CN104818554A - Blended yarn of jade fiber, coconut carbon fiber and Coolmax fiber and fabric thereof - Google Patents
Blended yarn of jade fiber, coconut carbon fiber and Coolmax fiber and fabric thereof Download PDFInfo
- Publication number
- CN104818554A CN104818554A CN201510161428.9A CN201510161428A CN104818554A CN 104818554 A CN104818554 A CN 104818554A CN 201510161428 A CN201510161428 A CN 201510161428A CN 104818554 A CN104818554 A CN 104818554A
- Authority
- CN
- China
- Prior art keywords
- fiber
- speed
- coolmax
- jade
- coconut palm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a blended yarn of jade fiber, coconut carbon fiber and Coolmax fiber and a fabric thereof. The yarns and the fabric are formed by jade fibers, coconut carbon fibers and Coolmax fibers, wherein the components includes, by weight percentage, 20-40% of jade fibers, 20-40% coconut carbon fibers and 40-70% of Coolmax fibers. Jade fibers, coconut carbon fibers and Coolmax fibers are reasonably matched and combined, thereby making the respective advantages fibers complementary to each other and reducing disadvantages. The fabric obtained is moisture-absorbing, ventilating and antibiotic, and is applicable to the fields of various high-quality clothes and home textiles.
Description
Technical field
The present invention relates to multifilament blended yarn and fabric thereof, particularly relate to blended yarn and the fabric thereof of jade fiber, coconut palm Carbon fibe and Coolmax, belong to Textile Engineering field.
Background technology
Jade from ancient times like by people, to human body, there is medical care effect, containing to the useful mineral matter of human body and trace element in jade, prolonged permeation human body cell, can improve microcirculation, enhance metabolism, thus reaches the effect of prevent disease, dispelling fatigue.Jade fiber uses extraction and nanometer technology, makes jade and other mineral materials reach Subnano-class level, then fuse among spinning melt, make through spinning process, jade has microcellular structure, improves the sucting wet air permeability of fiber, heat can be taken away very soon, reach the effect of cooling.
Coconut palm Carbon fibe belongs to low cost natural fabric, it is the lignocellulose fiber obtained from coconut fruit, it is that the cellulosic of cocoanut husk is heated to 1600 DEG C, generate active carbon, mix with polyester again and add the coconut palm charcoal master batch that other chemical substances make, and be that carrier dilutes with polyester, be pumped into the long fine and short fiber of coconut palm charcoal.Coconut palm Carbon fibe adopts new modified polyester fiber carrier material, utilize discarded coconut husk, meet the development trend of the resource that can be recycled, also there is moisture absorption taste removal simultaneously, produce anion, the function such as emitting far-infrared, antiultraviolet, and due to the micropore area in coconut palm charcoal than bamboo charcoal also large 4-6 doubly, than bamboo charcoal gas permeability, better, therefore adsorption capacity is stronger, in addition coconut palm charcoal lead wet effective, rapidly the sweat of human body can be discharged to clothes skin, make that maintenance is dry and comfortable does not comfortablely paste skin.
Coolmax is the functional fiber that E.I.Du Pont Company exclusively researchs and develops, and not only unique-four tubuloses of cross sectional shape, be again doughnut, and the tube wall of fiber are also breathed freely.Just because of the unique physical structure of this fiber, result in its moisture absorption, perspire, ventilating performance, namely fabric has good capillary effect.At any time making soaked with sweat on skin can be detached skin, be transferred to web surface thus evaporate rapidly, make skin keep dry and comfortable and comfortable.
Summary of the invention
The object of the present invention is to provide blended yarn and the fabric thereof of jade fiber, coconut palm Carbon fibe and the Coolmax that sucting wet air permeability is good.
For solving the problems of the technologies described above, the present invention adopts following technical scheme to realize:
The blended yarn of jade fiber, coconut palm Carbon fibe and Coolmax fiber, fibrous by jade fiber, coconut palm Carbon fibe and Coolmax, by weight percentage, each component proportion is: jade fiber 20 ~ 40%, coconut palm Carbon fibe 20 ~ 40%, Coolmax fiber 40 ~ 70%.
The blended yarn woven fabric that the blended yarn of jade fiber, coconut palm Carbon fibe and Coolmax fiber is made into, its warp thread and weft yarn are all for raw material with jade fiber, coconut palm Carbon fibe and Coolmax fiber, raw material weight percentages, the content of each raw material components in finished product fabric: jade fiber 20 ~ 40%, coconut palm Carbon fibe 20 ~ 40%, Coolmax fiber 40 ~ 70%.
