CN111778776A - 一种可擦拭型油墨印刷纸及其制备方法和应用 - Google Patents
一种可擦拭型油墨印刷纸及其制备方法和应用 Download PDFInfo
- Publication number
- CN111778776A CN111778776A CN202010723604.4A CN202010723604A CN111778776A CN 111778776 A CN111778776 A CN 111778776A CN 202010723604 A CN202010723604 A CN 202010723604A CN 111778776 A CN111778776 A CN 111778776A
- Authority
- CN
- China
- Prior art keywords
- layer
- ink
- pvp
- ink printing
- printing paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种可擦拭型油墨印刷纸及其制备方法和应用。所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、PVP隔离层、油墨层和覆膜层。所述可擦拭型油墨印刷纸通过少量水轻拭油墨即可消除,同时所述可擦拭型油墨印刷纸具有优良的耐磨、耐刮、耐撕裂和防水性能。
Description
技术领域
本发明属于油墨印刷技术领域,具体涉及一种可擦拭型油墨印刷纸及其制备方法。
背景技术
目前,电子商务急速发展,物流行业的快递业务被推上高速增长的风口,快递业的迅速发展极大的方便了人们的日常生活,但同时存在快递面单泄露个人信息的问题,包括住址、姓名、电话等,部分快递面单还印有产品明细。随手丢弃的快递面单,极大地泄露了消费者的隐私。现有的处理快递面单上个人信息的方法,主要是撕碎面单,或者使用遮挡笔涂黑。这些都是消费者为了保护自己的隐私而采取的遮挡手段,快递业还未出现行之有效的技术手段。
CN203651242U公开了一种可以防水和防摩擦,使用户填写的信息保存更完好的快递单;它包括至少两联相叠的用于保存快递信息的单据,位于最底层的一联单据的背面设有第一胶水涂层;所述的第一胶水涂层下表面上设有第一覆膜;所述的第一覆膜为透明覆膜,所述第一覆膜的下表面上设有胶状物,所述的胶状物上设有第二覆膜;所述的第一覆膜被撕下后可通过下表面上的胶状物粘贴于快递单的最上层的单据。该快递单虽然能够防水和防摩擦,但是快递面上印刷的信息只能依靠剪刀划花、撕碎、墨水涂黑、酒精擦拭等手段消除,很难去除干净且过程麻烦。
因此,开发一种能够简便擦拭即能消除面单上的信息,同时还具有优良的耐磨、耐刮、耐撕裂、防水性能的面单纸是本领域目前研究的重点。
发明内容
针对现有技术的不足,本发明的目的在于提供一种可擦拭型油墨印刷纸及其制备方法和应用。所述可擦拭型油墨印刷纸通过少量水轻拭油墨即可消除;同时所述可擦拭型油墨印刷纸具有优良的耐磨、耐刮、耐撕裂和防水性能。
为达此目的,本发明采用以下技术方案:
第一方面,本发明提供一种可擦拭型油墨印刷纸,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、PVP隔离层、油墨层和覆膜层。
