CN110079236A - 一种装修防护地垫 - Google Patents
一种装修防护地垫 Download PDFInfo
- Publication number
- CN110079236A CN110079236A CN201910451884.5A CN201910451884A CN110079236A CN 110079236 A CN110079236 A CN 110079236A CN 201910451884 A CN201910451884 A CN 201910451884A CN 110079236 A CN110079236 A CN 110079236A
- Authority
- CN
- China
- Prior art keywords
- layer
- film
- polyethylene
- polyethylene foam
- blow moulding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种装修防护地垫,由上至下依次包括如下结构层:第一层:流延法聚乙烯CPE膜,第二层:印刷层,第三层:淋膜PE,第四层:聚乙烯发泡棉,第五层:聚乙烯气泡膜,第六层:吹塑法聚乙烯PE膜,第七层:水性不干胶,第八层:吹塑法聚乙烯离型PE膜;或第一层:流延法聚乙烯CPE膜,第二层:印刷层,第三层:聚乙烯气泡膜,第四层:聚乙烯发泡棉,第五层:淋膜PE,第六层:吹塑法聚乙烯PE膜,第七层:水性不干胶,第八层:吹塑法聚乙烯离型PE膜。本发明重量轻,保护效果好,防滑性好,绿色环保。
Description
技术领域
本发明涉及地垫生产技术领域,特别涉及一种装修防护地垫。
背景技术
装修通常都会先铺设地面,所以在地面铺设后再次施工就需要对施工过的地面进行保护,以避免后续施工时对前面施工好的地面造成破坏,现有技术中,对施工过的地面进行保护,一般采用地板装修保护膜,地板装修保护膜的厚度较小,不防滑,易破损,在装修过程中重物的跌落、设备放置均易对地面损伤而无法做到有效的保护,保护效果差,且材料不环保。常规的地板装修保护膜为了防止移动,通常还需要粘贴胶带固定,不环保的同时,还造成后续清理困难。
CN208122350U的实用新型专利公开了一种装修用地面防护垫,包括凹型外板,所述的凹型外板开口处连接设有耐磨硬板,所述的凹型外板和耐磨硬板之间填充橡胶球,所述的凹型外板包括底板和壁板,所述的壁板外侧均设有T型扣,相邻两个T型扣之间设有T型槽,所述的T型槽内壁设有第一橡胶垫,所述的耐磨硬板上设有凹槽,所述的凹槽内设有防滑条,所述的防滑条上嵌有第二橡胶垫,所述的第二橡胶垫上连接设有弹簧柱,所述的弹簧柱另一端连接防滑条)底部,所述的第二橡胶垫自然状态与耐磨硬板表面水平。该地面防护垫存在着结构复杂、成本高、重量大,不适合大面积防护,不易运输,不环保等问题。
本产品针对目前市场所有在售的地板装修保护膜,保护效果差,不防滑,不环保的缺陷而进行开发的一款新型的装修保护材料。
发明内容
本发明的目的在于解决现有地板装修保护膜存在的保护效果差、不防滑、不环保的缺陷,提供一种装修防护地垫,重量轻,保护效果好,防滑性好,绿色环保。
