CN107604692A - A kind of terylene Glove suede fabric dyeing and finishing process - Google Patents
A kind of terylene Glove suede fabric dyeing and finishing process Download PDFInfo
- Publication number
- CN107604692A CN107604692A CN201710612803.6A CN201710612803A CN107604692A CN 107604692 A CN107604692 A CN 107604692A CN 201710612803 A CN201710612803 A CN 201710612803A CN 107604692 A CN107604692 A CN 107604692A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- agent
- fabric
- terylene
- sanding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of terylene Glove suede fabric dyeing and finishing process, its processing step includes：--- alkali fibrillation --- rinse dehydration --- preboarding --- sanding --- dyeing --- reduction cleaning --- finished product setting --- secondary sanding that fabric is selected.The dyeing is dyed using HTHP overflow machine, and dyeing recipe is：Disperse dyes：1 30g/L, Disperse Leveler：Anti-creasing agent in 1g/L, bath：2g/L, metal block agent：0.5g/L, bath raio 1:10.The present invention solves the problems such as common uneven dyeing of superfine fibre, dyeing defect；With gas permeability soft, that drapability is good, stability is strong, good, pest control and anticorrosion corrosion.
Description
Technical field
The present invention relates to printing technology field, and in particular to a kind of terylene Glove suede fabric dyeing and finishing process.
Background technology
The raw material of dacron suede fabric is super fine polyester, and because superfine fibre density is small, pulp freeness is big, colouring
Comparatively fast, it is uneven to easily cause dyeing, produces the defect such as poor reproducibility and dyeing defect.Surface area is big simultaneously, and dyestuff is than equal colors
Conventional fibre is higher by several times, and every fastness has declined than conventional fibre, and drapability is poor, and flexibility is poor.
The content of the invention
For above-mentioned deficiency, the present invention provides a kind of terylene Glove suede fabric dyeing and finishing process.
To achieve the above object, the technical solution adopted by the present invention is：
A kind of terylene Glove suede fabric dyeing and finishing process, its processing step include：Fabric selects --- alkali fibrillation --- washing
Dehydration --- preboarding --- sanding --- dyeing --- reduction cleaning --- finished product setting --- secondary sanding.
Specifically include：
(1) fabric is selected：Warp-wise 200D chamois leather fabrics, warp-wise sea island filament：It is 6 to twist the twist, broadwise dacron thread, density：
13*5*28, yarn count：105D*200D.
(2) alkali fibrillation：
Prescription：NaO H：16~20g/L, anti wrinkling agent PLA4 in bath：1g/L, chelate soaping agent：2g/L, bath raio 1：12.
Technique：40 DEG C of chargings, 130 DEG C are warming up to 1 DEG C/min speed, 50~60min is incubated, is cooled to 2 DEG C/min
70 DEG C, overflow washing.
(3) rinse dehydration：In washing plus proper amount of acetic acid neutralizes, and cloth cover pH value is reached 6-7.
(4) preboarding：Preboarding temperature is 150~160 DEG C, speed 30-50m/min.
(5) sanding.
(6) dye：Dyed using HTHP overflow machine, dyeing recipe is：Disperse dyes：1-30g/L, scattered level dyeing
Agent：Anti-creasing agent in 1g/L, bath：2g/L, metal block agent：0.5g/L, bath raio 1:10；Dyeing flow：With 98% ice at 40 DEG C
For vinegar acid for adjusting pH value to 5, first adding assistant injects charging bucket by the dyestuff that dissolving is stirred after fabric operating 10min in machine, dilute
Release and slowly inject, 135 DEG C of insulation 50min are warming up to 1 DEG C/min, are then cooled to 80 DEG C with 0.5 DEG C/min.
(7) reduction cleaning：With the washing lotion reduction treatment 20min containing soda ash 0.75%, sodium hydrosulfite 0.75%, cold water overflow water
Wash to 60 DEG C, exclude raffinate, then washed with soaping agent 105, untill water is clear.
(8) finished product shapes：Whole cloth pads silicone softening agent, and setting is dried at a temperature of 150 DEG C.
(9) secondary sanding.