在本发明中,在所述面单纸层和油墨层间设置PVP隔离层,起到屏障的作用,防止油墨分子渗透到面单纸内,使得印制的信息借助少量水就可以轻易擦除,方便简洁。对承印面单纸层无特殊要求,普通面单纸层表面添加PVP隔离层后,所印制的油墨就可擦除,且采用普通油墨印刷即可,无需特殊油墨或工艺,可用范围广。同时,本发明还在所述油墨层油墨层上设置覆膜层,从而使所述可擦拭型油墨印刷纸具备了优良的耐磨、耐刮、耐撕裂、防水性能,可以防止其他意外导致的快递面单与水接触后,面单字迹墨化的情况。
优选地,所述PVP隔离层的厚度为50-100μm,例如可以是50μm、60μm、70μm、80μm、90μm、100μm等。
优选地,所述PVP隔离层的制备原料按重量百分含量计包括:聚乙烯吡咯烷酮4-6%、环氧类丙烯酸酯8-15%、硅烷基环氧改性丙烯酸酯8-15%、脂肪族聚氨酯丙烯酸酯30-35%、二缩三丙二醇二丙烯酸酯15-20%、三羟甲基丙烷三丙烯酸酯8-12%和光引发剂3-8%,余量为水。
本发明中,所述PVP隔离层的制备原料以聚乙烯吡咯烷酮、环氧类丙烯酸酯、硅烷基环氧改性丙烯酸酯、脂肪族聚氨酯丙烯酸酯为主剂,具有良好的成膜性,涂膜坚硬,韧性好,光亮度大,拒水防潮效果好,附着力强,不易脱落,涂敷于面单纸上再印刷油墨时能够防止油墨分子渗透到面单纸内,使得印制的信息借助少量水就可以轻易擦除。同时,以二缩三丙二醇二丙烯酸酯和三羟甲基丙烷三丙烯酸酯为活性单体,能有效降低混合物体系的粘度,加快反应速度,参与反应。
以所述PVP隔离层的制备原料质量为100%计,所述聚乙烯吡咯烷酮含量为4-6%,例如可以是4%、4.5%、5%、5.5%、6%等。
以所述PVP隔离层的制备原料质量为100%计,所述环氧类丙烯酸酯含量为8-15%,例如可以是8%、9%、10%、11%、12%、13%、14%、15%等。
以所述PVP隔离层的制备原料质量为100%计,所述硅烷基环氧改性丙烯酸酯含量为8-15%,例如可以是8%、9%、10%、11%、12%、13%、14%、15%等。
以所述PVP隔离层的制备原料质量为100%计,所述脂肪族聚氨酯丙烯酸酯酯含量为30-35%,例如可以是30%、31%、32%、33%、34%、35%等。
以所述PVP隔离层的制备原料质量为100%计,所述二缩三丙二醇二丙烯酸酯含量为15-20%,例如可以是15%、16%、17%、18%、19%、20%等。
以所述PVP隔离层的制备原料质量为100%计,所述三羟甲基丙烷三丙烯酸酯含量为8-12%,例如可以是8%、8.5%、9%、9.5%、10%、10.5%、11%、11.5%、12%等。
以所述PVP隔离层的制备原料质量为100%计,所述光引发剂含量为3-8%,例如可以是3%、4%、5%、6%、7%、8%等。
优选地,所述聚乙烯吡咯烷酮的K值为27-32.4,例如可以是27、28、29、30、31、32、32.4等。
优选地,所述光引发剂包括2-羟基-2-甲基-1-苯基丙酮和/或2-羟基-2-甲基-1-对羟乙基醚基丙酮。
优选地,所述PVP隔离层的制备原料中还包括流平剂、润湿剂或消泡剂中的任意一种或至少两种的组合。
优选地,所述流平剂占所述隔离层的制备原料总质量的1-2%,例如可以是1%、1.2%、1.4%、1.6%、1.8%、2%等。
优选地,所述流平剂为丙烯酸酯类流平剂。
优选地,所述润湿剂占所述隔离层的制备原料总质量的1-3%,例如可以是1%、1.2%、1.4%、1.6%、1.8%、2%、2.2%、2.4%、2.6%、2.8%、3%等。
优选地,所述润湿剂为丙烯酸类润湿剂。
优选地,所述消泡剂占所述隔离层的制备原料总质量的0.5-1.5%,例如可以是0.5%、0.7%、0.9%、1.1%、1.3%、1.5%等。
优选地,所述消泡剂为有机硅消泡剂和/或矿物油型消泡剂。
