CN110051092A - Ancient method gold production method - Google Patents
Ancient method gold production method Download PDFInfo
- Publication number
- CN110051092A CN110051092A CN201910301935.6A CN201910301935A CN110051092A CN 110051092 A CN110051092 A CN 110051092A CN 201910301935 A CN201910301935 A CN 201910301935A CN 110051092 A CN110051092 A CN 110051092A
- Authority
- CN
- China
- Prior art keywords
- gold
- jewelry
- raw material
- molding
- gold jewelry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ancient method gold production methods, comprising the following steps: S1: raw material is chosen: the gold raw material pure from regular shop buying quality；S2: molding is beaten in melting: gold raw material described in S1 is put into melting in golden bowl, and melt processed is carried out to it using Multifunctional welder, after gold raw material is all fused into Jinsui River, stop fusing soldering welder operation, after equal Jinsui River cooling a period of time, when forming round knob-like, it is quickly clipped in forging stage using pliers and beat repeatedly and uniformly with hammer.The present invention heats gold raw material with ancient method technique and beats support gold jewelry repeatedly, so that gold jewelry is more densely cross-linked, quality is more hale and more hearty, it is not easy to deform, and after gold jewelry molding, by carrying out frosted processing and coloring treatment to its surface layer, gold jewelry can not only be made to be not easy to leave fingerprint and sweat print, and also improve the wearability and corrosion resistance of gold jewelry.
Description
Technical field
The present invention relates to gold jewelry processing technique field more particularly to a kind of ancient method gold production methods.
Background technique
Gold jewelry refers to the jewellery made using gold as primary raw material, and proof gold and karat gold two can be divided into from its gold content
Class, the gold content of proof gold jewellery reach as high as 99.99% 99% or more, and proof gold jewellery quality is softer, and tooth has stung print, are easy
Bending, golden yellow color, pure, soft, feel is heavy, there is heavy feeling, and gold jewelry can be with red, white, black any one
Kind color blends.Ardent atmosphere is formed with red series of combination, is first choice of young, optimistic women, especially in various happinesses
The occasion of celebrating is praised highly.Form mysterious, noble style with black series of combination, for it is cold complete, arrogance women likes, usually exist
Occur in dinner party, make us looking over so as to check unforgettable, combines to form pure aesthetic feeling with white series.
It in the prior art, is mostly formed using machine batch machining for the production method of gold jewelry, although maintaining
The flexibility of gold jewelry, but it is internal but not closely knit enough, and especially hollow gold jewelry is very easy to deform, and intolerant to
It is dirty, not wear-resisting, it easily leaves fingerprint, sweat print and generates scratch, propose a kind of ancient method gold production method thus.
Summary of the invention
Technical problems based on background technology, the invention proposes ancient method gold production methods.
Gu method gold production method proposed by the present invention, comprising the following steps:
S1: raw material is chosen: the gold raw material pure from regular shop buying quality；
S2: molding is beaten in melting: gold raw material described in S1 being put into melting in golden bowl, and uses multi-functional melting welding
Machine carries out melt processed to it, after gold raw material is all fused into Jinsui River, stops fusing soldering welder operation, waits Jinsui River one section cooling
After time, when forming round knob-like, it is quickly clipped to using pliers in forging stage and carried out repeatedly and uniformly with hammer
Beat, so that it is beaten rectangularity gold bullion A；
S3: reverse mould molding: the A of rectangle gold bullion described in S2 is put on reverse mould iron and is beaten repeatedly again, is obtained
To molding gold jewelry B；
S4: after the molding gold jewelry B described in the S3 is completely cooling, gold will first deburring, cleaning: be formed using scissors
Flash on jewellery B is cut, and is then carried out grinding process using sander, after polishing, is reused polishing machine and polished
Processing, clears up finally, the molding gold jewelry B after polishing is put into service sink, obtains semi-finished product gold jewelry C；
S5: the production of bronze water: a clean plastic containers are taken, are then successively put into ammonia in proportion into plastic containers
Water, basic copper carbonate, sodium carbonate, hydroquinone and glacial acetic acid after placing 20-24 hours, obtain bronze water D after evenly mixing；
S6: dilution: will be added 3~6 times of clear water in bronze water D described in S5, after evenly mixing, obtain the dilution of bronze water
Liquid E；
S7: coloring treatment: frosted processing is carried out to the C of semi-finished product gold jewelry described in S4 using wire drawing cloth, then will
It is put into bronze water diluent E and carries out immersion treatment, takes out after a period of time, be subsequently placed into service sink carry out it is secondary
Cleaning, removes remaining bronze water diluent E；
S8: dehydration, waxing: the gold jewelry C after coloring treatment described in S7 is put into drying box and is dried
Processing, after taking-up, reuses 3D wax sprayer and carries out waxing processing to it, after waxing, can obtain finished product gold jewelry.
