CN110614111A - 载体为球形三介孔凹凸棒石复合材料的异丁烷脱氢催化剂及其制备方法和应用 - Google Patents
载体为球形三介孔凹凸棒石复合材料的异丁烷脱氢催化剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN110614111A CN110614111A CN201810638460.5A CN201810638460A CN110614111A CN 110614111 A CN110614111 A CN 110614111A CN 201810638460 A CN201810638460 A CN 201810638460A CN 110614111 A CN110614111 A CN 110614111A
- Authority
- CN
- China
- Prior art keywords
- mesoporous
- filter cake
- isobutane
- carrier
- dehydrogenation catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及催化剂领域,公开了一种载体为球形三介孔凹凸棒石复合材料的异丁烷脱氢催化剂及制法和应用。该方法包括:(a)制备1号介孔材料滤饼和2号介孔材料滤饼;(b)提供硅胶滤饼;(c)将所述1号介孔材料滤饼、2号介孔材料滤饼、硅胶滤饼和凹凸棒石混合并球磨,并将球磨后得到的固体粉末制浆后进行干燥,再将所得产物中的模板剂脱除,得到球形三介孔凹凸棒石复合材料载体;(d)将前述球形三介孔凹凸棒石复合材料载体在含有Pt组分前驱体和Zn组分前驱体的溶液中进行浸渍处理,然后依次进行去除溶剂处理、干燥和焙烧。所得异丁烷脱氢催化剂具有较好的脱氢活性和抗积碳性。
Description
技术领域
本发明涉及催化剂领域,具体地,涉及一种载体为球形三介孔凹凸棒石复合材料的异丁烷脱氢催化剂及其制备方法和由该方法制备的异丁烷脱氢催化剂以及该异丁烷脱氢催化剂在异丁烷脱氢制异丁烯中的应用。
背景技术
异丁烯是一种非常重要的有机化工原料,主要用于制备甲基叔丁基醚、丁基橡胶、甲乙酮、聚异丁烯、甲基异丁烯酸酯、异戊二烯、叔丁酚、叔丁胺、1,4-丁二醇和ABS树脂等各种有机原料和精细化学品。异丁烯的主要来源是石脑油蒸气裂解制乙烯装置的副产C4馏分、炼厂流化催化裂化(FCC) 装置的副产C4馏分和Halcon法环氧丙烷合成中的副产物叔丁醇(TAB)。
近年来,随着异丁烯下游产品的开发利用,异丁烯的需求量逐年增长,传统的异丁烯生产已不能满足化工行业对异丁烯的巨大需求,因此异丁烯生产新技术的研究开发工作成为化工行业的一大热点。其中,最有竞争力的技术有异丁烷脱氢、正丁烯骨架异构化和新型FCC装置增产异丁烯。在这些方法中,异丁烷直接脱氢制异丁烯反应研究较早,已经实现了工业化生产。我国有丰富的C4资源,但是我国C4馏分的化工利用率较低,大多数异丁烷直接用作燃料,浪费严重。合理利用C4资源是石油化工研究领域面临的一项迫切任务。因此,异丁烷脱氢制异丁烯在我国有很大的发展前景。
异丁烷脱氢制异丁烯的催化剂主要有两类:氧化物催化剂和贵金属催化剂。氧化物催化剂主要包括Cr2O3、V2O5、Fe2O3、MoO3、ZnO等以及它们的复合氧化物V-Sb-O、V-Mo-O、Ni-V-O、V-Nb-O、Cr-Ce-O、钼酸盐等。与贵金属催化剂相比,氧化物催化剂价格偏低。但是,该类催化剂易于积碳,催化活性、选择性和稳定性都比较低。另外,多数氧化物催化剂含有毒性较大的成分,不利于环保。贵金属催化剂上的脱氢反应研究已经有很长的历史,与其它金属氧化物催化剂相比,贵金属催化剂活性较高,选择性较好,并且对环境更加友好。但是,由于贵金属价格昂贵导致催化剂成本较高,并且该类催化剂的性能也还没有达到满意程度。
为了改善异丁烷脱氢制异丁烯催化剂的反应性能,研究人员做了很多工作。比如:通过改变催化剂的制备方法改善催化剂性能(工业催化,2014, 22(2):148-153),通过添加助剂提高催化剂稳定性(Catal.Today,2000, 55(3):213-223),通过改善载体性能提高催化剂抗积碳能力(燃料化学学报, 2013,41(12):1481-1487)。然而,目前常用的载体比表面积较小,既不利于活性金属组分在载体表面的分散,也不利于反应过程中原料及产物的扩散。
因此,如何改善异丁烷脱氢催化剂的反应性能是异丁烷脱氢制异丁烯领域一个亟待解决的问题。
凹凸棒石粘土(简称凹土)是一种含水镁铝硅酸盐晶体矿物,其基本结构单元为两层硅氧四面体夹一层镁氧八面体组成的单元层,在每个2:1层中,四面体片角顶隔一定距离方向颠倒而形成层链状结构,在四面体条带间形成与c轴方向平行的孔道,具有独特的层链状晶体结构和多孔的晶体形态。凹土具有很高的比表面积、吸附性能、催化作用、流变性和耐热性,能够应用于工业印染废水处理、除臭剂、助滤剂、净化剂、脱色剂、胶体泥浆、触变剂和粘结剂等领域。由于凹土表面积积大,晶体结构中具有特殊通道,存在大量活化中心,具有有机反应中正碳离子化作用、酸碱协同催化作用和分子筛的择形催化裂解作用。
在现有的负载型催化剂中,通常使用介孔分子筛材料作为载体。介孔分子筛材料具有孔道有序、孔径可调、比表面积和孔容较大等优点,使得采用这些介孔分子筛材料作为载体制成的负载型催化剂在有机催化反应中的制备工艺中表现出很多优点,例如,催化活性高、副反应少、后处理简单等,然而,大的比表面积和高的孔容使得这些介孔分子筛材料具有较强的吸水、吸潮能力,从而会导致这些负载型催化剂在催化反应过程中发生团聚。
此外,常规的负载型异丁烷脱氢催化剂使用的载体在纯化过程中多采取使用板框式压滤机进行过滤的手段以去除杂质,然而板框式压滤机占地面积较大,同时,并且板框式压滤机为间断式运行,效率低,操作间环境较差,产生二次污染,此外,由于所述板框式压滤机需要使用滤布,去除杂质的效果较差,并且洗涤后的废液不能够再生利用,在洗涤过程中极为浪费水源,同时由于排出废水无法处理,又造成环境污染和二次浪费。
