CN110713756A - 一种防伪用印刷温变油墨及其制备方法 - Google Patents
一种防伪用印刷温变油墨及其制备方法 Download PDFInfo
- Publication number
- CN110713756A CN110713756A CN201911075558.5A CN201911075558A CN110713756A CN 110713756 A CN110713756 A CN 110713756A CN 201911075558 A CN201911075558 A CN 201911075558A CN 110713756 A CN110713756 A CN 110713756A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- mixture
- printing temperature
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及印刷防伪技术领域，尤其涉及一种防伪用印刷温变油墨及其制备方法。该防伪用印刷温变油墨按照质量份，包括聚乙烯醇缩丁醛7‑9份、富马酸化松香酯1.5‑2.5份、微胶囊温变色粉11‑13份、滑石粉9‑11份、乙酰柠檬酸三丁酯1.5‑2.5份以及溶剂64‑68份。其具有制备简单，可批量生产，且生产成本低廉的特点。同时，于香烟接装纸上印刷该温变油墨时，不会影响香烟本身的燃烧特性，不会产生有毒物质，且具有良好的防伪效果。
Description
技术领域
本发明涉及印刷防伪技术领域，尤其涉及一种防伪用印刷温变油墨及其制备方法。
背景技术
现有印刷防伪技术有如下几种：
（1）平凸合印，即利用凸版印刷机压力大，着墨均匀的长处大面积的实地色块，用平版印刷机压力平柔的长处印四色连续调和复杂线条部分，还可以采用手、凸、凹和平、凸、凹漏等多工序合印。印刷工序愈复杂、印刷难度愈大，防伪效果就愈好。因此为了达到较好的防伪效果，其不可避免地具有印刷复杂、操作成本高的缺点。
（2）多色串印，即根据印品要求，在墨槽里放置隔板后，再在不同隔版里分别放入多种色相的油墨。在串墨辊的串动作用下，使相邻部分的油墨混合后再传至印版上。从印品上很难看出墨槽隔板的放置距离，能起到一定的防伪作用。这种技术一方面浪费油墨、另一方面也不便于客户对真假品的分辨。
（3）凹印技术，即印版上图文部位是凸起的，印出来的图文，其油墨也是凸起的，而图文线条清晰，层次分明，手触即能感觉。这种防伪技术具有易于被模仿的缺点。
（4）激光全息虹膜印刷，即采用激光全息摄影手段，在防震室中制出模版，然后通过一定压力将图纹转移到某种载体上。其产品在45度点光源照射下，可产生色彩斑斓的彩虹状的独特效果，图像的立体感极强。这种技术具有操作复杂、印刷成本高的缺点。
（5）手工雕刻版压印，即选用质地较好的铜版材，靠雕刻师手工技艺将用户要求的图文(主要是图案)用雕刀分层次雕出，雕刻师的技艺不是短时间内能够掌握的，且不同的雕刻师有不同的雕刻风格，即使是同一雕刻师也不可能刻出两块一模一样的模版，因而具有较强的防伪作用。这种防伪技术具有费时费力的缺点。
（6）特种光泽印刷，目前主要有金属光泽印刷、珠光印刷、珍珠光泽印刷、折光印刷、可变光泽印刷、激光全息虹膜印刷、结晶体光泽印刷、仿金属蚀刻印刷和哑光印刷等。其中金属光泽印刷是采用铝箔类金属复合纸，着以较透明的油墨，在印品上形成特殊金属光泽效果。这种防伪技术具有易于被仿制的缺点。
（7）温变油墨，将可逆显色或区间显色的温变油墨以logo、防伪标识、或其他方式印刷至套印的最后一道印刷，常温下不显色，经升温显色，logo或防伪标识开始显现出来；或以可逆消色油墨进行印刷，经升温后，常温下显示的logo或防伪标识开始消失，恢复常温后，logo或防伪标识重新出现，从而达到防伪的效果。
在实际应用时，通常把温变油墨的变色温度点设置为接近人体的体温，这样我们可以靠双手的触摸就可使商品图案发生颜色变化从而对防伪标识进行鉴别。因为防伪的使用对象是普通老百姓，这种防伪方法简单容易，一看就懂。同时，由于不同的温变油墨具有不同的显色温度范围和颜色范围，且温变油墨可批量生产、生产成本也较低，因此采用温变油墨做防伪技术具有良好的优势。
