CN109880446A - 一种水性pp、pe塑料涂料 - Google Patents
一种水性pp、pe塑料涂料 Download PDFInfo
- Publication number
- CN109880446A CN109880446A CN201910170102.0A CN201910170102A CN109880446A CN 109880446 A CN109880446 A CN 109880446A CN 201910170102 A CN201910170102 A CN 201910170102A CN 109880446 A CN109880446 A CN 109880446A
- Authority
- CN
- China
- Prior art keywords
- parts
- aqueous
- agent
- plastic paint
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性PP、PE塑料涂料，通过添加纳米碳酸钙、超细滑石粉、纳米二氧化硅、硅酸铝、硫酸钡、钛白粉、磷酸锌与附着力促进剂及硅烷偶联剂作用，可有效增强与水性氯化聚烯烃树脂、水性丙烯酸树脂、水性聚氨酯分散体的结合力强，不仅具有很好的防水性能，且制品密度高，硬度大；流平剂、抗菌剂、消泡剂、防霉剂、润湿剂混合作用，可提高涂料的沉降性、触变性及耐刷性，涂膜表面光滑且不易开裂。
Description
技术领域
本发明属于复合涂料技术领域，尤其涉及一种时硬度大，附着力强的水性PP、PE塑料涂料。
背景技术
随着现代工业的飞速发展，塑料广泛应用于汽车、摩托车、家用电器、水暖器材、小装饰品、化妆品包装、旋钮等轻工产品的各个方面。为了装饰美化和保护塑料表面，往往还要在其表面涂刷一层装饰性涂料，但由于塑料表面密度较高，一般涂料不能很好的粘贴在塑料的表面，所以待涂膜干燥时，涂层附着力差，轻轻一撕就会撕掉整张，如何制备一种塑料用具有超强附着力且硬度高的涂料成为目前需要解决的技术问题。
发明内容
本发明所要解决的技术问题是，能很好的粘附塑料的表面，同时硬度大，附着力强的水性PP、PE塑料涂料。
为解决上述问题，本实发明的技术方案是：一种水性PP、PE塑料涂料，按重量份包括水性氯化聚烯烃树脂20-40份，水性丙烯酸树脂20-40份，水性聚氨酯分散体15-30份， 硅烷偶联剂2-5份，纳米碳酸钙20-40份，超细滑石粉5-10份，纳米二氧化硅 10-20份，硅酸铝5-15份，硫酸钡1-6份，钛白粉1-3份，磷酸锌1-4份，附着力促进剂1-4份，二甲基乙醇胺0.5-2.5份，流平剂1-2份，抗菌剂1-2份，消泡剂1-2份，防霉剂1-2份，润湿剂1-2份。
进一步的，所述水性丙烯酸树脂固含量为65-75％。
进一步的，所述水性丙烯酸树脂固粒的粒径为20-40nm。
进一步的，所述附着力促进剂按重量份将50-100份氯苯、5-10 份醋酸丁酯、1-3份环己酮、20-40份氯化丙烯酸树脂、5-10份氯化聚丙烯树脂、 1-4份马来酸酐混合搅拌，首先40-50℃搅拌20-40min，升温至65-70℃继续搅 拌10-20min，降温至30-36℃静置保温20-50min。
本发明的有益效果：通过水性氯化聚烯烃树脂、水性丙烯酸树脂、水性聚氨酯分散体协同作用制备的涂料，使得涂膜的各性能指标与油性类相当，同时与二甲基乙醇胺作用，可有效提高漆膜的硬度与附着力。
由于采用水作为稀释溶剂，有效降低了有害溶剂的释放，进一步通过合理控制水性丙烯酸树脂的固含量与粒径。
通过添加纳米碳酸钙、超细滑石粉、纳米二氧化硅、硅酸铝、硫酸钡、钛白粉、磷酸锌与附着力促进 剂及硅烷偶联剂作用，可有效增强与水性氯化聚烯烃树脂、水性丙烯酸树脂、 水性聚氨酯分散体的结合力强，不仅具有很好的防水性能，且制品密度高，硬度大；流平剂、抗菌剂、消泡剂、防霉剂、润湿剂混合作用，可提高涂料的沉 降性、触变性及耐刷性，涂膜表面光滑且不易开裂。