It is an advantage of the invention that：The present invention solves the problems such as common uneven dyeing of superfine fibre, dyeing defect；With feel
Softness, the gas permeability that drapability is good, stability is strong, good, pest control and anticorrosion corrosion.
Embodiment
Embodiment：
A kind of terylene Glove suede fabric dyeing and finishing process, its processing step include：
(1) fabric is selected：Warp-wise 200D chamois leather fabrics, warp-wise sea island filament：It is 6 to twist the twist, broadwise dacron thread, density：
13*5*28, yarn count：105D*200D.
(2) alkali fibrillation：
Prescription：NaO H：20g/L, anti wrinkling agent PLA4 in bath：1g/L, chelate soaping agent：2g/L, bath raio 1：12.
Technique：40 DEG C of chargings, 130 DEG C are warming up to 1 DEG C/min speed, 50min is incubated, 70 DEG C is cooled to 2 DEG C/min,
Overflow is washed.
(10) rinse dehydration：In washing plus proper amount of acetic acid neutralizes, and cloth cover pH value is reached 6.
(11) preboarding：Preboarding temperature is 160 DEG C, speed 30m/min.
(12) sanding.
(13) dye：Dyed using HTHP overflow machine, dyeing recipe is：Disperse dyes：10g/L, Disperse Leveler：
Anti-creasing agent in 1g/L, bath：2g/L, metal block agent：0.5g/L, bath raio 1:10；Dyeing flow：With 98% glacial acetic acid at 40 DEG C
PH value is adjusted to 5, for first adding assistant by will dissolve the dyestuff injection charging bucket being stirred after fabric operating 10min in machine, dilution is slow
Slow injection, 135 DEG C of insulation 50min are warming up to 1 DEG C/min, are then cooled to 80 DEG C with 0.5 DEG C/min.
(14) reduction cleaning：With the washing lotion reduction treatment 20min containing soda ash 0.75%, sodium hydrosulfite 0.75%, cold water overflow
Wash to 60 DEG C, exclude raffinate, then washed with soaping agent 105, untill water is clear.
(15) finished product shapes：Whole cloth pads silicone softening agent, and setting is dried at a temperature of 150 DEG C.
(16) secondary sanding.
Described above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (1)
1. a kind of terylene Glove suede fabric dyeing and finishing process, it is characterised in that processing step includes：
(1) fabric is selected：Warp-wise 200D chamois leather fabrics, warp-wise sea island filament：It is 6 to twist the twist, broadwise dacron thread, density：13*5*
28, yarn count：105D*200D；
(2) alkali fibrillation：
Prescription：NaO H：16~20g/L, anti wrinkling agent PLA4 in bath：1g/L, chelate soaping agent：2g/L, bath raio 1：12；
Technique：40 DEG C of chargings, 130 DEG C are warming up to 1 DEG C/min speed, 50~60min is incubated, 70 DEG C is cooled to 2 DEG C/min,
Overflow is washed；
(3) rinse dehydration：In washing plus proper amount of acetic acid neutralizes, and cloth cover pH value is reached 6-7；
(4) preboarding：Preboarding temperature is 150~160 DEG C, speed 30-50m/min；
(5) sanding；
(6) dye：Dyed using HTHP overflow machine, dyeing recipe is：Disperse dyes：1-30g/L, Disperse Leveler：1g/
L, anti-creasing agent in bathing：2g/L, metal block agent：0.5g/L, bath raio 1:10；Dyeing flow：Adjusted at 40 DEG C with 98% glacial acetic acid
PH value is saved to 5, first adding assistant will dissolve the dyestuff injection charging bucket being stirred by after fabric operating 10min in machine, and dilution is slowly
Injection, 135 DEG C of insulation 50min are warming up to 1 DEG C/min, are then cooled to 80 DEG C with 0.5 DEG C/min；
(7) reduction cleaning：With the washing lotion reduction treatment 20min containing soda ash 0.75%, sodium hydrosulfite 0.75%, cold water overflow washing is arrived
60 DEG C, raffinate is excluded, then is washed with soaping agent 105, untill water is clear；
(8) finished product shapes：Whole cloth pads silicone softening agent, and setting is dried at a temperature of 150 DEG C；
(9) secondary sanding.