CN110258110A - A kind of method for processing after of ready-made non-ironing garment - Google Patents
A kind of method for processing after of ready-made non-ironing garment Download PDFInfo
- Publication number
- CN110258110A CN110258110A CN201910514559.9A CN201910514559A CN110258110A CN 110258110 A CN110258110 A CN 110258110A CN 201910514559 A CN201910514559 A CN 201910514559A CN 110258110 A CN110258110 A CN 110258110A
- Authority
- CN
- China
- Prior art keywords
- ready
- processing
- fabric
- made non
- ironing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method for processing after of ready-made non-ironing garment, material spray in ready-made non-ironing garment manufacturing procedure carries out the liquid carrying rate of spraying feeding to fabric 60~90% using resin finishing liquid, in terms of 1L resin finishing liquid, the formula of resin finishing liquid are as follows: the Fixapret F-AP resin of 140~180 g, the magnesium chloride of 15~20 g, the softening agent of 50~60 g, the penetrating agent JFC of 2 g；Sand washing process in ready-made clothes washing final finishing manufacturing procedure are as follows: the ready-made clothes after baking is put into rinsing machine, float stone is added after adding water, carries out sand washing, wherein, the weight ratio of float stone and ready-made clothes is 3~5:1, and sand washing temperature is 30~60 DEG C; bath raio is 1:8~15, and the sand washing time is 30~60 minutes.The present invention obtains the special apricot skin feel of ready-made clothes fabric under the premise of retaining the strength of non-ironing face fabric as far as possible, and the ready-made clothes processed has excellent appearance after laundering flatness, graceful appearance, good dimensional stability and comfortable velvet.
Description
Technical field
The present invention relates to the ready-made clothes method for processing after of field of textiles, the post-processing of specifically a kind of ready-made non-ironing garment is processed
Method.
Background technique
In press finish for ready process, have washing step after non-ironing, effect be remove residual resin on fabric and
Other auxiliary chemicals.The principle of press finish for ready is fiber with resin reaction, although the ironing-free performance of ready-made clothes can be improved,
The disadvantage is that on the one hand will cause feeling hard for fabric, the strength loss of fabric on the other hand will cause.
Therefore, how under conditions of retaining non-ironing face fabric strength as far as possible, the feel of ready-made non-ironing garment clothes is effectively improved
Hardening is the technical matters for needing to solve.In consideration of it, the present invention proposes a kind of method for processing after of ready-made non-ironing garment.
Summary of the invention
The technical problem to be solved by the present invention is in view of the deficiencies of the prior art, provide a kind of rear place of ready-made non-ironing garment
Processing method is managed, under the premise of retaining the strength of non-ironing face fabric as far as possible, obtains the special apricot skin feel of ready-made clothes fabric, processing
Obtained ready-made clothes has excellent appearance after laundering flatness, graceful appearance, good dimensional stability and comfortable velvet.
The technical scheme of the invention to solve the technical problem is: a kind of post-processing processing side of ready-made non-ironing garment
Method, including ready-made non-ironing garment manufacturing procedure and ready-made clothes washing final finishing manufacturing procedure, the ready-made non-ironing garment manufacturing procedure include pre-
Wash, be dehydrated, drying, material spray, preliminary drying, pressing and baking, the ready-made clothes washing final finishing manufacturing procedure include sand washing, washing,
Drying, handcuff button, it is whole scald and packaging, the material spray using resin finishing liquid carry out the liquid carrying rate of spraying feeding to fabric 60~
90%, in terms of resin finishing liquid described in 1L, the formula of the resin finishing liquid are as follows: the Fixapret F-AP of 140~180g
Resin, the magnesium chloride of 15~20g, the softening agent of 50~60g, the penetrating agent JFC of 2g；The sand washing process are as follows: after baking
Ready-made clothes be put into rinsing machine, add and add float stone after water, carry out sand washing, wherein the weight ratio of float stone and ready-made clothes is 3~5:1,
Sand washing temperature is 30~60 DEG C, and bath raio is 1:8~15, and the sand washing time is 30~60 minutes.
The spy of the two process flows of present invention combination ready-made non-ironing garment manufacturing procedure and ready-made clothes washing final finishing manufacturing procedure
Point, innovatively using specific resin finishing liquid and in ready-made clothes washing final finishing manufacturing procedure in ready-made non-ironing garment manufacturing procedure
Middle that specific sand washing is used to arrange as leather washed, two aspects act synergistically to improve the feel and appearance style of fabric.