本发明解决其技术问题所采用的技术方案是:
一种装修防护地垫,由上至下依次包括如下结构层:
第一层:流延法聚乙烯CPE膜
第二层:印刷层
第三层:淋膜PE
第四层:聚乙烯发泡棉
第五层:聚乙烯气泡膜
第六层:吹塑法聚乙烯PE膜
第七层:水性不干胶
第八层:吹塑法聚乙烯离型PE膜;
或由上至下依次包括如下结构层:
第一层:流延法聚乙烯CPE膜
第二层:印刷层
第三层:聚乙烯气泡膜
第四层:聚乙烯发泡棉
第五层:淋膜PE
第六层:吹塑法聚乙烯PE膜
第七层:水性不干胶
第八层:吹塑法聚乙烯离型PE膜。
第一层:流延法聚乙烯CPE膜,第二层:印刷层,第三层:淋膜PE,第四层:聚乙烯发泡棉,第五层:聚乙烯气泡膜,第六层:吹塑法聚乙烯PE膜,第七层:水性不干胶,第八层:吹塑法聚乙烯离型PE膜;这个结构,适应与一般较为光滑的地面,如釉面地砖、大理石地面、等表面光滑平整的装修材料。水性不干胶只需较弱粘性即可。并便于在装修工作完工后,轻易的撤除本发明。吹塑法聚乙烯PE膜是水性不干胶载体,并起到与气泡膜的粘合的功能,吹塑法聚乙烯离型PE膜保护不干胶在使用之前不受到污染。水性不干胶,环保无异味,不残留。
第一层:流延法聚乙烯CPE膜,第二层:印刷层,第三层:聚乙烯气泡膜,第四层:聚乙烯发泡棉,第五层:淋膜PE,第六层:吹塑法聚乙烯PE膜,第七层:水性不干胶,第八层:吹塑法聚乙烯离型PE膜。该结构与结构主要差异在于聚乙烯气泡膜与聚乙烯发泡棉对换,因为,聚乙烯发泡棉的表面较气泡膜更为平整,平面收缩力更小,因此,可以涂布强粘力的水性不干胶,使防护垫具有更强的粘结力。该结构产品可应用在,表面较为粗糙的装修建材,如防滑瓷砖、磨砂地板、哑光实木地板、表面有压花花纹的原木、仿木等建材。
作为方案延伸,第二层的印刷层可以省略,是否存在印刷层均不影响本发明功能的实现,均属于本申请的保护范围,其结构如:第一层:流延法聚乙烯CPE膜,第二层:聚乙烯气泡膜,第三层:聚乙烯发泡棉,第四层:淋膜PE,第五层:吹塑法聚乙烯PE膜,第六层:水性不干胶,第七层:吹塑法聚乙烯离型PE膜;若有设备直接加工水性不干胶,则第六层的吹塑法聚乙烯PE膜可以省略,这个不影响本发明功能的实现,是否存在吹塑法聚乙烯PE膜均属于本申请的保护范围,其结构如:第一层:流延法聚乙烯CPE膜,第二层:印刷层,第三层:淋膜PE,第四层:聚乙烯发泡棉,第五层:聚乙烯气泡膜,第六层:水性不干胶,第七层:吹塑法聚乙烯离型PE膜。
作为优选,所述聚乙烯气泡膜为单层气泡的聚乙烯气泡膜,厚度为2-5mm。单层气泡膜的结构为上下两层为PE膜,在两层PE膜之间均匀分布圆柱形气泡。
作为优选,所述聚乙烯气泡膜为双层气泡的膜聚乙烯气泡膜,厚度为4-10mm。双层气泡膜为两个单层气泡膜热贴合复合而成。
作为优选,所述聚乙烯气泡膜的气泡为圆柱形气泡。单层的气泡高度约为2-5mm。2-5mm高的圆柱形气泡,强力抗震。
作为优选,制备方法为:
(1)将流延法聚乙烯CPE膜进行印刷形成复合有印刷层的流延法聚乙烯CPE膜,然后通过淋膜PE将复合有印刷层的流延法聚乙烯CPE膜与聚乙烯发泡棉复合形成半成品A;
