CN110981434A - 一种保温墙体材料及其制备方法 - Google Patents

一种保温墙体材料及其制备方法 Download PDF

Info

Publication number
CN110981434A
CN110981434A CN201911243085.5A CN201911243085A CN110981434A CN 110981434 A CN110981434 A CN 110981434A CN 201911243085 A CN201911243085 A CN 201911243085A CN 110981434 A CN110981434 A CN 110981434A
Authority
CN
China
Prior art keywords
parts
wall material
heat
sintering
coarse aggregate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911243085.5A
Other languages
English (en)
Inventor
黄伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wenzhou Beiyuan Environmental Protection Technology Co.,Ltd.
Original Assignee
Xi'an Zhongke Beiang Environmental Protection Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xi'an Zhongke Beiang Environmental Protection Technology Co ltd filed Critical Xi'an Zhongke Beiang Environmental Protection Technology Co ltd
Priority to CN201911243085.5A priority Critical patent/CN110981434A/zh
Publication of CN110981434A publication Critical patent/CN110981434A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种保温墙体材料，按以下原料重量份数配比制成：水泥70‑80份、石蜡15‑40份、高岭土5‑12份、再生粗骨料20‑30份、水30‑60份、木质纤维3‑5份、膨胀珍珠岩30‑55份、秸秆灰渣2‑7份、玻璃纤维10‑15份、硼砂15‑24份、大理石灰10‑15份。其制备方法为：按照上述配比称量原料，并分两次将上述原料进行搅拌，然后烧结，自然冷却即得。该保温墙体材料解决了现有保温墙体材料保温性能低，强度差的缺点。

Description

一种保温墙体材料及其制备方法
技术领域
本发明属于建筑材料制备技术领域，具体涉及一种保温墙体材料；本发明还涉及一种保温墙体材料的制备方法。
背景技术
随着社会发展，国家实行墙体改革政策，以实现保护土地、节约能源的目的。近几年在社会上出现的新型墙体材料种类越来越多，其中应用较多的，有石膏或水泥轻质隔墙板、彩钢板、加气混凝土砌块、钢丝网架泡沫板、小型混凝土空心砌块、石膏板、石膏砌块、陶粒砌块、烧结多孔砖、页岩砖、实心混凝土砖、PC大板、水平孔混凝土墙板、活性炭墙体、新型隔墙板等。
目前墙体使用的保温材料主要存在耐久性差，使用寿命短，并且保温效果不强，自重较大。因此对建筑用墙体保温材料进行研究是十分必要的。
发明内容
本发明的目的是提供一种保温墙体材料，解决了现有保温墙体材料保温性能低，强度差的缺点。
本发明的另一个目的是提供一种保温墙体材料的制备方法。
本发明所采用的技术方案是，一种保温墙体材料，按以下原料重量份数配比制成：水泥70-80份、石蜡15-40份、高岭土5-12份、再生粗骨料20-30份、水30-60份、木质纤维3-5份、膨胀珍珠岩30-55份、秸秆灰渣2-7份、玻璃纤维10-15份、硼砂15-24份、大理石灰10-15份。
本发明的特点还在于，
再生粗骨料粒径范围为15-20mm。
本发明所采用的另一种技术方案是：一种保温墙体材料的制备方法，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥70-80份、石蜡15-40份、高岭土5-12份、再生粗骨料20-30份、水30-60份、木质纤维3-5份、膨胀珍珠岩30-55份、秸秆灰渣2-7份、玻璃纤维10-15份、硼砂15-24份、大理石灰10-15份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌80s～120s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌50s～150s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
本发明的特点还在于，
再生粗骨料粒径范围为15-20mm。
步骤4中，人工搅拌时间为5-10min。
步骤4中，烧结分两个阶段：第一阶段烧结温度为300-400℃，烧结时间为20-30min，第二阶段烧结温度为800-1100℃，烧结时间为10-15min。
本发明的有益效果是，本发明的保温墙体材料具有保温隔热性，其抗压强度较高，自重轻，在施工后，不会出现开裂脱落现象，可直接在其表面进行涂饰；可以有效的提高建筑的施工质量，建筑的使用价值得到充分的发挥，提高了其社会经济效益。恶意消纳固体废弃物，减少资源消费，减轻对环境的污染，达到节能减排和发展循环经济的目的。
具体实施方式
下面结合具体实施方式对本发明进行详细说明。
本发明提供了一种保温墙体材料，按以下原料重量份数配比制成：水泥70-80份、石蜡15-40份、高岭土5-12份、再生粗骨料20-30份、水30-60份、木质纤维3-5份、膨胀珍珠岩30-55份、秸秆灰渣2-7份、玻璃纤维10-15份、硼砂15-24份、大理石灰10-15份。
再生粗骨料粒径范围为15-20mm。
本发明还提供上述一种保温墙体材料的制备方法，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥70-80份、石蜡15-40份、高岭土5-12份、再生粗骨料20-30份、水30-60份、木质纤维3-5份、膨胀珍珠岩30-55份、秸秆灰渣2-7份、玻璃纤维10-15份、硼砂15-24份、大理石灰10-15份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌80s～120s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌50s～150s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
再生粗骨料粒径范围为15-20mm。
步骤4中，人工搅拌时间为5-10min。
步骤4中，烧结分两个阶段：第一阶段烧结温度为300-400℃，烧结时间为20-30min，第二阶段烧结温度为800-1100℃，烧结时间为10-15min。
实施例1
一种保温墙体材料的制备方法，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥70份、石蜡15份、高岭土5份、再生粗骨料20份、水30份、木质纤维3份、膨胀珍珠岩30份、秸秆灰渣2份、玻璃纤维10份、硼砂15份、大理石灰10份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌80s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌50s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
再生粗骨料粒径范围为15mm。
步骤4中，人工搅拌时间为5min。
步骤4中，烧结分两个阶段：第一阶段烧结温度为300℃，烧结时间为20min，第二阶段烧结温度为800-1100℃，烧结时间为10min。
实施例2
一种保温墙体材料的制备方法，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥80份、石蜡40份、高岭土12份、再生粗骨料30份、水60份、木质纤维5份、膨胀珍珠岩55份、秸秆灰渣7份、玻璃纤维15份、硼砂24份、大理石灰15份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌120s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌150s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
再生粗骨料粒径范围为20mm。
步骤4中，人工搅拌时间为10min。
步骤4中，烧结分两个阶段：第一阶段烧结温度为400℃，烧结时间为30min，第二阶段烧结温度为1100℃，烧结时间为15min。
实施例3
一种保温墙体材料的制备方法，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥75份、石蜡30份、高岭土6份、再生粗骨料25份、水40份、木质纤维4份、膨胀珍珠岩40份、秸秆灰渣6份、玻璃纤维12份、硼砂20份、大理石灰12份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌100s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌100s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
再生粗骨料粒径范围为16mm。
步骤4中，人工搅拌时间为6min。
步骤4中，烧结分两个阶段：第一阶段烧结温度为350℃，烧结时间为25min，第二阶段烧结温度为800-1100℃，烧结时间为12min。
实施例4
一种保温墙体材料的制备方法，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥75份、石蜡15份、高岭土8份、再生粗骨料30份、水60份、木质纤维4份、膨胀珍珠岩40份、秸秆灰渣5份、玻璃纤维15份、硼砂20份、大理石灰12份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌80s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌50s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
再生粗骨料粒径范围为20mm。
步骤4中，人工搅拌时间为10min。
步骤4中，烧结分两个阶段：第一阶段烧结温度为400℃，烧结时间为30min，第二阶段烧结温度为1100℃，烧结时间为15min。
实施例5
一种保温墙体材料的制备方法，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥80份、石蜡140份、高岭土12份、再生粗骨料20份、水60份、木质纤维3份、膨胀珍珠岩55份、秸秆灰渣2份、玻璃纤维15份、硼砂20份、大理石灰12份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌100s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌60s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
再生粗骨料粒径范围为16mm。
步骤4中，人工搅拌时间为7min。
步骤4中，烧结分两个阶段：第一阶段烧结温度为350℃，烧结时间为30min，第二阶段烧结温度为1100℃，烧结时间为12min。

