CN109811441A - A kind of flame-proof antibiotic is warming to make instruction fabric and its preparation process - Google Patents
A kind of flame-proof antibiotic is warming to make instruction fabric and its preparation process Download PDFInfo
- Publication number
- CN109811441A CN109811441A CN201910146166.7A CN201910146166A CN109811441A CN 109811441 A CN109811441 A CN 109811441A CN 201910146166 A CN201910146166 A CN 201910146166A CN 109811441 A CN109811441 A CN 109811441A
- Authority
- CN
- China
- Prior art keywords
- processing
- polyimides
- flame
- fabric
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of flame-proof antibiotic is warming to make instruction fabric and its preparation process, it is related to new material, high molecular material, the preparation of new functional macromolecule material and applied technical field.It by blended 28 Siro-spinnings of ternary and at doublet cord as warp thread and weft yarn, it the organization design of bonded fabric and is formed by weaving using purpose, the blended 28 Siro-spinning raw materials of ternary are polyimides, high-strength fire-retarding polyvinyl and flame retardant viscose fiber, the proportion of raw material of blended 28 Siro-spinnings of ternary are as follows: polyimides/high-strength fire-retarding polyvinyl/flame retardant viscose fiber=20/35/45.The invention has the following beneficial effects: polyimides, high strength vinylon can play basic twisting action using limited situation because intensity is low to domestic anti-flaming viscose.Polyimides, high strength vinylon and the collocation of domestic anti-flaming viscose are used, product strength can be greatly improved while optimizing flame retardant effect, will also enhance protection effect, and prolong the service life.
Description
Technical field
The present invention relates to new material, high molecular material, the preparation of new functional macromolecule material and applied technical field, tools
Body is related to that a kind of flame-proof antibiotic is warming to make instruction fabric and its preparation process.
Background technique
Certain novel training clothes quality index is as follows: grammes per square metre≤180g/m2;Tension failure: through to >=1400N, broadwise >=
1000N, tearing resistance: through to >=150N, broadwise >=100N.It is fire-retardant: after flame time≤2S, smoldering time≤2S, char length
≤ 100mm, air penetrability >=300mm/s, rate of perviousness >=10000g/m2.d, antibacterial initially >=90%, wash 50 times >=80%.Original work
It is as follows that instruction takes quality index: grammes per square metre≤180g/m2;Tension failure: through to >=650N, broadwise >=550N, tearing resistance: through to
>=100N, broadwise >=70N, antibacterial initially >=90%, wash 20 times >=80%.In former training clothes quality index to ultimate strength, tear
Broken strength index request is not high, and each quality index can be completed after high temperature bakes after addition finishing functions liquid when passing through final finishing.
Former training clothes poor flame retardant properties, not wash resistant, fracture, wear-resisting property, moisture permeability are undesirable.
Ultimate strength, tearing brute force standard are substantially improved in novel training clothes quality index, fire-retardant in current art, antibacterial
The realization of function generally passes through final finishing padding finishing liquid, and high temperature, which bakes, to be realized, but this ultimate strength, tearing brute force to fabric
Damage larger, finishing functions are difficult to meet the requirement of strength index.And final finishing finishing functions are not wash resistant, fire-retardant, antibacterial function
Energy persistence is not strong.
Summary of the invention
Make instruction fabric in view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of flame-proof antibiotic is warming
And its preparation process, polyimides, high strength vinylon can play root using limited situation due to intensity is low to domestic anti-flaming viscose
This twisting action.Polyimides, high strength vinylon and the collocation of domestic anti-flaming viscose are used, it can be in the same of optimization flame retardant effect
When, product strength is greatly improved, will also enhance protection effect, and prolong the service life.