因此,有必要尝试将常规的介孔材料和凹凸棒石优点相结合,同时采用新型纯化方法,合成出贵金属活性组分的分散性匀、催化活性高、稳定性好和抗积碳性强,且流动性好的异丁烷脱氢催化剂,以推动载体催化剂和异丁烷脱氢工艺的进一步发展。
发明内容
本发明的目的是为了克服现有的制备异丁烷脱氢催化剂的方法纯化效率低、效果差、操作繁琐、用水量大、污染环境、贵金属活性组分分散不均匀及稳定性较差的缺陷,进而导致由现有的异丁烷脱氢催化剂的催化活性差等缺陷,提供一种载体为球形三介孔凹凸棒石石复合材料的异丁烷脱氢催化剂及其制备方法和由该方法制备的异丁烷脱氢催化剂以及该异丁烷脱氢催化剂在异丁烷脱氢制异丁烯中的应用,由本发明提供的方法易于操作、环境友好且成本低廉,且由该方法制得的异丁烷脱氢催化剂,在贵金属负载量很低的情况下,就能够达到较好的脱氢活性、选择性、稳定性和抗积碳性。
为了实现上述目的,本发明一方面提供一种异丁烷脱氢催化剂的方法,其特征在于,该方法包括以下步骤:
(a)在第一模板剂、三甲基戊烷和乙醇的存在下,将四甲氧基硅烷与酸剂进行第一接触,并将第一接触后得到的产物晶化并过滤,得到1号介孔材料滤饼;在第二模板剂的存在下,将正硅酸乙酯与氨水进行第二接触,并将第二接触后得到的混合物进行过滤,得到2号介孔材料滤饼;
(b)将水玻璃与无机酸进行接触,并将接触后得到的产物过滤,得到硅胶滤饼;
(c)将所述1号介孔材料滤饼、2号介孔材料滤饼、硅胶滤饼和凹凸棒石混合并球磨,并将球磨后得到的固体粉末用水制浆后进行喷雾干燥,再将得到的产物中的所述模板剂脱除,得到球形三介孔凹凸棒石复合材料载体;
(d)将步骤(c)所得球形三介孔凹凸棒石复合材料载体在含有Pt组分前驱体和Zn组分前驱体的溶液中进行浸渍处理,然后依次进行去除溶剂处理、干燥和焙烧。
本发明第二方面提供一种由前述方法制备的异丁烷脱氢催化剂。
本发明第三方面提供一种由前述方法制备的异丁烷脱氢催化剂在异丁烷脱氢制异丁烯中的应用,其中,该异丁烷脱氢制异丁烯的方法包括:在催化剂和氢气的存在下,将异丁烷进行脱氢反应。
本发明的发明人经过深入研究后发现,贵金属催化剂的载体结构(包括比表面积、孔容、孔径分布等物理结构和表面酸性位、电子性能等化学结构) 不仅对活性金属组分的分散度有重要影响,而且还直接影响反应过程中的传质与扩散。因此,多相催化剂的活性、选择性和稳定性等催化性能既取决于活性组分的催化特征,又与催化剂载体的特征有关。为了尽量降低催化剂中的贵金属含量,同时提高催化剂的活性和稳定性,载体的制备过程至关重要。大多数的商售活性氧化铝表面羟基过多、酸性过强。使用这类氧化铝为载体制备脱氢催化剂,在反应过程中催化剂表面易于积碳,进而导致迅速失活。
与现有技术相比,由本发明提供的方法制备的异丁烷脱氢催化剂具有以下优点:
(1)由本发明提供的制备异丁烷脱氢催化剂的方法制备工艺简单,条件易于控制,产品重复性好;
(2)由本发明提供的方法制备的异丁烷脱氢催化剂可以在主要活性组分(即贵金属)负载量很低的情况下,就能够达到较好的脱氢活性、选择性、稳定性和抗积碳性,能够有效降低异丁烷脱氢催化剂的制备成本;
(3)由本发明提供的方法制备的异丁烷脱氢催化剂中,结构氧化的Zn 中心在高温还原条件下稳定性很高,可以抑制载体负载单一Pt组分的失活,减少积碳,并有效地中和载体表面的强酸中心,使载体表面无酸性,并通过几何效应提高Pt组分的分散度,从而可以显著降低异丁烷无氧脱氢制异丁烯反应过程中的积碳风险、提高目的产物的选择性以及异丁烷脱氢催化剂的稳定性;
(4)本发明利用成本低廉的硅源合成出球状、比表面积较大、孔体积较大的介孔分子筛材料,有利于贵金属组分在载体表面良好分散,进而保证异丁烷催化剂在反应过程中不易因活性金属粒子团聚而失活;
(5)由本发明提供的方法制备的异丁烷脱氢催化剂用于异丁烷无氧脱氢制异丁烯反应时表现出了很好的催化性能,异丁烷转化率高,异丁烯选择性高,催化剂稳定性好,积碳量低。
本发明的其它特征和优点将在随后的具体实施方式部分予以详细说明。
附图说明
附图是用来提供对本发明的进一步理解,并且构成说明书的一部分,与下面的具体实施方式一起用于解释本发明,但并不构成对本发明的限制。在附图中:
图1是实施例1的球形三介孔凹凸棒石复合材料载体的X-射线衍射谱图;
图2是实施例1的球形三介孔凹凸棒石复合材料载体的SEM扫描电镜图;
图3是实施例1的球形三介孔凹凸棒石复合材料载体的孔径结构分布图。
具体实施方式
在本文中所披露的范围的端点和任何值都不限于该精确的范围或值,这些范围或值应当理解为包含接近这些范围或值的值。对于数值范围来说,各个范围的端点值之间、各个范围的端点值和单独的点值之间,以及单独的点值之间可以彼此组合而得到一个或多个新的数值范围,这些数值范围应被视为在本文中具体公开。
如前所述,本发明的第一方面提供了一种制备异丁烷脱氢催化剂的方法,该方法包括以下步骤:
(a)在第一模板剂、三甲基戊烷和乙醇的存在下,将四甲氧基硅烷与酸剂进行第一接触,并将第一接触后得到的产物晶化并过滤,得到1号介孔材料滤饼;在第二模板剂的存在下,将正硅酸乙酯与氨水进行第二接触,并将第二接触后得到的混合物进行过滤,得到2号介孔材料滤饼;
(b)将水玻璃与无机酸进行接触,并将接触后得到的产物过滤,得到硅胶滤饼;
(c)将所述1号介孔材料滤饼、2号介孔材料滤饼、硅胶滤饼和凹凸棒石混合并球磨,并将球磨后得到的固体粉末用水制浆后进行喷雾干燥,再将得到的产物中的所述模板剂脱除,得到球形三介孔凹凸棒石复合材料载体;
(d)将步骤(c)所得球形三介孔凹凸棒石复合材料载体在含有Pt组分前驱体和Zn组分前驱体的溶液中进行浸渍处理,然后依次进行去除溶剂处理、干燥和焙烧。
在上述球形三介孔凹凸棒石复合材料载体的形成过程中,主要通过控制 1号介孔材料滤饼、2号介孔材料滤饼和硅胶滤饼的组成将孔径分布控制为三峰分布,并使该球形三介孔凹凸棒石复合材料载体具有三孔分布结构,并且通过控制成型方法(即,先将1号介孔材料滤饼、2号介孔材料滤饼和硅胶滤饼混合并球磨,然后将得到的固体粉末用水制浆后喷雾干燥)将所述球形三介孔凹凸棒石复合材料载体的微观形貌控制为球形,便可以使用常见易得的原料、在简易的操作条件下合成出兼具一维六方孔道分布结构的介孔分子筛材料、二维六方孔道分布结构的介孔分子筛材料以及球形载体的优点的球形三介孔凹凸棒石复合材料载体,所述载体兼具一维六方和二维六方孔道分布结构的介孔分子筛材料的多孔结构、比表面积大、孔体积较大的特点,并通过浸渍处理负载Pt组分和Zn组分,即可制得表面无酸性、脱氢活性好、选择性高、稳定性强和抗积碳性好的异丁烷脱氢催化剂。
