CN111267443A - 一种抗静电消光膜及其制备方法 - Google Patents

一种抗静电消光膜及其制备方法 Download PDF

Info

Publication number
CN111267443A
CN111267443A CN202010063841.2A CN202010063841A CN111267443A CN 111267443 A CN111267443 A CN 111267443A CN 202010063841 A CN202010063841 A CN 202010063841A CN 111267443 A CN111267443 A CN 111267443A
Authority
CN
China
Prior art keywords
parts
layer
film
antistatic
raw materials
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010063841.2A
Other languages
English (en)
Inventor
齐先锋
方文彬
王兆中
方勇
张国宗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Gettel High New Material Co ltd
Original Assignee
Anhui Gettel High New Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Gettel High New Material Co ltd filed Critical Anhui Gettel High New Material Co ltd
Priority to CN202010063841.2A priority Critical patent/CN111267443A/zh
Publication of CN111267443A publication Critical patent/CN111267443A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗静电消光膜及其制备方法，抗静电消光膜为三层结构，从上到下依次包括抗粘连层、芯层、消光层；抗粘连层由如下原料按重量份组成：聚丙烯80‑90份、防黏剂1‑3份；芯层由如下原料按重量份组成：聚丙烯80‑90份、抗静电剂2‑4份；消光层由如下原料按重量份组成：消光母料90‑96份、爽滑剂2‑3份；抗静电消光膜的三层结构是通过熔融共挤和双向拉伸后形成的。本发明制备的消光膜膜面晶点、白点少，具有较高的雾度和较低的光泽度，消光层手感光滑细腻，白色哑光效果比较美观，可用于电子产品的表面保护作用，让电子产品在生产过程中起到防尘、刮花作用，也适合做高端商品的外包装。

