CN110337347B - 金属粘结磨料制品及制备金属粘结磨料制品的方法 - Google Patents

金属粘结磨料制品及制备金属粘结磨料制品的方法 Download PDF

Info

Publication number
CN110337347B
CN110337347B CN201880014168.4A CN201880014168A CN110337347B CN 110337347 B CN110337347 B CN 110337347B CN 201880014168 A CN201880014168 A CN 201880014168A CN 110337347 B CN110337347 B CN 110337347B
Authority
CN
China
Prior art keywords
metal
abrasive article
particles
metal bond
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201880014168.4A
Other languages
English (en)
Chinese (zh)
Other versions
CN110337347A (zh
Inventor
让-路西·瑞法特
巴德理·维尔拉哈万
蒂洛·若姆霍夫
布赖恩·D·格斯
安德烈亚斯·M·格尔德马赫
罗伯特·L·W·史密森
普热梅斯瓦夫·P·马尔科维茨
约翰尼斯·芬克
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Publication of CN110337347A publication Critical patent/CN110337347A/zh
Application granted granted Critical
Publication of CN110337347B publication Critical patent/CN110337347B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
    • B24D3/02—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent
    • B24D3/04—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic
    • B24D3/06—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic metallic or mixture of metals with ceramic materials, e.g. hard metals, "cermets", cements
    • B24D3/10—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic metallic or mixture of metals with ceramic materials, e.g. hard metals, "cermets", cements for porous or cellular structure, e.g. for use with diamonds as abrasives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/16—Metallic particles coated with a non-metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/17—Metallic particles coated with metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/18—Non-metallic particles coated with metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/20—Direct sintering or melting
    • B22F10/28—Powder bed fusion, e.g. selective laser melting [SLM] or electron beam melting [EBM]
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/60—Treatment of workpieces or articles after build-up
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/06—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools
    • B22F7/08—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools with one or more parts not made from powder
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D11/00—Constructional features of flexible abrasive materials; Special features in the manufacture of such materials
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D18/00—Manufacture of grinding tools or other grinding devices, e.g. wheels, not otherwise provided for
    • B24D18/0009—Manufacture of grinding tools or other grinding devices, e.g. wheels, not otherwise provided for using moulds or presses
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D18/00—Manufacture of grinding tools or other grinding devices, e.g. wheels, not otherwise provided for
    • B24D18/0027—Manufacture of grinding tools or other grinding devices, e.g. wheels, not otherwise provided for by impregnation
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
    • B24D3/02—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent
    • B24D3/04—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic
    • B24D3/06—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic metallic or mixture of metals with ceramic materials, e.g. hard metals, "cermets", cements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D5/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor
    • B24D5/02—Wheels in one piece
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D5/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor
    • B24D5/10—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor with cooling provisions, e.g. with radial slots
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D5/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting only by their periphery; Bushings or mountings therefor
    • B24D5/14—Zonally-graded wheels; Composite wheels comprising different abrasives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D7/00—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting otherwise than only by their periphery, e.g. by the front face; Bushings or mountings therefor
    • B24D7/06—Bonded abrasive wheels, or wheels with inserted abrasive blocks, designed for acting otherwise than only by their periphery, e.g. by the front face; Bushings or mountings therefor with inserted abrasive blocks, e.g. segmental
    • B24D7/066—Grinding blocks; their mountings or supports
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y10/00—Processes of additive manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y40/00—Auxiliary operations or equipment, e.g. for material handling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y70/00—Materials specially adapted for additive manufacturing
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
    • C09K3/00—Materials not provided for elsewhere
    • C09K3/14—Anti-slip materials; Abrasives
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C26/00—Alloys containing diamond or cubic or wurtzitic boron nitride, fullerenes or carbon nanotubes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/30—Process control
    • B22F10/34—Process control of powder characteristics, e.g. density, oxidation or flowability
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/30—Process control
    • B22F10/36—Process control of energy beam parameters
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/30—Process control
    • B22F10/36—Process control of energy beam parameters
    • B22F10/366—Scanning parameters, e.g. hatch distance or scanning strategy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/60—Treatment of workpieces or articles after build-up
    • B22F10/64—Treatment of workpieces or articles after build-up by thermal means
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/10—Auxiliary heating means
    • B22F12/17—Auxiliary heating means to heat the build chamber or platform
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/40—Radiation means
    • B22F12/41—Radiation means characterised by the type, e.g. laser or electron beam
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/05—Light metals
    • B22F2301/052—Aluminium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/05—Light metals
    • B22F2301/058—Magnesium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/15—Nickel or cobalt
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/20—Refractory metals
    • B22F2301/205—Titanium, zirconium or hafnium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/25—Noble metals, i.e. Ag Au, Ir, Os, Pd, Pt, Rh, Ru
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/35—Iron
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2302/00—Metal Compound, non-Metallic compound or non-metal composition of the powder or its coating
    • B22F2302/10—Carbide
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2302/00—Metal Compound, non-Metallic compound or non-metal composition of the powder or its coating
    • B22F2302/20—Nitride
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2998/00—Supplementary information concerning processes or compositions relating to powder metallurgy
    • B22F2998/10—Processes characterised by the sequence of their steps
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2999/00—Aspects linked to processes or compositions used in powder metallurgy
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P10/00—Technologies related to metal processing
    • Y02P10/25—Process efficiency

