CN111808475B - 用于在无孔基材上进行喷墨印刷的水性油墨组合物 - Google Patents

用于在无孔基材上进行喷墨印刷的水性油墨组合物 Download PDF

Info

Publication number
CN111808475B
CN111808475B CN202010195646.5A CN202010195646A CN111808475B CN 111808475 B CN111808475 B CN 111808475B CN 202010195646 A CN202010195646 A CN 202010195646A CN 111808475 B CN111808475 B CN 111808475B
Authority
CN
China
Prior art keywords
latex
ink composition
aqueous ink
primary
functionalized
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202010195646.5A
Other languages
English (en)
Other versions
CN111808475A (zh
Inventor
C·雷赛特克
S·阿里
C·布朗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xerox Corp
Original Assignee
Xerox Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xerox Corp filed Critical Xerox Corp
Publication of CN111808475A publication Critical patent/CN111808475A/zh
Application granted granted Critical
Publication of CN111808475B publication Critical patent/CN111808475B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明题为“用于在无孔基材上进行喷墨印刷的水性油墨组合物”。本发明公开了一种用于在无孔基材上进行喷墨印刷的水性油墨组合物及一种用于形成该水性油墨组合物的方法。例如，该方法包括制备具有芳族官能团、氢键基团、柔性侧链和离子官能团的初级聚合物胶乳，并且将初级聚合物胶乳与次级胶乳粘合剂和一种或多种共溶剂混合。

Description

用于在无孔基材上进行喷墨印刷的水性油墨组合物
本公开整体涉及一种油墨组合物，并且更具体地讲，涉及一种用于在无孔基材上进行喷墨印刷的带有具有低毒性的组分的水性油墨组合物以及用于制备该水性油墨组合物的方法。
背景技术
数字印刷，具体地讲油墨的喷墨印刷可以在多孔纸基材上进行。油墨可以干燥并保持到多孔纸基材上而不会产生涂污。用于喷墨印刷的油墨可以具有某些属性，以允许通过喷墨打印机中使用的印刷头来控制和喷射油墨。喷墨打印机可以被数字地控制以从印刷头的喷嘴分配或喷射油墨。
由于在包装中使用了塑料膜，因此在无孔基材上进行印刷是期望的。对于某些包装，诸如食品包装，油墨必须具有低毒性以防止油墨组分的迁移可能引起的潜在健康问题。然而，可以被印刷在无孔基材上的喷墨油墨(诸如UV固化油墨)具有化学组分，该化学组分可以从包装迁移到产品中并对消费者造成影响。另选地，当前可用的具有低毒性的水性油墨不能有效地印刷在无孔基材上。