优选地,所述油墨层0.2-1μm,例如可以是0.2μm、0.3μm、0.4μm、0.5μm、0.6μm、0.7μm、0.8μm、0.9μm、1μm等。
优选地,所述覆膜层的材质为PE。
优选地,所述覆膜层的厚度为1-10μm,例如可以是1μm、2μm、3μm、4μm、5μm、6μm、7μm、8μm、9μm、10μm。
第二方面,本发明提供一种如第一方所述的可擦拭型油墨印刷纸的制备方法,所述可擦拭型油墨印刷纸的制备方法为:在所述面单纸层一侧涂覆PVP隔离层后固化,再在PVP隔离层上印刷油墨层,最后在所述油墨层上粘结覆膜层,得到所述可擦拭型油墨印刷纸。
优选地,所述紫外光的能量为400-1200mJ/cm2,例如可以是400mJ/cm2、600mJ/cm2、800mJ/cm2、1000mJ/cm2、1200mJ/cm2等。
第三方面,本发明提供一种如第一方面所述的可擦拭型油墨印刷纸在制备快递单纸张中的应用。
本发明中,将所述的可擦拭型油墨印刷纸制备得到的快递单纸张,消费者不再需要剪刀划花、撕碎或墨水涂黑等手段消除信息,消费者仅需揭掉覆膜层后,少量水轻拭油墨层,就可以消除面单上的信息,从而解决快递单上信息泄露的问题。而在快递单上的覆膜层具有优良的耐磨、耐刮、耐撕裂、防水性能。
相对于现有技术,本发明具有以下有益效果:
本发明按所述可擦拭型油墨印刷纸通过少量水轻拭油墨,就可以消除面单上的信息,从而解决信息泄露问题;同时所述可擦拭型油墨印刷纸具有优良的耐磨、耐刮、耐撕裂和防水性能。
附图说明
图1为本发明可擦拭型油墨印刷纸的结构示意图;
其中,1为面单纸层,2为PVP隔离层,3为油墨层,4为覆膜层。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。本领域技术人员应该明了,所述实施例仅仅是帮助理解本发明,不应视为对本发明的具体限制。
图1为本发明可擦拭型油墨印刷纸的结构示意图,如图1所示,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层1、PVP隔离层2、油墨层3和覆膜层4。
下述各组分来源如下所示:聚乙烯吡咯烷酮K30(厂家:安徽省沃土化工有限公司、牌号:9003-39-8)、环氧类丙烯酸酯(厂家:广东昊辉新材料有限公司、牌号:CR90426)、硅烷基环氧改性丙烯酸酯(厂家:广东昊辉新材料有限公司、牌号:HE3203)、脂肪族聚氨酯丙烯酸酯(厂家:广东昊辉新材料有限公司、牌号:0039A)、二缩三丙二醇二丙烯酸酯(厂家:长兴化学、牌号:EM223)、三羟甲基丙烷三丙烯酸酯(厂家:广州市仲皓璟高分子材料有限公司、牌号:T003)、丙烯酸酯类流平剂(厂家:上海忠诚精细化工有限公司、牌号:RM-2020)、丙烯酸类润湿剂(厂家:亚洲海名斯特殊化学、牌号:levaslol w-469)、矿物油型消泡剂(厂家:亚洲海名斯特殊化学、牌号:defom w-0506);油墨购于(厂家:太平洋油墨),PE膜购于(厂家:深圳市三上高分子环保新材料股份有限公司)。
实施例1
本实施例提供一种可擦拭型油墨印刷纸,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、PVP隔离层、油墨层和覆膜层,所述PVP隔离层的厚度为80μm,所述油墨层0.5μm,所述覆膜层为PE膜,厚度为8μm。
所述PVP隔离层的制备原料按重量百分含量计包括:聚乙烯吡咯烷酮K305%、环氧类丙烯酸酯11.26%、硅烷基环氧改性丙烯酸酯11.26%、脂肪族聚氨酯丙烯酸酯33.78%、二缩三丙二醇二丙烯酸酯18.8%、三羟甲基丙烷三丙烯酸酯9.3%、光引发剂(2-羟基-2-甲基-1-苯基丙酮)6%、丙烯酸酯类流平剂1.6%、丙烯酸类润湿剂2%、矿物油型消泡剂1%,余量为水。