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Physics & Mathematics (AREA)
  • Ceramic Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Plasma & Fusion (AREA)
  • Organic Chemistry (AREA)
  • Composite Materials (AREA)
  • Automation & Control Theory (AREA)
  • Metallurgy (AREA)
  • General Health & Medical Sciences (AREA)
  • Toxicology (AREA)
  • Thermal Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Optics & Photonics (AREA)
  • Polishing Bodies And Polishing Tools (AREA)
  • Dental Tools And Instruments Or Auxiliary Dental Instruments (AREA)
  • Welding Or Cutting Using Electron Beams (AREA)
  • Laser Beam Processing (AREA)
  • Powder Metallurgy (AREA)
CN201880014168.4A 2017-02-28 2018-01-25 金属粘结磨料制品及制备金属粘结磨料制品的方法 Active CN110337347B (zh)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
US201762464632P 2017-02-28 2017-02-28
US62/464,632 2017-02-28
US201762549161P 2017-08-23 2017-08-23
US62/549,161 2017-08-23
PCT/US2018/015134 WO2018160297A1 (en) 2017-02-28 2018-01-25 Metal bond abrasive articles and methods of making metal bond abrasive articles

Publications (2)

Publication Number Publication Date
CN110337347A CN110337347A (zh) 2019-10-15
CN110337347B true CN110337347B (zh) 2022-07-12

Family

ID=63370218

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201880014168.4A Active CN110337347B (zh) 2017-02-28 2018-01-25 金属粘结磨料制品及制备金属粘结磨料制品的方法

Country Status (6)

Country Link
US (1) US11383350B2 (enExample)
EP (1) EP3589450A4 (enExample)
JP (1) JP2020511317A (enExample)
KR (1) KR102464517B1 (enExample)
CN (1) CN110337347B (enExample)
WO (1) WO2018160297A1 (enExample)

