百分比包括：癸二酸二辛脂50%、油酸乙酯磺酸钾28%、仲烷基醇聚氧乙烯醚5%、三乙醇胺0.6%、油酸3%、渗透剂5%、椰子油乙二醇酰胺1%；水余量。
（4）卷绕：上油丝束经预网络器、导丝盘、主网络器，开始卷绕纺丝，纺丝速度为680m/min,得到POY长丝。
（5）空气包覆：在空气包覆机上以氨纶为芯，与上述制备得到的POY长丝包覆合成锦纶磁疗保健空气包覆丝，氨纶丝为十字异形氨纶丝；具体工艺为：
将氨纶丝经由喂丝罗拉、止捻器、牵伸罗拉、变形热箱加热进入牵伸罗拉，再进入冷却装置，假捻引出后经过牵伸处理，变形热箱的温度为175-178℃；冷却装置中冷却温度为10℃；牵伸处理采用三段牵伸法，牵伸倍数为依次为1.5倍、2倍和1.5倍；
然后作为芯纱，以上述制备得到的多根POY长丝为外包纱，经过网络喷嘴的气流将POY长丝和氨纶丝包缠在一起，通过牵伸罗拉、变形热箱加热，进入牵伸罗拉，冷却装置，再通过上油罗拉上油后收卷，制成锦纶磁疗保健空气包覆丝；牵伸倍数为1.3-1.5倍，变形热箱的温度为190-200℃，再次牵伸倍数为1.1-1.5倍，冷却温度为15℃。
实施例2：
首先，是制备磁石理疗母粒，采用螺杆挤出机采用常规工艺按照以下配比挤出造粒，碳化复合磁石25%、砭石微粉5%、硬脂酸锌3%、 SanstabTPO330 0.5%、季戊四醇硬脂酸酯3%，余量为锦纶6切片。
然后按照以下制备工艺制备包覆丝：
（1）熔融纺丝：将聚酰胺切片和磁石理疗母粒在氮气保护条件下喂入料仓，进入双螺杆挤出机，在挤出机内经过各区段加热、在250-260℃熔融混合均匀后，通过喷丝板熔融纺丝；磁石理疗母粒的加入量为原料总量的3%。
（2）侧吹风冷却：在温度为25℃，湿度为70%，风速为0.6m/s的条件下侧吹风冷却成型。
（3）上油集束：经侧吹风冷却的纤维经上油装置的油雾喷嘴上油集束，上油率为0.6%；所用油剂按重量百分比包括：癸二酸二辛脂55%、油酸乙酯磺酸钾20%、仲烷基醇聚氧乙烯醚8%、三乙醇胺0.5%、油酸8%、渗透剂2%、椰子油乙二醇酰胺3%；水余量。
（4）卷绕：上油丝束经预网络器、导丝盘、主网络器，开始卷绕纺丝，纺丝速度为680m/min,得到POY长丝。
（5）空气包覆：在空气包覆机上以氨纶为芯，与上述制备得到的POY长丝包覆合成锦纶磁疗保健空气包覆丝，氨纶丝为十字异形氨纶丝；具体工艺为：
将氨纶丝经由喂丝罗拉、止捻器、牵伸罗拉、变形热箱加热进入牵伸罗拉，再进入冷却装置，假捻引出后经过牵伸处理，变形热箱的温度为175-178℃；冷却装置中冷却温度为8℃；牵伸处理采用三段牵伸法，牵伸倍数为依次为1.5倍、2倍和1.5倍；
然后作为芯纱，以上述制备得到的多根POY长丝为外包纱，经过网络喷嘴的气流将POY长丝和氨纶丝包缠在一起，通过牵伸罗拉、变形热箱加热，进入牵伸罗拉，冷却装置，再通过上油罗拉上油后收卷，制成锦纶磁疗保健空气包覆丝；牵伸倍数为1.3-1.5倍，变形热箱的温度为190-200℃，再次牵伸倍数为1.1-1.5倍，冷却温度为10℃。
实施例3：
首先，是制备磁石理疗母粒，采用螺杆挤出机采用常规工艺按照以下配比挤出造粒，碳化复合磁石18%、砭石微粉12%、硬脂酸锌2%、 SanstabTPO330 0.8%、季戊四醇硬脂酸酯2%，余量为锦纶6切片。
然后按照以下制备工艺制备包覆丝：
（1）熔融纺丝：将聚酰胺切片和磁石理疗母粒在氮气保护条件下喂入料仓，进入双螺杆挤出机，在挤出机内经过各区段加热、在250-260℃熔融混合均匀后，通过喷丝板熔融纺丝；磁石理疗母粒的加入量为原料总量的4%。
（2）侧吹风冷却：在温度为20℃，湿度为70%，风速为0.6m/s的条件下侧吹风冷却成型。
（3）上油集束：经侧吹风冷却的纤维经上油装置的油雾喷嘴上油集束，上油率为0.6%；所用油剂按重量百分比包括：癸二酸二辛脂50%、油酸乙酯磺酸钾20%、仲烷基醇聚氧乙烯醚8%、三乙醇胺0.5%、油酸8%、渗透剂2%、椰子油乙二醇酰胺3%；水余量。
（4）卷绕：上油丝束经预网络器、导丝盘、主网络器，开始卷绕纺丝，纺丝速度为680m/min,得到POY长丝。