发明内容
根据本文所示的各方面，提供了一种用于在无孔基材上进行喷墨印刷的具有低毒性的水性油墨组合物以及形成该水性油墨组合物的方法。实施方案的一个公开特征是一种方法，该方法包括制备具有芳族官能团、氢键基团、柔性侧链和离子官能团的初级聚合物胶乳，并且将初级聚合物胶乳与次级胶乳粘合剂和一种或多种共溶剂混合。
实施方案的另一公开的特征是在无孔基材上的低毒性水性油墨组合物。在一个实施方案中，低毒性水性油墨组合物包含5重量％-40重量％的官能化低毒性初级胶乳、5重量％-20重量％的次级胶乳粘合剂、以及一种或多种共溶剂。官能化低毒性初级胶乳包含芳族官能团、氢键基团、柔性侧链和离子官能团。低毒性水性油墨组合物在25摄氏度下的粘度低于10毫帕·秒(mPa·s)。
附图说明
通过结合附图考虑以下具体实施方式可以容易地理解本公开的教学内容，在附图中：
图1示出了本公开的官能化胶乳的示例性结构；
图2示出了本公开的具有强氢键的示例性官能团；
图3示出了本公开的离子稳定的不含表面活性剂的胶乳的示例；并且
图4示出了用于形成用于在本公开的无孔基材上进行喷墨印刷的水性油墨组合物的示例性方法的流程图；并且
为了便于理解，在可能的情况下已经使用了相同的附图标号来指定附图共有的相同元件。
具体实施方式
本公开提供了一种用于在无孔基材上进行喷墨印刷的、含有具有低毒性的组分的水性油墨组合物以及用于制备该水性油墨组合物的方法。如上所述，可能期望的是在无孔基材(诸如塑料)上使用喷墨印刷。然而，当前可用于喷墨印刷的可用油墨包含潜在有害的化学组分或不可用于无孔基材上，因为油墨可能会涂污或不能粘附在无孔基材上。
本公开提供了一种具有低毒性的水基油墨组合物。该水基油墨组合物可以用于印刷在食品应用中使用的无孔基材(诸如塑料包装)上。此外，水基油墨组合物具有诸如低粘度和期望的粒径的属性，该属性允许油墨用于喷墨印刷头或打印机中。
本公开的实施方案提供包含若干胶乳和/或粘合剂的水性油墨组合物，该水性油墨组合物在塑料基材上提供油墨的增强作用。因此，这些油墨在塑料基材上具有良好的成膜性、具有对塑料膜的良好粘附性、并且是耐摩擦的。
在一个实施方案中，低毒性水性油墨组合物可以包含低毒性官能化初级胶乳和次级胶乳或粘合剂。水性油墨组合物可以与水基溶液中的一种或多种共溶剂和添加剂组合。
在一个实施方案中，初级胶乳可以是低毒性胶乳，其可以用于与食品间接接触的无孔或塑料包装材料中。低毒性初级胶乳的示例可以包含利用氨稳定的、粒径为100纳米-300纳米(nm)的聚苯乙烯共聚物。根据联邦法规175.330，低毒性初级胶乳可以由用于食品接触物质的间接添加剂清单上的聚合物组成。示例性聚苯乙烯共聚物可以包含聚(马来酸酐-苯乙烯)。
此外，初级胶乳可以具有低毒性，因为胶乳可以是水基的并且不含通常在紫外(UV)固化油墨中使用的任何催化剂或(光)引发剂。此外，整个水性油墨组合物可以使用具有低毒性的共溶剂(例如丙二醇，诸如丙二醇甲基醚、丙二醇正丙基醚、二丙二醇甲醚)。
可以将初级胶乳官能化以具有某些特性，以允许水性油墨组合物用于喷墨打印机并印刷到无孔基材上。无孔基材可以包括塑料膜，该塑料膜包括柔性和/或可拉伸的塑料膜。塑料类型可以包含在包装中无处不在的聚烯烃材料，诸如聚对苯二甲酸乙二醇酯、聚苯乙烯、聚乙烯和聚丙烯。其他无孔基材可以包括金属(例如，钢、铝等)或玻璃。