具体实施方式
下面结合具体的实施例对本发明作进一步的阐述。
实施例一
一种水性PP、PE塑料涂料，其原料按重量份包括水性氯化聚 烯烃树脂20-40份，水性丙烯酸树脂20-40份，水性聚氨酯分散体15-30份， 硅烷偶联剂2-5份，纳米碳酸钙20-40份，超细滑石粉5-10份，纳米二氧化硅 10-20份，硅酸铝5-15份，硫酸钡1-6份，钛白粉1-3份，磷酸锌1-4份，附 着力促进剂1-4份，二甲基乙醇胺0.5-2.5份，流平剂1-2份，抗菌剂1-2份， 消泡剂1-2份，防霉剂1-2份，润湿剂1-2份。
优选地，水性丙烯酸树脂固含量为65-75％，粒径为20-40nm。
优选地，水性聚氨酯分散体采用如下工艺制备：将异佛尔酮二异氰酸酯、甲基丙二醇、二羟甲基丙酸和丙酮混合均匀后得到预聚物，将该预聚物分散于去离子水中，再加入二甲基乙醇胺发生扩链反应，从而制备得到所需水性聚氨酯分散体。并采用上述工艺制备水性聚氨酯分散体，制品的硬度及附着力极好。
优选地，附着力促进剂采用如下工艺制备：按重量份将50-100份氯苯、5-10 份醋酸丁酯、1-3份环己酮、20-40份氯化丙烯酸树脂、5-10份氯化聚丙烯树脂、 1-4份马来酸酐混合搅拌，首先40-50℃搅拌20-40min，升温至65-70℃继续搅 拌10-20min，降温至30-36℃静置保温20-50min，得到附着力促进剂。采用上述工艺制备的附着力促进剂可有效改变塑料表面的密度，有效粘结塑料表面与涂料，即使在强烈震动下涂膜也不会剥落。
实施例二
一种水性PP、PE塑料涂料，其原料按重量份包括水性氯化聚烯烃树脂30-36份，水性丙烯酸 树脂30-35份，水性聚氨酯分散体20-25份，硅烷偶联剂3-4.5份，纳米碳酸 钙30-34份，超细滑石粉6-8份，纳米二氧化硅14-17份，硅酸铝10-13份， 硫酸钡2-4份，钛白粉1.5-2份，磷酸锌2-3份，附着力促进剂2-2.6份，二 甲基乙醇胺2-2.3份，流平剂1.2-1.5份，抗菌剂1.6-1.8份，消泡剂1.2-1.5 份，防霉剂1.5-1.8份，润湿剂1.4-1.8份。
本领域的普通技术人员将会意识到，这里所述的实施例是为了帮助读者理解本发明的原理，应被理解为本发明的保护范围并不局限于这样的特别陈述和实施例。本领域的普通技术人员可以根据本发明公开的这些技术启示做出各种不脱离本发明实质的其它各种具体变形和组合，这些变形和组合仍然在本发明的保护范围内。
Claims (4)
1.一种水性PP、PE塑料涂料，其特征在于：按重量份包括水性氯化聚烯烃树脂20-40份，水性丙烯酸树脂20-40份，水性聚氨酯分散体15-30份， 硅烷偶联剂2-5份，纳米碳酸钙20-40份，超细滑石粉5-10份，纳米二氧化硅 10-20份，硅酸铝5-15份，硫酸钡1-6份，钛白粉1-3份，磷酸锌1-4份，附着力促进剂1-4份，二甲基乙醇胺0.5-2.5份，流平剂1-2份，抗菌剂1-2份，消泡剂1-2份，防霉剂1-2份，润湿剂1-2份。
2.根据权利要求1所述的一种水性PP、PE塑料涂料，其特征在于：所述水性丙烯酸树脂固含量为65-75％。
3.根据权利要求1或2所述的一种水性PP、PE塑料涂料，其特征在于：所述水性丙烯酸树脂固粒的粒径为20-40nm。
4.根据权利要求1所述的一种水性PP、PE塑料涂料，其特征在于：所述附着力促进剂按重量份将50-100份氯苯、5-10 份醋酸丁酯、1-3份环己酮、20-40份氯化丙烯酸树脂、5-10份氯化聚丙烯树脂、 1-4份马来酸酐混合搅拌，首先40-50℃搅拌20-40min，升温至65-70℃继续搅 拌10-20min，降温至30-36℃静置保温20-50min。