The manufacturing technique of the blended yarn woven fabric of described jade fiber, coconut palm Carbon fibe and Coolmax fiber comprises the steps: to spin → weave front preparation → weave → ferment treatment → dyeing → oven dry → sizing → perching → rolling, is specifically:
(1) spinning process:
(1) spinning specification
A, resultant yarn: 13.1 ~ 19.8tex single thread, the twist 1050 ~ 1150T/m
B, weight proportion:
Jade fiber: coconut palm Carbon fibe: Coolmax fiber=20 ~ 40%: 20 ~ 40%: 40 ~ 70%
(2) opening or cleaning: fibre uniformity is good, only need to remove the hard doubling in fiber, picker hired roughneck all adopts compared with the soft opening of low velocity, and the speeds control of each hired roughneck, in 400 ~ 750r/min, reduces fibre damage;
(3) combing:
Bar weight: 3.3 ~ 3.6g/m
Sliver exporting speed: 20 ~ 22 revs/min
(4) spin: spinning is fixed heavy: 2.5 ~ 2.6g/10m, ingot speed 10000 ~ 12000 revs/min;
(2) front preparatory technology is weaved
Warping: batch warping, tension in Warping 20 ~ 22dN, speed of beaming 400r/min;
Starching: select farina slurry to be main slurry, auxiliary adhesive agent selects PAM, CMC, slurry viscosity 6 ~ 10, and sizing speed is 40 ~ 80m/min, the rate of sizing 7 ~ 12%;
(3) weave
Weaving step: adopt air-jet loom, fabric width 190 ~ 340cm, back beam height 60 ~ 80mm, opening time is 290 ~ 310mm, fabric width 160 ~ 320cm, grammes per square metre 60 ~ 180g/m
2;
(4) ferment treatment
Acetic acid 0.6g/L, enzyme 2g/L, refining agent 1g/L, process 45 ~ 50 minutes at 50 DEG C;
(5) dye
First bath: by dispersion, REACTIVE DYES, two baths, two-step process dyeing: room temperature adds DISPERSE DYES, is warming up to 120 DEG C with the speed of 2 DEG C/min, keep 45 minutes, be cooled to 40 DEG C with the speed of 2 DEG C/min and soap, then be warming up to 80 DEG C at full speed, be incubated 15 minutes, cooling after washing;
Second bath: reactive dyeing: room temperature adds REACTIVE DYES, is warming up to 70 DEG C with the speed of 2 DEG C/min, is incubated 50 minutes, is cooled to 40 DEG C soaps with the speed of 2 DEG C/min, then be warming up to 80 DEG C at full speed, be incubated 15 minutes, cooling after washing;
(6) dry: be dried to eighty per cant dry;
(7) shape: use softener 30g/L, 170 DEG C of sizings, the speed of a motor vehicle 30 ~ 40m/min;
(8) inspection, clot packaging.
Beneficial effect of the present invention: the reasonably combined and combination that present invention achieves jade fiber, coconut palm Carbon fibe and Coolmax fiber, achieve the mutual supplement with each other's advantages of each fiber and inferior position abatement, knit fabric there is moisture absorption, breathe freely, the good characteristic of antibiotic health care, wearability be excellent; The product produced meets today's trend and market popularity trend, is the optimal selection of high-grade clothing, family's textile fabric.
Detailed description of the invention
In order to make the object, technical solutions and advantages of the present invention clearly understand, below in conjunction with specific embodiment, technical scheme of the present invention is described in detail.
(1) spinning process:
(1) spinning specification
Raw material prepares: jade fiber 1.33dtex × 38mm; Coconut palm Carbon fibe 1.33dtex × 38mm; Coolmax fiber: 1.33dtex × 38mm
Spinning specification: jade fiber/coconut palm Carbon fibe Coolmax fiber=30/30/40%
Resultant yarn: 16.8tex single thread, twist 1100T/m
(2) opening or cleaning: fibre uniformity is good, only need to remove the hard doubling in fiber, picker hired roughneck all adopts compared with the soft opening of low velocity, and the speeds control of each hired roughneck, in 550r/min, reduces fibre damage.
(3) combing:
Bar weight: 3.4g/m
Sliver exporting speed: 20 revs/min
(4) spin: spinning is fixed heavy: 2.5g/10m, ingot speed 10000 revs/min.
(2) front preparatory technology is weaved
Warping: batch warping, tension in Warping 20dN, speed of beaming 400r/min.
Starching: select farina slurry to be main slurry, auxiliary adhesive agent selects PAM, CMC, and slurry viscosity 8, sizing speed is 60m/min, the rate of sizing 9%.
(3) weave
Weaving step: adopt air-jet loom, fabric width 260cm, back beam height 70mm, opening time is 300mm, fabric width 290cm, grammes per square metre 120g/m
2.
(4) ferment treatment
Acetic acid 0.6g/L, enzyme 2g/L, refining agent 1g/L, process 45 minutes at 50 DEG C.
(5) dye
First bath: by dispersion, REACTIVE DYES, two baths, two-step process dyeing: room temperature adds DISPERSE DYES, is warming up to 120 DEG C with the speed of 2 DEG C/min, keep 45 minutes, be cooled to 40 DEG C with the speed of 2 DEG C/min and soap, then be warming up to 80 DEG C at full speed, be incubated 15 minutes, cooling after washing.
