CN109930282A - The preparation method of blended silk like fabric fabric - Google Patents
The preparation method of blended silk like fabric fabric Download PDFInfo
- Publication number
- CN109930282A CN109930282A CN201910054283.0A CN201910054283A CN109930282A CN 109930282 A CN109930282 A CN 109930282A CN 201910054283 A CN201910054283 A CN 201910054283A CN 109930282 A CN109930282 A CN 109930282A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- temperature
- washing
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of blended silk like fabric fabric.The preparation method of the blended silk like fabric fabric is the following steps are included: mix spinning, dyeing, fabric weaving, alkali decrement treatment, sizing, hanging；The preparation method of blended silk like fabric fabric disclosed by the invention, selection is environmentally protective, using poly- 1, 4- cyclohexanedimethanol phthalic acid ester fiber and corn fiber blending weave fabric, improve the pendency sense and texture of silk like fabric fabric, by mix spinning, dyeing, fabric weaving, alkali decrement treatment, sizing, the preparation method of hanging, obtained blended silk like fabric fabric has good comfort level, the perspiration of body appropriateness when can also effectively absorb movement or higher temperature, keep body and mind pleasant, it is not easy to wrinkle simultaneously, it is easy to clean, it is not limited by silk fabric washing methods, strong operability.
Description
Technical field
The present invention relates to a kind of textile technologies, more specifically, it relates to a kind of preparation method of blended silk like fabric fabric.
Background technique
Constant, silk fabrics represents always noble quality, the life of quality, main reason is that, silk fabrics
Pendency sense and feel are especially comfortable, are also special pro-skin when wearing, light sensation is full, and pole creates an aesthetic feeling.Meanwhile silk fabric is
Ideal summer clothing fabric and underwear fabric, when not perspiring in large quantities, silk fabric shows good snugness of fit.But
Movement or sweltering heat summer perspire when, the absorbing sweat effect of silk fabric just show it is clearly disadvantageous, application range therefore by
Limit.Also the hygroscopicity of mainly silk is high, moisture releasing is slow, and wearing in perspiration can not feel well for a long time,
It is that silk oilfields are limited, relative price is higher, and cost performance is not fine.More and more researchs are dedicated to silk like fabric face at present
Material, with the gloss and comfort as silk, cost of manufacture is again low, while raw material sources are abundant.
Chinese patent CN104746211A discloses a kind of preparation method of terylene viscose glue silk like fabric color-woven fabric, step
It include: spinning → dyeing → warping → weaving → fabric maintenance → Alkali reduction → sizing → calendering → preshrunk.Wherein Polyester Yarns is spun
Yarn uses pure polyester network yarn to be woven into such a way that S twirl, Z twirl are alternate.Alkali reduction, amount of caustic soda 5-10g/L, treatment temperature
It is 50-70 DEG C, time 30-60min；150 DEG C of setting temperature, hydroscopic fast-drying finishing agent is padded, the moisture absorption for improving Polyester Yarns is fast
Dry effect；Calendering operation, using hot calendering, temperature is 100 DEG C, pressure 5-10kg, speed 30-50m/min, improves feel, is assigned
Give the gloss as silk, feel.Terylene viscose glue silk like fabric color-woven fabric using dyeing and finishing processing method production has as silk
Style, while twill distortion makes fabric have sericeous smooth hand within 3.0% by alkali decrement treatment
Sense, caustic soda are obvious not as good as effect of the organic base to fiber treatment as inorganic base.
Chinese patent CN102965976A discloses a kind of biodegradable copolyester polymerization filament finished fabric manufacturer
Method, it is characterised in that the following steps are included: (1) obtains fabric using PBST as warp or weft according to the conventional method；(2)
By fabric refining, washing, dyeing, dehydration, tentering, finished product is obtained；Wherein, the temperature control of dyeing course is three phases, first
First start temperature is 10 DEG C, after being warming up to 70 DEG C with the heating rate of 1.5 DEG C/min；In 70 DEG C of heat preservation 60min, then it is cooled to
10℃；Fuel solution: being 1g/LMF using low temperature disperse dyes, diffusant, and with weak acid tune pH value of solution to 5~7；Bath raio:
1:50；The cleaning agent of reduction cleaning includes: sodium hydrosulfite 2g/L, 60 DEG C of caustic soda 2g/L cleaning temperature, scavenging period 10min, bath raio
1:50.Fabric gas permeability is strong, and soft, excellent spring, color is bright and new full, there is imitative natural and ultranatural style, this kind of face
Expect good extending performance, it is comfortable and easy to wear, and silk broadcloth elasticity deficiency can be improved, product specification and function are promoted, is dyed in the invention
Fabric color afterwards is bright-coloured, but fabric elasticity is bad.