（5）空气包覆：在空气包覆机上以氨纶为芯，与上述制备得到的POY长丝包覆合成锦纶磁疗保健空气包覆丝，氨纶丝为十字异形氨纶丝；具体工艺为：
将氨纶丝经由喂丝罗拉、止捻器、牵伸罗拉、变形热箱加热进入牵伸罗拉，再进入冷却装置，假捻引出后经过牵伸处理，变形热箱的温度为175-178℃；冷却装置中冷却温度为5-10℃；牵伸处理采用三段牵伸法，牵伸倍数为依次为1.5倍、2倍和1.5倍；
然后作为芯纱，以上述制备得到的多根POY长丝为外包纱，经过网络喷嘴的气流将POY长丝和氨纶丝包缠在一起，通过牵伸罗拉、变形热箱加热，进入牵伸罗拉，冷却装置，再通过上油罗拉上油后收卷，制成锦纶磁疗保健空气包覆丝；牵伸倍数为1.3-1.5倍，变形热箱的温度为190-200℃，再次牵伸倍数为1.1-1.5倍，冷却温度为10-15℃。
本发明制备的产品通过测试后的性能指标如下：
纤度变异系数CV%≤1.20，断裂强度≥3.20cN/dtex，断裂强度变异系数CV%≤8.20%，断裂伸长率M1±3%，断裂伸长率变异系数≤10.0%，染色均匀度≥4级，网络度≥90个/米。
将上述的包覆纱制成面料后，穿着该产品制成的衣物能够吸收人体向外发散的热量并反射回人体需要的4-14μm波长的远红外线，促进人体的血液循环和新陈代谢，锦纶磁疗保健空气包覆丝产品同时还具有吸湿快干和优良的热效应功能等特点。
对于本领域技术人员而言显而易见的是，实施上述实施方案不需要这些具体细节。因此，出于说明和描述的目的呈现了对本文所述的具体实施方案的上述描述。对于本领域技术人员而言显而易见的是，在上述教导内容的基础，还能够进行一定的修改、组合和以及变型。
Claims (6)
1.一种锦氨磁疗保健空气包覆丝，其特征在于：该空气包覆丝采用聚酰胺切片和磁石理疗母粒制备而成，所述磁石理疗母粒，按重量百分比包括以下原料：碳化复合磁石15-25%、砭石微粉5-15%、硬脂酸锌1.5-3%、 SanstabTPO330 0.5-0.8%、季戊四醇硬脂酸酯1-3%，余量为锦纶6切片。
2.根据权利要求1所述的一种锦纶磁疗保健空气包覆丝，其特征在于：所述磁石理疗母粒的加入量为原料总量的2-5%。
3.根据权利要求1所述的一种锦纶磁疗保健空气包覆丝，其特征在于：所述锦纶磁疗保健空气包覆丝的制备工艺如下：
（1）熔融纺丝：将聚酰胺切片和磁石理疗母粒在氮气保护条件下喂入料仓，进入双螺杆挤出机，在挤出机内经过各区段加热、在250-260℃熔融混合均匀后，通过喷丝板熔融纺丝；
（2）侧吹风冷却：在温度为16-25℃，湿度为70-80%，风速为0.4-0.6m/s的条件下侧吹风冷却成型；
（3）上油集束：经侧吹风冷却的纤维经上油装置的油雾喷嘴上油集束，上油率为0.6%；
（4）卷绕：上油丝束经预网络器、导丝盘、主网络器，开始卷绕纺丝，纺丝速度为680m/min,得到POY长丝；
（5）空气包覆：在空气包覆机上以氨纶为芯，与上述制备得到的POY长丝包覆合成锦纶磁疗保健空气包覆丝。
4.根据权利要求3所述的一种锦纶磁疗保健空气包覆丝，其特征在于：步骤（3）中所用油剂按重量百分比包括：癸二酸二辛脂50-55%、油酸乙酯磺酸钾20-28%、仲烷基醇聚氧乙烯醚5-8%、三乙醇胺0.5-0.6%、油酸3-8%、渗透剂2-5%、椰子油乙二醇酰胺1-3%；水余量。
5.根据权利要求3所述的一种锦纶磁疗保健空气包覆丝，其特征在于：步骤（5）的具体工艺为：
将氨纶丝经由喂丝罗拉、止捻器、牵伸罗拉、变形热箱加热进入牵伸罗拉，再进入冷却装置，假捻引出后经过牵伸处理，变形热箱的温度为175-178℃；冷却装置中冷却温度为5-10℃；牵伸处理采用三段牵伸法，牵伸倍数为依次为1.5倍、2倍和1.5倍；
然后作为芯纱，以上述制备得到的多根POY长丝为外包纱，经过网络喷嘴的气流将POY长丝和氨纶丝包缠在一起，通过牵伸罗拉、变形热箱加热，进入牵伸罗拉，冷却装置，再通过上油罗拉上油后收卷，制成锦纶磁疗保健空气包覆丝；牵伸倍数为1.3-1.5倍，变形热箱的温度为190-200℃，再次牵伸倍数为1.1-1.5倍，冷却温度为10-15℃。
6.根据权利要求3所述的一种锦纶磁疗保健空气包覆丝，其特征在于：所述氨纶丝为十字异形氨纶丝。