CN110184059A - 钼酸锂钇掺杂镝绿色发光粉及其制备方法 - Google Patents

钼酸锂钇掺杂镝绿色发光粉及其制备方法 Download PDF

Info

Publication number
CN110184059A
CN110184059A CN201910560052.7A CN201910560052A CN110184059A CN 110184059 A CN110184059 A CN 110184059A CN 201910560052 A CN201910560052 A CN 201910560052A CN 110184059 A CN110184059 A CN 110184059A
Authority
CN
China
Prior art keywords
moo
powder
luminescent powder
green emitting
dysprosium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910560052.7A
Other languages
English (en)
Inventor
巴学巍
谢斐
孙博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qiqihar University
Original Assignee
Qiqihar University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qiqihar University filed Critical Qiqihar University
Priority to CN201910560052.7A priority Critical patent/CN110184059A/zh
Publication of CN110184059A publication Critical patent/CN110184059A/zh
Pending legal-status Critical Current

Abstract

采用固相反应法制备Li7Y3(1‑x)(MoO4)8：Dyax发光粉的方法，涉及一种近紫外或蓝光激发的掺杂镝的钼酸锂钇绿色发光粉。采用Li2CO3、Y2Ox、MoO3和Dy2O3为原料，按照称量、配料、研磨混合、煅烧、冷却、二次研磨等工艺过程，制备发光粉。其中，x取值范围是0.001～0.6。本发明制备环节少、周期短，热处理温度较低，合成成本低，发光性能好，应用前景广泛。

Description

钼酸锂钇掺杂镝绿色发光粉及其制备方法
技术领域
本发明涉及一种近紫外或蓝光激发的掺杂镝的钼酸锂钇绿色发光粉，属于显示和照明荧光粉技术领域。
背景技术
近年来，白光发光二极管(WLED)因其优异的发光特性、良好的稳定性、节能、发光效率高、环境友好、成本低而引起了人们的广泛关注和研究。白光LED既可以通过蓝光芯片与黄光荧光粉结合的方式获得，也可以通过用蓝光或紫外光激发红、蓝、绿等三种颜色的荧光粉相结合来实现。
稀土镝离子(Dy3+)在紫外线和蓝光的激发下会产生一系列光发射，例如：基于4F9/2-6H15/2跃迁而在450～500nm区域具有蓝光发射，基于4F9/2-6H13/2跃迁而在550～600nm区域具有橙色光发射。将镝离子掺杂到不同的发光基质材料中，由于化学成分和晶体结构的差异，导致上述蓝光和橙色光的相对强度发生改变。在一些材料中，镝离子由于蓝光与橙色光强度相近，引起宏观上白光发光特征。而在另一些材料中，蓝光的强度低于橙色光，则引起宏观上的绿光发光特征。因此，镝离子掺杂的化合物不仅可以为白光发光二极管提供白光发光粉，也可以提供绿光发光粉。
近年来，以钼酸盐为基质的白光LED用发光粉受到了业内的关注。通过掺杂不同离子，或者调整组成元素的种类或比例，可以获得发光效率高、具有不同发光波长的新型发光粉。
发明内容
针对现有白光LED技术市场上缺少绿光发射的发光粉的问题，本发明提供一种近紫外或蓝光激发的掺杂镝的钼酸锂钇绿色发光粉。本发明通过以下技术方案实现。
一种近紫外或蓝光激发的掺杂镝的钼酸锂钇绿色发光粉，所述的该绿色发光粉的表达式为Li7Y3(1-x)(MoO4)8：Dy3x，其中x表示0.001～0.6的摩尔值。
所述的绿色发光粉，由Li2CO3、Y2O3、MoO3和Dy2O3原料按照物质的量7∶3(1-x)∶8∶3x比例制备，其中x可以在0.001～0.6范围变化。
上述近紫外或蓝光激发的掺杂镝的钼酸锂钇绿色发光粉的制备方法，其具体步骤如下：
采用固相反应法制备Li7Y3(1-x)(MoO1)8：Dy3、发光粉。首先，将Li2CO3、Y2O3、MoO3和Dy2O3原料按照物质的量7∶3(1-x)∶8∶3x比例称量，然后充分研磨混合，获得原料混合物。再将原料混合物在空气气氛、温度为550～800℃、煅烧时间为0.5～16小时的条件下热处理。最后经过自然冷却，再经过二次研磨，获得近紫外或蓝光激发的掺杂镝的钼酸锂钇绿光发射发光粉。
本发明的有益效果：该发光粉在近紫外到蓝光波长范围能够被有效激发而产生绿光发射。其次，该发光粉具有良好的化学稳定性和热稳定性。再次，该发光粉制备环节少、周期短，热处理温度较低，合成成本低。
附图说明
图1是本发明实施例1所制备的绿色发光粉的激发光谱。
图2是本发明实施例1所制备的绿色发光粉的发射光谱。
图3是本发明实施例1所制备的绿色发光粉的X射线衍射图谱。
具体实施方式
下面结合附图和具体实施方式，对本发明作进一步说明。
实施例1
该近紫外或蓝光激发的掺杂镝的钼酸锂钇绿色发光粉，所述该发光粉的化学表达式为Li7Y3(1-x)(MoO4)8：Dy3x，其中x表示0.16的物质的量。该近紫外或蓝光激发的掺杂镝的钼酸锂钇绿色发光粉的激发光谱和发射光谱如图1和2所示，X射线衍射图谱如图3所示。该发光粉的制备过程如下：称取0.3173克碳酸锂、0.3491克氧化钇、1.4128克氧化钼和0.1098克氧化镝，依次将四种原料倒入玛瑙研钵，用玛瑙材质的研磨棒均匀混合原料45分钟，得到均化的原料混合物。然后，用刚玉坩埚做容器，装载均化的原料混合物，一起移入箱式电阻炉中，进行煅烧处理。煅烧温度为600℃，煅烧时间为8小时，煅烧气氛为空气。待保温结束，切断电源，自然冷却至室温。所合成的块状发光粉在玛瑙研钵中进行破碎和研磨，获得粒径细小的发光粉。

Claims (4)

1.采用固相反应法制备Li7Y3(1-x)(MoO4)8：Dy3x发光粉的方法，其特征在于，以Li2CO3、Y2O3、MoO3和Dy2O3为原料，按照称量、配料、研磨混合、煅烧、冷却、二次研磨等工艺过程，制备发光粉。
2.根据权利要求书1所述的Li7Y3(1-x)(MoO4)8：Dy3x发光粉的方法，其特征在于，Dy3+离子是激活剂，Li7Y3(MoO4)8是基质。
3.根据权利要求书1所述的Li7Y3(1-x)(MoO4)8：Dy3x发光粉的方法，其特征在于，Dy3+离子的掺杂量x取值范围是0.001～0.6。
4.根据权利要求书1所述的Li7Y3(1-x)(MoO4)8：Dy3x发光粉的方法，其特征在于，煅烧温度范围为550～800℃、煅烧时间范围为0.5～16小时，煅烧气氛为空气。
CN201910560052.7A 2019-06-19 2019-06-19 钼酸锂钇掺杂镝绿色发光粉及其制备方法 Pending CN110184059A (zh)