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110337347B (zh) 2017-02-28 2022-07-12 3M创新有限公司 金属粘结磨料制品及制备金属粘结磨料制品的方法
JP7012276B2 (ja) * 2018-09-07 2022-01-28 石川県 砥粒付工具、砥粒付工具の製造方法及び砥粒固着方法
AT16308U3 (de) * 2018-11-19 2019-12-15 Plansee Se Additiv gefertigtes Refraktärmetallbauteil, additives Fertigungsverfahren und Pulver
CN109628772B (zh) * 2018-12-25 2020-04-10 华中科技大学 一种超短周期高强度-高延展性镍铝青铜合金及制备方法
CN109483418B (zh) * 2018-12-28 2023-11-17 西安增材制造国家研究院有限公司 金属基微量润滑砂轮及金属基微量润滑砂轮的制作方法
DE102019207350A1 (de) * 2019-05-20 2020-11-26 Siemens Aktiengesellschaft Schweißverfahren mit ummantelten abrasiven Teilchen, ummanteltes abrasives Teilchen, Schichtsystem und Dichtungssystem
US11965398B2 (en) * 2019-06-27 2024-04-23 Schlumberger Technology Corporation Wear resistant self-lubricating additive manufacturing parts and part features
CN112140015A (zh) * 2019-06-28 2020-12-29 圣戈班磨料磨具有限公司 磨料制品及其形成方法
DE102019209992A1 (de) * 2019-07-08 2021-01-14 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Verfahren zur Herstellung eines Verbundbauteils
WO2021038438A1 (en) 2019-08-28 2021-03-04 3M Innovative Properties Company Dental bur, manufacturing method therefor and data stream
MX2022004618A (es) * 2019-10-16 2022-05-06 Saint Gobain Abrasives Inc Articulos abrasivos y metodos de formacion.
CN112743443A (zh) * 2019-10-29 2021-05-04 山西钜星超硬工具制品有限公司 一种珩磨油石
CN110901049B (zh) * 2019-11-15 2020-10-02 华中科技大学 一种适用于宽温度梯度下选择性熔化成型的喷印打印设备
KR102335793B1 (ko) * 2020-03-09 2021-12-08 신한다이아몬드공업 주식회사 Cmp 패드 컨디셔너 제조방법 및 이를 이용한 cmp 패드 컨디셔너
US11481524B2 (en) * 2020-06-26 2022-10-25 Microsoft Technology Licensing, Llc Conformal coating iteration
CN111633575A (zh) * 2020-06-30 2020-09-08 郑州高新磨料磨具有限公司 一种加工止推面用金属结合剂cbn砂轮及其制备方法
CN111940742B (zh) * 2020-08-08 2022-07-05 邹爱忠 一种梯度硬质合金的制备方法
KR102286383B1 (ko) * 2021-01-13 2021-08-04 양회준 코발트를 사용하지 않는 다이아몬드 세그멘트를 이용한 본드재 및 그 다이아몬드 세그멘트
JP2024509814A (ja) 2021-03-05 2024-03-05 サンーゴバン アブレイシブズ，インコーポレイティド 研磨物品及びそれを形成するための方法
CN117279744A (zh) * 2021-03-05 2023-12-22 圣戈班磨料磨具有限公司 磨料制品及其形成方法
WO2023130082A1 (en) 2021-12-30 2023-07-06 Saint-Gobain Abrasives, Inc. Abrasive articles and methods for forming same
CN115138859B (zh) * 2022-08-17 2023-07-07 南京农业大学 一种一体化成形的金刚石砂轮及其制备方法
CN118880116B (zh) * 2024-07-09 2025-09-19 广东水利电力职业技术学院（广东省水利电力技工学校） 一种含金刚石的复合材料、制备方法和用途

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3650714A (en) * 1969-03-04 1972-03-21 Permattach Diamond Tool Corp A method of coating diamond particles with metal
US6416560B1 (en) * 1999-09-24 2002-07-09 3M Innovative Properties Company Fused abrasive bodies comprising an oxygen scavenger metal
US20060162967A1 (en) * 2005-01-27 2006-07-27 Brackin Van J Abrasive-impregnated cutting structure having anisotropic wear resistance and drag bit including same
CN101132884A (zh) * 2004-12-09 2008-02-27 宋健民 使超研磨颗粒于金属基质中的保持率最大化的方法
CN103703208A (zh) * 2011-06-22 2014-04-02 贝克休斯公司 涂覆的颗粒和相关方法
US20150290771A1 (en) * 2012-03-27 2015-10-15 Yundong Li Abrasive article and method for making the same
TW201622972A (zh) * 2014-10-17 2016-07-01 應用材料股份有限公司 由積層製造製程所生產之硏磨墊
US20160354901A1 (en) * 2013-11-04 2016-12-08 Applied Materials, Inc. Printed chemical mechanical polishing pad having abrasives therein and system for printing
CN106312843A (zh) * 2016-10-31 2017-01-11 湖南城市学院 一种金刚石砂轮及其生产方法