Claims (6)

1.一种保温墙体材料，其特征在于，按以下原料重量份数配比制成：水泥70-80份、石蜡15-40份、高岭土5-12份、再生粗骨料20-30份、水30-60份、木质纤维3-5份、膨胀珍珠岩30-55份、秸秆灰渣2-7份、玻璃纤维10-15份、硼砂15-24份、大理石灰10-15份。
2.根据权利要求1所述的一种保温墙体材料，其特征在于，所述再生粗骨料粒径范围为15-20mm。
3.一种保温墙体材料的制备方法，其特征在于，包括以下步骤：
步骤1，按照以下原料的配比备料，
水泥70-80份、石蜡15-40份、高岭土5-12份、再生粗骨料20-30份、水30-60份、木质纤维3-5份、膨胀珍珠岩30-55份、秸秆灰渣2-7份、玻璃纤维10-15份、硼砂15-24份、大理石灰10-15份；
步骤2、将步骤1中水泥、石蜡、高岭土、再生粗骨料、水、木质纤维份倒入搅拌机，搅拌80s～120s；
步骤3、再将膨胀珍珠岩、秸秆灰渣、玻璃纤维、硼砂、大理石灰倒入搅拌机，搅拌50s～150s；
步骤4、将步骤3得到的混合物人工搅拌，最后经挤压成型、干燥、烧结，自然降至室温，即得。
4.根据权利要求3所述的一种保温墙体材料的制备方法，其特征在于，所述再生粗骨料粒径范围为15-20mm。
5.根据权利要求3所述的一种保温墙体材料的制备方法，其特征在于，步骤4中，人工搅拌时间为5-10min。
6.根据权利要求3所述的一种保温墙体材料的制备方法，其特征在于，步骤4中，烧结分两个阶段：第一阶段烧结温度为300-400℃，烧结时间为20-30min，第二阶段烧结温度为800-1100℃，烧结时间为10-15min。
CN201911243085.5A 2019-12-06 2019-12-06 一种保温墙体材料及其制备方法 Pending CN110981434A (zh)