CN110579395A - 一种竹席类产品耐水摩擦色牢度检测方法 - Google Patents
一种竹席类产品耐水摩擦色牢度检测方法 Download PDFInfo
- Publication number
- CN110579395A CN110579395A CN201810622759.1A CN201810622759A CN110579395A CN 110579395 A CN110579395 A CN 110579395A CN 201810622759 A CN201810622759 A CN 201810622759A CN 110579395 A CN110579395 A CN 110579395A
- Authority
- CN
- China
- Prior art keywords
- bamboo mat
- rubbing
- color fastness
- water
- sample
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种色牢度检测方法,更具体地,涉及一种竹席类产品耐水摩擦色牢度检测方法。通过将标准物质在特定检测环境下预处理后,分别采用干摩擦和带有水的湿摩擦的方式对待检测样进行擦拭,然后在D65光源下用沾色用灰色样卡分别对试验后的标准物质进行对比评级完成检测。本发明通过模拟消费者使用竹席类产品过程,提供了一种操作简便、准确性高、重现性高的竹席类产品色牢度的检测方法,具有广泛的适用性和现实意义,是对竹席类产品色牢度检测方法的创新。
Description
技术领域
本发明涉及一种色牢度检测方法,更具体地,涉及一种竹席类产品耐水摩擦色牢度检测方法。
背景技术
随着人们生活品质的提高,对竹席类产品的质量要求也越来越高,但是当前市场上竹席类产品的质量参差不齐,在抽检过程中总是会出现产品色牢度不合格的情况。究其原因,主要体现在产品质量不过关和色牢度的测定方法有待改进这两个方面。竹席类产品市场占有率上升的同时,色牢度不合格引起的消费者的权益受到冲击的比例也在增加。竹席类产品的生产企业也因产品质量问题屡屡受挫,因此,不论是站在消费者的角度还是站在生产企业的角度,都急需探索一种客观评定竹席类产品色牢度的检测方法。目前,竹席类产品色牢度的测定方法是用充分浸透65%乙醇的脱脂纱布,在有色部位用力往返擦拭10次,目测脱脂纱布上是否有颜色。该方法不是模拟竹席类产品的使用过程而制定的。传统检测方法存在以下问题:首先所用试剂在实际使用过程中与人体分泌物不同。其次擦拭布并非标准物质,且对擦拭布的带液率、擦拭力度及擦拭动程未做定量指标。再次对检测结果的评价方法不合理,“目测脱脂纱布上有颜色即为不合格”,该评价方法过于草率,明显不适合评价竹席类产品的质量状况。综上所述,现有竹席类产品色牢度的检测方法可操作性差,检测结果重现性差,且为非仪器检测,不同检测人员检测的结果差异很大,且检测结果评价不合理,因此,解决上述问题就显得十分重要了。
发明内容
本发明为克服上述现有技术所述的缺陷,提供一种竹席类产品耐水摩擦色牢度检测方法,通过模拟消费者使用竹席类产品过程,将标准物质在特定检测环境下预处理后,分别采用干摩擦和带有试剂的湿摩擦的方式对待测竹席类产品试样进行擦拭,在D65光源下用沾色用灰色样卡分别对试验后的摩擦布进行对比评级的方式完成检测。本发明具有操作简便、准确性高、重现性高的特点,具有广泛的适用性和现实意义,是对竹席类产品色牢度检测方法的创新。
本发明的目的是提供一种色纱耐摩擦色牢度检测方法,包括有以下步骤:
a、竹席横向和纵向纹理不同需要准备好长度方向分别沿样品的长度方向和宽度方向的竹席类产品试样、标准物质和试剂;
b、模拟竹席日常使用情况,设定恒温恒湿室,温度为20℃±2℃,相对湿度:65%±4%;
c、对待测竹席类产品试样进行干摩擦,然后将标准物质置于评级灯箱D65光源下与GB/T 251 评定沾色用灰色样卡对比评级;
d、对待测竹席类产品试样进行湿摩擦,然后将摩擦布晾干调湿后置于评级灯箱D65光源下与GB/T 251 评定沾色用灰色样卡对比评级。
进一步的,所述干摩擦是参照GB/T 3920-2008中的检测方法,根据竹席类产品自身的特点和模拟竹席类产品实际使用过程对检测设备进行改造,施加压力范围为9N~15N,样品夹持器的夹持隔距范围为2mm~15mm;摩擦循环次数范围为10个~50个。竹席类产品的长度方向和宽度方向各检测一次。
进一步的,所述湿摩擦是将标准物质在试剂中完全浸湿,保证标准物质的含水率范围为65%~100%,然后参照GB/T 3920-2008中的检测方法,根据竹席类产品自身的特点和模拟竹席类产品实际使用过程对检测设备进行改造,施加压力范围为9N~15N,样品夹持器的夹持隔距范围为2mm~15mm;摩擦循环次数范围为10个~50个。竹席类产品的长度方向和宽度方向各检测一次,将湿摩擦布晾干。