在一个实施方案中，初级胶乳可以被官能化或处理以包含四种主要的化学官能团。例如，初级胶乳可以与提供不同化学官能团的不同分子混合或化学改性。官能团可以包含芳族官能团、氢键基团、柔性侧链和离子官能团。芳族官能团可以用于成膜。芳族官能团可以包含苯乙烯、邻苯二甲酸盐、吡咯烷酮等。
氢键基团可以在无孔基材上提供油墨的机械增强作用。换句话讲，氢键基团可以有助于水基油墨组合物在被印刷到无孔基材上时为耐摩擦的，并且提供对无孔基材的良好粘附性。
初级胶乳可以利用包含强氢键基团(诸如羟基、胺和酰胺)的分子官能化。分子可以包含耦接到环状分子和/或芳族分子的酰胺官能团。示例分子可以包含尿素、尿囊素、酪胺、葡萄糖、丙烯酰基呋喃葡萄糖(MAGP)、N-[三(羟甲基)甲基]丙烯酰胺、丙烯酰胺基苯硼酸、氨基乙基甲基丙烯酰胺、丙烯酰吗啉、丙烯酸乙酰氧苯乙酯等。
可以掺入聚合物胶乳中的柔性侧链，以更好地与柔性基材(诸如塑料膜)相容。柔性侧链的示例可以包括含烷基分子(例如丁基、己基、辛基、癸基等，以及相关的异构体，诸如异烷基、仲烷基或叔烷基)。此类烷基的示例可以包含丙烯酸异丁酯、丙烯酸(异)辛酯、丙烯酸异癸酯等。
聚合物胶乳中的离子官能团可以赋予聚合物胶乳颗粒在水溶液中的稳定性，并且由于胶乳颗粒之间的静电排斥而具有低粘度。例如，在25摄氏度(℃)下，官能化初级胶乳在水中的重量百分比为30重量％(wt％)时，其粘度可以低于20毫帕·秒(mPa·s)。在一个示例中，粘度在25℃下可以低于10Cps。另外，初级胶乳中的离子官能团可以使得不含表面活性剂的聚合物自乳化，这增强了初级胶乳的稳定性，因为通常使用的表面活性剂不能被解吸和/或被不稳定化。
离子官能团可以确保初级胶乳在水和水溶液中保持稳定。离子官能团可以防止在水中的聚集、絮凝、成浆、沉淀和/或析出。
在一个实施方案中，可以掺入到初级胶乳中的离子官能团可以包含羧酸、磺酸和相关的盐，诸如铵。具有离子官能团的起始单体的附加示例可以包含丙烯酸、乙基丙烯酸、甲基丙烯酸、甲基丙烯酸、丙烯酸磺丙酯、[2-(丙烯酰氧基)乙基]三甲基氯化铵等。
可以通过将含胺的分子与聚(马来酸酐-苯乙烯)的亲核加成反应来合成具有上述不同官能团的不同分子。不同水性油墨组合物的示例更详细地描述于下文中。
在一个实施方案中，官能化初级胶乳的分子量可以介于约1000道尔顿至100000道尔顿(Da)之间。在一个示例中，具有较低重量(例如，大约2000Da)的聚合物可以允许胶乳更容易分散在水中并形成具有较低多分散性指数(例如，<0.2)的小颗粒(例如，<大约150nm-200nm)。另一方面，具有更高分子量的聚合物由于更大的链缠结而可以提供更好的机械属性。
在一个实施方案中，聚合物胶乳中每个官能团的含量可以在5wt％-80wt％的范围内。在一个实施方案中，聚合物胶乳中的苯乙烯含量可以为至少50wt％或更大，以获得基材上最终水性油墨组合物的足够的稳健性和机械属性。在一个实施方案中，聚合物胶乳中的离子单体(例如离子官能团)的含量可为大约5wt％-10wt％。氢键单体(例如，聚合物胶乳中的氢键基团)的含量可以为大约5wt％-10wt％。
在一个实施方案中，次级胶乳和/或粘合剂也可以具有强氢键基团。次级胶乳的示例可以包含分子量为30kDa-100kDa的聚氨酯、聚酰胺、聚酯、聚氧乙烯、聚(乙烯醇)、聚(乙烯吡咯烷酮)、聚(乙二醇)、羟乙基纤维素等。在另一个实施方案中，次级胶乳可以是分子量约为200kDa或更高的丙烯酸共聚物树脂。丙烯酸共聚物树脂分散体的示例可以包括商品名已知的产品，诸如Joncryl FLX 5201、Joncryl FLX 5100、Joncryl DFC 3040和JoncrylECO 2177。