发明内容
本发明要解决上述问题，提供一种防伪用印刷温变油墨及其制备方法。
本发明解决问题的技术方案是，提供一种防伪用印刷温变油墨，按照质量份，包括聚乙烯醇缩丁醛7-9份、富马酸化松香酯1.5-2.5份、微胶囊温变色粉11-13份、滑石粉9-11份、乙酰柠檬酸三丁酯1.5-2.5份以及溶剂64-68份。
优选地，所述富马酸化松香酯由松香、富马酸和多元醇以100：（5-8）：（10-15）的质量比混合制得。
优选地，所述多元醇选用乙二醇、甘油、季戊四醇中的一种。
优选地，所述多元醇选用季戊四醇。
优选地，所述富马酸化松香酯的制备步骤包括：将100份松香、5-8份富马酸和0.1-0.2份三聚甲醛混合后于真空搅拌加热至190-195℃，保温1h后升温至220℃，加入10-15份季戊四醇和0.2-0.3份催化剂，升温至260-280℃并回流反应6-7h后，脱色脱油得到富马酸松香季戊四醇酯。
优选地，还包括以下步骤：将富马酸松香季戊四醇酯溶于邻苯二甲酸二丁酯得到油溶液，将AgI、Ag2S、HgI2和油溶液共同分散于浓度为0.5%碳酸氢钠溶液中，加入乳化剂后搅拌，向乳化体系中加入水溶性单体二乙烯三胺，并不断搅拌。以微胶囊技术保持热敏颜料的活性。
优选地，所述AgI、Ag2S、HgI2以10:（0.8-1.2）：（4-6）的质量比混合。
优选地，所述溶剂选用乙醇、异丙醇、正丁醇、醋酸乙酯、醋酸异丙酯和环己酮中的一种。
优选地，所述溶剂选用乙醇。
本发明的另一个目的是提供第一种防伪用印刷温变油墨的制备方法，包括以下步骤：
（1）将聚乙烯醇缩丁醛、不饱和聚酯树脂混合于部分溶剂，于35-48℃搅拌分散得到混合物1；
（2）向混合物1中加入微胶囊温变色粉和滑石粉，于40-45℃搅拌分散后，磨细至细度10-15μm得到混合物2；
（3）向混合物2中加入乙酰柠檬酸三丁酯和剩余溶剂，过滤包装得到防伪用印刷温变油墨。
本发明的有益效果：
制备简单，可批量生产，且生产成本低廉。于香烟接装纸上印刷时，不会影响香烟本身的燃烧特性，不会产生有毒物质，且具有良好的防伪效果。
具体实施方式
以下是本发明的具体实施方式，并对本发明的技术方案作进一步的描述，但本发明并不限于这些实施例。
实施例1
一种防伪用印刷温变油墨，按照质量份，包括聚乙烯醇缩丁醛8份、富马酸化松香酯2份、微胶囊温变色粉12份、滑石粉10份、乙酰柠檬酸三丁酯2份以及乙醇66份。
其中，富马酸化松香酯由松香、富马酸和季戊四醇以100：7：12的质量比混合制得。富马酸化松香酯的制备步骤包括：将100份松香、7份富马酸和0.15份三聚甲醛混合后于真空搅拌加热至192℃，保温1.5h后升温至210℃，加入12份季戊四醇和0.25份催化剂（催化剂选用氧化锌和氢氧化锂混合物），升温至270℃并回流反应6.5h后，脱色脱油得到富马酸松香季戊四醇酯。然后将富马酸松香季戊四醇酯溶于邻苯二甲酸二丁酯得到油溶液，将AgI、Ag2S、HgI2以10：1：5的质量比混合后和油溶液共同分散于浓度为0.5%碳酸氢钠溶液中，加入乳化剂后搅拌，向乳化体系中加入水溶性单体二乙烯三胺，并不断搅拌。
一种防伪用印刷温变油墨的制备方法，包括以下步骤：
（1）将聚乙烯醇缩丁醛、不饱和聚酯树脂混合于部分溶剂，于40℃搅拌分散得到混合物1；
（2）向混合物1中加入微胶囊温变色粉和滑石粉，于42℃搅拌分散后，磨细至细度12μm得到混合物2；
（3）向混合物2中加入乙酰柠檬酸三丁酯和剩余溶剂，过滤包装得到防伪用印刷温变油墨。
实施例2
一种防伪用印刷温变油墨，按照质量份，包括聚乙烯醇缩丁醛9份、富马酸化松香酯2.5份、微胶囊温变色粉13份、滑石粉11份、乙酰柠檬酸三丁酯2.5份以及乙醇68份。
其中，富马酸化松香酯由松香、富马酸和季戊四醇以100：8：15的质量比混合制得。富马酸化松香酯的制备步骤包括：将100份松香、8份富马酸和0.2份三聚甲醛混合后于真空搅拌加热至195℃，保温2h后升温至220加入15季戊四醇和0.3剂（催化剂选用氢氧化锂），升温至280℃并回流反应7h后，脱色脱油得到富马酸松香季戊四醇酯。然后将富马酸松香季戊四醇酯溶于邻苯二甲酸二丁酯得到油溶液，将AgI、Ag2S、HgI2以10：1.2：6的质量比混合后和油溶液共同分散于浓度为0.5%碳酸氢钠溶液中，加入乳化剂后搅拌，向乳化体系中加入水溶性单体二乙烯三胺，并不断搅拌。