根据本发明,在制备1号介孔材料滤饼和2号介孔材料滤饼的过程中,各物质的用量可以在较宽的范围内进行选择和调整。例如,在步骤(a)中,所述第一模板剂、乙醇、三甲基戊烷与四甲氧基硅烷的用量摩尔比为1: (100-500):(200-600):(50-200),优选为1:(200-400):(250-400):(70-150);所述正硅酸乙酯、第二模板剂、氨水中的氨和水的用量摩尔比为1:(0.1-1): (0.1-5):(100-200),优选为1:(0.2-0.5):(1.5-3.5):(120-180)。
根据本发明,为了使得到的1号介孔材料滤饼具有一维六方孔道分布结构,所述第一模板剂的种类优选为三嵌段共聚物聚乙二醇-聚丙三醇-聚乙二醇,所述酸剂优选以水溶液的形式使用,其pH值可以为1-6,优选为3-5。更优选地,所述酸剂为pH值为1-6(更优选3-5)的乙酸和乙酸钠缓冲溶液。其中,该第一模板剂可以通过商购得到(例如,可以购自Aldrich公司,商品名为P123,分子式为EO20PO70EO20,平均分子量Mn为5800),也可以通过现有的各种方法制备得到。当所述第一模板剂为三嵌段共聚物聚乙二醇- 聚丙三醇-聚乙二醇时,所述模板剂的摩尔数根据聚乙二醇-聚丙三醇-聚乙二醇的平均分子量计算得到。
根据本发明,四甲氧基硅烷与酸剂进行第一接触的条件可以包括:温度为10-60℃,时间为10-72h,pH值为1-7。为了更有利于各物质间的均匀混合,所述四甲氧基硅烷与酸剂的第一接触优选在搅拌条件下进行。所述酸剂的用量优选使得四甲氧基硅烷与酸剂的第一接触反应体系的pH值为1-7。
根据本发明,所述晶化的条件可以包括:温度为30-150℃,时间为10-72h。优选情况下,所述晶化的条件包括:温度为40-100℃,时间为20-40h。所述晶化可以通过水热晶化法来实施。
根据本发明,为了使得到的2号介孔材料滤饼具有二维六方孔道分布结构,所述第二模板剂的种类优选为十六烷基三甲基溴化铵(CTAB)。
根据本发明,所述正硅酸乙酯与氨水接触的条件可以包括:温度为 25-100℃,时间为10-72小时;优选情况下,所述正硅酸乙酯和氨水溶液接触的条件可以包括:温度为30-150℃,时间为10-72小时。
此外,本发明对所述第一模板剂、三甲基戊烷、乙醇、四甲氧基硅烷和酸剂之间的接触方式没有特别地限定,例如,可以将第一模板剂、乙醇、三甲基戊烷和四甲氧基硅烷同时进行混合,也可以将任意两种或三种混合,再加入其他组分混合均匀。根据一种优选的实施方式,先将第一模板剂、乙醇、酸剂和三甲基戊烷混合均匀,然后再加入四甲氧基硅烷。所述第一接触的方式为先将所述第一模板剂、乙醇和酸剂混合均匀,并将得到的混合物置于10-60℃的水浴中,然后保持温度不变,再将三甲基戊烷缓慢滴加到上述混合物中,并搅拌反应5-20h,然后保持温度不变,再将四甲氧基硅烷缓慢滴加到上述混合物中,并搅拌反应20-40h。以1g的第一模板剂为基准,所述三甲基戊烷的滴加速率可以为0.1-1g/min,所述四甲氧基硅烷的滴加速率可以为0.1-1g/min。
本发明对所述第二模板剂、正硅酸乙酯与氨水进行接触的方式没有特别地限定,例如,可以将第二模板剂、正硅酸乙酯和氨水溶液同时进行混合,也可以将任意两种混合,再加入其他组分混合均匀。根据一种优选的实施方式,将第二模板剂和正硅酸乙酯一起加入到氨水溶液中混合均匀。所述第二接触的方式为先将所述第二模板剂和正硅酸乙酯一起加入到氨水溶液中混合均匀,并将得到的混合物置于25-100℃的水浴中搅拌至溶解,然后保持温度不变,并搅拌反应20-40h。
根据本发明提供的制备异丁烷脱氢催化剂的方法,在步骤(b)中,所述水玻璃与无机酸接触的条件可以包括:温度可以为10-60℃,优选为 20-40℃;时间可以为1-5小时,优选为1.5-3小时,pH值为2-4。为了更有利于各物质间的均匀混合,所述水玻璃与无机酸接触优选在搅拌条件下进行。
根据本发明,所述水玻璃为本领域常规的硅酸钠的水溶液,其浓度可以为10-50重量%,优选为12-30重量%。
根据本发明,所述无机酸可以为硫酸、硝酸和盐酸中的一种或多种。所述无机酸可以以纯态的形式使用,也可以以其水溶液的形式使用。所述无机酸的用量优选使得水玻璃与无机酸的接触条件反应体系的pH值为2-4。
此外,在上述制备1号介孔材料滤饼、2号介孔材料滤饼和硅胶滤饼的过程中,通过过滤以获得滤饼的过程可以包括:在过滤之后,用蒸馏水反复洗涤(洗涤次数可以为2-10),然后进行抽滤。优选地,制备2号介孔材料滤饼的过程中的洗涤使得滤饼pH为7,制备硅胶滤饼的过程中的洗涤使得钠离子含量低于0.02重量%。
根据本发明,在步骤(c)中,所述1号介孔材料滤饼、2号介孔材料滤饼和硅胶滤饼的用量可以根据预期得到的球形三介孔凹凸棒石复合材料载体的组分进行选择,优选情况下,以100重量份的所述1号介孔材料滤饼和2号介孔材料滤饼的总用量为基准,所述硅胶滤饼的用量可以为1-200重量份,优选为50-150重量份;所述1号介孔材料滤饼与2号介孔材料滤饼的重量比可以为1:(0.1-10),优选为1:(0.5-2)。
根据本发明,以100重量份的所述2号介孔材料滤饼的用量为基准,所述硅胶的用量为1-200重量份,所述凹凸棒石的用量为1-50重量份;
优选地,以100重量份的所述2号介孔材料滤饼的用量为基准,所述硅胶的用量为50-150重量份,所述凹凸棒石的用量为20-50重量份。