(2)将吹塑法聚乙烯PE膜、水性不干胶及吹塑法聚乙烯离型PE膜形成的复合膜与聚乙烯气泡膜复合形成半成品B;
(3)将半成品A和半成品B在热风作用下热复合。
作为优选,制备方法为:
(1)将流延法聚乙烯CPE膜进行印刷,然后与聚乙烯气泡膜复合形成半成品A;
(2)将吹塑法聚乙烯PE膜、水性不干胶及吹塑法聚乙烯离型PE膜形成的复合膜通过淋膜PE与聚乙烯发泡棉复合形成半成品B;
(3)将半成品A和半成品B在热风作用下热复合。
作为优选,所述热风温度为250-300℃。
作为优选,流延法聚乙烯CPE膜表面具有3D压花纹。
本发明的有益效果是:
本发明将多种不同性能的基材进行组合,充分利用聚乙烯发泡棉和气泡膜的抗压特性,两者优势叠加,使防护性能更出色。
本发明正面采用流延CPE薄膜,经宽幅多色组的凹版彩印,使产品更具装饰美感。
本发明表面进行3D压花处理,即使在表层有水渍、油漆、涂料的情况下,也能有效的防止人员滑倒。
本发明在背面设计环保的水性不干胶涂层,不干胶层与木地板、强化地板、地砖、大理石等表面装饰材料都能有效的粘接,防止装修登高设施因保护垫的滑动而造成安全事故的发生。并且因为使用了环保的水性不干胶,使产品没有异味,不干胶层在被粘物上没有胶体残留,避免了二次污染,大大减轻了装修完成后的清洁工作强度。
本发明使用宽幅设备生产,可以裁切2米以内任意宽度的订制。
本发明所有原材料均符合食品包装要求,无毒无异味。
本发明所有材料均为聚乙烯,符合环保要求,可以全部回收利用。
本发明以卷材形式出售,若以1米宽50米长的一卷为例,它的重量在12KG左右,直径在560mm左右,会非常方便的进行运输和利用电梯运送入户。
附图说明
图1是本发明的一种结构示意图。
图2是本发明的另一种结构示意图。
图中:1、流延法聚乙烯CPE膜,2、印刷层,3、淋膜PE,4、聚乙烯发泡棉,5、聚乙烯气泡膜,6、吹塑法聚乙烯PE膜,7、水性不干胶,8、吹塑法聚乙烯离型PE膜。
具体实施方式
下面通过具体实施例,对本发明的技术方案作进一步的具体说明。
本发明中,若非特指,所采用的原料和设备等均可从市场购得或是本领域常用的。下述实施例中的方法,如无特别说明,均为本领域的常规方法。
A:流延法聚乙烯CPE膜,本公司使用汕头市新中阳机械厂的CM-T90/135/90-2400三层共挤流延机组生产该薄膜,树脂采用流延级原料,例如陶氏2036、4404等牌号,也可采用市售产品;
B:淋膜PE,淋膜树脂采用淋膜级树脂,如韩国955、国产燕山石化1071c等牌号,淋膜机组为常州腾诚机械制造有限公司生产的SJPM-2300复合淋膜机;
C:聚乙烯发泡棉(EPE)采用LDPE树脂,使用重庆捷成塑胶有限公司的JC-F180EPE生产线生产该PE发泡棉;发泡棉发泡倍率25-30倍,具有抗震、保温、轻质的特点,也可采用市售产品;
D:带离型膜的PE不干胶薄膜,市售。
实施例1:
如图1所示的一种装修防护地垫,由上至下依次包括如下结构层:
第一层:流延法聚乙烯CPE膜1
第二层:印刷层2
第三层:淋膜PE3
第四层:聚乙烯发泡棉4
第五层:聚乙烯气泡膜5
第六层:吹塑法聚乙烯PE膜6
第七层:水性不干胶7
第八层:吹塑法聚乙烯离型PE膜8;