Preferably, in the S2, the model JX3-5 of fusing soldering welder, when carrying out melt processed to gold raw material, bonding machine spray
The injection temperation of rifle should be arranged in 1100~1300 DEG C.
Preferably, it in the S4, after cleaning molding gold jewelry B, also needs to put it into drying box to be dried
Dry-cure, the model 101A-2 of drying box, drying time are 5~8min.
Preferably, in the S5, the dosage of ammonium hydroxide is 150g/L, and the dosage of basic copper carbonate is 250g/L, sodium carbonate
Dosage is 8g/L, and the dosage of hydroquinone is 5g/L, and the dosage of glacial acetic acid is 50g/L, when mixing, is carried out using plastic stir rod
Uniform stirring, mixing time are 3~5min.
Preferably, in the S7, the soaking time of semi-finished product gold jewelry C is 3~5min.
Preferably, it in the S7, needs to wear Acid-proof plastic hand during carrying out coloring treatment to semi-finished product gold jewelry C
Set need to be rinsed with clear water immediately after bronze water diluent E contacts skin.
Preferably, in the S8, the model CPX3000 of 3D wax-polishing machine.
Beneficial effects of the present invention: carrying out heating to gold raw material with ancient method technique and it is first to beat support gold repeatedly
Decorations, so that gold jewelry is more densely cross-linked, quality is more hale and more hearty, it is not easy to deform, and after gold jewelry molding, by its surface layer
Frosted processing and coloring treatment are carried out, gold jewelry can not only be made to be not easy to leave fingerprint and sweat print, and also improve gold head
The wearability and corrosion resistance of decorations.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Embodiment
Ancient method gold production method is proposed in the present embodiment, comprising the following steps:
S1: raw material is chosen: the gold raw material pure from regular shop buying quality；
S2: molding is beaten in melting: gold raw material described in S1 being put into melting in golden bowl, and uses multi-functional melting welding
Machine carries out melt processed to it, after gold raw material is all fused into Jinsui River, stops fusing soldering welder operation, waits Jinsui River one section cooling
After time, when forming round knob-like, it is quickly clipped to using pliers in forging stage and carried out repeatedly and uniformly with hammer
Beat, so that it is beaten rectangularity gold bullion A；
S3: reverse mould molding: the A of rectangle gold bullion described in S2 is put on reverse mould iron and is beaten repeatedly again, is obtained
To molding gold jewelry B；
S4: after the molding gold jewelry B described in the S3 is completely cooling, gold will first deburring, cleaning: be formed using scissors
Flash on jewellery B is cut, and is then carried out grinding process using sander, after polishing, is reused polishing machine and polished
Processing, clears up finally, the molding gold jewelry B after polishing is put into service sink, obtains semi-finished product gold jewelry C；
S5: the production of bronze water: a clean plastic containers are taken, are then successively put into ammonia in proportion into plastic containers
Water, basic copper carbonate, sodium carbonate, hydroquinone and glacial acetic acid after placing 24 hours, obtain bronze water D after evenly mixing；
S6: the clear water that 3 times are added in bronze water D described in S5 dilution: is obtained into bronze water diluent after evenly mixing
E；
S7: coloring treatment: frosted processing is carried out to the C of semi-finished product gold jewelry described in S4 using wire drawing cloth, then will
It is put into bronze water diluent E and carries out immersion treatment, takes out after a period of time, be subsequently placed into service sink carry out it is secondary
Cleaning, removes remaining bronze water diluent E；
S8: dehydration, waxing: the gold jewelry C after coloring treatment described in S7 is put into drying box and is dried
Processing, after taking-up, reuses 3D wax sprayer and carries out waxing processing to it, after waxing, can obtain finished product gold jewelry.