根据本发明,所述球磨的具体操作方法和条件以不破坏或基本不破坏介孔材料的结构并使硅胶进入介孔材料孔道为准。本领域技术人员可以根据上述原则选择各种合适的条件来实施本发明。具体地,所述球磨在球磨机中进行,其中,球磨机中磨球的直径可以为2-3mm;磨球的数量可以根据球磨罐的大小进行合理地选择,对于大小为50-150mL的球磨罐,通常可以使用1 个磨球;所述磨球的材质可以是玛瑙、聚四氟乙烯等,优选为玛瑙。所述球磨的条件包括:磨球的转速可以为300-500r/min,球磨罐内的温度可以为 15-100℃,球磨的时间可以为0.1-100小时。
发明中,所述喷雾干燥的具体操作方法和条件优选为:将由所述固体粉末和水配成的浆体加入到雾化器内高速旋转以实现喷雾干燥。其中,所述喷雾干燥的条件可以包括:温度可以为100-300℃,旋转的转速可以为 10000-15000r/min;优选情况下,所述喷雾干燥的条件包括:温度为150-250℃,旋转的转速为11000-13000r/min;最优选情况下,所述喷雾干燥的条件包括:温度为200℃,旋转的转速为12000r/min。
根据本发明,脱除模板剂的方法优选为煅烧法。所述脱除模板剂的条件可以包括:温度为300-600℃,优选为350-550℃,最优选为500℃;时间为 10-80小时,优选为20-30小时,最优选为24小时。
根据本发明,在步骤(d)中,所述球形三介孔凹凸棒石复合材料载体负载金属组分可以采用浸渍的方式,依靠所述载体的孔道结构的毛细压力使金属组分进入所述球形三介孔凹凸棒石复合材料载体的孔道内,同时金属组分还会在所述球形三介孔凹凸棒石复合材料载体的表面吸附,直到金属组分在所述载体的表面达到吸附平衡。所述浸渍处理可以为共浸渍处理,也可以为分步浸渍处理。为了节约制备成本,简化实验工艺,所述浸渍处理优选为共浸渍处理;进一步优选地,所述共浸渍处理的条件包括:将球形三介孔凹凸棒石复合材料载体在含有Pt组分前驱体和Zn组分前驱体的溶液进行混合接触,所述浸渍的温度可以为25-50℃,所述浸渍的时间可以为2-6h。
根据本发明,所述Pt组分前驱体优选为H2PtCl6,所述Zn组分前驱体优选为Zn(NO3)2。
本发明对所述含有Pt组分前驱体和Zn组分前驱体的溶液的浓度没有特别的限定,可以为本领域的常规选择,例如,所述Pt组分前驱体的浓度可以为0.001-0.003mol/L,所述Zn组分前驱体的浓度可以为0.015-0.1mol/L。
根据本发明,所述去除溶剂处理的过程可以采用本领域常规的方法,例如可以采用旋转蒸发仪去除体系中的溶剂。
根据本发明,在步骤(d)中,所述干燥可以在干燥箱中进行,所述焙烧可以在马弗炉中进行。所述干燥的条件可以包括:温度为110-150℃,时间为3-6h;所述焙烧的条件可以包括:温度为600-650℃,时间为5-8h。
根据本发明,在步骤(d)中,所述球形三介孔凹凸棒石复合材料载体、 Pt组分前驱体和Zn组分前驱体的用量使得制备的异丁烷脱氢催化剂中,以所述异丁烷脱氢催化剂的总重量为基准,所述载体的含量为98-99.4重量%,所述Pt组分以Pt元素计的含量为0.1-0.5重量%,所述Zn组分以Zn元素计的含量为0.5-1.5重量%。
优选情况下,所述球形三介孔凹凸棒石复合材料载体、Pt组分前驱体和 Zn组分前驱体的用量使得制备的异丁烷脱氢催化剂中,以所述异丁烷脱氢催化剂的总重量为基准,所述载体的含量为98.4-99重量%,所述Pt组分以 Pt元素计的含量为0.2-0.4重量%,所述Zn组分以Zn元素计的含量为0.8-1.2 重量%。
本发明第二方面提供了由前述方法制备的异丁烷脱氢催化剂。
根据本发明,所述异丁烷脱氢催化剂包括载体以及负载在所述载体上的 Pt组分和Zn组分,其中,所述异丁烷脱氢催化剂包括载体以及负载在所述载体上的Pt组分和Zn组分,其中,所述载体为球形三介孔凹凸棒石复合材料载体,所述球形三介孔凹凸棒石复合材料载体含有具有一维六方孔道分布结构的介孔分子筛材料和具有二维六方孔道分布结构的介孔分子筛材料,所述球形三介孔凹凸棒石复合材料载体的平均粒径为20-50μm,比表面积为 150-600m2/g,孔体积为0.5-1.5mL/g,孔径分布为三峰分布,且所述三峰对应的最可几孔径分别为2-4nm、5-15nm和10-40nm。
根据本发明,所述异丁烷脱氢催化剂中,作为载体的球形三介孔凹凸棒石复合材料载体具有特殊的一维六方和二维六方孔道分布结构,其颗粒的平均粒径采用激光粒度分布仪测得,比表面积、孔体积和最可几孔径根据氮气吸附法测得。在本发明中,粒度是指原料颗粒的颗粒尺寸,当原料颗粒为球体时则粒度用球体的直径表示,当原料颗粒为立方体时则粒度用立方体的边长表示,当原料颗粒为不规则的形状时则粒度用恰好能够筛分出该原料颗粒的筛网的网孔尺寸表示。
根据本发明,所述球形三介孔凹凸棒石复合材料载体通过将球形三介孔凹凸棒石复合材料载体的颗粒尺寸控制在上述范围之内,可以确保所述球形三介孔凹凸棒石复合材料载体不易发生团聚,并且将其用作载体制成的负载型催化剂可以提高异丁烷脱氢制异丁烯反应过程中的反应原料转化率。当所球形三介孔凹凸棒石复合材料载体的比表面积小于150m2/g和/或孔体积小于0.5mL/g时,将其用作载体制成的负载型催化剂的催化活性会显著降低;当所述球形三介孔凹凸棒石复合材料载体的比表面积大于600m2/g和/或孔体积大于1.5mL/g时,将其用作载体制成的负载型催化剂在异丁烷脱氢制异丁烯反应过程中容易发生团聚,从而影响异丁烷脱氢制异丁烯反应过程中的反应原料转化率。
在优选情况下,所述球形三介孔凹凸棒石复合材料载体的平均粒径为 30-50μm,比表面积为180-600m2/g,孔体积为0.8-1.4mL/g,孔径分布为三峰分布,且所述三峰对应的最可几孔径分别为2.5-4nm、5.5-10nm和20-30nm。
根据本发明,以所述异丁烷脱氢催化剂的总重量为基准,所述载体的含量为98-99.4重量%,所述Pt组分以Pt元素计的含量为0.1-0.5重量%,所述 Zn组分以Zn元素计的含量为0.5-1.5重量%。
优选情况下,以所述异丁烷脱氢催化剂的总重量为基准,所述载体的含量为98.4-99重量%,所述Pt组分以Pt元素计的含量为0.2-0.4重量%,所述 Zn组分以Zn元素计的含量为0.8-1.2重量%。
