CN110157332B - 一种聚硅氮烷涂层材料、制备方法和应用方法 - Google Patents
一种聚硅氮烷涂层材料、制备方法和应用方法 Download PDFInfo
- Publication number
- CN110157332B CN110157332B CN201910434076.8A CN201910434076A CN110157332B CN 110157332 B CN110157332 B CN 110157332B CN 201910434076 A CN201910434076 A CN 201910434076A CN 110157332 B CN110157332 B CN 110157332B
- Authority
- CN
- China
- Prior art keywords
- polysilazane
- solution
- coating material
- initiator
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
组别 | 接触角(度)酒精处理区 | 接触角(度)酒精未处理区 |
实施例1 | 61 | 62 |
实施例2 | 63 | 63 |
实施例3 | 61 | 60 |
实施例4 | 62 | 60 |
实施例5 | 61 | 62 |
实施例6 | 62 | 61 |
实施例7 | 61 | 59 |
对比例1 | 72 | 64 |
对比例2 | 71 | 63 |
Claims (6)