CN109570929A - A kind of noble metal melting welding color-dividing process - Google Patents

A kind of noble metal melting welding color-dividing process Download PDF

Info

Publication number
CN109570929A
CN109570929A CN201811476995.3A CN201811476995A CN109570929A CN 109570929 A CN109570929 A CN 109570929A CN 201811476995 A CN201811476995 A CN 201811476995A CN 109570929 A CN109570929 A CN 109570929A
Authority
CN
China
Prior art keywords
color
parts
noble metal
melting welding
dividing process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201811476995.3A
Other languages
Chinese (zh)
Other versions
CN109570929B (en
Inventor
周林洪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Kingli Jewellery Co Ltd
Original Assignee
Shenzhen Kingli Jewellery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Kingli Jewellery Co Ltd filed Critical Shenzhen Kingli Jewellery Co Ltd
Priority to CN201811476995.3A priority Critical patent/CN109570929B/en
Publication of CN109570929A publication Critical patent/CN109570929A/en
Application granted granted Critical
Publication of CN109570929B publication Critical patent/CN109570929B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of noble metal melting welding color-dividing process, comprising the following steps: step 1: production part mould;Step 2: making model with precious metal raw material;Step 3: shaping workpiece surface treatment;Step 4: melting welding synthesizes color separation alloy material;Step 5: artificial post-processing;The noble metal includes: platinum, 18K is red, 18K is yellow;Wherein the platinum parts by weight are 50~80 parts, and the red parts by weight of 18K are 20~50 parts, and the 18K Huang parts by weight are 20~50 parts, are chosen on demand according to each Parts by Ingredients in different decorative pattern products.A kind of noble metal melting welding color-dividing process of the invention, based on the technical characteristic being manually surface-treated after noble metal melting welding, forge polishing by hand through craftsman, mirror surface or the combination of black or yellowish or pink single or multi-effect can be presented in workpiece jewellery surface, obtained ornaments color is clearly demarcated, the jewellery of different surfaces can be customized according to customer special demands, customization processability is good, has wide economic benefit.

Description

A kind of noble metal melting welding color-dividing process
Technical field
The present invention relates to bullion production technologies, and in particular, to a kind of noble metal melting welding color-dividing process.
Background technique
Currently, jewel in the market is to synthesize work with the color separation of pure gold with material different colours of the same race or platinum Skill, can not be suitable for crowd at the color separation material of these materials synthesis the shortcomings that there are color separation is unobvious and product treatment single effect The different demands of more customers.
Summary of the invention
It is an object of the invention to overcome the deficiencies of existing technologies, your gold that a kind of surface can do multi-effect processing provided Belong to melting welding color-dividing process.
To achieve the above object, the invention adopts the following technical scheme:
A kind of noble metal melting welding color-dividing process, comprising the following steps:
Step 1: production part mould;
Step 2: making model with precious metal raw material;
Step 3: shaping workpiece surface treatment;
Step 4: melting welding synthesizes color separation alloy material;
Step 5: artificial post-processing;
The noble metal includes: platinum, 18K is red, 18K is yellow;Wherein the platinum parts by weight are 50~80 parts, the 18K Red parts by weight are 20~50 parts, and the 18K Huang parts by weight are 20~50 parts, on-demand according to each Parts by Ingredients in different decorative pattern products It chooses.
Its further technical solution are as follows: the step 2 specifically: several different metal materials are made into flakiness, according to The processing dimension of smelting furnace cuts sheet metal.
Its further technical solution are as follows: be surface-treated in the step 3 are as follows: it is polished with sand paper and forms workpiece surface, and Polishing rear surface is cleaned using the acid solution after dilution.
Its further technical solution are as follows: the step 4 specifically: after sheet metal layering overlapping, be put into one group of steel plate Between, it pressurizes and fixes at steel plate both ends;Sheet metal group and steel plate are put into smelting furnace to bake, reach each gold after fusing point Belong to thin slice to combine together.
Its further technical solution are as follows: the step 5 includes:
Step 6: artificial to beat production texture;
Step 7: the workpiece of different texture is surface-treated.
Its further technical solution are as follows: the step 7 includes gloss finish and color treatments;The gloss finish is on-demand It selects to polish bright, and/or polishing sand, and/or polish silk process of surface treatment and workpiece is surface-treated;The color treatments For by workpiece be tempered it is secondary bake, after cleaning keep metal primary colors, required surface color effect is obtained after oxidation.
Its further technical solution are as follows: the metal primary colors includes: to be showed according to synthesis raw metal type difference White, red or yellow.
Compared with prior art the utility model has the advantages that
A kind of noble metal melting welding color-dividing process of the invention, based on the technology being manually surface-treated after noble metal melting welding Feature forges polishing through craftsman by hand, and mirror surface can be presented in workpiece jewellery surface or black or yellowish or pink list is one or more Kind combination of effects, obtained ornaments color is clearly demarcated, and the jewellery of different surfaces can be customized according to customer special demands, customize processability It is good, there is wide economic benefit.
It is with reference to the accompanying drawing and specific real in order to be more clearly understood that above-mentioned purpose of the invention, characteristics and advantages Applying mode, the present invention is described in further detail.
Detailed description of the invention
Fig. 1 is process flow chart of the invention.
Specific embodiment
Many details are elaborated in following specific descriptions to facilitate a thorough understanding of the present invention, still the present invention is gone back It can be different from the other modes of this description using other to realize, therefore, protection scope of the present invention is not by described below Specific embodiment limitation.
As shown in Figure 1, in specific embodiment 1,
A kind of noble metal melting welding color-dividing process, comprising the following steps:
Step 1: production part mould;
Step 2: making model with precious metal raw material;Several different metal materials are specially made into flakiness, according to molten The processing dimension of furnace cuts sheet metal.Wherein noble metal includes: platinum, 18K is red, 18K is yellow;Wherein platinum parts by weight are 50 ~80 parts, the red parts by weight of 18K are 20~50 parts, and 18K Huang parts by weight are 20~50 parts, according to each Ingredients Weight in different decorative pattern products Part is chosen on demand.
Step 3: shaping workpiece surface treatment;Surface treatment is specially to be polished to form workpiece surface with sand paper, and utilize Acid solution after dilution cleans polishing rear surface.
Step 4: melting welding synthesizes color separation alloy material;Specially by sheet metal layering overlapping after, be put into one group of steel plate it Between, it pressurizes and fixes at steel plate both ends;Sheet metal group and steel plate are put into smelting furnace to bake, reach each metal after fusing point Thin slice combines together.
Step 5: artificial post-processing, comprising the following steps:
Step 6: artificial to beat production texture;
Step 7: the workpiece of different texture being surface-treated, including gloss finish and color treatments;Gloss finish is It selects to polish bright, and/or polishing sand, and/or polish silk process of surface treatment on demand and workpiece is surface-treated;Color treatments For by workpiece be tempered it is secondary bake, after cleaning keep metal primary colors, required surface color effect is obtained after oxidation.Wherein, metal Primary colors includes: white, red or the yellow showed according to synthesis raw metal type difference.
In conclusion a kind of noble metal melting welding color-dividing process of the invention of the invention, based on being carried out after noble metal melting welding The technical characteristic of artificial surface processing, polishing is forged through craftsman, mirror surface or black or light can be presented in workpiece jewellery surface by hand Yellow or pink single or multi-effect combination, obtained ornaments color is clearly demarcated, can customize different tables according to customer special demands The jewellery in face, customization processability is good, has wide economic benefit.
It is above-mentioned that technology contents of the invention are only further illustrated with embodiment, in order to understand, but do not represent the present invention Embodiment be only limitted to this, it is any to extend according to the technology done of the present invention or recreation, by protection of the invention.This hair Bright protection scope is subject to claims.