在一个实施方案中，就油墨中的固体含量而言，水性油墨组合物可以包含5wt％-40wt％的官能化初级胶乳和5wt％-20wt％的次级胶乳或粘合剂。在一个实施方案中，次级胶乳或粘合剂与官能化初级胶乳的比率可以介于5wt％-100wt％之间。在一个实施方案中，比率可为约20wt％。
如上所述，在约20wt％的次级胶乳与官能化初级胶乳的比率下，可以加入共溶剂体系和添加剂以提供水基油墨组合物在无孔基材上的良好润湿和粘附性。在一个实施方案中，可以使用丙二醇，诸如丙二醇甲基醚、丙二醇正丙基醚和二丙二醇甲醚。在一个实施方案中，添加剂可以包含pH调节剂(例如三乙醇胺)、表面活性剂(例如，Surfynol 420)或增粘剂(例如BYK 4500)。
图1示出了官能化初级胶乳的示例性化学结构。例如，官能化初级胶乳可以包含“x”数目的苯乙烯单体作为芳族官能团。官能化初级胶乳可以包含“y”数目的氢键基团。官能化初级胶乳可以包含“z”数目的含羧酸铵盐的单体，以提供离子官能团。官能化初级胶乳可以包含“n”数目的柔性侧链。
图2示出了图1中的“R”基团的不同示例。例如，“R”基团可以是不同的含羟基和酰胺的分子，诸如尿素或尿囊素。
图3示出了在图1中示出的官能化初级胶乳分散于水中时产生的胶乳颗粒的示例。然后可以将胶乳颗粒加入水基油墨中并用于可以通过喷墨印刷头喷射的喷墨打印机。
图4示出了用于形成用于在无孔基材上进行喷墨印刷的、具有低毒性的水性油墨组合物的示例性方法400的流程图。在框402处，方法400开始。在框404处，方法400制备具有芳族官能团、氢键基团、柔性侧链和离子官能团的初级聚合物胶乳。如上所讨论，可以将不同的分子加入低毒性聚合物中以官能化聚合物(例如，聚(马来酸酐-苯乙烯))。每个官能团可以为官能化初级聚合物胶乳提供不同的功能，该功能允许水性油墨组合物具有低粘度、对无孔基材具有良好的润湿性和粘附性、以及可以用于喷墨打印机的良好的耐磨性。
在框406处，方法400将利用次级胶乳粘合剂官能化的初级胶乳与一种或多种共溶剂和添加剂混合。在一个实施方案中，可以将次级胶乳粘合剂和一种或多种共溶剂和添加剂加入到官能化初级胶乳中并搅拌。
在一个实施方案中，可以将官能化初级胶乳、次级胶乳粘合剂和一种或多种共溶剂的组合加入到水基油墨中。然后可以使用喷墨打印机将油墨用于在无孔基材上印刷。油墨还可以提供低毒性以允许油墨印刷在食品工业中使用的塑料膜上。在框408处，方法400结束。
以下是根据上述方法制备的官能化初级胶乳的实施例。
实施例1
利用辛胺(32毫摩尔(mmol)，3.9g)通过在室温下搅拌混合物24小时对苯乙烯-马来酸酐交替共聚物(数均分子量(Mn)为2300、10g溶于50毫升(mL)丙酮中)进行改性，从而得到聚(苯乙烯-马来酸酐-正辛基马来酸)。为了将离子官能团引入到聚合物中，将1.25gNH4OH(29wt％)加入聚合物溶液中并搅拌30分钟。为了制备胶乳，利用100mL的丙酮进一步稀释丙酮中的聚(苯乙烯-马来酸酐-正辛基马来酸)溶液，并且加热至50℃。在机械搅拌下，在60℃下将丙酮中的聚合物溶液逐滴加到75mL的水中。通过在40℃下加热并搅拌、通过蒸发溶剂，将胶乳冷凝至30wt％的固体。
实施例2