进一步优选地,所述异丁烷脱氢催化剂的平均粒子直径为30-60μm,比表面积为200-650m2/g,孔体积为0.6-1.2mL/g,孔径分布为三峰分布,且所述三峰对应的最可几孔径分别为2.1-3.5nm、5.5-10nm和20-30nm。
根据本发明,在所述球形三介孔凹凸棒石复合材料载体中,所述具有一维六方孔道分布结构的介孔分子筛材料和具有二维六方孔道分布结构的介孔分子筛材料的含量的重量比可以为1:(0.1-10),优选为1:(0.5-2)。
根据本发明,所述球形三介孔凹凸棒石复合材料载体还可以含有通过硅胶引入的二氧化硅。“通过硅胶引入的二氧化硅”是指在所述球形三介孔凹凸棒石复合材料载体的制备过程中,由硅胶作为制备原料带入最终制备的球形三介孔凹凸棒石复合材料载体中的二氧化硅组分。在所述球形三介孔凹凸棒石复合材料载体中,相对于100重量份的所述具有一维六方孔道分布结构的介孔分子筛材料和具有二维六方孔道分布结构的介孔分子筛材料的总重量,所述通过硅胶引入的二氧化硅的含量可以为1-200重量份,优选为50-150 重量份。
根据本发明,所述具有一维六方孔道分布结构的介孔分子筛材料和二维六方孔道分布结构的介孔分子筛材料各自可以根据前述的方法制备得到。
如前所述,本发明第三方面提供一种由前述方法制备的异丁烷脱氢催化剂在异丁烷脱氢制异丁烯中的应用,其中,该异丁烷脱氢制异丁烯的方法包括:在催化剂和氢气的存在下,将异丁烷进行脱氢反应。
由本发明提供的方法制备的异丁烷脱氢催化剂用于催化异丁烷脱氢制异丁烯时,能够使异丁烷的转化率和异丁烯的选择性均有较大幅度地提高。
根据本发明,为了提高异丁烷转化率和防止所述催化剂结焦,优选情况下,异丁烷的用量与氢气的用量的摩尔比为(0.5-1.5):1。
本发明对所述脱氢反应的条件没有特别的限定,可以为本领域的常规选择,例如,所述脱氢反应的条件可以包括:反应温度为550-650℃,反应压力为0.05-0.2MPa,反应时间为20-40h,异丁烷质量空速为2-5h-1。
以下将通过实施例对本发明进行详细描述。
以下实施例中,三嵌段共聚物聚乙二醇-聚丙三醇-聚乙二醇购自Aldrich 公司,简写为P123,分子式为EO20PO70EO20,在美国化学文摘的登记号为 9003-11-6的物质,平均分子量Mn为5800。
以下实施例和对比例中,X射线衍射分析在购自德国Bruker AXS公司的型号为D8Advance的X射线衍射仪上进行;扫描电镜分析在购自美国FEI 公司的型号为XL-30的扫描电子显微镜上进行;孔结构参数分析在购自美国 Micromeritics公司生产的ASAP2020-M+C型吸附仪上进行,样品的比表面积和孔体积计算采用BET方法;样品的粒径分布在马尔文激光粒度仪上进行;旋转蒸发仪为德国IKA公司生产,型号为RV10 digital;异丁烷脱氢催化剂的活性组分负载量在购自荷兰帕纳科公司型号为Axios-Advanced的波长色散X射线荧光光谱仪上测定;反应产物成分的分析在购自安捷伦公司型号为7890A的气相色谱仪上进行;干燥箱为上海一恒科学仪器有限公司生产,型号DHG-9030A;马弗炉为CARBOLITE公司生产,型号CWF1100;超声波发生器为昆山市超声仪器有限公司生产的KQ-300GTDV高频恒温数控超声波清洗器,超声频率为80kHz,工作电压为220V。
样品的氮吸脱附实验是在美国Micromeritics公司生产的ASAP2020 M+C型全自动物化吸附分析仪上进行的。样品测定之前在350℃下真空脱气 4小时。采用BET法计算样品比表面积,采用BJH模型计算孔体积和平均孔径。
样品的NH3-TPD实验是在美国Micromeritics公司生产的 AUTOCHEM2920全自动化学吸附仪上进行的。样品首先在480℃, 10%H2-90%Ar气氛中还原1小时。之后在He气氛中升温至700℃,停留1 小时后降温至40℃吸附氨气至饱和。在He气气氛中吹扫1h后以10℃/min 的速率由40℃升温至700℃,同时使用TCD检测器记录氨脱附数据。
制备的脱氢催化剂中各金属组分的含量通过制备时原料投料计算确定。
异丁烷转化率的计算方法如下:
异丁烷转化率=反应消耗的异丁烷的量/异丁烷的初始量×100%;
异丁烯选择性的计算方法如下:
异丁烯选择性=生成异丁烯消耗的异丁烷的量/异丁烷的总消耗量×100%;
异丁烯产率的计算方法如下:
异丁烯产率=异丁烷转化率×异丁烯选择性×100%。
实施例1
本实施例用于说明异丁烷脱氢催化剂及其制备方法。
(1)球形三介孔凹凸棒石复合材料载体的制备
将1g(0.0002mol)三嵌段共聚物表面活性剂P123和1.69g(0.037mol) 乙醇加入到28ml、pH值为4的乙酸和乙酸钠缓冲液中,在15℃下搅拌至 P123完全溶解,之后向得到的溶液中加入6g(0.053mol)三甲基戊烷,在 15℃下搅拌8h,再向其中加入2.13g(0.014mol)四甲氧基硅烷,在15℃、 pH值为4.5的条件下搅拌20h,然后将得到的溶液转移至聚四氟乙烯内衬的反应釜中,在60℃下晶化24h,接着进行过滤和并用去离子水洗涤4次,然后抽滤得到具有一维六方孔道单孔分布结构的1号介孔分子筛材料滤饼A1;
将十六烷基三甲基溴化铵和正硅酸乙酯加入到浓度为25重量%的氨水溶液中,其中,正硅酸乙酯的加入量为1g,正硅酸乙酯、十六烷基三甲基溴化铵、氨水中的氨和水的摩尔比为1:0.37:2.8:142,并在80℃下搅拌至溶解,接着将得到的溶液进行过滤和并用去离子水洗涤4次,然后抽滤得到具有二维六方孔道结构的2号介孔分子筛材料的滤饼A2。
将浓度为15重量%的水玻璃和浓度为12重量%的硫酸溶液以重量比为 5:1进行混合并在30℃下接触反应2h,接着用浓度为98重量%的硫酸调整 pH值至3,然后对得到的反应物料进行抽滤,并用蒸馏水洗涤至钠离子含量为0.02重量%,得到硅胶滤饼B1。
将上述制备的10g滤饼A1、10g滤饼A2、10g滤饼B1和10g凹凸棒石一起放入100ml球磨罐中,其中,球磨罐的材质为聚四氟乙烯,磨球材质为玛瑙,磨球的直径为3mm,数量为1个,转速为400r/min。封闭球磨罐,在球磨罐内温度为60℃下球磨1小时,得到30g固体粉末;将该固体粉末溶解在30克去离子水中,在200℃下在转速为12000r/min下喷雾干燥;将喷雾干燥后得到的产物在马弗炉中在500℃下煅烧24小时,脱除模板剂,得到 30g具有一维六方孔道和二维六方孔道分布结构的球形三介孔凹凸棒石复合材料载体C1。