To achieve the above object, the present invention is using following technical scheme: one kind is fire-retardant, antibacterial, keeps warm and makees instruction fabric, it
By blended 28 Siro-spinnings of ternary and at doublet cord as warp thread and weft yarn, the organization design of bonded fabric and use purpose
It is formed by weaving, the blended 28 Siro-spinning raw materials of ternary are polyimides, high-strength fire-retarding polyvinyl and flame retardant viscose fiber, institute
State the proportion of raw material of blended 28 Siro-spinnings of ternary are as follows: polyimides/high-strength fire-retarding polyvinyl/flame retardant viscose fiber=20/
35/45。
A kind of fire-retardant, antibacterial, the warming preparation process for making instruction fabric, it is comprised the steps of:
Step 1: polyimides and flame retardant viscose fiber are first mixed pre-drawing processing, then again by high-strength fire-retarding polyvinyl cotton carding
Processing；
Step 2: again by the pre-drawing of polyimides, anti-flaming viscose obtained in step 1 and the high-strength resistance handled by cotton carding
It fires polyvinyl and carries out mix spinning；Easily kink forms handle yarn when to solve resultant yarn unwinding, guarantees that later process smoothly produces, right
Resultant yarn and and at strand vacuumize the wet dead twist of heat and handle；
Step 3: the mix spinning Savio winder in step 2 is carried out doff processing；
Step 4: the spinning for passing through doff processing in step 3 is carried out warping processing by Benniger warping machine；
Step 5: by sizing processing is carried out by Benniger Ze Er sizing machine by whole processed spinning in step 4；
Step 6: the spinning of sizing processing will be passed through in step 5 by the weaving molding of saliva field coltfoal ZAX-N air-jet loom；
Step 7: the molding textile finishing sizing that will weave in step 6；
Step 8: the fabric for arranging sizing in step 7 to be tested for the property and analyze；
Step 9: Properties Testing qualification in step 8, as a kind of fire-retardant, antibacterial keep warm and make instruction fabric.
Polyimides and flame retardant viscose fiber pre-drawing processing process in the step 1 is as follows:
The processing of A1, FA006C griping cotton machine；
The processing of A2, FA113B opener；
The processing of six storehouse cotton blender machine of A3, FA2008C；
The processing of A4, JWF1124 scutcher；
The processing of A5, FA151 dust removal machine；
The processing of A6, FA177B hopper；
The processing of A7, FA221D carding machine；
The processing of A8, FA311 drawing frame；
A9, the pre-drawing for obtaining polyimides, anti-flaming viscose.
High-strength fire-retarding polyvinyl cotton carding processing process flow in the step 1 is as follows:
The processing of B1, FA006C griping cotton machine；
The processing of B2, FA113B opener；
The processing of six storehouse cotton blender machine of B3, FA2008C；
The processing of B4, JWF1124 scutcher；
The processing of B5, FA151 dust removal machine；
The processing of B6, FA177B hopper；
The processing of B7, FA221D carding machine.
Mix spinning processing process in the step 2 is as follows:
The mixing of C1, FA311F drawing frame is handled together；
C2, FA311F drawing frame mixing two is simultaneously handled；
C3, FA320A drawing frame mixing three is simultaneously handled；
The processing of C4, FA457 fly frame；
The processing of C5, FA506 spinning frame.
After adopting the above technical scheme, the invention has the following beneficial effects: each composition material of fabric is fire proofing, no matter
How many times are washed, anti-flammability is all had.Because having lacked damage of the high temperature baking to strength without rear road flame-proof treatment, fabric
Ultimate strength, tearing brute force are guaranteed.
Material itself has antibiotic property, is not necessarily to antibiotic finish, therefore does not fear washing, and anti-microbial property has persistence.Original work instruction
Clothes use cotton, polyamide fibre for main component, and warmth retention property, comfort are much worse than the design.This product is without the complexity such as fire-retardant, antibacterial
Final finishing reduces pollution of the dyeing process to environment.
Polyimides, high strength vinylon can play basic torsion using limited situation because intensity is low to domestic anti-flaming viscose
Transfer to use.Polyimides, high strength vinylon and the collocation of domestic anti-flaming viscose are used, it can be while optimizing flame retardant effect, substantially
Product strength is improved, will also enhance protection effect, and prolong the service life.