进一步的,所述标准物质优选为棉摩擦布,具体规格如下:单位面积质量:(115±10)g/m2;白度值:Y10=89±2,W10=80±3,TW,10=-1±1;(Y10为明度值,W10为白度值,TW,10为淡色调指数)水萃取液pH值:7.0±0.5。
进一步的,所述试剂优选为三级水,具体规格如下:25℃时,pH值范围为5.0~7.5,电导率≤0.50mS/m;可氧化物质含量(以O计)≤0.4mg/L,蒸发残渣(105℃±2℃)含量≤2.0mg/L。
与现有技术相比,本发明的有益效果:
本发明通过模拟消费者使用竹席类产品过程,本发明是根据竹席类产品和摩擦标物的特点,将标准物质在特定环境下预处理后,运用合适的试剂,采用标准物质在恒定的压力下使用仪器检测,并将检测后的沾色标物在标准光源下与标准沾色卡对比、评级,给出沾色级数的科学的检测方法。提供了一种操作简便、准确性高、重现性高的竹席类产品色牢度的检测方法,具有广泛的适用性和现实意义,是对竹席类产品色牢度检测方法的创新。
附图说明
图1为竹席类产品试样。
图2为检测摩擦布图片。
图3为重复性实验检测摩擦布图片。
具体实施方式
附图仅用于示例性说明,不能理解为对本专利的限制;下面通过实施例对本发明进一步具体描述,但本发明的保护范围并不局限于此,凡在本发明基础上做出的非实质性改动都将落入本发明的保护范围之内。
实施例1
本实施例提供一种竹席类产品耐水摩擦色牢度检测方法,包括以下步骤:
a、准备好长度方向分别沿样品的长度方向和宽度方向约200mm×80mm的竹席类产品试样各两块、(50±2)mm×(50±2)mm大小的棉摩擦布若干块和三级水;
b、棉摩擦布在温度(20.0±2.0)℃和相对湿度(65.0±5.0)%的环境下放置24h以上;
c、对待测竹席类产品试样进行干摩擦,采用调湿过标准物质在压力范围为9N~15N,样品夹持器的夹持隔距范围为2mm~15mm,摩擦动程为(104±3)mm的条件下往复摩擦10个~50个循环,竹席类产品的长度方向和宽度方向各测试一次,然后将标准物质置于评级灯箱D65光源下与GB/T 251 评定沾色用灰色样卡对比评级;
d、对待测竹席类产品试样进行湿摩擦,将棉摩擦布在试剂中完全浸湿,保证摩擦布的含水(液)率范围为65%~100%,在压力范围为9N~15N,样品夹持器的夹持隔距范围为2mm~15mm,摩擦动程为(104±3)mm的条件下往复摩擦10个~50个循环,竹席类产品的长度方向和宽度方向各测试一次,然后将摩擦布晾干调湿后置于评级灯箱D65光源下与GB/T 251 评定沾色用灰色样卡对比评级。
按照上述条件,检验结果如下表所示:
类别 | 单位 | 长度方向 | 宽度方向 |
干摩擦 | 级 | 4-5 | 4-5 |
三级水湿摩擦 | 级 | 4 | 4 |
实施例2
本实施例在实施例1的基础上让不同人员对本发明进行重现性实验,检验结果如下表所示:
由此可见,本实施例与实施例1的结果差异在0.5级以内,检测方法符合重现性要求。
Claims (7)
1.一种竹席类产品耐水摩擦色牢度检测方法,其特征在于,包括以下步骤:
a、准备好长度方向分别沿样品的长度方向和宽度方向的竹席类产品试样、标准物质和试剂;
b、设定恒温恒湿室;
c、对待测竹席类产品试样进行干摩擦,然后将标准物质置于评级灯箱D65光源下与GB/T 251 评定沾色用灰色样卡对比评级;
d、对待测竹席类产品试样进行湿摩擦,然后将摩擦布晾干调湿后置于评级灯箱D65光源下与GB/T 251 评定沾色用灰色样卡对比评级。
2.根据权利要求1所述的一种竹席类产品耐水摩擦色牢度检测方法,其特征在于,所述恒温恒湿室的温度优选为20℃±2℃,相对湿度优选为65%±4%。
3.根据权利要求1所述的一种竹席类产品耐水摩擦色牢度检测方法,其特征在于,所述干摩擦采用调湿过标准物质在压力范围为9N~15N,样品夹持器的夹持隔距范围为2mm~15mm,摩擦动程为(104±3)mm的条件下往复摩擦10个~50个循环。
4.根据权利要求1所述的一种竹席类产品耐水摩擦色牢度检测方法,其特征在于,所述湿摩擦需要将棉摩擦布在试剂中完全浸湿,保证摩擦布的含水(液)率范围为65%~100%。
5.根据权利要求1所述的一种竹席类产品耐水摩擦色牢度检测方法,其特征在于,所述湿摩擦在压力范围为9N~15N,样品夹持器的夹持隔距范围为2mm~15mm,摩擦动程为(104±3)mm的条件下往复摩擦10个~50个循环。
6.根据权利要求1所述的一种竹席类产品耐水摩擦色牢度检测方法,其特征在于,所述标准物质优选为棉摩擦布。
7.根据权利要求1所述的一种竹席类产品耐水摩擦色牢度检测方法,其特征在于,所述试剂优选为三级水。