CN110876508A - 一种远红外线保健鞋垫的制备方法 - Google Patents
一种远红外线保健鞋垫的制备方法 Download PDFInfo
- Publication number
- CN110876508A CN110876508A CN201911260382.0A CN201911260382A CN110876508A CN 110876508 A CN110876508 A CN 110876508A CN 201911260382 A CN201911260382 A CN 201911260382A CN 110876508 A CN110876508 A CN 110876508A
- Authority
- CN
- China
- Prior art keywords
- percent
- far infrared
- auxiliary agent
- polyether polyol
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种远红外线保健鞋垫的制备方法,由以下重量百分比的原料制成:聚醚多元醇及助剂混合料55‑60%、催化剂0.5‑0.9%、硬化剂2.0‑2.5%、水0.5‑1%、抗菌剂0.01‑0.05%、远红外材料5‑8%和聚异氰酸酯及助剂混合料30‑35%,制备过程包括先将除聚异氰酸酯及助剂混合料以外其他原料预先混合,然后再加入聚异氰酸酯及助剂混合料搅拌均匀,恒温固化后脱模即得鞋垫,本发明使用聚醚多元醇及助剂混合料和聚异氰酸酯及助剂混合料作为基材制备柔软舒适弹性佳的聚氨酯鞋垫,赋予产品良好的抗压缩负荷性能及变形复原性能,另外,采用远红外材料和药物相互结合,产品能产生对人体最有益红外波段,赋予产品良好的保健性能。
Description
技术领域
本发明涉及一种保健类鞋垫,特别是一种远红外线保健鞋垫的制备方法。
背景技术
随着人们生活水平的提高,人们对鞋子的舒适度和保健功能也越来越重视,远红外线对于人体非常有益,可改善血液循环,促进新陈代谢,但是许多设计仅仅在鞋垫内设置远红外线层或远红外配件,难以实现均匀、全面的保健效果,市面上也有设计混入远红外线材质制成的鞋垫,但是配方较为单一,效果有限,难以满足用户需求。
发明内容
为了克服现有技术的不足,本发明提供一种远红外线保健鞋垫制备方法。
本发明解决其技术问题所采用的技术方案是:
一种远红外线保健鞋垫的制备方法,由以下重量百分比的原料制成:A料65-70%和B料30-35%;
其中:
所述A料包括:聚醚多元醇及助剂混合料55-60%、催化剂0.5-0.9%、硬化剂2.0-2.5%、水0.5-1%、抗菌剂0.01-0.05%和远红外材料5-8%;
所述聚醚多元醇及助剂混合料包括聚醚多元醇54-59%、三乙二胺0.8-1%和聚醚改性硅氧烷0.8-1%;
所述催化剂包括聚醚多元醇0.49-0.88%,乙二醇0.01-0.02%;
所述硬化剂包括乙二醇2.0-2.5%;
所述抗菌剂为紫外线吸收剂混合物;
所述远红外材料包括:滑石粉1-1.5%、二氧化硅1-2%、白石脂1-2%、竹炭2.5-3%、酞酐0.5-1%、氧化铝0.5-1.0%、硫酸钙1-1.5%、沸石0.5-1%和明矾0.1-0.5%;
所述B料为聚异氰酸酯及助剂混合料,所述聚异氰酸酯及助剂混合料包括:二苯甲烷二异氰酸酯21-24.5%、聚醚多元醇7.8-9.1%、三乙二胺0.6-0.7%和聚醚改性硅氧烷0.6-0.7%。
一种制备所述远红外线矫正鞋垫的方法,其步骤如下:
(1)预处理:将所述A料按组分比例预先混合;
(2)计量混合:将步骤(1)中制得的A料与所述B料分别经过计量泵执行计量后,输送至混合腔,混合腔内以2800-3000r/min的速度搅拌混合;
(3)吐料成型:步骤(2)混合后的混合料和B料定量注入模具,经烘道恒温35℃-40℃固化8分钟,脱模后即为鞋垫。
本发明的有益效果是:本发明提供一种远红外线保健鞋垫的制备方法,使用聚醚多元醇及助剂混合料和聚异氰酸酯及助剂混合料作为基材制备柔软舒适弹性佳的聚氨酯鞋垫,赋予产品良好的抗压缩负荷性能及变形复原性能,另外,采用远红外材料和药物相互结合,产品能产生对人体最有益红外波段,赋予产品良好的保健性能。
附图说明
下面结合附图和实施例对本发明进一步说明。
图1是本发明的制作流程图。
具体实施方式
参照图1,一种远红外线保健鞋垫的制备方法,由以下重量百分比的原料制成:A料65-70%和B料30-35%;
其中:
所述A料包括:聚醚多元醇及助剂混合料55-60%、催化剂0.5-0.9%、硬化剂2.0-2.5%、水0.5-1%、抗菌剂0.01-0.05%和远红外材料5-8%;
所述远红外材料包括:滑石粉1-1.5%、二氧化硅1-2%、白石脂1-2%、竹炭2.5-3%、酞酐0.5-1%、氧化铝0.5-1.0%、硫酸钙1-1.5%、沸石0.5-1%和明矾0.1-0.5%;