Description

一种抗静电消光膜及其制备方法
技术领域
本发明涉及薄膜生产领域，具体是一种抗静电消光膜及其制备方法。
背景技术
双向拉伸聚丙烯薄膜(BOPP)物理稳定性好、机械强度大、气密性较好，透明度和光泽度较高，坚韧耐磨，是应用最广泛的薄膜，一般使用厚度为10～100μm。目前双向拉伸聚丙烯薄膜又分为光膜和消光膜两大类，消光膜可分为单面消光，双面消光及热封消光等品种。消光膜的开发成功，极大的拓展了薄膜的使用范围。然而由于原料的不同，生产设备的不同，生产的参数也需要不断摸索，市场上的消光膜普遍存在分散差，膜面白点、晶点多等问题，产品的品质也需要进一步提高。
发明内容
本发明提供了一种抗静电消光膜及其制备方法，以解决上述技术问题。
一种抗静电消光膜，所述抗静电消光膜为三层结构，从上到下依次包括抗粘连层、芯层、消光层；
所述抗粘连层由如下原料按重量份组成：聚丙烯80-90份、防黏剂1-3份；
所述芯层由如下原料按重量份组成：聚丙烯80-90份、抗静电剂2-4份；
所述消光层由如下原料按重量份组成：消光母料90-96份、爽滑剂2-3份；
所述抗静电消光膜的三层结构是通过熔融共挤和双向拉伸后形成的。
优选的，所述防黏剂为合成二氧化硅、玻璃微珠、有机硅聚合物或甲基丙烯酸醋的聚合物。
优选的，所述抗静电剂为抗静电剂HZ-1或抗静电剂HZ-14或乙二醇月桂酸酰胺或乙氧基化烷基胺。
优选的，所述爽滑剂为油酸酰胺、芥酸酰胺、硬脂酸钙、硅酮中的一种。
优选的，所述的抗静电消光膜的制备方法，包括如下步骤：
S1、分别将抗粘连层、芯层、消光层对应的原料定量投入第一挤出机、第二挤出机、第三挤出机；
S2、抗粘连层、芯层、消光层对应的原料分别在第一挤出机、第二挤出机、第三挤出机内加热成熔融状态，分别经过过滤网过滤后，在三层结构模头中汇合挤出成膜片，然后通过激冷辊和水池快速冷却定型为厚片；
S3、厚片经过预热、纵向拉伸、定型，得到厚膜；
S4、厚膜再经过预热、横向拉伸、定型、冷却，得到薄膜；
S5、薄膜经过TDO冷却，牵引辊冷却和电晕处理，然后收卷得到成品。
优选的，所述步骤S2中第一挤出机、第二挤出机、第三挤出机的加热温度为250℃，模头温度为240℃。
优选的，所述步骤S3中预热温度为125-138℃，纵向拉伸温度为122-128℃，定型温度为127-139℃。
优选的，所述步骤S4中预热温度为168-172℃,横向拉伸温度为155℃,定型温度为167℃。
本发明的有益效果是：
本发明制备的消光膜膜面晶点、白点少，具有较高的雾度和较低的光泽度，消光层手感光滑细腻，白色哑光效果比较美观，可用于电子产品的表面保护作用，让电子产品在生产过程中起到防尘、刮花作用，也适合做高端商品的外包装。
具体实施方式
以下对本发明的实施例进行详细说明，但是本发明可以由权利要求限定和覆盖的多种不同方式实施。
以下通过具体实施例对本发明进行详细描述。
实施例1
一种抗静电消光膜及其制备方法，抗静电消光膜为三层结构，从上到下依次包括抗粘连层、芯层、消光层；
抗粘连层由如下原料按重量份组成：聚丙烯80份、防黏剂1份；
芯层由如下原料按重量份组成：聚丙烯80份、抗静电剂2份；
消光层由如下原料按重量份组成：消光母料90份、爽滑剂2份；
上述抗静电消光膜的三层结构是通过熔融共挤和双向拉伸后形成的。
上述防黏剂为合成二氧化硅、玻璃微珠、有机硅聚合物或甲基丙烯酸醋的聚合物。
上述抗静电剂为抗静电剂HZ-1或抗静电剂HZ-14或乙二醇月桂酸酰胺或乙氧基化烷基胺。
上述爽滑剂为油酸酰胺、芥酸酰胺、硬脂酸钙、硅酮中的一种。
上述抗静电消光膜的制备方法，包括如下步骤：
S1、分别将抗粘连层、芯层、消光层对应的原料定量投入第一挤出机、第二挤出机、第三挤出机；
S2、抗粘连层、芯层、消光层对应的原料分别在第一挤出机、第二挤出机、第三挤出机内加热成熔融状态，分别经过过滤网过滤后，在三层结构模头中汇合挤出成膜片，然后通过激冷辊和水池快速冷却定型为厚片，第一挤出机、第二挤出机、第三挤出机的加热温度为250℃，模头温度为240℃；
S3、厚片经过预热、纵向拉伸、定型，得到厚膜，预热温度为125℃，纵向拉伸温度为122℃，定型温度为127℃；
S4、厚膜再经过预热、横向拉伸、定型、冷却，得到薄膜，预热温度为168℃,横向拉伸温度为155℃,定型温度为167℃；
S5、薄膜经过TDO冷却，牵引辊冷却和电晕处理，然后收卷得到成品。
以下各实施例与实施例1的区别仅在于，
实施例2
一种抗静电消光膜及其制备方法，抗静电消光膜为三层结构，从上到下依次包括抗粘连层、芯层、消光层；
抗粘连层由如下原料按重量份组成：聚丙烯85份、防黏剂2份；
芯层由如下原料按重量份组成：聚丙烯85份、抗静电剂3份；
消光层由如下原料按重量份组成：消光母料93份、爽滑剂2.5份；
上述抗静电消光膜的三层结构是通过熔融共挤和双向拉伸后形成的。
上述抗静电消光膜的制备方法，包括如下步骤：
S1、分别将抗粘连层、芯层、消光层对应的原料定量投入第一挤出机、第二挤出机、第三挤出机；
S2、抗粘连层、芯层、消光层对应的原料分别在第一挤出机、第二挤出机、第三挤出机内加热成熔融状态，分别经过过滤网过滤后，在三层结构模头中汇合挤出成膜片，然后通过激冷辊和水池快速冷却定型为厚片，第一挤出机、第二挤出机、第三挤出机的加热温度为250℃，模头温度为240℃；
S3、厚片经过预热、纵向拉伸、定型，得到厚膜，预热温度为131.5℃，纵向拉伸温度为125℃，定型温度为133℃；
S4、厚膜再经过预热、横向拉伸、定型、冷却，得到薄膜，预热温度为170℃,横向拉伸温度为155℃,定型温度为167℃；
S5、薄膜经过TDO冷却，牵引辊冷却和电晕处理，然后收卷得到成品。
实施例3
一种抗静电消光膜及其制备方法，抗静电消光膜为三层结构，从上到下依次包括抗粘连层、芯层、消光层；
抗粘连层由如下原料按重量份组成：聚丙烯90份、防黏剂3份；
芯层由如下原料按重量份组成：聚丙烯90份、抗静电剂4份；
消光层由如下原料按重量份组成：消光母料96份、爽滑剂3份；
上述抗静电消光膜的三层结构是通过熔融共挤和双向拉伸后形成的。
上述抗静电消光膜的制备方法，包括如下步骤：
S1、分别将抗粘连层、芯层、消光层对应的原料定量投入第一挤出机、第二挤出机、第三挤出机；
S2、抗粘连层、芯层、消光层对应的原料分别在第一挤出机、第二挤出机、第三挤出机内加热成熔融状态，分别经过过滤网过滤后，在三层结构模头中汇合挤出成膜片，然后通过激冷辊和水池快速冷却定型为厚片，第一挤出机、第二挤出机、第三挤出机的加热温度为250℃，模头温度为240℃；
S3、厚片经过预热、纵向拉伸、定型，得到厚膜，预热温度为138℃，纵向拉伸温度为128℃，定型温度为139℃；
S4、厚膜再经过预热、横向拉伸、定型、冷却，得到薄膜，预热温度为172℃,横向拉伸温度为155℃,定型温度为167℃；
S5、薄膜经过TDO冷却，牵引辊冷却和电晕处理，然后收卷得到成品。
以上所述的本发明实施方式，并不构成对本发明保护范围的限定,任何在本发明的精神和原则之内所作的修改、等同替换和改进等，均应包含在本发明的权利要求保护范围之内。