Specific embodiment
Present embodiment the technical solution adopted is that: a kind of fire-retardant, antibacterial, it is warming make instruction fabric, it is mixed by ternary
Spin 28 Siro-spinnings and at doublet cord as warp thread and weft yarn, the organization design of bonded fabric and using purpose weaving and
At the blended 28 Siro-spinning raw materials of ternary are polyimides, high-strength fire-retarding polyvinyl and flame retardant viscose fiber, the ternary
The proportion of raw material of blended 28 Siro-spinnings are as follows: polyimides/high-strength fire-retarding polyvinyl/flame retardant viscose fiber=20/35/45.
A kind of fire-retardant, antibacterial, the warming preparation process for making instruction fabric, it is comprised the steps of:
Step 1: it is easy to produce static electricity in polyimides, anti-flaming viscose and vinylon fibre production process, it is existing around roller, rubber roller, cushion rubber
As, for the spinnability for improving fiber, a certain proportion of antistatic agent is added before manufacture and is pre-processed, the spray of antistatic lotion
The amount of spilling accounts for the 8% of proportion of fibers；Polyimides and flame retardant viscose fiber are first mixed into pre-drawing processing, then again by high-strength fire-retarding
The processing of polyvinyl cotton carding；
Step 2: again by the pre-drawing of polyimides, anti-flaming viscose obtained in step 1 and the high-strength resistance handled by cotton carding
It fires polyvinyl and carries out mix spinning；Easily kink forms handle yarn when to solve resultant yarn unwinding, guarantees that later process smoothly produces, right
Resultant yarn and and at strand vacuumize the wet dead twist of heat and handle；
Step 3: the mix spinning Savio winder in step 2 is carried out doff processing；It is adopted to reduce electrostatic and filoplume, winder
With metal drum, winder, speed of beaming suitably slows down is advisable；
Step 4: the spinning for passing through doff processing in step 3 is carried out warping processing by Benniger warping machine；
Step 5: by sizing processing is carried out by Benniger Ze Er sizing machine by whole processed spinning in step 4；For hair
Wave excellent fire-retardant, the anti-microbial property of polyimides, anti-flaming viscose, flame vinylon fiber, it is ensured that final finishing can desizing take off only,
Sizing starching cannot use PVA chemical sizwe, use the potato slurry of the easy desizing of high-performance, upper grout, wet setting technique；
Step 6: the spinning of sizing processing will be passed through in step 5 by the weaving molding of saliva field coltfoal ZAX-N air-jet loom；
Step 7: the molding textile finishing sizing that will weave in step 6；
Step 8: the fabric for arranging sizing in step 7 to be tested for the property and analyze；
Step 9: Properties Testing qualification in step 8, as a kind of fire-retardant, antibacterial keep warm and make instruction fabric.
Polyimides and flame retardant viscose fiber pre-drawing processing process in the step 1 is as follows:
The processing of A1, FA006C griping cotton machine；
The processing of A2, FA113B opener；
The processing of six storehouse cotton blender machine of A3, FA2008C；
The processing of A4, JWF1124 scutcher；To reduce electrostatic, in scutching cotton process, relative humidity is controlled in 60%-65%；
The processing of A5, FA151 dust removal machine；
The processing of A6, FA177B hopper；
The processing of A7, FA221D carding machine；
The processing of A8, FA311 drawing frame；
A9, the pre-drawing for obtaining polyimides, anti-flaming viscose.
High-strength fire-retarding polyvinyl cotton carding processing process flow in the step 1 is as follows:
The processing of B1, FA006C griping cotton machine；
The processing of B2, FA113B opener；
The processing of six storehouse cotton blender machine of B3, FA2008C；
The processing of B4, JWF1124 scutcher；To reduce electrostatic, in scutching cotton process, relative humidity is controlled in 60%-65%；
The processing of B5, FA151 dust removal machine；
The processing of B6, FA177B hopper；
The processing of B7, FA221D carding machine；For reduce fiber damage, avoid the carded sliver from blocking up horn mouth, using big gauge, small noil,
Sufficiently transfer, appropriate to comb, gently quantitative technological principle, appropriate to reduce licker-in and cylinder speed.
