CN110628267A - 一种烟用珠光效果的印刷油墨 - Google Patents
一种烟用珠光效果的印刷油墨 Download PDFInfo
- Publication number
- CN110628267A CN110628267A CN201910980901.4A CN201910980901A CN110628267A CN 110628267 A CN110628267 A CN 110628267A CN 201910980901 A CN201910980901 A CN 201910980901A CN 110628267 A CN110628267 A CN 110628267A
- Authority
- CN
- China
- Prior art keywords
- parts
- pearlescent
- printing ink
- cigarettes
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种烟用珠光效果的印刷油墨，该种油墨按质量份包含以下组份：珠光色料11‑15份、聚合体26‑38份、交联剂3‑5份、分散剂5‑9份和去离子水45‑60份。该种油墨采用珠光粉、银粉和铝粉三种珠光效果颜料进行珠光效果的点缀，由于三种颜料的珠光效果强度不同，所以在固化后呈现的珠光色彩较为真实、并且色彩分明，同时，通过三种颜料粒径的变化，达到珠光效果的层次感变化，更加绚丽夺目。
Description
技术领域
本发明涉及香烟包装印刷技术领域，具体涉及一种烟用珠光效果的印刷油墨。
背景技术
中国不仅是一个人口大国，而且也是一个香烟消耗大国，近些年来，随着人们的生活水平的日益提高，人们不仅仅关注于香烟的口感和口味，同时对香烟的包装盒也是逐渐的挑剔起来，特别是一些成功人士，或者女士吸烟群众，对香烟的包装盒外观要求越来越关注，目前香烟外包装印刷工艺大多较为单一，图文色彩也略显单调，已无法满足现有市场的急切需求。
公开号为CN201310600459.0的国内发明专利，一种一次印刷紫外光固化珠光油墨，由下列重量份的原料制备而成：有机颜料1-2、E-12环氧树脂20-23、纳米铁矿尾渣粉1-2、双酚A环氧丙烯酸酯30-35、聚酯丙烯酸酯14-18、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、1173光引发剂4-7、二氨基二苯基砜5-7、肉桂精油1-2、抗氧剂10352-3、助剂4-5；
所述助剂由下列重量份的原料制备而成：纳米硅藻土粉0.2-0.3、纳米云母粉0.2-0.3、硅烷偶联剂KH-5502-3、茶多酚2-3、新戊二醇5-7、对叔丁基苯甲酸1-2、抗氧剂10351-2、2-丁氧基乙醇3-4、交联剂TAC2-3、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、没食子酸丙酯2-3、薏仁油1-2；其制备方法是将各物料混合，加热至60-70℃，搅拌反应30-40分钟，即得。
其组份复杂，在固化交联时很容易产生组份间的不兼容造成的固化不彻底现象，直接影响印刷质量，同时产生珠光效果的纳米铁矿尾渣粉颜色暗淡、成分单一，无法更好的呈现珠光效果。
发明内容
本发明的目的在于，针对上述现有技术的不足，提出一种烟用珠光效果的印刷油墨，该种油墨通过复合而成的珠光色料和合理的粒径范围实现层次分明、效果明显的珠光彩。
本发明提出的一种烟用珠光效果的印刷油墨，按质量份包含以下组份：珠光色料11-15份、聚合体26-38份、交联剂3-5份、分散剂5-9份和去离子水45-60份。
进一步地，所述珠光色料为按质量份包含珠光粉4-6份、银粉3-6份和铝粉3-4份。
进一步地，所述珠光色料的粒径为7-15μm。本发明中的珠光粉、银粉和铝粉实际粒径大小关系为珠光粉＞银粉＞铝粉，这样在固化后不仅呈现不同强度的珠光色彩，同时也可实现不同程度的分层现象，实现珠光立体感效果，层次化清晰，珠光效果最佳。
进一步地，所述聚合体按质量份包含环氧树脂13-17份、丙烯酸乳液10-15份和三羟甲基丙烷三丙烯酸酯单体3-6份。
进一步地，所述交联剂为二甲胺基丙胺。
进一步地，所述分散剂聚丙烯酸钠。
一种烟用珠光效果的印刷油墨的制备方法，包括以下步骤：
S1：将聚合体、交联剂和分散剂加入到分散容器中，进行预分散，得到均匀分散液；
S2：向分散液中加入珠光色料，再次进行分散，得到最终分散液；
S3：将最终分散液加入至珠磨机中研磨，得到半成品；
S4：将半成品过滤、得到一种烟用珠光效果的印刷油墨。
进一步地，S1中预分散采用2-5μm锆珠，分散速度为700r/min～750r/min，分散时间为20～30min。
进一步地，S2中分散采用2-5μm锆珠，分散速度为850r/min～900r/min，分散时间为40～60min。