所述聚乙烯气泡膜为单层气泡的聚乙烯气泡膜,气泡为圆柱形气泡。
实施例2:
本实施例与实施例1不同之处在于:聚乙烯气泡膜为双层气泡的膜聚乙烯气泡膜。
实施例3:
如图2所示的一种装修防护地垫,由上至下依次包括如下结构层:
第一层:流延法聚乙烯CPE膜1
第二层:印刷层2
第三层:聚乙烯气泡膜5
第四层:聚乙烯发泡棉4
第五层:淋膜PE3
第六层:吹塑法聚乙烯PE膜6
第七层:水性不干胶7
第八层:吹塑法聚乙烯离型PE膜8;
所述聚乙烯气泡膜为单层气泡的聚乙烯气泡膜,气泡为圆柱形气泡。
实施例4:
本实施例与实施例3不同之处在于:聚乙烯气泡膜为双层气泡的膜聚乙烯气泡膜。
本发明各层的厚度可以采用如下设置:流延法聚乙烯CPE膜0.02-0.05mm,印刷层0.01-0.02mm,聚乙烯气泡膜2-5mm或4-10mm,聚乙烯发泡棉3-5mm,淋膜PE0.02-0.03mm,吹塑法聚乙烯PE膜0.04-0.05mm,水性不干胶0.015-0.02mm,吹塑法聚乙烯离型PE膜0.02-0.03mm。
实施例1-2结构的制备方法为:
(1)在流延法聚乙烯CPE膜背面印刷得到复合有印刷层的流延法聚乙烯CPE膜,然后通过淋膜机将淋膜PE淋于复合有印刷层的流延法聚乙烯CPE膜与聚乙烯发泡棉之间,在复合钢辊作用下复合形成半成品A;复合钢辊表面具有3D花纹,复合后,在材料的表面压出各种花纹,起到防滑的效果。
(2)将吹塑法聚乙烯PE膜、水性不干胶及吹塑法聚乙烯离型PE膜形成的复合膜(带离型膜的PE不干胶薄膜,市售)与聚乙烯气泡膜在复合钢辊作用下复合形成半成品B。聚乙烯气泡膜的表层为淋膜加工而成,因此在聚乙烯气泡膜加工时与吹塑法聚乙烯PE膜复合能起到粘结作用,聚乙烯气泡膜的加工为常规技术。
(3)将半成品A和半成品B在250℃热风作用下热复合得产品。
实施例3-4结构的制备方法为:
(1)在流延法聚乙烯CPE膜背面印刷得到复合有印刷层的流延法聚乙烯CPE膜,然后在复合钢辊作用下与聚乙烯气泡膜复合形成半成品A。
(2)通过淋膜机将淋膜PE淋于吹塑法聚乙烯PE膜、水性不干胶及吹塑法聚乙烯离型PE膜形成的复合膜(带离型膜的PE不干胶薄膜,市售)与聚乙烯发泡棉之间,在复合钢辊作用下复合形成半成品B。
(3)将半成品A和半成品B在300℃热风作用下热复合。
应用
本产品可以根据客户要求,订制宽幅,并以卷材的形式出售。
本产品可以在装修过程中,使用在地板、地砖、大理石、家具、门窗、等需要防护的材料上。
本产品使用时,需先清洁被保护物表面,后将本产品内层PE离型保护膜揭去,滚动本产品至需要尺寸并裁断,此时本产品已牢固黏在被保护物上。在本产品上安置装修设备、和摆放装修材料均不会造成对被保护物的的损坏。最后,装修完成后揭去本产品即可。
本产品在应用时,防护垫之间的不需要像目前市售的产品那样用胶带进行粘接固定,因此使用时更方便快捷。
本发明的功能原理