Final finishing processing method of the present invention other than adding float stone, no longer adds traditional Sand Wash Process during sand washing
The cellulase fibrillation of middle addition, it is therefore an objective to reduce the damage to fabric fiber strength, rub and improve simply by surface physics
The surface velvet of ready-made clothes fabric obtains the special apricot skin feel of fabric to effectively improve fabric hand feel.
Preferably, the softening agent is polyurethane.Further, the softening agent is that high Gao Huagong (China) has
The polyurethane RPU-N of limit company production.Polyurethane is different from having in common ready-made non-ironing garment formula as reactive softening agent
On the one hand the flat appearance degree of fabric can be improved in machine silicon class softening agent, on the other hand polyurethane is several to fabric when non-ironing reaction
There is no strength loss, to the strength of fabric can be made to reduce less on the basis of guaranteeing fabric flat appearance degree, effectively protected
More fabric strengths have been stayed, provide preferable strength basis for the sand washing process of lower ready-made clothes washing together.
Preferably, the Fixapret F-AP resin is the modification of high Gao Huagong (China) Co., Ltd production
Hydroxymethyl-2 dihydroxy-ethylene urea class crosslinked at low temperature resin.
Preferably, the float stone is irregular bulk, partial size is less than 3cm, in order to which each position of fabric can
Obtain uniform sand washing effect.
Preferably, the float stone is Turkey's white float stone.Turkey's white float stone medium density, during sand washing
It is non-friable, too violent impact will not be caused to the frictional force of fabric, the local strength damage that can avoid fabric is excessive.
Preferably, fabric is 40~50% containing damp rate after the preliminary drying.40~50% rate containing tide can ensure that
The reaction of resin is efficiently and uniform when pressing.
Preferably, the fabric is the fabric that English props up 60/2,80/2,100/2 or 200/4.This kind of fabric is especially suitable
It is processed in processing method after applying the present invention, makes fabric stretching with higher and tearing brute force.
Compared with prior art, the present invention has the advantage that the post-processing processing side of ready-made non-ironing garment disclosed by the invention
Method, in conjunction with the characteristics of ready-made non-ironing garment manufacturing procedure and ready-made clothes washing final finishing the two process flows of manufacturing procedure, innovatively
Specific resin finishing liquid is used in ready-made non-ironing garment manufacturing procedure and in ready-made clothes washing final finishing manufacturing procedure using specific
Sand washing arranged as leather washed, two aspect synergistic effects are to improve the feel and appearance style of fabric.Of the invention is rear whole
Processing method is managed, under the premise of retaining the strength of non-ironing face fabric as far as possible, obtains the special apricot skin feel of ready-made clothes fabric, processing
Obtained ready-made clothes has excellent appearance after laundering flatness, graceful appearance, good dimensional stability and comfortable velvet.
Specific embodiment
Present invention is further described in detail with reference to embodiments.
Embodiment 1: it is served as a contrast for ready-made clothes made of the twill fabric that fabric specification is CPT100/2*CPT100/2 150*100
Shirt carries out final finishing processing using the method for the present invention, method particularly includes:
Firstly, ready-made clothes shirt 300 total 90KG is taken to carry out ready-made non-ironing garment processing: it is pre- first to carry out clear water in industrial washing machine
It washes, the prewashing 30 minutes at a temperature of 40 DEG C, then is dehydrated, dries；Then spraying feeding (i.e. material spray) is carried out using resin finishing liquid,
Make the liquid carrying rate of fabric 80%, wherein in terms of 1L resin finishing liquid, the formula of resin finishing liquid are as follows: the Fixapret of 140g
F-AP resin, the magnesium chloride of 16g, the penetrating agent JFC of the polyurethane RPU-N, 2g of 60g；Be dried to fabric in advance later is containing damp rate
45%；Next upper pressing machine carries out subregion pressing, whole pressings to each position such as the anter of shirt, rear piece, sleeve and collar
After the completion, ready-made clothes Fang Ru oven is baked.
Secondly, carrying out washing final finishing processing to ready-made clothes shirt: 300 total 90KG of ready-made clothes shirt after taking non-ironing processing are extremely
In rinsing machine, add water 1000mL, add Turkey white float stone 30KG, carry out sand washing, sand washing temperature is 40 DEG C, the sand washing time
It is 30 minutes, takes out ready-made clothes shirt later and carry out common clear water washing, then dries, puts handcuffs on button, whole boiling hot and packaging.
Ready-made clothes shirt through final finishing processing in embodiment 1 has apricot skin feel, dimensionally stable, flat appearance, every
The performance test results are shown in Table 1.