一种防伪用印刷温变油墨的制备方法，包括以下步骤：
（1）将聚乙烯醇缩丁醛、不饱和聚酯树脂混合于部分溶剂，于48℃搅拌分散得到混合物1；
（2）向混合物1中加入微胶囊温变色粉和滑石粉，于45℃搅拌分散后，磨细至细度15μm得到混合物2；
（3）向混合物2中加入乙酰柠檬酸三丁酯和剩余溶剂，过滤包装得到防伪用印刷温变油墨。
实施例3
一种防伪用印刷温变油墨，按照质量份，包括聚乙烯醇缩丁醛7份、富马酸化松香酯1.5份、微胶囊温变色粉11份、滑石粉9份、乙酰柠檬酸三丁酯1.5份以及乙醇64份。
其中，富马酸化松香酯由松香、富马酸和季戊四醇以100：5：10的质量比混合制得。富马酸化松香酯的制备步骤包括：将100份松香、5份富马酸和0.1份三聚甲醛混合后于真空搅拌加热至190℃，保温1h后升温至200℃，加入10份季戊四醇和0.2份催化剂（催化剂选用氧化锌），升温至260℃并回流反应6h后，脱色脱油得到富马酸松香季戊四醇酯。然后将富马酸松香季戊四醇酯溶于邻苯二甲酸二丁酯得到油溶液，将AgI、Ag2S、HgI2以10：0.8：4的质量比混合后和油溶液共同分散于浓度为0.5%碳酸氢钠溶液中，加入乳化剂后搅拌，向乳化体系中加入水溶性单体二乙烯三胺，并不断搅拌。
一种防伪用印刷温变油墨的制备方法，包括以下步骤：
（1）将聚乙烯醇缩丁醛、不饱和聚酯树脂混合于部分溶剂，于35℃搅拌分散得到混合物1；
（2）向混合物1中加入微胶囊温变色粉和滑石粉，于40℃搅拌分散后，磨细至细度10μm得到混合物2；
（3）向混合物2中加入乙酰柠檬酸三丁酯和剩余溶剂，过滤包装得到防伪用印刷温变油墨。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。
Claims (10)
1.一种防伪用印刷温变油墨，其特征在于：按照质量份，包括聚乙烯醇缩丁醛7-9份、富马酸化松香酯1.5-2.5份、微胶囊温变色粉11-13份、滑石粉9-11份、乙酰柠檬酸三丁酯1.5-2.5份以及溶剂64-68份。
2.根据权利要求1所述的一种防伪用印刷温变油墨，其特征在于：所述富马酸化松香酯由松香、富马酸和多元醇以100：（5-8）：（10-15）的质量比混合制得。
3.根据权利要求2所述的一种防伪用印刷温变油墨，其特征在于：所述多元醇选用乙二醇、甘油、季戊四醇中的一种。
4.根据权利要求3所述的一种防伪用印刷温变油墨，其特征在于：所述多元醇选用季戊四醇。
5.根据权利要求4所述的一种防伪用印刷温变油墨，其特征在于：所述富马酸化松香酯的制备步骤包括：将100份松香、5-8份富马酸和0.1-0.2份三聚甲醛混合后于真空搅拌加热至190-195℃，保温1-2h后升温至200-220℃，加入10-15份季戊四醇和0.2-0.3份催化剂，升温至260-280℃并回流反应6-7h后，脱色脱油得到富马酸松香季戊四醇酯。
6.根据权利要求5所述的一种防伪用印刷温变油墨，其特征在于：还包括以下步骤：将富马酸松香季戊四醇酯溶于邻苯二甲酸二丁酯得到油溶液，将AgI、Ag2S、HgI2和油溶液共同分散于浓度为0.5%碳酸氢钠溶液中，加入乳化剂后搅拌，向乳化体系中加入水溶性单体二乙烯三胺，并不断搅拌。
7.根据权利要求6所述的一种防伪用印刷温变油墨，其特征在于：所述AgI、Ag2S、HgI2以10：（0.8-1.2）：（4-6）的质量比混合。
8.根据权利要求1所述的一种防伪用印刷温变油墨，其特征在于：所述溶剂选用乙醇、异丙醇、正丁醇、醋酸乙酯、醋酸异丙酯和环己酮中的一种。
9.根据权利要求8所述的一种防伪用印刷温变油墨，其特征在于：所述溶剂选用乙醇。
10.一种根据权利要求1-9任一项所述的防伪用印刷温变油墨的制备方法，其特征在于：包括以下步骤：
(1)将聚乙烯醇缩丁醛、不饱和聚酯树脂混合于部分溶剂，于35-48℃搅拌分散得到混合物1；
(2)向混合物1中加加入微胶囊温变色粉和滑石粉，于40-45℃搅拌分散后，磨细至细度10-15μm得到混合物2；
(3)向混合物2中加入乙酰柠檬酸三丁酯和剩余溶剂，过滤包装得到防伪用印刷温变油墨。