Claims (7)

1. a kind of noble metal melting welding color-dividing process, which comprises the following steps:
Step 1: production part mould;
Step 2: making model with precious metal raw material;
Step 3: shaping workpiece surface treatment;
Step 4: melting welding synthesizes color separation alloy material;
Step 5: artificial post-processing;
The noble metal includes: platinum, 18K is red, 18K is yellow;Wherein the platinum parts by weight are 50~80 parts, and the 18K is red heavy Measuring part is 20~50 parts, and the 18K Huang parts by weight are 20~50 parts, is selected on demand according to each Parts by Ingredients in different decorative pattern products It takes.
2. noble metal melting welding color-dividing process according to claim 1, which is characterized in that the step 2 specifically: will be several Different metal materials make flakiness, cut sheet metal according to the processing dimension of smelting furnace.
3. noble metal melting welding color-dividing process according to claim 2, which is characterized in that be surface-treated in the step 3 are as follows: It is polished with sand paper and forms workpiece surface, and polishing rear surface is cleaned using the acid solution after dilution.
4. noble metal melting welding color-dividing process according to claim 3, which is characterized in that the step 4 specifically: by metal After thin slice layering overlapping, it is put between one group of steel plate, pressurizes and fix at steel plate both ends;Sheet metal group and steel plate are put into melting Furnace is baked, and each sheet metal combines together after reaching fusing point.
5. noble metal melting welding color-dividing process according to claim 4, which is characterized in that the step 5 includes:
Step 6: artificial to beat production texture;
Step 7: the workpiece of different texture is surface-treated.
6. noble metal melting welding color-dividing process according to claim 5, which is characterized in that the step 7 includes gloss finish And color treatments;The gloss finish is to select to polish bright, and/or polishing sand, and/or polishing silk process of surface treatment pair on demand Workpiece is surface-treated;The color treatments be workpiece is tempered it is secondary bake, metal primary colors is kept after cleaning, after oxidation To required surface color effect.
7. noble metal melting welding color-dividing process according to claim 6, which is characterized in that the metal primary colors includes: basis White, red or the yellow that synthesis raw metal type difference shows.
CN201811476995.3A 2018-12-04 2018-12-04 Precious metal fusion welding color separation process Active CN109570929B (en)