Table 1
Embodiment 2: it is ready-made clothes shirt made of CPT80/2*CPT80/2 130*90 twill fabric for fabric specification, adopts
Final finishing processing is carried out with the method for the present invention, method particularly includes:
Firstly, ready-made clothes shirt 300 total 90KG is taken to carry out ready-made non-ironing garment processing: it is pre- first to carry out clear water in industrial washing machine
It washes, the prewashing 40 minutes at a temperature of 40 DEG C, then is dehydrated, dries；Then spraying feeding (i.e. material spray) is carried out using resin finishing liquid,
Make the liquid carrying rate of fabric 85%, wherein in terms of 1L resin finishing liquid, the formula of resin finishing liquid are as follows: the Fixapret of 160g
F-AP resin, the magnesium chloride of 16g, the penetrating agent JFC of the polyurethane RPU-N, 2g of 50g；Be dried to fabric in advance later is containing damp rate
50%；Next upper pressing machine carries out subregion pressing, whole pressings to each position such as the anter of shirt, rear piece, sleeve and collar
After the completion, ready-made clothes Fang Ru oven is baked.
Secondly, carrying out washing final finishing processing to ready-made clothes shirt: 300 total 90KG of ready-made clothes shirt after taking non-ironing processing are extremely
In rinsing machine, add water 1000mL, add Turkey white float stone 30KG, carry out sand washing, sand washing temperature is 50 DEG C, the sand washing time
It is 40 minutes, takes out ready-made clothes shirt later and carry out common clear water washing, then dries, puts handcuffs on button, whole boiling hot and packaging.
Ready-made clothes shirt through final finishing processing in embodiment 2 has apricot skin feel, dimensionally stable, flat appearance, every
The performance test results are shown in Table 2.
Table 2
In above-described embodiment, Fixapret F-AP resin selects the modification of high Gao Huagong (China) Co., Ltd production
Hydroxymethyl-2 dihydroxy-ethylene urea class crosslinked at low temperature resin, appearance clarification, can use cold water infinite dilution.Polyurethane RPU-N is selected
The product of high Gao Huagong (China) Co., Ltd production, it is a kind of heat reactivity polyurethane that appearance, which is clear liquid, ionic
For nonionic, the pH value of stoste is 5 ± 1, can be dissolved in cold water in any proportion, until boiling does not generate flash-point, storage temperature
It can at least be stored 12 months at lower than 40 DEG C.
Claims (8)
1. work is processed in a kind of method for processing after of ready-made non-ironing garment, including ready-made non-ironing garment manufacturing procedure and ready-made clothes washing final finishing
Sequence, the ready-made non-ironing garment manufacturing procedure include prewashing, dehydration, drying, material spray, preliminary drying, pressing and bake, the ready-made clothes water
Washing final finishing manufacturing procedure includes sand washing, washing, drying, handcuff button, whole boiling hot and packaging, it is characterised in that: the material spray uses
Resin finishing liquid carries out the liquid carrying rate of spraying feeding to fabric in 60~90 %, described in terms of resin finishing liquid described in 1L
The formula of resin finishing liquid are as follows: the Fixapret F-AP resin of 140~180 g, the magnesium chloride of 15~20 g, 50~60 g's
Softening agent, the penetrating agent JFC of 2 g；The sand washing process are as follows: the ready-made clothes after baking is put into rinsing machine, is added again after adding water
Enter float stone, carry out sand washing, wherein the weight ratio of float stone and ready-made clothes is 3~5:1, and sand washing temperature is 30~60 DEG C, bath raio 1:8
~15, the sand washing time is 30~60 minutes.
2. a kind of method for processing after of ready-made non-ironing garment according to claim 1, it is characterised in that: the softening agent
For polyurethane.
3. a kind of method for processing after of ready-made non-ironing garment according to claim 2, it is characterised in that: the softening agent
For the polyurethane RPU-N for holding high the production of Gao Huagong (China) Co., Ltd.
4. a kind of method for processing after of ready-made non-ironing garment according to claim 1, it is characterised in that: described
Fixapret F-AP resin is that the hydroxymethyl-2 dihydroxy-ethylene urea class of the modification of high Gao Huagong (China) Co., Ltd production is low
Warm crosslinked resin.
5. a kind of method for processing after of ready-made non-ironing garment according to claim 1, it is characterised in that: the float stone is
Irregular blocky, partial size is less than 3 cm.
6. a kind of method for processing after of ready-made non-ironing garment according to claim 1, it is characterised in that: the float stone is
Turkey's white float stone.
7. a kind of method for processing after of ready-made non-ironing garment according to claim 1, it is characterised in that: the preliminary drying
Afterwards, fabric is 40~50 % containing damp rate.
8. a kind of method for processing after of ready-made non-ironing garment according to claim 1, it is characterised in that: the fabric is
English props up 60/2,80/2,100/2 or 200/4 fabric.