In the present embodiment, in S2, the model JX3-5 of fusing soldering welder, when carrying out melt processed to gold raw material, bonding machine spray
The injection temperation of rifle should be arranged in 1100~1300 DEG C；In S4, after cleaning molding gold jewelry B, also need to put it into
Drying and processing, the model 101A-2 of drying box, drying time 5min are carried out in drying box；In S5, the dosage of ammonium hydroxide is
150g/L, the dosage of basic copper carbonate are 250g/L, and the dosage of sodium carbonate is 8g/L, and the dosage of hydroquinone is 5g/L, ice second
The dosage of acid is 50g/L, when mixing, is uniformly stirred using plastic stir rod, mixing time 5min；In S7, half at
The soaking time of product gold jewelry C is 5min；In S7, need to wear during carrying out coloring treatment to semi-finished product gold jewelry C
Acid-proof plastic gloves need to be rinsed with clear water immediately after bronze water diluent E contacts skin；In S8, the model of 3D wax-polishing machine
CPX3000。
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. ancient method gold production method, which comprises the following steps:
S1: raw material is chosen: the gold raw material pure from regular shop buying quality；
S2: molding is beaten in melting: gold raw material described in S1 being put into melting in golden bowl, and uses Multifunctional welder pair
It carries out melt processed, after gold raw material is all fused into Jinsui River, stops fusing soldering welder operation, waits Jinsui River cooling a period of time
Afterwards, when forming round knob-like, it is quickly clipped in forging stage using pliers and strike repeatedly and uniformly with hammer
It beats, it is made to beat rectangularity gold bullion A；
S3: reverse mould molding: the A of rectangle gold bullion described in S2 is put on reverse mould iron and is beaten repeatedly again, is obtained into
Type gold jewelry B；
S4: after the molding gold jewelry B described in the S3 is completely cooling, gold jewelry will first deburring, cleaning: be formed using scissors
Flash on B is cut, and is then carried out grinding process using sander, after polishing, is reused polishing machine and be processed by shot blasting,
It is cleared up finally, the molding gold jewelry B after polishing is put into service sink, obtains semi-finished product gold jewelry C；
S5: the production of bronze water: a clean plastic containers are taken, are then successively put into ammonium hydroxide, alkali in proportion into plastic containers
Formula copper carbonate, sodium carbonate, hydroquinone and glacial acetic acid after placing 20-24 hours, obtain bronze water D after evenly mixing；
S6: the clear water that 3~6 times are added in bronze water D described in S5 dilution: is obtained into bronze water diluent E after evenly mixing；
S7: coloring treatment: frosted processing is carried out to the C of semi-finished product gold jewelry described in S4 using wire drawing cloth, is then put
Enter and carry out immersion treatment into bronze water diluent E, taken out after a period of time, be subsequently placed into service sink carry out it is secondary clear
It washes, removes remaining bronze water diluent E；
S8: dehydration, waxing: the gold jewelry C after coloring treatment described in S7 being put into drying box and carries out drying and processing,
It after taking-up, reuses 3D wax sprayer and waxing processing is carried out to it, after waxing, finished product gold jewelry can be obtained.
2. Gu method gold production method according to claim 1, which is characterized in that in the S2, the model of fusing soldering welder
JX3-5, when carrying out melt processed to gold raw material, the injection temperation of bonding machine spray gun should be arranged in 1100~1300 DEG C.
3. Gu method gold production method according to claim 1, which is characterized in that in the S4, to molding gold jewelry B
After cleaning, also needs to put it into and carry out drying and processing in drying box, the model 101A-2 of drying box, drying time 5
~8min.
4. Gu method gold production method according to claim 1, which is characterized in that in the S5, the dosage of ammonium hydroxide is
150g/L, the dosage of basic copper carbonate are 250g/L, and the dosage of sodium carbonate is 8g/L, and the dosage of hydroquinone is 5g/L, ice second
The dosage of acid is 50g/L, when mixing, is uniformly stirred using plastic stir rod, and mixing time is 3~5min.
5. Gu method gold production method according to claim 1, which is characterized in that in the S7, semi-finished product gold jewelry C
Soaking time be 3~5min.
6. Gu method gold production method according to claim 1, which is characterized in that first to semi-finished product gold in the S7
Decorations C carries out needing to wear Acid-proof plastic gloves during coloring treatment, need to be immediately with clear after bronze water diluent E contacts skin
Water rinses.
7. Gu method gold production method according to claim 1, which is characterized in that in the S8, the model of 3D wax-polishing machine
For CPX3000.