利用辛胺(32mmol，3.9g)通过在室温下搅拌混合物24小时对苯乙烯-马来酸酐交替共聚物(Mn为2300、10g溶于50mL丙酮中)进行改性。为了引入氢键尿囊素官能团，将9.6mmol、1.5g的尿囊素溶解于二甲基亚砜中并加入到聚合物溶液中，并且在室温下搅拌24小时。在减小的压力下蒸发溶剂，然后将官能化聚合物在50℃下溶解于150mL的丙酮中。为了制备胶乳，利用100mL的丙酮进一步稀释聚合物溶液，并且加热至50℃。在机械搅拌下，在60℃下将聚合物溶液逐滴加到75mL的水中。通过在40℃下加热并搅拌、通过蒸发溶剂，将胶乳冷凝至30wt％的固体。
实施例3
利用辛胺(32mmol，3.9g)通过在室温下搅拌混合物24小时对苯乙烯-马来酸酐交替共聚物(Mn为2300、10g溶于50mL丙酮中)进行改性。为了引入氢键尿素官能团，将9.6mmol、0.58g的尿素溶解于二甲基亚砜中并加入到聚合物溶液中，并且在室温下搅拌24小时。在减小的压力下蒸发溶剂，然后将官能化聚合物在50℃下溶解于150mL的丙酮中。为了制备胶乳，利用100mL的丙酮进一步稀释聚合物溶液，并且加热至50℃。在机械搅拌下，在60℃下将聚合物溶液逐滴加到75mL的水中。通过在40℃下加热并搅拌、通过蒸发溶剂，将胶乳冷凝至30wt％固体。
官能化初级胶乳的属性
胶乳和油墨的粒径较低，在150nm-250nm的范围内，并且当样品在室温下储存约1个月时，粒径保持不变。这证实了胶乳中的离子官能团有效地稳定了水中的胶乳颗粒。
粒径
Figure BDA0002417490140000071
30wt％下的官能化胶乳的粘度较低，这使得它们适于多种印刷工艺，尤其是喷墨印刷。胶乳的低粘度可以归因于颗粒之间的低分子间相互作用，这是由于离子官能团在胶乳颗粒的表面上的强静电排斥和稳定化导致的。
官能化聚合物胶乳的粘度
Figure BDA0002417490140000072
下面是含有官能化初级胶乳的水性油墨制剂的实施例的表，该官能化初级胶乳具有次级胶乳和共溶剂体系的不同组合物。在下文的实施例后示出的表1提供了具有官能化初级胶乳的油墨的属性，包括耐磨性和粘附特性。
实施例4具有官能团聚(苯乙烯-马来酸酐-正辛基马来酸)胶乳的水性油墨。
Figure BDA0002417490140000081
实施例5具有聚(苯乙烯-马来酸酐-正辛基马来酸)胶乳和聚氨酯胶乳(BayhydrolUH2606)的水性油墨。
Figure BDA0002417490140000082
实施例6具有聚(苯乙烯-马来酸酐-正辛基马来酸)尿囊素官能化胶乳和聚氨酯胶乳(Bayhydrol UH2606)的水性油墨。
Figure BDA0002417490140000091
实施例7不含官能化胶乳的比较性油墨。
组分 质量(g) ％重量
Bayhydrol UH2606 50 76.0
Clariant Colanyl黑N500-MX 4 6.1
二丙二醇甲醚 3.8 5.8
二甘醇乙醚 3.8 5.8
三甘醇 3.8 5.8
Surfynol 420 0.2 0.3
BYK4500 0.2 0.3
总计 65.8 100.0
实施例8具有Joncryl FLX 5201胶乳的比较性水性油墨。
组分 质量(g) ％重量
Joncryl FLX 5201(40wt.％) 75 59.9
水 25 20.0
Clariant Colanyl黑N500-MX 3 2.4
二丙二醇甲醚 7.3 5.8