本发明的一种烟用珠光效果的印刷油墨，该种油墨采用珠光粉、银粉和铝粉三种珠光效果颜料进行珠光效果的点缀，由于三种颜料的珠光效果强度不同，所以在固化后呈现的珠光色彩较为真实、并且色彩分明，同时，通过三种颜料粒径的变化，达到珠光效果的层次感变化，更加绚丽夺目。
具体实施方式
为下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外，本领域技术人员对本发明所做的各种改动或修改，这些等价形式同样落于本申请所要求保护的范围内。本发明实施例中的配比均为以重量计。
实施例1
S1：将含环氧树脂13份、丙烯酸乳液10份和三羟甲基丙烷三丙烯酸酯单体3份、二甲胺基丙胺3份和聚丙烯酸钠5份和去离子水加入到分散容器中，进行预分散，采用2μm锆珠，分散速度为700r/min，分散时间为20min得到均匀分散液；
S2：向分散液中加入珠光色料，珠光色料为按质量份包含珠光粉4份、银粉3份和铝粉3份，再次进行分散，采用2μm锆珠，分散速度为850r/min，分散时间为40min得到最终分散液；
S3：将最终分散液加入至珠磨机中研磨，得到半成品；
S4：将半成品过滤、得到一种烟用珠光效果的印刷油墨。
将得到的印刷油墨进行烟用包装盒的印刷生产，得到一种具有珠光色彩的烟用包装盒。
实施例2
S1：将含环氧树脂15份、丙烯酸乳液13份和三羟甲基丙烷三丙烯酸酯单体5份、二甲胺基丙胺4份和聚丙烯酸钠7份和去离子水加入到分散容器中，进行预分散，采用3μm锆珠，分散速度为720r/min，分散时间为25min得到均匀分散液；
S2：向分散液中加入珠光色料，珠光色料为按质量份包含珠光粉5份、银粉4份和铝粉4份，再次进行分散，采用4μm锆珠，分散速度为870r/min，分散时间为50min得到最终分散液；
S3：将最终分散液加入至珠磨机中研磨，得到半成品；
S4：将半成品过滤、得到一种烟用珠光效果的印刷油墨。
将得到的印刷油墨进行烟用包装盒的印刷生产，得到一种具有珠光色彩的烟用包装盒。
实施例3
S1：将含环氧树脂17份、丙烯酸乳液15份和三羟甲基丙烷三丙烯酸酯单体6份、二甲胺基丙胺5份和聚丙烯酸钠9份和去离子水加入到分散容器中，进行预分散，采用5μm锆珠，分散速度为750r/min，分散时间为30min得到均匀分散液；
S2：向分散液中加入珠光色料，珠光色料为按质量份包含珠光粉6份、银粉6份和铝粉4份，再次进行分散，采用5μm锆珠，分散速度为900r/min，分散时间为60min得到最终分散液；
S3：将最终分散液加入至珠磨机中研磨，得到半成品；
S4：将半成品过滤、得到一种烟用珠光效果的印刷油墨。
将得到的印刷油墨进行烟用包装盒的印刷生产，得到一种具有珠光色彩的烟用包装盒。
以上对本发明的实施例进行了示例性说明，但所述内容仅为本发明的较佳实施例，不能被认为用于限定本发明的实施范围。凡依据本发明申请范围的均等变化与改进等，均应归属于本发明的专利涵盖范围之内。
Claims (10)
1.一种烟用珠光效果的印刷油墨，其特征在于：按质量份包含以下组份：珠光色料11-15份、聚合体26-38份、交联剂3-5份、分散剂5-9份和去离子水45-60份。
2.如权利要求1所述的一种烟用珠光效果的印刷油墨，其特征在于：所述珠光色料为按质量份包含珠光粉4-6份、银粉3-6份和铝粉3-4份。
3.如权利要求1所述的一种烟用珠光效果的印刷油墨，其特征在于：所述珠光色料的粒径为7-15μm。
4.如权利要求3所述的一种烟用珠光效果的印刷油墨，其特征在于：所述珠光粉、银粉和铝粉实际粒径大小关系为珠光粉＞银粉＞铝粉。
5.如权利要求1所述的一种烟用珠光效果的印刷油墨，其特征在于：所述聚合体按质量份包含环氧树脂13-17份、丙烯酸乳液10-15份和三羟甲基丙烷三丙烯酸酯单体3-6份。
6.如权利要求1所述的一种烟用珠光效果的印刷油墨，其特征在于：所述交联剂为二甲胺基丙胺。
7.如权利要求1所述的一种烟用珠光效果的印刷油墨，其特征在于：所述分散剂聚丙烯酸钠。
8.如权利要求1-7任意一项的一种烟用珠光效果的印刷油墨的制备方法，其特征在于：包括以下步骤：
S1：将聚合体、交联剂和分散剂加入到分散容器中，进行预分散，得到均匀分散液；
S2：向分散液中加入珠光色料，再次进行分散，得到最终分散液；
S3：将最终分散液加入至珠磨机中研磨，得到半成品；
S4：将半成品过滤、得到一种烟用珠光效果的印刷油墨。
9.如权利要求8所述的一种烟用珠光效果的印刷油墨的制备方法，其特征在于：S1中预分散采用2-5μm锆珠，分散速度为700r/min～750r/min，分散时间为20～30min。
10.如权利要求8所述的一种烟用珠光效果的印刷油墨，其特征在于：S2中分散采用2-5μm锆珠，分散速度为850r/min～900r/min，分散时间为40～60min。