Chinese patent CN104233572A discloses a kind of preparation method of silk like fabric fabric, and step includes: (1) selection:
Warp thread is adopted as BB.FDY diamond filament drafting silk Pure Yarn, and weft yarn chooses soybean fiber and milk protein fiber mixed yarn；
(2) warp thread is handled: BB.FDY diamond filament drafting silk → TW-N type warping machine → KSH300 type slurry silk machine → KB20 type warp rebeaming machine →
TD type splitting machine → drawing-in → A；(3) weft yarn is handled: soybean fiber and milk protein fiber mixed yarn → doff → B；(4)
A and B is with ZA205i air-jet loom weaving at cloth；(5) it arranges, silk like fabric fabric is prepared using mix spinning, without further alkali
The feel of decrement treatment, fabric is not good enough, and upper Color uniformity is poor.
Therefore, the present invention has good moisture pick-up properties and bullet in view of the above problems, inventing a kind of blended silk like fabric fabric
Property, while upper Color uniformity is good, comfortable feel, wears pro-skin.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of preparation side of blended silk like fabric fabric
Method.
To achieve the above object, the present invention adopts the following technical scheme: a kind of preparation method of blended silk like fabric fabric, packet
Include following steps,
(1) 28~40 parts of drawn polyester fiber, 54~58 parts of zein fiber, 17~20 parts of wool fiber；
(2) zein fiber is stood into washing 30min with 45~50 DEG C of water, it is spare after material processing；(3) wool fiber
Be put into heating sieve, 60 DEG C at a temperature of vibrate fluffy 15min, it is spare after material processing；
(4) polyester fiber carries out preliminary alkali process with caustic soda, and zein fiber is carried out at preliminary alkali with diisopropyl ethyl ammonia
Reason, washing lixiviating and drying after the completion of processing；
(5) using wool fiber as central spindle, polyester fiber and zein fiber wire drawing are blended, obtain fabric weaving raw material；
(6) the fabric weaving raw material obtained is under the conditions of temperature is 120 DEG C~130 DEG C, bath raio 1:18, dyeing 10min~
15min；
(7) the fabric weaving raw material after dyeing obtains fabric using the cooperation double side weft knitting weaving of four phase tatting woven singles；
(8) fabric obtained is in the environment of 48 DEG C~50 DEG C, with the caustic soda of the atomization shower spray 6.8g/L of 300 mesh
Solution carries out alkali decrement treatment, carries out neutralization washing after the completion of processing with the slightly acidic water of pH=6.8, neutralizes after washing again with pH
=7, the water that temperature is 35 DEG C carries out room temperature washing；
(9) it is placed in style keeping liquid after the fabric for handling previous step well dries in the shade and impregnates 15~20min, it is pre- after the completion of immersion
Dehydration, then drying is protected from light in 60 DEG C~65 DEG C of environment；
(8) fabric obtained carries out hanging with the starch solution of 1:30, is then 30 DEG C in temperature, the ring that humidity is 70%
30~40min is dried in the shade under border to complete to be dehydrated.
Preferably, the polyester fiber is using poly- 1,4-CHDM phthalic acid ester fiber.
Preferably, the preliminary alkali process of polyester fiber is polyester fiber under the conditions of temperature is 110 DEG C~115 DEG C
It is respectively placed in the NaOH solution of 2.5g/L~3.5g/L, keeps 10~15min, the preliminary alkali process of zein fiber is temperature
Under conditions of 45 DEG C~50 DEG C, zein fiber is placed in the diisopropyl ethyl ammonia solution of 1:17, with the revolving speed of 1rad/s
Stir 15~20min.
Preferably, the room temperature washing is carried out in three steps, and the first step, washing temperature is 75 DEG C~85 in step (8)
DEG C, washing time 2min~3min；Second step, washing temperature are 55 DEG C~65 DEG C, washing time 5min~10min；Third
Step, washing temperature are 25 DEG C~35 DEG C, washing time 8min~12min.
Preferably, the style keeping liquid be 0.05g/L~0.08g/L AC solution, the setting temperature be 130 DEG C~
138℃。
The present invention compares compared with the prior art to be had the advantage that by mix spinning, dyeing, fabric weaving, Alkali reduction
The preparation method of processing, sizing, hanging, obtained blended silk like fabric fabric have good comfort level, can also effectively absorb
The perspiration of body appropriateness when movement or temperature are higher keeps body and mind pleasure, while being not easy to wrinkle, is easy to clean, not by true
The limitation of silk face fabric washing methods, strong operability, compared to traditional silk like fabric fabric, the preparation of the blended silk like fabric fabric
For method using wool fiber as the mandrel of blended spinning yarn, polyester fiber uses poly- 1,4-CHDM phthalic acid ester
Fiber, so that there is longer length of yarn and yarn strength using blended silk like fabric fabric made from the preparation method, thus
Bigger structural strength is obtained, while the compliance of its quality and sag are also risen, cooperates hanging step, subsequent cutting
Also more convenient.