(2)异丁烷脱氢催化剂的制备
将0.080g H2PtCl6·6H2O和0.457g Zn(NO3)2·6H2O溶于100ml去离子水中,得到混合物溶液,将步骤(1)制备得到的10g球形三介孔凹凸棒石复合材料载体C1浸渍在所述混合物溶液中,在25℃下浸渍5h后,用旋转蒸发仪蒸去体系中的溶剂水,得到固体产物,将固体产物置于温度为120℃的干燥箱中,干燥3h。然后在马弗炉中,温度为600℃焙烧6h,得到异丁烷脱氢催化剂Cat-1(以异丁烷脱氢催化剂Cat-1的总重量为基准,Pt组分以Pt元素计的含量为0.3重量%,Zn组分以Zn元素计的含量为1重量%,其余为载体)。
用XRD、扫描电子显微镜和ASAP2020-M+C型吸附仪来对球形三介孔凹凸棒石复合材料载体C1和异丁烷脱氢催化剂Cat-1进行表征。
图1是C1的X-射线衍射图谱,其中,a为球形三介孔凹凸棒石复合材料载体C1的XRD谱图,横坐标为2θ,纵坐标为强度,由XRD谱图出现的小角度谱峰可知,球形三介孔凹凸棒石复合材料载体C1的XRD谱图a具有介孔材料所特有的一维和二维的六方孔道结构;
图2是C1的SEM扫描电镜图,由图可知,球形三介孔凹凸棒石复合材料载体C1的微观形貌为颗粒度为30-50μm的介孔球;
图3是C1的孔径分布曲线图,由图可知,球形三介孔凹凸棒石复合材料载体C1的孔径分布为三峰分布,且所述三峰对应的最可几孔径分别为 3.9nm、7.5nm和25nm。
表1为球形三介孔凹凸棒石复合材料载体C1和异丁烷脱氢催化剂Cat-1 的孔结构参数。
表1
样品 | 比表面积(m<sup>2</sup>/g) | 孔体积(ml/g) | 最可几孔径<sup>*</sup>(nm) | 粒径(μm) |
载体C1 | 263 | 0.9 | 3.9,7.5,25 | 30-60 |
催化剂Cat-1 | 250 | 0.8 | 2.8,6.3,22.1 | 30-60 |
*:第一最可几孔径、第二最可几孔径和第三最可几孔径用逗号隔开:按照由左至右的顺序依次是第一最可几孔径、第二最可几孔径和第三最可几孔径。
由表1的数据可以看出,球形三介孔凹凸棒石复合材料载体在负载Pt 组分和Zn组分之后,比表面积和孔体积均有所减小,这说明在负载反应过程中,Pt组分和Zn组分进入到球形三介孔凹凸棒石复合材料载体的内部。
对比例1
本对比例用于说明参比的异丁烷脱氢催化剂及其制备方法。
根据实施例1的方法制备载体和异丁烷脱氢催化剂,所不同的,在制备载体的过程中使用相同重量的氧化铝载体代替球形三介孔凹凸棒石复合材料C1,从而分别制得载体D1和异丁烷脱氢催化剂Cat-D-1。
对比例2
根据实施例1的方法制备载体和异丁烷脱氢催化剂,所不同的,在制备载体的过程中使用商购的ES955硅胶(GRACE公司)替代所述球形三介孔凹凸棒石复合材料C1作为载体D2,从而分别制得载体D2和异丁烷脱氢催化剂Cat-D-2。
对比例3
根据实施例1的方法制备载体和异丁烷脱氢催化剂,所不同的是,在制备异丁烷脱氢型催化剂的浸渍过程中,未加入Zn(NO3)2·6H2O,仅加入0.080g H2PtCl6·6H2O,通过共浸渍法仅将单一Pt组分负载在作为载体的球形三介孔凹凸棒石复合材料上,从而制得异丁烷脱氢催化剂Cat-D-3,以异丁烷脱氢催化剂Cat-D-3的总重量为基准,Pt组分以Pt元素计的含量为0.3重量%,其余为载体)。
实施例2
本实施例用于说明异丁烷脱氢催化剂及其制备方法。
(1)载体的制备
将1g(0.0002mol)三嵌段共聚物表面活性剂P123和1.84g(0.04mol) 乙醇加入到28ml、pH值为5的乙酸和乙酸钠缓冲液中,在15℃下搅拌至 P123完全溶解,之后向得到的溶液中加入9.12g(0.08mol)三甲基戊烷,在 15℃下搅拌8h,再向其中加入3.04g(0.02mol)四甲氧基硅烷,在25℃、 pH值为5.5的条件下搅拌15h,然后将得到的溶液转移至聚四氟乙烯内衬的反应釜中,在100℃下晶化10h,接着进行过滤和并用去离子水洗涤4次,然后抽滤得到具有一维六方孔道单孔分布结构的1号介孔分子筛材料滤饼 A3;
将十六烷基三甲基溴化铵和正硅酸乙酯加入到浓度为25重量%的氨水溶液中,其中,正硅酸乙酯的加入量为1g,正硅酸乙酯、十六烷基三甲基溴化铵、氨水中的氨和水的摩尔比为1:0.5:3.2:140,并在90℃下搅拌至溶解,接着将得到的溶液进行过滤和并用去离子水洗涤4次,然后抽滤得到具有二维六方孔道结构的2号介孔分子筛材料的滤饼A4。
将浓度为15重量%的水玻璃和浓度为12重量%的硫酸溶液以重量比为 4:1进行混合并在40℃下接触反应1.5h,接着用浓度为98重量%的硫酸调整 pH值至2,然后对得到的反应物料进行抽滤,并用蒸馏水洗涤至钠离子含量为0.02重量%,得到硅胶滤饼B2。
将上述制备的17g滤饼A3、11g滤饼A4、10g滤饼B2和10g凹凸棒石一起放入100ml球磨罐中,其中,球磨罐的材质为聚四氟乙烯,磨球材质为玛瑙,磨球的直径为3mm,数量为1个,转速为300r/min。封闭球磨罐,在球磨罐内温度为80℃下球磨0.5小时,得到38g固体粉末;将该固体粉末溶解在12g去离子水中,在250℃下在转速为11000r/min下喷雾干燥;将喷雾干燥后得到的产物在马弗炉中在500℃下煅烧15小时,脱除模板剂,得到 35g具有一维六方孔道和二维六方孔道分布结构的球形三介孔凹凸棒石复合材料载体C2。
(2)异丁烷脱氢催化剂的制备
将0.080g H2PtCl6·6H2O和0.457g Zn(NO3)2·6H2O溶于100ml去离子水中,得到混合物溶液,将步骤(1)制备得到的10g球形三介孔凹凸棒石复合材料载体C2浸渍在所述混合物溶液中,在25℃下浸渍5h后,用旋转蒸发仪蒸去体系中的溶剂水,得到固体产物,将固体产物置于温度为120℃的干燥箱中,干燥3h。然后在马弗炉中,温度为600℃焙烧6h,得到异丁烷脱氢催化剂Cat-2(以异丁烷脱氢催化剂Cat-2的总重量为基准,Pt组分以Pt元素计的含量为0.3重量%,Zn组分以Zn元素计的含量为1重量%,其余为载体)。
