CN109929097A - 一种无溶剂涂料用可降解的聚合物多元醇及其合成方法 - Google Patents
一种无溶剂涂料用可降解的聚合物多元醇及其合成方法 Download PDFInfo
- Publication number
- CN109929097A CN109929097A CN201910210689.3A CN201910210689A CN109929097A CN 109929097 A CN109929097 A CN 109929097A CN 201910210689 A CN201910210689 A CN 201910210689A CN 109929097 A CN109929097 A CN 109929097A
- Authority
- CN
- China
- Prior art keywords
- degree
- degradable polymer
- solventless coatings
- polymer polyalcohol
- cooled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种无溶剂涂料用可降解的聚合物多元醇,合成配方包括以下质量百分比:(a)精制蓖麻油三甘油酯40‑45%(b)季戊四醇10‑14%(c)己内酯44‑48%(d)氢氧化锂0.02%(醇解助剂)(e)1.4‑丁二醇2‑3%。及一种无溶剂涂料用可降解的聚合物多元醇的合成工艺:将(a)与(b)投入反应釜开启搅拌并加入(d),升温至220‑230度,保温醇解反应2小时,冷却至200度加(c)、在此温度下保温酯化反应4小时,停止加温并冷却至50度加入(e),搅匀过滤出料,整个合成过程是在常压下进行,原材料均属非危化品,操作安全易控,无有毒有害付产物。
Description
技术领域
本发明属于涂料技术领域,涉及无溶剂PU系列产品,具体涉及一种无溶剂涂料用可降解的聚合物多元醇及其合成方法。
背景技术
现有的PU涂料主要为水性聚氨酯涂料,水性聚氨酯涂料是以水代替有机溶剂作为分散介质的新型聚氨酯体系。具有无气味、无污染、易擦洗、防火防爆、安全可靠、机械性能优良的特点。水性聚氨酯对基材有着极高的附着力,固化的漆膜耐腐蚀性、耐化学性能优异,涂膜收缩率小、硬度高、耐磨性好、电气绝缘性能优异,具有极高的物理和耐化学性能。同时克服了油性地坪漆不透气的缺点,提供更为耐久的使用寿命和保护功能。现有的PU涂料通常由A组份的高分子原料的成分物料和B组份固化剂合成。而随着新技术的研发,无溶剂PU系列产品正在逐渐应用。无溶剂PU系列产品属于国家提倡的绿色环保产品,其中,无溶剂的PU涂料的成分物料成为研究重点,特别是其如何解决无溶剂涂料的施工粘度问题,而合成出低粘度可涂装施工的涂料成为研究要点。
发明内容
本发明目的是提供一种无溶剂涂料用可降解的聚合物多元醇及其合成方法,解决了无溶剂涂料的施工粘度问题,涂料即无需加入有机溶剂,又可方便涂刷施工。
为了实现以上目的,本发明采用的技术方案为:一种无溶剂涂料用可降解的聚合物多元醇,合成配方包括以下质量百分比:
(a)精制蓖麻油三甘油酯 40-45%
(b)季戊四醇 10-14%
(c)己内酯 44-48%
(d)氢氧化锂 0.02%(醇解助剂)
(e)1.4-丁二醇 2-3%。
一种无溶剂涂料用可降解的聚合物多元醇的合成工艺:
将(a)与(b)投入反应釜开启搅拌并加入(d),升温至220-230度,保温醇解反应2小时,冷却至200度加(c)、在此温度下保温酯化反应4小时,停止加温并冷却至50度加入(e),搅匀过滤出料,整个合成过程是在常压下进行,原材料均属非危化品,操作安全易控,无有毒有害付产物。
以上合成配方可根据用户要求随机微调以形成产品的系列化,如加入量少的(a)及相应的其他原料配比,该配比必须在上述质量比范围内,得到的无溶剂涂料用可降解的聚合物多元醇干性好;再如加入量多的(a)及相应的其他原料配比,该配比同样须在上述质量比范围内,得到的无溶剂涂料用可降解的聚合物多元醇则会光泽好。