本实施例所述可擦拭型油墨印刷纸的制备方法为:在所述面单纸层一侧涂覆PVP隔离层后在紫外灯下固化,所述紫外光的能量为800mJ/cm2,固化后再在PVP隔离层上印刷油墨层,最后在所述油墨层上粘结覆膜层,得到所述可擦拭型油墨印刷纸。
实施例2
本实施例提供一种可擦拭型油墨印刷纸,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、PVP隔离层、油墨层和覆膜层,所述PVP隔离层的厚度为100μm,所述油墨层1μm,所述覆膜层为PE膜,厚度为10μm。
所述PVP隔离层的制备原料按重量百分含量计包括:聚乙烯吡咯烷酮K305%、环氧类丙烯酸酯11.26%、硅烷基环氧改性丙烯酸酯11.26%、脂肪族聚氨酯丙烯酸酯33.78%、二缩三丙二醇二丙烯酸酯18.8%、三羟甲基丙烷三丙烯酸酯9.3%、光引发剂(2-羟基-2-甲基-1-苯基丙酮)6%、丙烯酸酯类流平剂1.6%、丙烯酸类润湿剂2%、矿物油型消泡剂1%,余量为水。
本实施例所述可擦拭型油墨印刷纸的制备方法为:在所述面单纸层一侧涂覆PVP隔离层后在紫外灯下固化,所述紫外光的能量为1000mJ/cm2,固化后再在PVP隔离层上印刷油墨层,最后在所述油墨层上粘结覆膜层,得到所述可擦拭型油墨印刷纸。
实施例3
本实施例提供一种可擦拭型油墨印刷纸,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、PVP隔离层、油墨层和覆膜层,所述PVP隔离层的厚度为50μm,所述油墨层0.2μm,所述覆膜层为PE膜,厚度为10μm。
所述PVP隔离层的制备原料按重量百分含量计包括:聚乙烯吡咯烷酮K305%、环氧类丙烯酸酯11.26%、硅烷基环氧改性丙烯酸酯11.26%、脂肪族聚氨酯丙烯酸酯33.78%、二缩三丙二醇二丙烯酸酯18.8%、三羟甲基丙烷三丙烯酸酯9.3%、光引发剂(2-羟基-2-甲基-1-苯基丙酮)6%、丙烯酸酯类流平剂1.6%、丙烯酸类润湿剂2%、矿物油型消泡剂1%,余量为水。
本实施例所述可擦拭型油墨印刷纸的制备方法为:在所述面单纸层一侧涂覆PVP隔离层后在紫外灯下固化,所述紫外光的能量为1200mJ/cm2,固化后再在PVP隔离层上印刷油墨层,最后在所述油墨层上粘结覆膜层,得到所述可擦拭型油墨印刷纸。
实施例4
本实施例提供一种可擦拭型油墨印刷纸,与实施例1的区别仅在于,所述PVP隔离层的厚度为40μm。
实施例5
本实施例提供一种可擦拭型油墨印刷纸,与实施例1的区别仅在于,所述PVP隔离层的厚度为200μm。
实施例6
本实施例提供一种可擦拭型油墨印刷纸,与实施例1的区别仅在于,将所述PVP隔离层的制备原料中的聚乙烯吡咯烷酮K30替换为聚乙烯吡咯烷酮K17。
实施例7
本实施例提供一种可擦拭型油墨印刷纸,与实施例1的区别仅在于,将所述PVP隔离层的制备原料中的聚乙烯吡咯烷酮K30替换为聚乙烯吡咯烷酮K60。
实施例8
本实施例提供一种可擦拭型油墨印刷纸,与实施例1的区别仅在于,所述覆膜层为PET膜。
对比例1
本对比例提供一种油墨印刷纸,与实施例1的区别仅在于,所述油墨印刷纸无PVP隔离层,所述油墨印刷纸仅包括依次层叠的面单纸层、油墨层和覆膜层,所述油墨层0.5μm,所述覆膜层为PE膜,厚度为8μm。
对比例2
本对比例提供一种油墨印刷纸,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、隔离层、油墨层和覆膜层,所述隔离层的厚度为80μm,所述油墨层0.5μm,所述覆膜层为PE膜,厚度为8μm。