表2为球形三介孔凹凸棒石复合材料载体C2和异丁烷脱氢催化剂Cat-2 的孔结构参数。
表2
样品 | 比表面积(m<sup>2</sup>/g) | 孔体积(ml/g) | 最可几孔径<sup>*</sup>(nm) | 粒径(μm) |
载体C2 | 280 | 1.1 | 3,6.8,29.5 | 25-45 |
催化剂Cat-2 | 270 | 0.9 | 2.2,6.1,25.2 | 25-45 |
*:第一最可几孔径、第二最可几孔径和第三最可几孔径用逗号隔开:按照由左至右的顺序依次是第一最可几孔径、第二最可几孔径和第三最可几孔径。
由表2的数据可以看出,球形三介孔凹凸棒石复合材料载体在负载Pt 组分和Zn组分之后,比表面积和孔体积均有所减小,这说明在负载反应过程中,Pt组分和Zn组分进入到球形三介孔凹凸棒石复合材料载体的内部。
实施例3
本实施例用于说明异丁烷脱氢催化剂及其制备方法。
(1)载体的制备
将1g(0.0002mol)三嵌段共聚物表面活性剂P123和2.76g(0.06mol) 乙醇加入到28ml、pH值为3的乙酸和乙酸钠缓冲液中,在15℃下搅拌至 P123完全溶解,之后向得到的溶液中加入5.7g(0.05mol)三甲基戊烷,在 15℃下搅拌8h,再向其中加入2.13g(0.014mol)四甲氧基硅烷,在40℃、 pH值为3.5的条件下搅拌10h,然后将得到的溶液转移至聚四氟乙烯内衬的反应釜中,在40℃下晶化40h,接着进行过滤和并用去离子水洗涤4次,然后抽滤得到具有一维六方孔道单孔分布结构的1号介孔分子筛材料滤饼A5;
将十六烷基三甲基溴化铵和正硅酸乙酯加入到浓度为25重量%的氨水溶液中,其中,正硅酸乙酯的加入量为1g,正硅酸乙酯、十六烷基三甲基溴化铵、氨水中的氨和水的摩尔比为1:0.3:3:150,并在90℃下搅拌至溶解,接着将得到的溶液进行过滤和并用去离子水洗涤4次,然后抽滤得到具有二维六方孔道结构的2号介孔分子筛材料的滤饼A6。
将浓度为15重量%的水玻璃和浓度为12重量%的硫酸溶液以重量比为 6:1进行混合并在20℃下接触反应3h,接着用浓度为98重量%的硫酸调整 pH值至4,然后对得到的反应物料进行抽滤,并用蒸馏水洗涤至钠离子含量为0.02重量%,得到硅胶滤饼B3。
将上述制备的13g滤饼A5、19g滤饼A6、30g滤饼B3和10g凹凸棒石一起放入100ml球磨罐中,其中,球磨罐的材质为聚四氟乙烯,磨球材质为玛瑙,磨球的直径为3mm,数量为1个,转速为550r/min。封闭球磨罐,在球磨罐内温度为40℃下球磨10小时,得到55g固体粉末;将该固体粉末溶解在30g去离子水中,在150℃下在转速为13000r/min下喷雾干燥;将喷雾干燥后得到的产物在马弗炉中在450℃下煅烧70小时,脱除模板剂,得到 53g具有一维六方孔道和二维六方孔道分布结构的球形三介孔凹凸棒石复合材料载体C3。
(2)异丁烷脱氢催化剂的制备
将0.080g H2PtCl6·6H2O和0.457g Zn(NO3)2·6H2O溶于100ml去离子水中,得到混合物溶液,将步骤(1)制备得到的10g球形三介孔凹凸棒石复合材料载体C3浸渍在所述混合物溶液中,在25℃下浸渍5h后,用旋转蒸发仪蒸去体系中的溶剂水,得到固体产物,将固体产物置于温度为120℃的干燥箱中,干燥3h。然后在马弗炉中,温度为600℃焙烧6h,得到异丁烷脱氢催化剂Cat-3(以异丁烷脱氢催化剂Cat-3的总重量为基准,Pt组分以Pt元素计的含量为0.3重量%,Zn组分以Zn元素计的含量为1重量%,其余为载体)。
表3为球形三介孔凹凸棒石复合材料载体C3和异丁烷脱氢催化剂Cat-3 的孔结构参数。
表3
样品 | 比表面积(m<sup>2</sup>/g) | 孔体积(ml/g) | 最可几孔径<sup>*</sup>(nm) | 粒径(μm) |
载体C3 | 255 | 1 | 2.7,7,28.8 | 30-50 |
催化剂Cat-3 | 245 | 0.8 | 2.1,6.5,23.7 | 30-50 |
*:第一最可几孔径、第二最可几孔径和第三最可几孔径用逗号隔开:按照由左至右的顺序依次是第一最可几孔径、第二最可几孔径和第三最可几孔径。
由表3的数据可以看出,球形三介孔凹凸棒石复合材料载体在负载Pt 组分和Zn组分之后,比表面积和孔体积均有所减小,这说明在负载反应过程中,Pt组分和Zn组分进入到球形三介孔凹凸棒石复合材料载体的内部。
实验实施例1
本实施例用于说明采用本发明的异丁烷脱氢催化剂制备异丁烯的方法
将0.5g异丁烷脱氢催化剂Cat-1装入固定床石英反应器中,控制反应温度为590℃,反应压力为0.1MPa,异丁烷:氢气的摩尔比为1:1,反应时间为24h,异丁烷质量空速为4h-1。经Al2O3-S分子筛柱分离的反应产物直接进入配有氢焰检测器(FID)的安捷伦7890A气相色谱仪进行在线分析,得到异丁烷转化率和异丁烯选择性如表4所示。反应结束后使用METTLER-TOLEDO公司的TGA/DSC1热重分析仪测定异丁烷脱氢催化剂 Cat-1中的积碳量,如表4所示。
实验实施例2-3
按照实验实施例1的方法进行异丁烷脱氢制异丁烯,不同的是,分别采用异丁烷脱氢催化剂Cat-2和异丁烷脱氢催化剂Cat-3代替异丁烷脱氢催化剂Cat-1。异丁烷转化率、异丁烯选择性及异丁烷脱氢催化剂的积碳量如表4 所示。
实验对比例1-3
按照实验实施例1的方法进行异丁烷脱氢制异丁烯,不同的是,分别采用异丁烷脱氢催化剂Cat-D-1、异丁烷脱氢催化剂Cat-D-2和异丁烷脱氢催化剂Cat-D-3代替异丁烷脱氢催化剂Cat-1。异丁烷转化率、异丁烯选择性及异丁烷脱氢催化剂的积碳量如表4所示。
表4
脱氢催化剂 | 异丁烷转化率 | 异丁烯选择性 | 催化剂积碳量 | |
实验实施例1 | Cat-1 | 49% | 95% | 1.3wt% |