Claims (8)

1.一种抗静电消光膜，其特征在于，所述抗静电消光膜为三层结构，从上到下依次包括抗粘连层、芯层、消光层；
所述抗粘连层由如下原料按重量份组成：聚丙烯80-90份、防黏剂1-3份；
所述芯层由如下原料按重量份组成：聚丙烯80-90份、抗静电剂2-4份；
所述消光层由如下原料按重量份组成：消光母料90-96份、爽滑剂2-3份；
所述抗静电消光膜的三层结构是通过熔融共挤和双向拉伸后形成的。
2.根据权利要求1所述的抗静电消光膜，其特征在于，所述防黏剂为合成二氧化硅、玻璃微珠、有机硅聚合物或甲基丙烯酸醋的聚合物。
3.根据权利要求1所述的抗静电消光膜，其特征在于，所述抗静电剂为抗静电剂HZ-1或抗静电剂HZ-14或乙二醇月桂酸酰胺或乙氧基化烷基胺。
4.根据权利要求1所述的抗静电消光膜，其特征在于，所述爽滑剂为油酸酰胺、芥酸酰胺、硬脂酸钙、硅酮中的一种。
5.根据权利要求1所述的抗静电消光膜的制备方法，其特征在于，包括如下步骤：
S1、分别将抗粘连层、芯层、消光层对应的原料定量投入第一挤出机、第二挤出机、第三挤出机；
S2、抗粘连层、芯层、消光层对应的原料分别在第一挤出机、第二挤出机、第三挤出机内加热成熔融状态，分别经过过滤网过滤后，在三层结构模头中汇合挤出成膜片，然后通过激冷辊和水池快速冷却定型为厚片；
S3、厚片经过预热、纵向拉伸、定型，得到厚膜；
S4、厚膜再经过预热、横向拉伸、定型、冷却，得到薄膜；
S5、薄膜经过TDO冷却，牵引辊冷却和电晕处理，然后收卷得到成品。
6.根据权利要求5所述的抗静电消光膜的制备方法，其特征在于，所述步骤S2中第一挤出机、第二挤出机、第三挤出机的加热温度为250℃，模头温度为240℃。
7.根据权利要求5所述的抗静电消光膜的制备方法，其特征在于，所述步骤S3中预热温度为125-138℃，纵向拉伸温度为122-128℃，定型温度为127-139℃。
8.根据权利要求5所述的抗静电消光膜的制备方法，其特征在于，所述步骤S4中预热温度为168-172℃,横向拉伸温度为155℃,定型温度为167℃。
CN202010063841.2A 2020-01-20 2020-01-20 一种抗静电消光膜及其制备方法 Pending CN111267443A (zh)