Family Cites Families (50)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2367404A (en) 1943-07-09 1945-01-16 Fish Schurman Corp Abrasive composition of matter and method of forming same
JPS5217913B1 (enExample) * 1966-07-11 1977-05-18
US3663191A (en) * 1970-07-23 1972-05-16 Dentsply Int Inc Diamond tool and method of making the same
JPS5217913A (en) 1975-07-31 1977-02-10 Nippon Telegraph & Telephone Dot matrix type head
US4314827A (en) 1979-06-29 1982-02-09 Minnesota Mining And Manufacturing Company Non-fused aluminum oxide-based abrasive mineral
US4623364A (en) 1984-03-23 1986-11-18 Norton Company Abrasive material and method for preparing the same
CA1254238A (en) 1985-04-30 1989-05-16 Alvin P. Gerk Process for durable sol-gel produced alumina-based ceramics, abrasive grain and abrasive products
US4612242A (en) 1985-06-03 1986-09-16 Minnesota Mining And Manufacturing Company Pressure-sensitive adhesive tape containing coated glass microbubbles
US4770671A (en) 1985-12-30 1988-09-13 Minnesota Mining And Manufacturing Company Abrasive grits formed of ceramic containing oxides of aluminum and yttrium, method of making and using the same and products made therewith
US4881951A (en) 1987-05-27 1989-11-21 Minnesota Mining And Manufacturing Co. Abrasive grits formed of ceramic containing oxides of aluminum and rare earth metal, method of making and products made therewith
US4848041A (en) 1987-11-23 1989-07-18 Minnesota Mining And Manufacturing Company Abrasive grains in the shape of platelets
AU4504089A (en) 1988-10-05 1990-05-01 Michael Feygin An improved apparatus and method for forming an integral object from laminations
US5433280A (en) 1994-03-16 1995-07-18 Baker Hughes Incorporated Fabrication method for rotary bits and bit components and bits and components produced thereby
US5839329A (en) 1994-03-16 1998-11-24 Baker Hughes Incorporated Method for infiltrating preformed components and component assemblies
BE1008917A3 (fr) 1994-11-16 1996-10-01 Diamant Boart Sa Outil abrasif, de coupe ou analogue et procede de fabrication de cet outil.
DE19533960C2 (de) 1995-09-13 1997-08-28 Fraunhofer Ges Forschung Verfahren und Vorrichtung zur Herstellung von metallischen Werkstücken
US6039641A (en) 1997-04-04 2000-03-21 Sung; Chien-Min Brazed diamond tools by infiltration
DE19834559A1 (de) 1998-07-31 2000-02-03 Friedrich Schiller Uni Jena Bu Verfahren zur Herstellung von Werkzeugen für die Bearbeitung von Oberflächen
DE19909882C2 (de) 1999-03-06 2002-01-10 Fraunhofer Ges Forschung Material zur schichtweisen Herstellung von Werkzeugen, Formen oder Bauteilen durch das Lasersinterverfahren
US6319108B1 (en) * 1999-07-09 2001-11-20 3M Innovative Properties Company Metal bond abrasive article comprising porous ceramic abrasive composites and method of using same to abrade a workpiece
CA2327634A1 (en) * 1999-12-07 2001-06-07 Powdermet, Inc. Abrasive particles with metallurgically bonded metal coatings
US6413286B1 (en) 2000-05-03 2002-07-02 Saint-Gobain Abrasives Technology Company Production tool process
US6551366B1 (en) 2000-11-10 2003-04-22 3M Innovative Properties Company Spray drying methods of making agglomerate abrasive grains and abrasive articles
US20020095875A1 (en) 2000-12-04 2002-07-25 D'evelyn Mark Philip Abrasive diamond composite and method of making thereof
