CN110614280A - 一种在线热卷温度均匀化的处理方法 - Google Patents
一种在线热卷温度均匀化的处理方法 Download PDFInfo
- Publication number
- CN110614280A CN110614280A CN201810631501.8A CN201810631501A CN110614280A CN 110614280 A CN110614280 A CN 110614280A CN 201810631501 A CN201810631501 A CN 201810631501A CN 110614280 A CN110614280 A CN 110614280A
- Authority
- CN
- China
- Prior art keywords
- coil
- temperature
- hot
- heat preservation
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种在线热卷温度均匀化的处理方法,热轧后卷取、打捆的热卷在15分钟内送入在线移动密闭空间保温或/和加热,同时通过钢卷运输链或移动小车直接移送至冷轧机组,在上述热卷运输过程中,采用密闭空间对热卷做在线保温处理;卷取温度控制在350~650℃,在线保温时间至少1小时,热卷直送冷轧机组。本发明方法温度均匀化处理,最终使钢卷头中尾、边中边、钢卷整体性能均匀化的目的。
Description
技术领域
本发明涉及热轧工艺,特别涉及一种在线热卷温度均匀化的处理方法。
背景技术
传统的热轧产线产出热卷,钢卷边部、尾部因冷却速率快,轧制、卷取过程中冷却用水的不均匀化,内外圈表面散热速率不均等一系列影响因素,使卷取后热卷温度存在不均匀的现象,进而引起钢卷性能波动。
目前钢厂制造工艺,主要通过以下方式均匀化处理:
1)热轧层流冷却采用边部遮挡,改善热卷边部温度偏低现象。
2)采用保温坑、保温炉、保温墙等,利用封闭式空间密闭后保温、使钢卷整体温度均匀化。
现有技术边部遮挡只针对改善带钢两侧边部温度;
传统温度均匀化处理:热卷→吊运至热库区、保温坑、保温墙等→吊出至运输链→冷轧,流程复杂、设备构造成本高、保温效果差。保温坑、保温炉、保温墙因为涉及钢卷长时间运输、吊运,保温前时间大于30分钟,过程流程复杂,且在此过程中中热量损失大,加剧内外圈、外层芯部温差变化。
其它热轧产线的方法如:热卷卷取后,通过运输链运输;经过长距离运输后,吊运至精整热库区,利用其它钢卷余热保温;或经过长距离运输后,用行车吊运至保温坑、保温墙等固定式保温空间保温;最后,吊出至运输链,运送至冷轧。
发明内容
本发明的目的在于提供一种热卷温度均匀化的处理方法,使钢卷头中尾、边中边、钢卷整体性能均匀化,且简化工艺流程。
为达到上述目的,本发明的技术方案是:
一种在线热卷温度均匀化的处理方法,其特征是,热轧后卷取、打捆的热卷在15分钟内送入在线移动密闭空间保温或/和加热,同时通过钢卷运输链或移动小车直接移送冷轧机组,在上述热卷运输过程中,采用密闭空间对热卷做在线保温处理;卷取温度控制在350~650℃,在线保温时间至少1小时,热卷直送至冷轧机组。
优选的,所述在线移动密闭空间采用保温罩。
优选的,所述在线保温时间为1~4小时。
热轧生产过程中,由于边部、中尾部散热快;轧制后钢卷经过层流冷却后,内外圈散热快;钢卷运输过程中钢卷会散发热量,特别钢卷内外圈、两侧面散热快;一系列因素导致了温差越来越大,导致钢卷性能不均匀。
为达到高效保温后的温度均匀化,本发明方法上从三个方面突破:
一、控制卷取温度350-650℃,需保证此卷取温度范围,利用钢卷在存在热量下加热或/和保温,热传递快及性能更稳定。如温度太低热传递缓慢,温度均匀化无明显效果,650℃为设计的最高卷取温度。
二、钢卷出卷取机后第一时间密闭加热、保温(15分钟内完成),防止钢卷出卷取机后的空冷加剧内外圈温差,由于出卷取机后钢卷内外圈空冷会快速降温,而15分钟内由于钢卷自身会散发热量弥补空冷散失的热量,内外圈不会降温,而超15分钟后会由于空冷散发热量超过钢卷散发热量上升速率,内外圈温度由于空冷下降,加剧温度偏差,所以要求15分钟完成。