Mix spinning processing process in the step 2 is as follows:
The mixing of C1, FA311F drawing frame is handled together；
C2, FA311F drawing frame mixing two is simultaneously handled；
C3, FA320A drawing frame mixing three is simultaneously handled；The drafting force that polyimides, anti-flaming viscose, vinylon fibre need is larger, and
It is easy to produce static electricity, for the extended parallelization and separating degree for improving fiber, therefore mixing in doubling step using jogging speed, big gauge, it is light quantitative,
The technological principle pressurizeed again；
The processing of C4, FA457 fly frame；To reduce viscous volume, installs rove device additional, and increase the pressure of calender roller, used after coiled
Plastic film cladding prevents moisture and finish from volatilizing；
The processing of C5, FA506 spinning frame；It is horizontal in order to improve resultant yarn strand and filoplume, using the spinning system of SEILE textile.
It is continuously increased with the progress of material and technology and raising.During the update of protective garment,
The development of textile fabric plays positive impetus.Fibrous raw material develops to differential, functionalization and high performance.This hair
The fire-retardant of bright exploitation, antibacterial, thermal fabric fabric using 20% polyimides, 50% high-strength fire-retarding polyvinyl, 30% it is fire-retardant viscous
Glue.
Polyimides is one of optimal high-molecular organic material of comprehensive performance, and high temperature resistant is used for a long time up to 400 DEG C or more
Temperature range -200~300 DEG C, partially without sharp melting point.The maximum fire-retardant feature of the fiber is to meet the carbonization of high temperature open fire not melt
Drop, it is almost smokeless non-toxic.Imide fiber has excellent flame retardant property, and limit oxygen index LOI is higher than 38%, fibrous fracture
Intensity 3.5CN/dtex, LOI are higher than 30%, and fibrous fracture intensity 1.8CN/dtex, limit oxygen index LOI are higher than 21%, and fiber is disconnected
Resistance to spalling 7.97CN/dte.Polyimides is efficient thermal insulation material, and thermal property is protected better than the tradition such as cotton, wool, natural feather, silk
Warm material, and bedding and clothing weight saving 40% or so can be made.Polyimides has natural lasting antibacterial action.To golden yellow grape
Coccus antibiotic rate is 71%, colibacillus rate 76%.
Anti-flaming viscose is soft, smooth, permanent fire retardant, breathes freely, moisture-inhibiting.
Introduce fire-retardant high-strength polyvinyl, it is ensured that ultimate strength, the tearing brute force of fabric are guaranteed.
Concrete specification of the invention are as follows: 59/60 ", polyimides/polyvinyl/viscose glue (20/35/45), (28/2*28/2),
61*50,2/1, camouflage printing series.
Three kinds of fibers have complementary advantages, and give full play to the characteristic and synergistic effect of each fiber, are better than the inside and outside index of product
Former training clothes.Novel each index of training clothes is as follows through authoritative institution's testing result: ultimate strength: through to 1680N, broadwise
1200N；Tearing resistance: through to 198N, broadwise >=160N char length: 30*32mm;Air penetrability: 273mm/s, vapor transfer rate
11810g/m2d. drips diffusion≤5；Fire-retardant, anti-microbial property is superior to national standard after tested.
After adopting the above technical scheme, the invention has the following beneficial effects: each composition material of fabric is fire proofing, no matter
How many times are washed, anti-flammability is all had.Because having lacked damage of the high temperature baking to strength without rear road flame-proof treatment, fabric
Ultimate strength, tearing brute force are guaranteed.
Material itself has antibiotic property, is not necessarily to antibiotic finish, therefore does not fear washing, and anti-microbial property has persistence.Original work instruction
Clothes use cotton, polyamide fibre for main component, and warmth retention property, comfort are much worse than the design.This product is without the complexity such as fire-retardant, antibacterial
Final finishing reduces pollution of the dyeing process to environment.