所述聚醚多元醇及助剂混合料为型号810M80-A的聚醚多元醇及助剂混合料(东莞泰欣新材料科技有限公司产),其成分为:聚醚多元醇96%,三乙二胺2%和聚醚改性硅氧烷2%;
所述催化剂为型号3050的聚醚多元醇及助剂混合料(东莞泰欣新材料科技有限公司产),其成分为:聚醚多元醇96%和乙二醇4%;
所述硬化剂为型号1110的聚醚多元醇(东莞泰欣新材料科技有限公司产),其成分为乙二醇100%;
所述抗菌剂为型号TISORB H1175的紫外线吸收剂混合物(东莞蓝泰新材料科技有限公司产);
所述B料为聚异氰酸酯及助剂混合料,所述聚异氰酸酯及助剂混合料包括:二苯甲烷二异氰酸酯21-24.5%、聚醚多元醇7.8-9.1%、三乙二胺0.6-0.7%和聚醚改性硅氧烷0.6-0.7%。
聚醚多元醇是由起始剂(含活性氢基团的化合物)与环氧乙烷、环氧丙烷、环氧丁烷等在催化剂存在下经加聚反应制得,毒性低,常用于制造通用聚氨酯泡沫塑料、胶黏剂和弹性体等,制得产品尺寸稳定性好,导热系数低,因此本发明采用聚醚多元醇为主要原料制作具有弹性的鞋垫,可以满足长期使用不易变形,给予人体行走时一定的缓冲力的可以增强本发明的舒适性能,另外,足部作为远离心脏端,容易受凉,本发明导热系数低,可以增强足部的保温性能,增强本发明的保健性能。
远红外线或称长波红外线,波长1.5-400μm,人体发射的远红外波长在9.6μm附近,在红外线区域中,对人体最有益的波段就是4到16μm这个波段范围,本发明采用了滑石粉、二氧化硅、白石脂、竹炭、酞酐、氧化铝、硫酸钙、沸石和明矾的混合剂作为远红外材料,其中二氧化硅红外波长为4.5μm、竹炭产生的红外波长在8μm-25μm、氧化铝红外波长为5.5μm等,所述远红外材料中能产生红外波长的材料与人体发射出来的远红外线的波长相近,能够与细胞产生共振效应,可将远红外热能传递到人体皮下较深的部分,本发明采用远红外材料和药物相互结合,令产品能够实现促进血液循环、强化各组织之间的新陈代谢、增加组织的再生能力、提高机体的免疫能力等医疗保健的作用,另外,远红外材料中的竹炭具有吸收气味的功能,可以吸收穿着过程中产生的汗味,给予本发明防臭的功能。
紫外线吸收剂是一种光稳定剂,能吸收阳光及荧光光源中的紫外线部分,而本身又不发生变化,紫外线吸收剂本身具有许多优点,稳定性好、混溶性好、耐浸洗、价廉易得等,主要包括水杨酸酯类、苯酮类、苯并三唑类、取代丙烯腈类、三嗪类和受阻胺类,以水杨酸苯酯为例,可以用作医药消毒防腐剂,可给予本发明抗菌性能。
聚异氰酸酯及助剂混合料是制造聚氨酯弹性体的主要原料,制得的聚氨酯制品显示出高的抗撕裂强度,耐低温柔软性,低导热系数等良好的化学稳定性等特点,使本发明即使在温度较低的情况下使用也不易变硬、不易撕裂,保持本发明的柔软舒适的性能,增强本发明的应用范围。
一种制备所述远红外线矫正鞋垫的方法,其步骤如下:
(1)预处理:将所述A料按组分比例预先混合;
(2)计量混合:将步骤(1)中制得的A料与所述B料分别经过计量泵执行计量后,输送至混合腔,混合腔内以2800-3000r/min的速度搅拌混合;
(3)吐料成型:步骤(2)混合后的混合料和B料定量注入模具,经烘道恒温35℃-40℃固化8分钟,脱模后即为鞋垫。
以上的实施方式不能限定本发明创造的保护范围,专业技术领域的人员在不脱离本发明创造整体构思的情况下,所做的均等修饰与变化,均仍属于本发明创造涵盖的范围之内。
Claims (2)
1.一种远红外线保健鞋垫的制备方法,其特征在于由以下重量百分比的原料制成:A料65-70%和B料30-35%;
其中:
所述A料包括:聚醚多元醇及助剂混合料55-60%、催化剂0.5-0.9%、硬化剂2.0-2.5%、水0.5-1%、抗菌剂0.01-0.05%和远红外材料5-8%;
所述聚醚多元醇及助剂混合料包括聚醚多元醇54-59%、三乙二胺0.8-1%和聚醚改性硅氧烷0.8-1%;
所述催化剂包括聚醚多元醇0.49-0.88%,乙二醇0.01-0.02%;
所述硬化剂包括乙二醇2.0-2.5%;
所述抗菌剂为紫外线吸收剂混合物;
所述远红外材料包括:滑石粉1-1.5%、二氧化硅1-2%、白石脂1-2%、竹炭2.5-3%、酞酐0.5-1%、氧化铝0.5-1.0%、硫酸钙1-1.5%、沸石0.5-1%和明矾0.1-0.5%;
所述B料为聚异氰酸酯及助剂混合料,所述聚异氰酸酯及助剂混合料包括:二苯甲烷二异氰酸酯21-24.5%、聚醚多元醇7.8-9.1%、三乙二胺0.6-0.7%和聚醚改性硅氧烷0.6-0.7%。
2.一种制备如权利要求1所述远红外线矫正鞋垫的方法,其特征在于其步骤如下:
(1)预处理:将所述A料按组分比例预先混合;
(2)计量混合:将步骤(1)中制得的A料与所述B料分别经过计量泵执行计量后,输送至混合腔,混合腔内以2800-3000r/min的速度搅拌混合;
(3)吐料成型:步骤(2)混合后的混合料和B料定量注入模具,经烘道恒温35℃-40℃固化8分钟,脱模后即为鞋垫。