实验实施例2 | Cat-2 | 48% | 94% | 1.6wt% |
实验实施例3 | Cat-3 | 47% | 93% | 1.4wt% |
实验对比例1 | Cat-D-1 | 9.6% | 70.4% | 5.3wt% |
实验对比例2 | Cat-D-2 | 7.8% | 65.3% | 4.0wt% |
实验对比例3 | Cat-D-3 | 6.2% | 55.9% | 5.5wt% |
从表4可以看出,采用本发明的球形三介孔海泡石复合材料载体制备的异丁烷脱氢催化剂用于异丁烷脱氢制异丁烯反应时,反应24小时后,依然可以得到较高的异丁烷转化率和异丁烯选择性,说明本发明的异丁烷脱氢催化剂不仅具有较好的催化性能,而且稳定性好。
以上详细描述了本发明的优选实施方式,但是,本发明并不限于此。在本发明的技术构思范围内,可以对本发明的技术方案进行多种简单变型,包括各个技术特征以任何其它的合适方式进行组合,这些简单变型和组合同样应当视为本发明所公开的内容,均属于本发明的保护范围。
Claims (11)
1.一种制备异丁烷脱氢催化剂的方法,其特征在于,该方法包括以下步骤:
(a)在第一模板剂、三甲基戊烷和乙醇的存在下,将四甲氧基硅烷与酸剂进行第一接触,并将第一接触后得到的产物晶化并过滤,得到1号介孔材料滤饼;在第二模板剂的存在下,将正硅酸乙酯与氨水进行第二接触,并将第二接触后得到的混合物进行过滤,得到2号介孔材料滤饼;
(b)将水玻璃与无机酸进行接触,并将接触后得到的产物过滤,得到硅胶滤饼;
(c)将所述1号介孔材料滤饼、2号介孔材料滤饼、硅胶滤饼和凹凸棒石混合并球磨,并将球磨后得到的固体粉末用水制浆后进行喷雾干燥,再将得到的产物中的所述模板剂脱除,得到球形三介孔凹凸棒石复合材料载体;
(d)将步骤(c)所得球形三介孔凹凸棒石复合材料载体在含有Pt组分前驱体和Zn组分前驱体的溶液中进行浸渍处理,然后依次进行去除溶剂处理、干燥和焙烧。
2.根据权利要求1所述的方法,其中,在步骤(a)中,所述第一模板剂、乙醇、三甲基戊烷与四甲氧基硅烷的用量摩尔比为1:(100-500):(200-600):(50-200);所述正硅酸乙酯、第二模板剂、氨水中的氨和水的用量摩尔比为1:(0.1-1):(0.1-5):(100-200),优选为1:(0.2-0.5):(1.5-3.5):(120-180);
优选地,所述第一模板剂为三嵌段共聚物聚乙二醇-聚丙三醇-聚乙二醇,所述酸剂为pH值为1-6的乙酸和乙酸钠的缓冲溶液,所述第二模板剂为十六烷基三甲基溴化铵;
进一步优选地,四甲氧基硅烷与所述酸剂进行第一接触的条件包括:温度为10-60℃,时间为10-72小时,pH值为1-7;正硅酸乙酯与氨水进行第二接触的条件包括:温度为25-100℃,时间为10-72小时;所述晶化的条件包括:温度为30-150℃,时间为10-72小时。
3.根据权利要求1所述的方法,其中,在步骤(b)中,所述水玻璃与无机酸接触的条件包括:温度为10-60℃,时间为1-5小时,pH值为2-4;所述无机酸为硫酸、硝酸和盐酸中的一种或多种。
4.根据权利要求1所述的方法,其中,在步骤(c)中,以100重量份的所述1号介孔材料滤饼和2号介孔材料滤饼的总用量为基准,所述硅胶滤饼的用量为1-200重量份,优选为50-150重量份,所述1号介孔材料滤饼与2号介孔材料滤饼的重量比为1:(0.1-10),优选为1:(0.5-2);
优选地,以100重量份的所述2号介孔材料滤饼的用量为基准,所述硅胶的用量为1-200重量份,所述凹凸棒石的用量为1-50重量份;
优选地,以100重量份的所述2号介孔材料滤饼的用量为基准,所述硅胶的用量为50-150重量份,所述凹凸棒石的用量为20-50重量份。
5.根据权利要求1所述的方法,其中,在步骤(d)中,所述球形三介孔凹凸棒石复合材料载体、Pt组分前驱体和Zn组分前驱体的用量使得制备的异丁烷脱氢催化剂中,以所述异丁烷脱氢催化剂的总重量为基准,所述载体的含量为98-99.4重量%,所述Pt组分以Pt元素计的含量为0.1-0.5重量%,所述Zn组分以Zn元素计的含量为0.5-1.5重量%。
6.由权利要求1-5中任意一项所述的方法制备的异丁烷脱氢催化剂。
7.根据权利要求6所述的异丁烷脱氢催化剂,其中,所述异丁烷脱氢催化剂包括载体以及负载在所述载体上的Pt组分和Zn组分,其中,所述载体为球形三介孔凹凸棒石复合材料载体,所述球形三介孔凹凸棒石复合材料载体含有具有一维六方孔道分布结构的介孔分子筛材料和具有二维六方孔道分布结构的介孔分子筛材料,所述球形三介孔凹凸棒石复合材料载体的平均粒径为20-50μm,比表面积为150-600m2/g,孔体积为0.5-1.5mL/g,孔径分布为三峰分布,且所述三峰对应的最可几孔径分别为2-4nm、5-15nm和10-40nm。
8.根据权利要求7所述的异丁烷脱氢催化剂,其中,以所述异丁烷脱氢催化剂的总重量为基准,所述载体的含量为98-99.4重量%,所述Pt组分以Pt元素计的含量为0.1-0.5重量%,所述Zn组分以Zn元素计的含量为0.5-1.5重量%;
优选地,所述异丁烷脱氢催化剂的平均粒子直径为30-60μm,比表面积为200-650m2/g,孔体积为0.6-1.2mL/g,孔径分布为三峰分布,且所述三峰对应的最可几孔径分别为2.1-3.5nm、5.5-10nm和20-30nm。
9.根据权利要求7所述的异丁烷脱氢催化剂,其中,在所述球形三介孔凹凸棒石复合材料载体中,所述具有一维六方孔道分布结构的介孔分子筛材料和具有二维六方孔道分布结构的介孔分子筛材料的重量比为1:(0.1-10),优选为1:(0.5-2)。
10.权利要求6-9中任意一项所述的异丁烷脱氢催化剂在异丁烷脱氢制异丁烯中的应用,其中,该异丁烷脱氢制异丁烯的方法包括:在催化剂和氢气的存在下,将异丁烷进行脱氢反应。
11.根据权利要求10所述的方法,其中,异丁烷的用量与氢气的用量的摩尔比为(0.5-1.5):1;
优选地,所述脱氢反应的条件包括:反应温度为550-650℃,反应压力为0.05-0.2MPa,反应时间为20-40h,异丁烷质量空速为2-5h-1。