三、在线处理,钢卷出卷取机后直接在运输链进行加热、保温处理,并运送至冷轧,与传统温度均匀化处理对比,避免送精整库区、保温坑、保温炉、保温墙处理且吊运过程热量散失加剧温度偏差,工艺流程更加简化,通过在线处理直接送冷轧机组,且温度均匀化处理效果更加明显。
本发明的有益效果:
本发明工艺方法由传统的热卷→吊运至热库区、保温坑、保温墙等→吊出至运输链→冷轧,变为热卷→在线移动加热、保温→冷轧,通过在线保温直接送冷轧方式,达到简化工艺流程的目的。
由传统的前期运输链长时间运送至精整区域保温(>30分钟后保温),变为卷取机后快速加热、保温(<15分钟),实现保温效果更好、温度更均匀化目的。
本发明根据不同钢种对在线保温制定带加热功能、及时补充热量,达到温度更均匀化目的。
本发明方法温度均匀化处理,最终使钢卷头中尾、边中边,钢卷整体性能均匀化的目的。
热轧钢卷卷取后,使钢卷本身存在的边中边、内外圈温度不均现象,本发明通过在线快速加入入密闭空间、经过加热或保温一定时间,使钢卷充分回温温度均匀后,再持续保温一段时间,使热态钢卷温度均匀化。
附图说明
图1为保温罩对钢卷温度均匀化效果的示意图。
图2为传统吊入精整热库区保温示意图。
图3为本发明在线热卷温度均匀化处理的示意图。
具体实施方式
本发明的一种在线热卷温度均匀化的处理方法,热轧后卷取、打捆的热卷在15分钟内送入在线移动密闭空间保温或/和加热,同时通过钢卷运输链或移动小车直接移送至冷轧机组,在上述热卷运输过程中,采用密闭空间对热卷做在线保温处理;卷取温度控制在350~650℃,在线保温时间至少1小时,热卷直送冷轧机组。
优选的,所述在线移动密闭空间采用保温罩。
优选的,所述在线保温时间为1~4小时。
实施例
热卷出卷取机15分钟内进入密闭空间加热、保温,持续保温1-4小时直接运送至冷轧。
效果:①直接送往冷轧,较其它工艺流程方法,节约工艺流程时间>1小时。
②省略吊入、吊出保温过程,省去吊运流程。
③加热保温效果更快速、温度均匀化效果更优。
对比实验QP钢系列实验效果:利用在线热卷温度均匀化的处理方法,能头中尾性能波动:<300MPa,传统吊入精整热库区保温性能波动:600MPa,如图2所示。
本发明方案通过对卷取后钢卷,本身存在的温度不均现象,通过快速加上在线移动加热、保温密闭方式(15分钟内完成密闭空间进行加热、保温),由于钢卷散发的热量会在密闭空间内形成高温气氛,高温气氛接触的为钢卷内外圈,正好弥补内外圈温度偏低现象,此后,钢卷散发的热量会越来越多,整个在线保温罩高温气氛也越来越高,使钢卷内外圈温度也不断升高,使得内外圈温度与钢卷整体温度达到一致,后持续进行保温,使钢卷整体温度均匀化,如图1所示,横坐标:表示钢卷温度均匀化处理过程,钢卷出卷取机、快速加保温罩、扣罩加热或保温、温度稳定阶段;纵坐标:钢卷温度均匀化处理过程中温度变化趋势从图1中可以看出钢卷出卷取机后,外圈温度比内圈温度高100℃左右,经过密闭空间加热或保温处理后,外圈温度与内卷温度逐渐趋于一致,并达到温度均匀化效果。
参见图2、图3,图中,横坐标:表示带钢长度方向长度(m),取带钢屈服强度典型波动大对应区域。纵坐标:带钢屈服强度(MPa)。
如图2所示,传统吊入精整库区保温:带钢长度方向屈服强度波动达到600MPa,通过对比,在线温度均匀化处理:带钢长度方向屈服强波动<300MPa,性能均匀性更加稳定,如图3所示。
Claims (3)
1.一种在线热卷温度均匀化的处理方法,其特征是,热轧后卷取、打捆的热卷在15分钟内送入在线移动密闭空间保温和/或加热,同时通过钢卷运输链或移动小车直接移送至冷轧机组,在上述热卷运输过程中,采用密闭空间对热卷做在线保温处理;卷取温度控制在350~650℃,在线保温时间至少1小时,热卷直送冷轧机组。
2.如权利要求1所述的在线热卷温度均匀化的处理方法,其特征是,所述在线移动密闭空间采用保温罩。
3.如权利要求1所述的在线热卷温度均匀化的处理方法,其特征是,所述在线保温时间为1~4小时。