Second bath: reactive dyeing: room temperature adds REACTIVE DYES, is warming up to 70 DEG C with the speed of 2 DEG C/min, is incubated 50 minutes, is cooled to 40 DEG C soaps with the speed of 2 DEG C/min, then be warming up to 80 DEG C at full speed, be incubated 15 minutes, cooling after washing.
(6) dry: be dried to eighty per cant dry.
(7) shape: use softener 30g/L, 170 DEG C of sizings, speed of a motor vehicle 35m/min.
(8) inspection, clot packaging.
(9) fabric performance test result
(1) pilling resistance: anti-fluffing and anti-pilling 4 grades
(2) dyefastness: color fastness to washing 4 grades, color fastness to hot pressing 4 grades, fastness to light 5 grades.
(3) ventilative, poisture-penetrability: Air permenbility, 182mm/s; Air permenbility, 12100g/m
2d.
(4) antibiotic property: good antibiotic property.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (3)
1. the blended yarn of jade fiber, coconut palm Carbon fibe and Coolmax fiber, it is characterized in that: described fabric is fibrous by jade fiber, coconut palm Carbon fibe and Coolmax, by weight percentage, each component proportion is: jade fiber 20 ~ 40%, coconut palm Carbon fibe 20 ~ 40%, Coolmax fiber 40 ~ 70%.
2. the blended yarn woven fabric be made into by the blended yarn of jade fiber according to claim 1, coconut palm Carbon fibe and Coolmax fiber, it is characterized in that: the warp thread of described blended yarn woven fabric and weft yarn are all for raw material with jade fiber, coconut palm Carbon fibe and Coolmax fiber, raw material weight percentages, the content of each raw material components in finished product fabric: jade fiber 20 ~ 40%, coconut palm Carbon fibe 20 ~ 40%, Coolmax fiber 40 ~ 70%.
3. the production technology of the blended yarn woven fabric of jade fiber, coconut palm Carbon fibe and Coolmax fiber, is characterized in that: the front preparation that comprises the steps: to spin → weave → weave → ferment treatment → dyeing → oven dry → sizing → perching → rolling, is specifically:
(1) spinning process:
(1) spinning specification
A, resultant yarn: 13.1 ~ 19.8tex single thread, the twist 1050 ~ 1150T/m
B, weight proportion:
Jade fiber: coconut palm Carbon fibe: Coolmax fiber=20 ~ 40%: 20 ~ 40%: 40 ~ 70%
(2) opening or cleaning: fibre uniformity is good, only need to remove the hard doubling in fiber, picker hired roughneck all adopts compared with the soft opening of low velocity, and the speeds control of each hired roughneck, in 400 ~ 750r/min, reduces fibre damage;
(3) combing:
Bar weight: 3.3 ~ 3.6g/m
Sliver exporting speed: 20 ~ 22 revs/min
(4) spin: spinning is fixed heavy: 2.5 ~ 2.6g/10m, ingot speed 10000 ~ 12000 revs/min;
(2) front preparatory technology is weaved
Warping: batch warping, tension in Warping 20 ~ 22dN, speed of beaming 400r/min;
Starching: select farina slurry to be main slurry, auxiliary adhesive agent selects PAM, CMC, slurry viscosity 6 ~ 10, and sizing speed is 40 ~ 80m/min, the rate of sizing 7 ~ 12%;
(3) weave
Weaving step: adopt air-jet loom, fabric width 190 ~ 340cm, back beam height 60 ~ 80mm, opening time is 290 ~ 310mm, fabric width 160 ~ 320cm, grammes per square metre 60 ~ 180g/m
2;
(4) ferment treatment
Acetic acid 0.6g/L, enzyme 2g/L, refining agent 1g/L, process 45 ~ 50 minutes at 50 DEG C;
(5) dye
First bath: by dispersion, REACTIVE DYES, two baths, two-step process dyeing: room temperature adds DISPERSE DYES, is warming up to 120 DEG C with the speed of 2 DEG C/min, keep 45 minutes, be cooled to 40 DEG C with the speed of 2 DEG C/min and soap, then be warming up to 80 DEG C at full speed, be incubated 15 minutes, cooling after washing;
Second bath: reactive dyeing: room temperature adds REACTIVE DYES, is warming up to 70 DEG C with the speed of 2 DEG C/min, is incubated 50 minutes, is cooled to 40 DEG C soaps with the speed of 2 DEG C/min, then be warming up to 80 DEG C at full speed, be incubated 15 minutes, cooling after washing;
(6) dry: be dried to eighty per cant dry;
(7) shape: use softener 30g/L, 170 DEG C of sizings, the speed of a motor vehicle 30 ~ 40m/min;
(8) inspection, clot packaging.