Polyimides, high strength vinylon can play basic torsion using limited situation because intensity is low to domestic anti-flaming viscose
Transfer to use.Polyimides, high strength vinylon and the collocation of domestic anti-flaming viscose are used, it can be while optimizing flame retardant effect, substantially
Product strength is improved, will also enhance protection effect, and prolong the service life.
The above is only used to illustrate the technical scheme of the present invention and not to limit it, and those of ordinary skill in the art are to this hair
The other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (5)
1. a kind of flame-proof antibiotic is warming to make instruction fabric, which is characterized in that it by blended 28 Siro-spinnings of ternary and at it is bifilar
Line the organization design of bonded fabric and is formed by weaving, blended 28 SEILE textiles of ternary as warp thread and weft yarn using purpose
Yarn raw material is polyimides, high-strength fire-retarding polyvinyl and flame retardant viscose fiber, the raw material of blended 28 Siro-spinnings of ternary
Ratio are as follows: polyimides/high-strength fire-retarding polyvinyl/flame retardant viscose fiber=20/35/45.
2. a kind of warming preparation process for making instruction fabric of flame-proof antibiotic, which is characterized in that it is comprised the steps of:
Step 1: polyimides and flame retardant viscose fiber are first mixed pre-drawing processing, then again by high-strength fire-retarding polyvinyl cotton carding
Processing；
Step 2: again by the pre-drawing of polyimides, anti-flaming viscose obtained in step 1 and the high-strength resistance handled by cotton carding
It fires polyvinyl and carries out mix spinning；Easily kink forms handle yarn when to solve resultant yarn unwinding, guarantees that later process smoothly produces, right
Resultant yarn and and at strand vacuumize the wet dead twist of heat and handle；
Step 3: the mix spinning Savio winder in step 2 is carried out doff processing；
Step 4: the spinning for passing through doff processing in step 3 is carried out warping processing by Benniger warping machine；
Step 5: by sizing processing is carried out by Benniger Ze Er sizing machine by whole processed spinning in step 4；
Step 6: the spinning of sizing processing will be passed through in step 5 by the weaving molding of saliva field coltfoal ZAX-N air-jet loom；
Step 7: the molding textile finishing sizing that will weave in step 6；
Step 8: the fabric for arranging sizing in step 7 to be tested for the property and analyze；
Step 9: Properties Testing qualification in step 8, as a kind of fire-retardant, antibacterial keep warm and make instruction fabric.
3. a kind of warming preparation process for making instruction fabric of flame-proof antibiotic according to claim 2, which is characterized in that the step
Polyimides and flame retardant viscose fiber pre-drawing processing process in rapid one is as follows:
The processing of A1, FA006C griping cotton machine；
The processing of A2, FA113B opener；
The processing of six storehouse cotton blender machine of A3, FA2008C；
The processing of A4, JWF1124 scutcher；
The processing of A5, FA151 dust removal machine；
The processing of A6, FA177B hopper；
The processing of A7, FA221D carding machine；
The processing of A8, FA311 drawing frame；
A9, the pre-drawing for obtaining polyimides, anti-flaming viscose.
4. a kind of warming preparation process for making instruction fabric of flame-proof antibiotic according to claim 2, which is characterized in that the step
High-strength fire-retarding polyvinyl cotton carding processing process flow in rapid one is as follows:
The processing of B1, FA006C griping cotton machine；
The processing of B2, FA113B opener；
The processing of six storehouse cotton blender machine of B3, FA2008C；
The processing of B4, JWF1124 scutcher；
The processing of B5, FA151 dust removal machine；
The processing of B6, FA177B hopper；
The processing of B7, FA221D carding machine.
5. a kind of warming preparation process for making instruction fabric of flame-proof antibiotic according to claim 2, which is characterized in that the step
Mix spinning processing process in rapid two is as follows:
The mixing of C1, FA311F drawing frame is handled together；
C2, FA311F drawing frame mixing two is simultaneously handled；
C3, FA320A drawing frame mixing three is simultaneously handled；
The processing of C4, FA457 fly frame；
The processing of C5, FA506 spinning frame.