Specific embodiment
The preparation method embodiment of the blended silk like fabric fabric of the present invention is described further below.
A kind of preparation method of blended silk like fabric fabric, includes the following steps,
(1) 28~40 parts of drawn polyester fiber, 54~58 parts of zein fiber, 17~20 parts of wool fiber；
(2) zein fiber is stood into washing 30min with 45~50 DEG C of water, it is spare after material processing；
(3) wool fiber is put into heating sieve, 60 DEG C at a temperature of vibrate fluffy 15min, it is spare after material processing；
(4) polyester fiber carries out preliminary alkali process with caustic soda, and zein fiber is carried out at preliminary alkali with diisopropyl ethyl ammonia
Reason, washing lixiviating and drying after the completion of processing；
(5) using wool fiber as central spindle, polyester fiber and zein fiber wire drawing are blended, obtain fabric weaving raw material；
(6) the fabric weaving raw material obtained is under the conditions of temperature is 120 DEG C~130 DEG C, bath raio 1:18, dyeing 10min~
15min；
(7) the fabric weaving raw material after dyeing obtains fabric using the cooperation double side weft knitting weaving of four phase tatting woven singles；
(8) fabric obtained is in the environment of 48 DEG C~50 DEG C, with the caustic soda of the atomization shower spray 6.8g/L of 300 mesh
Solution carries out alkali decrement treatment, carries out neutralization washing after the completion of processing with the slightly acidic water of pH=6.8, carries out again after neutralizing washing
Room temperature washing；
(9) it is placed in style keeping liquid after the fabric for handling previous step well dries in the shade and impregnates 15~20min, it is pre- after the completion of immersion
Dehydration, then drying is protected from light in 60 DEG C~65 DEG C of environment；
(8) fabric obtained carries out hanging with the starch solution of 1:30, is then 30 DEG C in temperature, the ring that humidity is 70%
30~40min is dried in the shade under border to complete to be dehydrated.
Polyester fiber is using poly- 1,4 cyclohexane dimethanol phthalic acid ester fiber.
The preliminary alkali process of polyester fiber is under the conditions of temperature is 110 DEG C~115 DEG C, and polyester fiber is respectively placed in
In the NaOH solution of 2.5g/L~3.5g/L, 10~15min is kept, the preliminary alkali process of zein fiber is that temperature is 45 DEG C~50
Under conditions of DEG C, zein fiber is placed in the diisopropyl ethyl ammonia solution of 1:17, with the revolving speed of 1rad/s stirring 15~
20min。
In step (8), room temperature washing is carried out in three steps, the first step, and washing temperature is 75 DEG C~85 DEG C, when washing
Between 2min~3min；Second step, washing temperature are 55 DEG C~65 DEG C, washing time 5min~10min；Third step, washing temperature
It is 25 DEG C~35 DEG C, washing time 8min~12min.
Style keeping liquid is the AC solution of 0.05g/L~0.08g/L, and the setting temperature is 130 DEG C~138 DEG C.
By mix spinning, dyeing, fabric weaving, alkali decrement treatment, sizing, hanging preparation method, what is obtained is blended
Silk like fabric fabric is with good comfort level, the perspiration of body appropriateness when can also effectively absorb movement or higher temperature,
It keeps body and mind pleasant, while being not easy to wrinkle, is easy to clean, do not limited by silk fabric washing methods, strong operability is compared
In traditional silk like fabric fabric, the preparation method of the blended silk like fabric fabric is using wool fiber as the core of blended spinning yarn
Axis, polyester fiber uses poly- 1,4-CHDM phthalic acid ester fiber, so that using blended made from the preparation method
Silk like fabric fabric has longer length of yarn and yarn strength, to obtain bigger structural strength, while its quality is soft
Compliance and sag are also risen, and hanging step is cooperated, and subsequent cutting is also more convenient.