1:更好的抗压、耐磨损性能,因为聚乙烯发泡棉,是高强度聚乙烯采用物理发泡原理产生无数个独立气泡组成,具有隔水防潮、防震、隔音、保温、可塑性能佳、韧性强、循环再造、环保、抗撞力强等诸多优点,亦具有很好的抗化学性能。与聚乙烯发泡棉结合的气泡膜,是以高压聚乙烯为主要原料,经200℃左右高温挤出吸塑成气泡的产品。是一种质地轻、透明性好、无毒、无味的新型塑料包装材料,可对产品起防湿、缓冲、保温等作用。聚乙烯发泡棉由无数个封闭的小气泡组成,对冲击力可以横向散发,但它的垂直抗穿刺性较差,而且聚乙烯发泡棉的抗撕裂强度低,不能承受横向的力量冲击,气泡膜的圆柱形气泡可以承受较大的垂直冲击力,气泡膜上下两层的PE能提供较大的横向撕裂强度,因此这两种材料的强强联合,使得本产品具备更高的防护性能。聚乙烯发泡棉通过弹性形变抗冲击性能好,聚乙烯气泡膜通过气泡缓冲抗冲击,且横向抗拉伸性能强,聚乙烯气泡膜能弥补聚乙烯发泡棉在受到斜向力时容易被撕裂的缺陷,聚乙烯气泡膜抗撕裂强度高。
2:独有的防滑性,市售的装修保护垫没有或是不具备良好的防滑功能,本产品正面及反面都具备防滑性能。产品正面进行了3D纹路的压花处理,背面有不干胶涂层,胶层与被保护物有效粘接,粘结力可达100g/in,使本产品能牢牢地固定在被保护物上。
性能检测:
。
制成成品后物性:
。
以上所述的实施例只是本发明的一种较佳的方案,并非对本发明作任何形式上的限制,在不超出权利要求所记载的技术方案的前提下还有其它的变体及改型。
Claims (8)
1.一种装修防护地垫,其特征在于,由上至下依次包括如下结构层:
第一层:流延法聚乙烯CPE膜
第二层:印刷层
第三层:淋膜PE
第四层:聚乙烯发泡棉
第五层:聚乙烯气泡膜
第六层:吹塑法聚乙烯PE膜
第七层:水性不干胶
第八层:吹塑法聚乙烯离型PE膜
或由上至下依次包括如下结构层:
第一层:流延法聚乙烯CPE膜
第二层:印刷层
第三层:聚乙烯气泡膜
第四层:聚乙烯发泡棉
第五层:淋膜PE
第六层:吹塑法聚乙烯PE膜
第七层:水性不干胶
第八层:吹塑法聚乙烯离型PE膜。
2.根据权利要求1所述的一种装修防护地垫,其特征在于:所述聚乙烯气泡膜为单层气泡的聚乙烯气泡膜,厚度为2-5mm。
3.根据权利要求1所述的一种装修防护地垫,其特征在于:所述聚乙烯气泡膜为双层气泡的膜聚乙烯气泡膜,厚度为4-10mm。
4.根据权利要求2或3所述的一种装修防护地垫,其特征在于:所述聚乙烯气泡膜的气泡为圆柱形气泡。
5.根据权利要求1所述的一种装修防护地垫,其特征在于,制备方法为:
(1)将流延法聚乙烯CPE膜进行印刷形成复合有印刷层的流延法聚乙烯CPE膜,然后通过淋膜PE将复合有印刷层的流延法聚乙烯CPE膜与聚乙烯发泡棉复合形成半成品A;
(2)将吹塑法聚乙烯PE膜、水性不干胶及吹塑法聚乙烯离型PE膜形成的复合膜与聚乙烯气泡膜复合形成半成品B;
(3)将半成品A和半成品B在热风作用下热复合。
6.根据权利要求1所述的一种装修防护地垫,其特征在于,制备方法为:
(1)将流延法聚乙烯CPE膜进行印刷,然后与聚乙烯气泡膜复合形成半成品A;
(2)将吹塑法聚乙烯PE膜、水性不干胶及吹塑法聚乙烯离型PE膜形成的复合膜通过淋膜PE与聚乙烯发泡棉复合形成半成品B;
(3)将半成品A和半成品B在热风作用下热复合。
7.根据权利要求5或6所述的一种装修防护地垫,其特征在于:所述热风温度为250-300℃。
8.根据权利要求1所述的一种装修防护地垫,其特征在于:流延法聚乙烯CPE膜表面具有3D压花纹。