二甘醇乙醚 7.3 5.8
三甘醇 7.3 5.8
Surfynol 420 0.2 0.2
BYK4500 0.2 0.2
总计 125.3 100.0
实施例9具有Joncryl FLX 5201胶乳和聚(苯乙烯-马来酸酐-正辛基马来酸)胶乳的水性油墨。
Figure BDA0002417490140000101
实施例10具有Joncryl FLX 5201胶乳和利用尿素官能化的聚(苯乙烯-马来酸酐-正辛基马来酸)胶乳的水性油墨。
Figure BDA0002417490140000102
具有官能化胶乳的水性油墨在塑料膜上的属性
表1具有不同胶乳类型的水性油墨在PET塑料膜上的属性
Figure BDA0002417490140000103
Figure BDA0002417490140000111
将含胶乳的水性油墨施用到未处理的聚对苯二甲酸乙二醇酯(PET)塑料膜上，并且在60℃下进行干燥。通过利用干纸光纤擦拭物在整个油墨表面上进行双摩擦测试耐擦性来评估油墨的机械属性。粘附性通过利用胶带进行的十字划线粘附带测试、使用0-5的标度来测试，其中0表示所有的油墨从基材上脱落，并且5表示所有的油墨保留在基材上。
官能化胶乳与具有强氢键的其他粘合剂和胶乳(诸如聚乙烯醇-乙烯)以及聚氨酯胶乳(诸如，Bayhydrol UH2606、Joncryl FLX 5201)组合尤其有效。与仅包含聚氨酯胶乳的油墨相比，官能化胶乳的加入显著增加了耐磨性(高达70次双摩擦)以及对PET塑料膜的粘附性(高达4级)。
与油墨制剂中的单一类型胶乳相反，比较性实施例展示了组合两种类型的胶乳(例如，上述的官能化初级胶乳和次级胶乳)的协同有益效果。利用两种不同的胶乳制备的油墨的属性的增强预期产生于增强聚合物膜的强氢键。单个官能化胶乳(实施例11)可以用于在PET基材上制备油墨和膜；然而，机械属性较差，尤其是低耐磨性。这些胶乳通常具有低分子量(<10kDa)，这不足以形成稳健的膜。另一方面，具有高分子量(>200kDa)(实施例7和实施例8)的胶乳产生具有更好的耐磨性但对塑料PET基材的粘附性较差的油墨。因此，两种胶乳的组合在良好的成膜性、耐磨性和对塑料的粘附性方面提供协同有益效果(实施例5、实施例6、实施例9、
实施例10)。
水性油墨的粘度较低，这使得它们适于多种印刷工艺，尤其是喷墨印刷。胶乳的低粘度可以归因于颗粒之间的低分子间相互作用，这是由于离子官能团在胶乳颗粒的表面上的强静电排斥和稳定化导致的。
水性油墨的粘度
Figure BDA0002417490140000121
应当理解的是，以上公开的和其他的特征和功能的变型或其另选方案可以被组合到许多其他不同的系统或应用中。本领域的技术人员随后可以做出各种目前未预见或未预料到的替换、修改、变化或改进，这些也旨在被所附权利要求书所涵盖。

Claims (14)

1.一种用于形成用于在无孔基材上进行喷墨印刷的水性油墨组合物的方法，包括：
制备具有芳族官能团、氢键基团、柔性侧链和离子官能团的初级聚合物胶乳；以及
将所述初级聚合物胶乳与次级胶乳粘合剂和一种或多种共溶剂和添加剂混合；
其中，用于使初级胶乳官能化以包含氢键基团的分子包括以下分子中的至少一种：尿素、尿囊素、酪胺、葡萄糖、丙烯酰基呋喃葡萄糖(MAGP)、N-[三(羟甲基)甲基]丙烯酰胺、丙烯酰胺基苯硼酸、氨基乙基甲基丙烯酰胺、丙烯酰吗啉、丙烯酸乙酰氧苯乙酯；所述离子官能团包括以下中的至少一种：羧酸、磺酸和铵，