Embodiment:
A kind of preparation method of blended silk like fabric fabric, includes the following steps,
(1) poly- 35 parts of 1,4-CHDM phthalic acid ester fiber are taken, 36 parts of zein fiber, wool fiber 20
Part；
(2) zein fiber is stood into washing 30min with 45 DEG C of water, it is spare after material processing；
(3) wool fiber is put into heating sieve, 60 DEG C at a temperature of vibrate fluffy 15min, it is spare after material processing；
(4) poly- 1,4-CHDM phthalic acid ester fiber is under the conditions of temperature is 110 DEG C DEG C, polyester fiber difference
Be placed in the NaOH solution of 3g/L, keep 12min, zein fiber with diisopropyl ethyl ammonia temperature be 48 DEG C under conditions of,
Zein fiber is placed in the diisopropyl ethyl ammonia solution of 1:17,20min, water after the completion of processing are stirred with the revolving speed of 1rad/s
Wash away alkali and drying；
(5) using wool fiber as central spindle, poly- 1,4-CHDM phthalic acid ester fiber and zein fiber wire drawing are mixed
It spins, obtains fabric weaving raw material；
(6) for the fabric weaving raw material obtained under the conditions of temperature is 130 DEG C, bath raio 1:18 dyes 13min；
(7) the fabric weaving raw material after dyeing obtains fabric using the cooperation double side weft knitting weaving of four phase tatting woven singles；
(8) fabric obtained in the environment of 50 DEG C, with 300 mesh atomization shower spray 6.8g/L soda bath into
Row alkali decrement treatment carries out neutralization washing after the completion of processing with the slightly acidic water of pH=6.8, carries out normal-temperature water again after neutralizing washing
It washes, the first step, washing temperature is 75 DEG C~85 DEG C, washing time 2min~3min；Second step, washing temperature are 55 DEG C~65
DEG C, washing time 5min~10min；Third step, washing temperature are 25 DEG C~35 DEG C, washing time 8min~12min.
(9) it is placed in after the fabric for handling previous step well dries in the shade in the AC solution of style keeping liquid 0.07g/L and impregnates 18min,
Setting temperature is 135 DEG C, pre-dehydration after the completion of immersion, then drying is protected from light in 62 DEG C of environment；
(8) fabric obtained carries out hanging with the starch solution of 1:30, is then 30 DEG C in temperature, the ring that humidity is 70%
36min is dried in the shade under border to complete to be dehydrated.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention, it is noted that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (5)
1. a kind of preparation method of blended silk like fabric fabric, it is characterised in that: include the following steps,
(1) 28~40 parts of drawn polyester fiber, 54~58 parts of zein fiber, 17~20 parts of wool fiber；
(2) zein fiber is stood into washing 30min with 45~50 DEG C of water, it is spare after material processing；
(3) wool fiber is put into heating sieve, 60 DEG C at a temperature of vibrate fluffy 15min, it is spare after material processing；
(4) polyester fiber carries out preliminary alkali process with caustic soda, and zein fiber carries out preliminary alkali process, place with diisopropyl ethyl ammonia
Washing lixiviating and drying after the completion of reason；
(5) using wool fiber as central spindle, polyester fiber and zein fiber wire drawing are blended, obtain fabric weaving raw material；
(6) the fabric weaving raw material obtained is under the conditions of temperature is 120 DEG C~130 DEG C, bath raio 1:18, dyeing 10min~
15min；
(7) the fabric weaving raw material after dyeing obtains fabric using the cooperation double side weft knitting weaving of four phase tatting woven singles；
(8) fabric obtained in the environment of 48 DEG C~50 DEG C, with 300 mesh atomization shower spray 6.8g/L soda bath into
Row alkali decrement treatment carries out neutralization washing after the completion of processing with the slightly acidic water of pH=6.8, carries out normal-temperature water again after neutralizing washing
It washes；
(9) it is placed in style keeping liquid after the fabric for handling previous step well dries in the shade and impregnates 15~20min, it is pre- de- after the completion of immersion
Water, then drying is protected from light in 60 DEG C~65 DEG C of environment；
(8) fabric obtained carries out hanging with the starch solution of 1:30, is then 30 DEG C in temperature, in the environment of humidity is 70%
30~40min dry in the shade to complete to be dehydrated.
2. the preparation method of blended silk like fabric fabric according to claim 1, it is characterised in that: the polyester fiber uses
Be poly- 1,4 cyclohexane dimethanol phthalic acid ester fiber.
3. the preparation method of blended silk like fabric fabric according to claim 1, it is characterised in that: the preliminary alkali of polyester fiber
Processing is under the conditions of temperature is 110 DEG C~115 DEG C, and polyester fiber is respectively placed in the NaOH solution of 2.5g/L~3.5g/L,
10~15min is kept, the preliminary alkali process of zein fiber is that under conditions of temperature is 45 DEG C~50 DEG C, zein fiber is placed in 1:
In 17 diisopropyl ethyl ammonia solution, 15~20min is stirred with the revolving speed of 1rad/s.
4. the preparation method of blended silk like fabric fabric according to claim 1, it is characterised in that: described normal in step (8)
Warm water, which is washed, to be carried out in three steps, the first step, and washing temperature is 75 DEG C~85 DEG C, washing time 2min~3min；Second step, washing temperature
Degree is 55 DEG C~65 DEG C, washing time 5min~10min；Third step, washing temperature are 25 DEG C~35 DEG C, washing time 8min~
12min。
5. the preparation method of blended silk like fabric fabric according to claim 1, it is characterised in that: the style keeping liquid is
The AC solution of 0.05g/L~0.08g/L, the setting temperature are 130 DEG C~138 DEG C.