CN103757196A - 一种高牌号电工钢的退火方法 - Google Patents

一种高牌号电工钢的退火方法 Download PDF

Info

Publication number
CN103757196A
CN103757196A CN201410010968.2A CN201410010968A CN103757196A CN 103757196 A CN103757196 A CN 103757196A CN 201410010968 A CN201410010968 A CN 201410010968A CN 103757196 A CN103757196 A CN 103757196A
Authority
CN
China
Prior art keywords
high grade
stay
annealing
coil
warm case
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410010968.2A
Other languages
English (en)
Other versions
CN103757196B (zh
Inventor
叶铁
胡洪旭
高振宇
马云龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Angang Steel Co Ltd
Original Assignee
Angang Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Angang Steel Co Ltd filed Critical Angang Steel Co Ltd
Priority to CN201410010968.2A priority Critical patent/CN103757196B/zh
Publication of CN103757196A publication Critical patent/CN103757196A/zh
Application granted granted Critical
Publication of CN103757196B publication Critical patent/CN103757196B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种高牌号电工钢的退火方法，采用铝板制作下端开口的方筒形外壳，外壳内衬450-550mm厚石棉保温板。将卷取温度在650-900℃的钢卷下线后立即放入保温罩内，保温24-96h；取下保温罩，自然冷却后直接进行冷轧。本发明由于采用保温罩退火方法，取消了硅钢常化退火工艺，从而缩短了硅钢生产的工艺流程，可极大减少能源消耗，降低生产成本，且所生产的高牌号电工钢性能指标与常规工艺相差不大，完全达到高牌号电工钢标准要求。

Description

一种高牌号电工钢的退火方法
技术领域
本发明属于轧钢生产工艺领域，尤其涉及一种用于取代常化工艺生产高牌号电工钢的退火方法。 
背景技术
高牌号电工钢是指50W400以上的各个牌号无取向硅钢。产品依据传统设计通常分为NGO产品，即高牌号产品：通常为35W270，50W310及以下牌号产品；GNGO产品，即高级别高牌号产品：通常为35W250，50W290及以上牌号产品。 
随着产品的发展又出现称为超高牌号的产品，包括35W210，50W210及以上国标中未涵盖产品等。高牌号无取向硅钢生产的全工艺过程，包括一次冷轧法和二次冷轧法：一次冷轧法采用常化退火工艺；而二次冷轧法则采用中间退火和临界变形冷轧过程。 
目前，世界上通用的生产高牌号电工钢的方法为一次冷轧法，是一种较为节能和短流程的方法。由于硅、铝含量高，碳含量低，连铸坯容易形成粗大的柱状晶。由于难以破碎的柱状晶和破碎的等轴晶尺寸相差较大，因此，经冷轧后退火钢板表面会形成有手感的沿轧向的瓦楞状缺陷，因此必须采用常化退火工艺，来消除热轧后破碎柱状晶粒和等轴晶粒在尺寸上的差异，使冷轧板表面不会产生瓦楞状缺陷。从而不仅增加了硅钢生产的工艺流程，而且极大增加了能源消耗和生产成本。 
发明内容
本发明旨在提供一种简单易行，可缩短硅钢生产的工艺流程，减少能源消耗，降低生产成本的高牌号电工钢的退火方法。 
为此，本发明采取的解决方案是： 
一种高牌号电工钢的退火方法，其特征在于，具体方法和步骤为：
1、制作保温罩：
采用铝板或钢板制作下端开口的方筒形外壳，外壳内衬450-550mm厚绝热材料，外壳上表面中间设有吊环。
2、将卷取温度在650-900℃的钢卷下线后立即放入保温罩内，保温24-96h。 
3、保温完成后取下保温罩，自然冷却后直接进行冷轧。 
所述内衬石棉保温板的保温罩内腔高度H为钢卷最大直径+（750-850）mm，长度L为钢卷最大直径+（550-650）mm，宽度W为钢卷最大直径+（550-650）mm。 
所述绝热材料为硅酸铝纤维、硅纤维、硅藻土、石棉。 
本发明的有益效果为： 
本发明由于采用保温罩退火方法，取消了硅钢常化退火工艺，从而缩短了硅钢生产的工艺流程，可极大减少能源消耗，降低生产成本，且所生产的高牌号电工钢性能指标与常规工艺相差不大，完全达到高牌号电工钢标准要求。
附图说明
图1是保温罩主视图； 
图2是保温罩左视图；
图3是保温罩俯视图。
图中：外壳1、吊环2、石棉保温板3。 
具体实施方式
实施例工艺流程为：铁水脱硫—冶炼—RH真空处理—连铸+电磁搅拌—热连轧—保温罩处理—冷轧。 
实施例1： 
钢种为50W290牌号冷轧电工钢，卷取后钢卷最大直径为2000mm。
其具体方法和步骤为： 
1、制作保温罩：
采用铝板制作下端开口的方筒形外壳1，外壳1内衬450mm厚石棉保温板绝热材料3，并在外壳1上表面中间位置焊接一吊环2。内衬石棉保温板3的保温罩内腔高度H为2750mm，长度L为2550mm，宽度W为2550mm。
2、将卷取温度在680℃的钢卷下线后立即放入保温罩内，保温29h。 
3、保温完成后取下保温罩，自然冷却后直接进行冷轧。 
实施例1处理后钢板与常规例1样品性能检验结果如表1。 
表1    实施例1与常规例1样品钢板性能检验结果 
Figure 278128DEST_PATH_IMAGE001
实施例2：
钢种为35W300牌号冷轧电工钢，卷取后钢卷最大直径为2000mm。
其具体方法和步骤为： 
1、制作保温罩：
采用钢板制作下端开口的方筒形外壳1，外壳1内衬530mm厚硅酸铝纤维板绝热材料3，并在外壳1上表面中间位置焊接一吊环2。内衬石棉保温板3的保温罩内腔高度H为2800mm，长度L为2650mm，宽度W为2650mm。
2、将卷取温度在740℃的钢卷下线后立即放入保温罩内，保温90h。 
3、保温完成后取下保温罩，自然冷却后直接进行冷轧。 
实施例2处理后钢板与常规例2样品性能检验结果如表2。 
表2    实施例2与常规例2样品钢板性能检验结果 
Figure 545161DEST_PATH_IMAGE002
实施例成品表面均没有瓦楞状缺陷。 

Claims (3)

1.一种高牌号电工钢的退火方法，其特征在于，具体方法和步骤为：
（1）、制作保温罩：
采用铝板或钢板制作下端开口的方筒形外壳，外壳内衬450-550mm厚绝热材料，外壳上表面中间设有吊环；
（2）、将卷取温度在650-900℃的钢卷下线后立即放入保温罩内，保温24-96h；
（3）、保温完成后取下保温罩，自然冷却后直接进行冷轧。
2.根据权利要求1所述的高牌号电工钢的退火方法，其特征在于，所述内衬石棉保温板的保温罩内腔高度H为钢卷最大直径+（750-850）mm，长度L为钢卷最大直径+（550-650）mm，宽度W为钢卷最大直径+（550-650）mm。
3.根据权利要求1所述的高牌号电工钢的退火方法，其特征在于，所述绝热材料为硅酸铝纤维、硅纤维、硅藻土、石棉。
CN201410010968.2A 2014-01-09 2014-01-09 一种高牌号电工钢的退火方法 Active CN103757196B (zh)