其中所述次级胶乳粘合剂包含以下中的至少一种：聚氨酯、聚酰胺、聚酯、聚氧乙烯或聚乙烯醇。
2.根据权利要求1所述的方法，其中所述分子包含以下中的至少一种：尿素、尿囊素或酪胺。
3.根据权利要求1所述的方法，其中利用所述柔性侧链制备所述初级聚合物胶乳包括：
利用具有以下中的至少一种的侧链的支链烷基化学改性所述初级聚合物胶乳：丁基、己基、辛基或癸基。
4.根据权利要求1所述的方法，其中所制备的所述初级聚合物胶乳在所述水性油墨组合物中包含5重量％-40重量％的固体。
5.根据权利要求1所述的方法，其中所述次级胶乳粘合剂在所述水性油墨组合物中包含5重量％-20重量％的固体。
6.根据权利要求1所述的方法，其中所述初级聚合物胶乳包含聚苯乙烯的共聚物。
7.根据权利要求1所述的方法，其中所述一种或多种共溶剂包含丙二醇。
8.根据权利要求7所述的方法，其中所述丙二醇包含以下中的至少一种：丙二醇甲基醚、丙二醇正丙基醚或二丙二醇甲醚。
9.一种用于在无孔基材上进行喷墨印刷的水性油墨组合物，包含：
5重量％-40重量％的不含表面活性剂的官能化初级胶乳，其中所述不含表面活性剂的官能化初级胶乳包含：
芳族官能团；
氢键基团，用以提供对无孔基材的粘附性，其中所述无孔基材包括聚烯烃材料，用于使初级胶乳官能化以包含氢键基团的分子包括以下分子中的至少一种：尿素、尿囊素、酪胺、葡萄糖、丙烯酰基呋喃葡萄糖(MAGP)、N-[三(羟甲基)甲基]丙烯酰胺、丙烯酰胺基苯硼酸、氨基乙基甲基丙烯酰胺、丙烯酰吗啉、丙烯酸乙酰氧苯乙酯；
柔性侧链；和
离子官能团，其中所述离子官能团包括以下中的至少一种：羧酸、磺酸和铵；
5重量％-20重量％的次级胶乳粘合剂；和
一种或多种共溶剂，其中所述水性油墨组合物在25摄氏度下的粘度低于10毫帕·秒(mPa·s)，
其中所述次级胶乳粘合剂包含以下中的至少一种：聚氨酯、聚酰胺、聚酯、聚氧乙烯或聚乙烯醇。
10.根据权利要求9所述的水性油墨组合物，其中所述不含表面活性剂的官能化初级胶乳包含聚苯乙烯与氨的低毒性共聚物，所述低毒性共聚物的粒径为100纳米-300纳米(nm)。
11.根据权利要求9所述的水性油墨组合物，其中所述一种或多种共溶剂包含丙二醇。
12.根据权利要求11所述的水性油墨组合物，其中所述丙二醇包含以下中的至少一种：丙二醇甲基醚、丙二醇正丙基醚或二丙二醇甲醚。
13.根据权利要求9所述的水性油墨组合物，其中所述柔性侧链包含具有以下中的至少一种的侧链的支链烷基：丁基、己基、辛基或癸基。
14.一种用于形成用于在无孔基材上进行喷墨印刷的水性油墨组合物的方法，包括：
将10克(g)数均分子量(Mn)为2300的苯乙烯-马来酸酐交替共聚物在50毫升(mL)丙酮中的混合物与3.9g的32毫摩尔(mmol)辛胺组合；
在室温下搅拌所述混合物二十四小时；
将含羟基和酰胺的化合物溶解于二甲基亚砜中；
向所述混合物中加入溶解在所述二甲基亚砜中的所述含羟基和酰胺的化合物，并且搅拌24小时以产生官能化聚合物；
通过在搅拌的同时将所述官能化聚合物加入到水中来制备胶乳；以及
通过将利用次级胶乳、共溶剂、pH调节剂、至少一种表面活性剂和增粘剂官能化的所述胶乳组合来制备所述水性油墨组合物，其中所述次级胶乳粘合剂包含以下中的至少一种：聚氨酯、聚酰胺、聚酯、聚氧乙烯或聚乙烯醇。
CN202010195646.5A 2019-04-10 2020-03-19 用于在无孔基材上进行喷墨印刷的水性油墨组合物 Active CN111808475B (zh)