所述PVP隔离层的制备原料按重量百分含量计包括:环氧类丙烯酸酯11.26%、硅烷基环氧改性丙烯酸酯11.26%、脂肪族聚氨酯丙烯酸酯33.78%、二缩三丙二醇二丙烯酸酯18.8%、三羟甲基丙烷三丙烯酸酯9.3%、光引发剂(2-羟基-2-甲基-1-苯基丙酮)6%、丙烯酸酯类流平剂1.6%、丙烯酸类润湿剂2%、矿物油型消泡剂1%,余量为水。
本对比例所述油墨印刷纸的制备方法为:在所述面单纸层一侧涂覆隔离层后在紫外灯下固化,所述紫外光的能量为800mJ/cm2,固化后再在隔离层上印刷油墨层,最后在所述油墨层上粘结覆膜层,得到所述可擦拭型油墨印刷纸。
对比例3
本对比例提供一种油墨印刷纸,与实施例1的区别仅在于,所述油墨印刷纸无覆膜层,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、PVP隔离层和油墨层,所述PVP隔离层的厚度为80μm,所述油墨层0.5μm。
性能测试:
对实施例1-8和制备得到的可擦拭型油墨印刷纸和对比例1-3制备的油墨印刷纸进行各项性能测试,具体测试方法如下所示:
(1)可擦拭性:揭开覆膜层后,取少量水轻拭油墨层(对比例3无覆膜层可直接用水轻拭),观测油墨层是否擦拭后的现象;
(2)耐磨性:将纸页置于恒温(23±1℃)、恒湿(50±1%)实验室中24h。用两张相同的纸页正反相对,均匀来回摩擦100次,观察纸页擦痕情况;
(3)耐刮性:将纸页置于恒温(23±1℃)、恒湿(50±1%)实验室中24h。用一元硬币在纸页表面(覆膜层)均匀来回剐蹭30次,观察纸页表面刮痕情况;
(4)耐撕裂性:按照GB/T 455.1纸撕裂度的测定法,测定纸页的耐撕裂性;
(5)防水性:按照GB/T 4857.9喷淋试验方法,将纸页置于恒温(23±1℃)、恒湿(50±1%)实验室中24h。用喷淋头(出水量100L/(m2h)±20L/(m2h))在纸页表面(覆膜层)连续喷淋60min,喷淋头与纸页高度差最少2m,喷淋期间纸页不能浸泡在水里,观察纸页印刷信息是否清楚。
具体测试结果如表1所示:
表1
项目 | 可擦拭性 | 耐磨 | 耐刮 | 耐撕裂 | 防水性能 |
实施例1 | 100% | 90%耐磨 | 90%耐刮 | 80%耐撕 | 100% |
实施例2 | 100% | 90%耐磨 | 90%耐刮 | 90%耐撕 | 100% |
实施例3 | 90% | 90%耐磨 | 90%耐刮 | 90%耐撕 | 100% |
实施例4 | 80% | 90%耐磨 | 90%耐刮 | 80%耐撕 | 100% |
实施例5 | 100% | 80%耐磨 | 90%耐刮 | 80%耐撕 | 100% |
实施例6 | 100% | 80%耐磨 | 90%耐刮 | 80%耐撕 | 100% |
实施例7 | 100% | 80%耐磨 | 90%耐刮 | 80%耐撕 | 100% |
实施例8 | 100% | 90%耐磨 | 70%耐刮 | 80%耐撕 | 100% |
对比例1 | 0% | 90%耐磨 | 90%耐刮 | 80%耐撕 | 90% |
对比例2 | 0% | 90%耐磨 | 90%耐刮 | 80%耐撕 | 90% |
对比例3 | 80% | 30%耐磨 | 30%耐刮 | 30%耐撕 | 0% |