JP2003039328A (ja) 2001-07-31 2003-02-13 Kurenooton Kk メタルボンドホイール及びその製造方法
US7544114B2 (en) 2002-04-11 2009-06-09 Saint-Gobain Technology Company Abrasive articles with novel structures and methods for grinding
JP2004009251A (ja) 2002-06-10 2004-01-15 Nippon Plastic Seito Kk 極薄超砥粒メタルボンド砥石およびその製造方法
US20060059785A1 (en) 2002-09-24 2006-03-23 Chien-Min Sung Methods of maximizing retention of superabrasive particles in a metal matrix
US6814926B2 (en) 2003-03-19 2004-11-09 3D Systems Inc. Metal powder composition for laser sintering
KR100489547B1 (ko) 2003-06-20 2005-05-16 일진디스플레이(주) 구리계 매트릭스 합금과의 소결성이 우수한 다이아몬드그릿과 그 제조방법 및 이를 사용한 소결공구
PL2316567T3 (pl) 2003-09-26 2018-07-31 3M Innovative Properties Co. Katalizatory, środki aktywujące, nośniki i metodologie użyteczne do wytwarzania układów katalizatora, w szczególności gdy katalizator jest osadzany na nośnikach z wykorzystaniem fizycznego osadzania z fazy gazowej
RU2366539C9 (ru) 2004-06-10 2010-02-10 Элломет Корпорейшн Способ уплотнения твердых порошков с жестким покрытием
US7875091B2 (en) 2005-02-22 2011-01-25 Saint-Gobain Abrasives, Inc. Rapid tooling system and methods for manufacturing abrasive articles
US20070031791A1 (en) 2005-08-03 2007-02-08 3M Innovative Properties Company Scanning models for digital orthodontics
WO2007121052A2 (en) 2006-04-13 2007-10-25 3M Innovative Properties Company Metal-coated superabrasive material and methods of making the same
US8882868B2 (en) * 2008-07-02 2014-11-11 Saint-Gobain Abrasives, Inc. Abrasive slicing tool for electronics industry
US8142531B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with a sloping sidewall
MX351393B (es) 2009-08-04 2017-10-13 Allomet Corp Partículas duras recubiertas resistentes consolidadas en una matriz de material resistente.
ES2654569T3 (es) 2009-12-31 2018-02-14 Saint-Gobain Abrasives, Inc. Artículo abrasivo que incorpora un segmento abrasivo infiltrado
EP2794089A4 (en) 2011-12-22 2015-09-09 3M Innovative Properties Co ETHYLENE DISTANCE MEDIUM
US9067299B2 (en) 2012-04-25 2015-06-30 Applied Materials, Inc. Printed chemical mechanical polishing pad
MX365368B (es) * 2012-09-27 2019-05-30 Allomet Corp Métodos para formar un artículo metálico o de cerámica que tiene una composición nueva de material graduado funcionalmente y artículos que contienen este material.
WO2014074947A2 (en) 2012-11-08 2014-05-15 Das, Suman Systems and methods for additive manufacturing and repair of metal components
JP2016538149A (ja) 2013-09-30 2016-12-08 サン−ゴバン セラミックス アンド プラスティクス，インコーポレイティド 形状化研磨粒子及び形状化研磨粒子を形成する方法
EP3132154B1 (en) * 2014-04-15 2018-02-28 Ferdiam S.r.l. Braking member for brake system and method for making it
US10888973B2 (en) 2015-06-25 2021-01-12 3M Innovative Properties Company Methods of making metal bond abrasive articles and metal bond abrasive articles
WO2016210057A1 (en) 2015-06-25 2016-12-29 3M Innovative Properties Company Vitreous bond abrasive articles and methods of making the same
KR102629658B1 (ko) 2016-01-21 2024-01-29 쓰리엠 이노베이티브 프로퍼티즈 캄파니 금속 접합제 및 유리질 접합제 연마 용품의 제조 방법, 및 연마 용품 전구체
WO2017173009A1 (en) 2016-03-30 2017-10-05 3M Innovative Properties Company Methods of making metal bond and vitreous bond abrasive articles, and abrasive article precursors
CN110337347B (zh) 2017-02-28 2022-07-12 3M创新有限公司 金属粘结磨料制品及制备金属粘结磨料制品的方法