本发明具有如下优点:本发明解决了无溶剂涂料的施工粘度问题,即合成出低粘度可涂装施工的涂料。改善了原有的聚合物多元醇的粘度及最终涂料成膜后的可降解性,并使得涂料即无需加入有机溶剂,又可方便涂刷施工。
具体实施方式
一种无溶剂涂料用可降解的聚合物多元醇,由下列成分按质量百分比配制而成:
(a)精制蓖麻油三甘油酯 40-45%
(b)季戊四醇 10-14%
(c)己内酯 44-48%
(d)氢氧化锂 0.02%
(e)1.4-丁二醇 2-3%。
一种无溶剂涂料用可降解的聚合物多元醇的合成方法,所述的无溶剂涂料用可降解的聚合物多元醇合成配方包括以下质量百分比:
(a)精制蓖麻油三甘油酯 40-45%
(b)季戊四醇 10-14%
(c)己内酯 44-48%
(d)氢氧化锂 0.02%
(e)1.4-丁二醇 2-3%;
将(a)与(b)投入反应釜开启搅拌并加入(d),升温至220-230度,保温醇解反应2小时,冷却至200度加(c)、在此温度下保温酯化反应4小时,停止加温并冷却至50度加入(e),搅匀过滤出料,整个合成过程是在常压下进行。
采用上述方案得到的无溶剂涂料用可降解的聚合物多元醇的技术指标:
羟值 200士50
固含量%。 99.5
成膜物质 100%
分子量 700士50
粘度(cps) 900士100
本发明产品的应用:该产品由于粘度较低,适用于高固含或无溶剂PU类涂料、粘合剂灌封、复合材料之用。且本发明产品已在不同领域如钢结构涂料、地坪涂料小范围应用。
下面是本发明的具体实施例:
实施例1:
采用无溶剂涂料用可降解的聚合物多元醇合成配方包括以下质量百分比:
(a)精制蓖麻油三甘油酯 40%
(b)季戊四醇 11%
(c)己内酯 46%
(d)氢氧化锂 0.02%
(e)1.4-丁二醇 2.98%;
将(a)与(b)投入反应釜开启搅拌并加入(d),升温至220度,保温醇解反应2小时,冷却至200度加(c)、在此温度下保温酯化反应4小时,停止加温并冷却至50度加入(e),搅匀过滤出料,整个合成过程是在常压下进行。
其技术指标:
羟值 198
固含量%。 99.5
成膜物质 100%
分子量 696
粘度(cps) 899。
实施例2:
采用无溶剂涂料用可降解的聚合物多元醇合成配方包括以下质量百分比:
(a)精制蓖麻油三甘油酯 43%
(b)季戊四醇 10%
(c)己内酯 44%
(d)氢氧化锂 0.02%
(e)1.4-丁二醇 2.98%;
将(a)与(b)投入反应釜开启搅拌并加入(d),升温至225度,保温醇解反应2小时,冷却至200度加(c)、在此温度下保温酯化反应4小时,停止加温并冷却至50度加入(e),搅匀过滤出料,整个合成过程是在常压下进行。
羟值 233
固含量%。 99.5
成膜物质 100%
分子量 722
粘度(cps) 939。
Claims (2)
1.一种无溶剂涂料用可降解的聚合物多元醇,其特征在于,由下列成分按质量百分比配制而成:
(a)精制蓖麻油三甘油酯 40-45%
(b)季戊四醇 10-14%
(c)己内酯 44-48%
(d)氢氧化锂 0.02%
(e)1.4-丁二醇 2-3%。
2.根据权利要求1所述的一种无溶剂涂料用可降解的聚合物多元醇的合成方法,其特征在于:所述的无溶剂涂料用可降解的聚合物多元醇合成配方包括以下质量百分比:
(a)精制蓖麻油三甘油酯 40-45%
(b)季戊四醇 10-14%
(c)己内酯 44-48%
(d)氢氧化锂 0.02%
(e)1.4-丁二醇 2-3%;
将(a)与(b)投入反应釜开启搅拌并加入(d),升温至220-230度,保温醇解反应2小时,冷却至200度加(c)、在此温度下保温酯化反应4小时,停止加温并冷却至50度加入(e),搅匀过滤出料,整个合成过程是在常压下进行。