由表1测试数据可知,本发明按所述可擦拭型油墨印刷纸可擦拭性在80%以上,耐磨性在80%以上,耐刮性在70%以上,耐撕裂性在80%以上,防水性能为100%。说明本发明所述可擦拭型油墨印刷纸通过少量水轻拭油墨,就可以消除面单上的信息,从而解决信息泄露问题;同时所述可擦拭型油墨印刷纸具有优良的耐磨、耐刮、耐撕裂和防水性能。
由实施例1和实施例4、5的对比可知,PVP隔离层过薄,可擦拭性较差,需要较多的水擦拭才能完全消除面单上的信息,PVP隔离层过厚,耐磨性能较差。由实施例1和实施例6、7的对比可知,所述PVP隔离层的制备原料中,聚乙烯吡咯烷酮的分子量过低或过高,均无法形成良好的PVP隔离层,耐磨性能较差。由实施例1和对比例8的对比可知,本发明所述覆膜层为PE膜,耐刮性能更好,采用PET膜耐刮性能差。
由实施例1和对比例1、2的对比可知,所述油墨印刷纸无隔离层或所述隔离层为非PVP隔离层,制备得到的油墨印刷纸揭开覆膜层后,取少量水轻拭油墨层,油墨层完全无法消除。由实施例1和对比例3的对比可知,所述油墨印刷纸无覆膜层,无论是可擦拭性,还是耐磨、耐刮、耐撕裂和防水性能均较差。
申请人声明,本发明通过上述实施例来说明本发明所述可擦拭型油墨印刷纸及其制备方法和应用,但本发明并不局限于上述实施例,即不意味着本发明必须依赖上述实施例才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
Claims (10)
1.一种可擦拭型油墨印刷纸,其特征在于,所述可擦拭型油墨印刷纸包括依次层叠的面单纸层、PVP隔离层、油墨层和覆膜层。
2.根据权利要求1所述的可擦拭型油墨印刷纸,其特征在于,所述PVP隔离层的厚度为50-100μm。
3.根据权利要求1或2所述的可擦拭型油墨印刷纸,其特征在于,所述PVP隔离层的制备原料按重量百分含量计包括:聚乙烯吡咯烷酮4-6%、环氧类丙烯酸酯8-15%、硅烷基环氧改性丙烯酸酯8-15%、脂肪族聚氨酯丙烯酸酯30-35%、二缩三丙二醇二丙烯酸酯15-20%、三羟甲基丙烷三丙烯酸酯8-12%和光引发剂3-8%,余量为水;
优选地,所述聚乙烯吡咯烷酮的K值为27-32.4;
优选地,所述光引发剂包括2-羟基-2-甲基-1-苯基丙酮和/或2-羟基-2-甲基-1-对羟乙基醚基丙酮。
4.根据权利要求1-3中任一项所述的可擦拭型油墨印刷纸,其特征在于,所述PVP隔离层的制备原料中还包括流平剂、润湿剂或消泡剂中的任意一种或至少两种的组合;
优选地,所述流平剂占所述隔离层的制备原料总质量的1-2%;
优选地,所述流平剂为丙烯酸酯类流平剂;
优选地,所述润湿剂占所述隔离层的制备原料总质量的1-3%;
优选地,所述润湿剂为丙烯酸类润湿剂;
优选地,所述消泡剂占所述隔离层的制备原料总质量的0.5-1.5%;
优选地,所述消泡剂为有机硅消泡剂和/或矿物油型消泡剂。
5.根据权利要求1-4中任一项所述的可擦拭型油墨印刷纸,其特征在于,所述油墨层0.2-1μm。
6.根据权利要求1-5中任一项所述的可擦拭型油墨印刷纸,其特征在于,所述覆膜层的材质为PE。
7.根据权利要求1-6中任一项所述的可擦拭型油墨印刷纸,其特征在于,所述覆膜层的厚度为1-10μm。
8.根据权利要求1-7中任一项所述的可擦拭型油墨印刷纸的制备方法,其特征在于,所述可擦拭型油墨印刷纸的制备方法为:在所述面单纸层一侧涂覆PVP隔离层后固化,再在PVP隔离层上印刷油墨层,最后在所述油墨层上粘结覆膜层,得到所述可擦拭型油墨印刷纸。
9.根据权利要求8所述的制备方法,其特征在于,所述固化采用紫外光照射,所述紫外光的能量为400-1200mJ/cm2。
10.根据权利要求1-7中任一项所述的可擦拭型油墨印刷纸在制备快递单纸张中的应用。