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3650714A (en) * 1969-03-04 1972-03-21 Permattach Diamond Tool Corp A method of coating diamond particles with metal
US6416560B1 (en) * 1999-09-24 2002-07-09 3M Innovative Properties Company Fused abrasive bodies comprising an oxygen scavenger metal
CN101132884A (zh) * 2004-12-09 2008-02-27 宋健民 使超研磨颗粒于金属基质中的保持率最大化的方法
US20060162967A1 (en) * 2005-01-27 2006-07-27 Brackin Van J Abrasive-impregnated cutting structure having anisotropic wear resistance and drag bit including same
CN103703208A (zh) * 2011-06-22 2014-04-02 贝克休斯公司 涂覆的颗粒和相关方法
US20150290771A1 (en) * 2012-03-27 2015-10-15 Yundong Li Abrasive article and method for making the same
US20160354901A1 (en) * 2013-11-04 2016-12-08 Applied Materials, Inc. Printed chemical mechanical polishing pad having abrasives therein and system for printing
TW201622972A (zh) * 2014-10-17 2016-07-01 應用材料股份有限公司 由積層製造製程所生產之硏磨墊
CN106312843A (zh) * 2016-10-31 2017-01-11 湖南城市学院 一种金刚石砂轮及其生产方法

Also Published As

Publication number Publication date
WO2018160297A1 (en) 2018-09-07
US20190375072A1 (en) 2019-12-12
CN110337347A (zh) 2019-10-15
EP3589450A1 (en) 2020-01-08
US11383350B2 (en) 2022-07-12
JP2020511317A (ja) 2020-04-16
EP3589450A4 (en) 2021-04-07
KR102464517B1 (ko) 2022-11-10
KR20190124720A (ko) 2019-11-05

Similar Documents

Publication Publication Date Title
CN110337347B (zh) 金属粘结磨料制品及制备金属粘结磨料制品的方法
US11597058B2 (en) Methods of making metal bond abrasive articles and metal bond abrasive articles
KR102427116B1 (ko) 배향된 연마 입자를 포함하는 접합된 연마 용품, 및 그의 제조 방법
JP5991574B2 (ja) 三次元形状造形物の製造方法
JP6303016B2 (ja) 積層造形物の製造方法
CN114286729B (zh) 用于叠层制造的粉末共混物
CN111050954A (zh) 用于增材制造的设备及方法
JP2020511317A5 (enExample)
JP2019508264A (ja) メタルボンド及びガラス質ボンド研磨物品の製造方法、並びに研磨物品前駆体
EP3436269A1 (en) Methods of making metal bond and vitreous bond abrasive articles, and abrasive article precursors
WO2021038438A1 (en) Dental bur, manufacturing method therefor and data stream
EP2334455B1 (en) Microwave plasma sintering
WO2021001730A1 (en) Methods of making metal bond abrasive articles and metal bond abrasive articles
TWI239874B (en) Metal powder composition for use in selective laser sintering, method of making same, and three-dimensional object shaped from same
JP6780697B2 (ja) 複合粒子、複合粉末、複合粒子の製造方法、および複合部材の製造方法
CN117324639A (zh) 一种镍铜基金刚石复合材料及其电子束增材制造工艺与应用
JP7730682B2 (ja) 銅基粉、その製造方法、および銅基粉を用いた光造形物の製造方法
JP2008018532A (ja) 研削砥石の製造方法
JP7012276B2 (ja) 砥粒付工具、砥粒付工具の製造方法及び砥粒固着方法
KR20190074295A (ko) 코팅된 충전제 입자를 갖는 금속 하이브리드 연삭 휠
JP2016191154A (ja) 三次元形状造形物の製造方法
TW202432460A (zh) 顆粒組合物及相關方法與用途以形成燒結碳化矽體
YANG et al. Analysis of the Mechanisms and Characteristics of Laser Sintering Diamond Fine Powder and Metallic Powder.

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant